Highly Accelerated Testing of Capacitors for Medical Applications Travis Ashburn, Dan Skamser KEMET Electronics Simpsonville, SC, USA [email protected], [email protected] ABSTRACT As the market for medical devices continues to grow and expand, it has become evident that product reliability must remain a top priority for medical device manufacturers. In order to guarantee reliability, device manufacturers must choose reliable medical-grade components for their highreliability applications. Reliability for passive components, especially capacitors, is typically conducted through accelerated and highly accelerated life testing (HALT). Models are used to fit the distributions of insulation resistance to provide prediction capability for lifetime estimates. Risk is minimized by correctly rating the capability (temperature and voltage) of capacitors based on the models. In this paper, Models and Time-to-Failure (TTF) predictions at application conditions for the widely used X7R and C0G ceramic capacitors will be discussed. INTRODUCTION The Medical Device market, much like the general electronics market, is continuously pushing for greater functionality while desiring to minimize board space. This technology trend is generally known in the industry as “Moore’s Law” and ceramic capacitor technology has continued to keep pace with this trend in miniaturization. Figure 1 illustrates the ever-increasing volumetric efficiency and available capacitance values for the EIA 0603 Class II 6.3V rated MLCC. Figure 1 Projected Capacitance Over Time (0603 Class II Max Cap) 1.E+03 1.E+06 175 49 93 329 1.E+05 22 10 10 4.7 1.E+01 1.E+04 2.2 1 1.E+00 0.22 0.33 0.47 1.E+03 VE (uF/cm3) Capacitance (uF) 1.E+02 0.1 0.047 1.E-01 1.E+02 0.022 0.01 1.E-02 2010 2009 2008 2007 2006 2005 2004 2003 2002 2001 2000 1999 1998 1997 1996 1995 1994 1.E+01 In the 90’s, capacitor technology shifted from Precious Metal Electrode (PME) technology to Base Metal Electrode (BME) technology. BME capacitor technology primarily utilizes nickel in the electrode system whereas PME technology utilizes a palladium-silver alloy electrode system. One of the primary advantages of using BME technology is the increased voltage stress capability over traditional PME dielectrics. The increase in voltage stress capability allows for the reduction of dielectric thickness without sacrificing voltage robustness. Figure 2 illustrates the formula for capacitance and volumetric efficiency of a ceramic capacitor. BME technology enables reduced dielectric thickness, increases in the number of active layers, and increases in the total active area. All of these improving variables significantly contribute to the increased capacitance and volumetric efficiency of ceramic capacitors over time. In keeping pace with the trend in Ceramic capacitor technology, KEMET has recently introduced two high-capacitance C0G and X7R platforms. Figure 2 C a p a c ita n c e a n d V o lu m e tric E ffic ie n c y E q u a tio n s T e r m in a tio n E le c tr o d e s C = C e ra m ic D ie le c tric + C a p a c ita n c e s in p a ra lle l a re a d d itiv e e oK A n t , VE = C V ~ e oK t2 C = C a p a c ita n c e V E = V o lu m e tric E ffic ie n c y V = v o lu m e e o = 8 .8 5 4 x 1 0 - 1 2 F / m K = D ie le c tric C o n sta n t A = O v e rla p A re a p e r a c tiv e n = N u m b e r o f a c tiv e s t = C e ra m ic T h ic k n e ss C T = C 1 + C 2 + C 3 + … .C n The EIA specification for X7R dielectrics requires that the capacitance variation from the room temperature (ΔC/C) should be within ±15% over the temperature range of -55°C to 125°C. Due to the need for high capacitance with such a controlled temperature variation of capacitance, the X7R dielectrics are based on barium titanate, BaTiO3. Several studies have discussed various aspects of microstructure and properties of X7R Multilayer Ceramic Capacitors (MLCC) [1-4]. Several dopants and additives are added to the barium titanate to achieve the desired capacitance characteristics along with high reliability under bias and temperature conditions. Typical dielectric constants (K) are in the range of 2700 to 3200. In the base metal electrode (BME, usually Ni electrodes) X7R systems, the common dopants and additives include oxides of manganese, alkaline earth elements (Ca, Mg, etc.), rare earth elements, and suitable sintering aids. These additives also play an important role of making the dielectric resistant toward reduction under the H2/N2/H2O atmosphere used during thermal processing of BME MLCC. SMTA Medical Electronics Symposium – Anaheim, California – 2008 There are several key factors involved in achieving high reliability in the X7R dielectric. These include: 1. 2. 3. 4. 5. 6. Choosing a barium titanate a. high purity b. high crystallinity c. controlled particle size d. controlled surface area Making a uniform coating of the dielectric Controlling microstructure Optimizing dopants & additives Controlling atmospheric conditions during thermal processing Ensuring a robust end termination process During the past decade, considerable amounts of research and development efforts have been expended at KEMET and other manufacturers to optimize these and many other parameters to make robust X7R MLCC products. In applications where capacitance needs to be precisely controlled over a wide temperature range, such as digital tuning and timing, the C0G dielectric is an optimum choice in a MLCC. The EIA specification for C0G dielectric is that the capacitance variation from room temperature (25°C) should be within 0±30 ppm/°C over the temperature range of -55°C to 125°C. Traditional C0G dielectric materials for precious metal electrodes (PME, such as Pd or Ag/Pd) are typically based on the barium neodymium titanate (BNT). The base metal electrode C0G dielectrics (BME, primarily Ni electrode) are CaZrO3-based materials with a dielectric constant (K) of ~31. Compared with PME C0G dielectric, these BME C0G dielectric systems have the additional benefit that they can offer much higher insulation resistance and better reliability (based on HALT and Life Test), and higher Q factor even at thinner dielectric thickness [5-7]. With the recent breakthroughs in coating thin dielectric layers (as thin as ~1 µm) and the capability of stacking hundreds of dielectric layers in BME technology, the volumetric efficiencies of BME C0G MLCCs are increasing significantly. Capacitance values of 1µF will soon be possible in a case size of 2824, along with a 0.68µF in a 2220. The CaZrO3-based dielectric with manganese additive is highly reduction-resistant under the H2/N2/H2O atmosphere used during the thermal processing of MLCCs consisting of Ni-electrodes. As discussed later in this paper, the BME-C0G system demonstrates excellent reliability characteristics at 125°C as well as 150°C. This paper examines two leading-edge BME C0G and X7R dielectric systems. The HALT testing performed is used to characterize the reliability of the capacitor behavior at accelerated conditions and then in turn used to extrapolate the reliability of the capacitor at typical use conditions. The Prokopowicz and Vaskas (P-V) [8] empirical equation is employed to correlate the reliability behavior at accelerated test conditions to operating conditions. Equation 1 depicts the P-V formula. Eq. 1 n ⎡E t1 ⎛ V2 ⎞ = ⎜⎜ ⎟⎟ exp ⎢ a t 2 ⎝ V1 ⎠ ⎢⎣ k ⎛ 1 1 ⎞⎟⎤ ⎜ − ⎥ ⎜ T1 ⎟⎥ T 2 abs ⎠ ⎦ ⎝ abs ti = time to failure under conditions i Vi = voltage under condition i n = voltage stress exponential Ea = activation energy for dielectric wear out k = Boltzmann’s constant (8.62E-5 eV/K) Ti = absolute temperature for condition i The P-V model has been used extensively in experiments and studies on ceramic capacitor reliability [9-12]. Because there are differences in voltage coefficients and activation energies, it is important to characterize each dielectric system across a range of dielectric thickness values and case sizes. This particular study will examine EIA case sizes 0402, 0603, 1206, and 1210 and voltage ratings of 16V, 25V, 50V, and 100V. These voltage ratings and case sizes are commonly used in the electronics industry. Capacitance values range from 1000pF up to 1.0µF depending on dielectric system and case size. Table 1 depicts a summary of the values studied. Table 1 Dielectric Case Size Voltage Rating X7R 0402 16V X7R 0603 50V X7R 1210 100V C0G 0402 25V C0G 0603 100V C0G 1206 25V Capacitance 0.1µF 0.1µF 1.0µF 0.001µF 0.0047µF 0.1µF General capacitor design characteristics for the capacitors selected are illustrated in Table 2. Table 2 Part Description C0G 0402 1nF 25V C0G 0603 4.7nF 100V C0G 1206 100nF 25V X7R 0402 100nF 16V X7R 0603 100nF 50V X7R 1210 1.0µF 100V Breakdown Dielectric Electrode Voltage Mean Thickness Thickness (µm) (µm) (V) 750 860 650 430 600 590 2.7 3.9 2.7 3.2 5.1 10.4 1.2 1.2 1.2 1.2 1.2 1.2 Active Layers Fired Margins (in) Active Area (in^2) K Value Grain Size (µm) 59 115 349 66 45 105 0.005 0.006 0.008 0.005 0.006 0.008 0.0276 0.0484 0.1041 0.0276 0.0476 0.1005 30 30 30 2800 2800 2800 0.8 to 1.2 0.8 to 1.2 0.8 to 1.2 0.4 to 0.6 0.4 to 0.6 0.4 to 0.6 EXPERIMENTAL METHODOLOGY It is assumed the mechanism for failure is both thermal and voltage activated following the empirical P-V model. This P-V equation can be simplified to a single function of time. Eq. 2 t = A V-n exp[Ea/k T-1] A = time constant (min) This simplified equation can be rewritten in a form that is more useful for experimental modeling by taking the natural log. SMTA Medical Electronics Symposium – Anaheim, California – 2008 Eq. 3 Ln(t) = Ln(A) – n Ln(V) + Ea/k T -1 Typically the time (t) used for reliability modeling is the median time to failure, MTTF or t50. Experimental HALT runs are completed to determine MTTF at various combinations of temperature and voltage to map out the model space. The Ln(MTTF) data is fit to the P-V model using a multiple regression computation with predictors Ln(V1) and T-1. Thus the model coefficients of time constant (A), voltage exponent (n) and the activation energy (Ea) are determined. These coefficients are substituted into the P-V equation to estimate time to failure for selected temperature and voltage levels. In addition to determining the MTTF at selected temperatures and voltages, it is desirable to predict the failures-in-time (FIT) based on the P-V model. The FIT model is used to predict failure rates at different operating conditions based on known application conditions. Eq. 4 η ⎛ ⎞⎛ VUse ⎞ # Failures Life ⎟⎜ ⎟ FIT = ⎜ ⎜ # Samples *# Hours ⎟⎜ V ⎟ Life Life ⎠⎝ Life ⎠ ⎝ ⎛ Ea *⎛⎜ 1 − 1 ⎞⎟ ⎞ ⎜ k ⎝⎜ TLife + 273.3 TUse + 273.3 ⎠⎟ ⎟ 9 ⎜e ⎟ ⋅ (1x10 ) ⎜ ⎟ ⎝ ⎠ FIT = Failures/Billion Hours @ Use Conditions V = Voltage (subscripts refer to life test and use conditions) T = Temperature in Celsius (subscripts refer to life test and use conditions) n = Voltage Stress Exponential (estimated from HALT Modeling) Ea = Activation Energy in eV (estimated from HALT Modeling) K = Boltzmann Constant in eV/K 8.62E-5 EXPERIMENTAL RESULTS All the HALT experiments were conducted in a commercial oven with maximum capabilities of 600V and 175ºC (Model CE9051, DM511, Micro Burn-in Technologies). The current of the parts was monitored in-situ during the run every 40 seconds. The current limit was set at 100µamps for determining a failure. The sample size was 20 parts per test trial. All test trials were run for 200 hours to generate sufficient data to allow prediction of MTTF. modes or extended tails, experienced discretion was taken to fit the data that most represented the wear-out behavior. For instance, the data for the X7R 0402 part at 100V in Figure 3 at 125ºC was fit to the lower distribution because it was parallel to the data at 75V. Another example for the C0G 1206 at 100V in Figure 4 at 155ºC, the upper distribution of the time distribution was fit because it was parallel to the data at 75V. Generally, the slopes of the linear fits were parallel at a given temperature. This demonstrates well-behaved experimental data that is failing due to one mechanism of failure. It is assumed this demonstrates the typical dielectric degradation mechanism of oxygen vacancies piling up along the grain boundaries ultimately leading to wear-out. However, in some cases the slopes are different indicating a change in the failure mechanism. This occurred mainly at the higher voltages, especially in the C0G parts. This likely indicates a different breakdown mechanism of the dielectric with application of extreme voltage stress on the part. Possibly, minor defects such as micro-pores or imperfections become hot spots for localized dielectric degradation due to the increased electric field imposed. The purpose of this paper is not to determine the exact mechanism for dielectric wear-out. Note that linear fits could not be determined for the C0G 0603 4.7nF 100V part because it was difficult to achieve failure during the HALT testing. Figure 5 shows only two failures occurred at highest temperature (175ºC) and 575V. Unfortunately, the HALT equipment was incapable of more stressful conditions and it was unrealistic to conduct test trials longer than 200 hours. The MTTF based on the linear estimation fits are shown in Table 3 for each part type. A value of time in minutes is given for selected temperature and voltages. In some cases the number of failures was minimal such that a MTTF could not be estimated. In these cases, just the number of failures is indicated. In all cases the data was well behaved. Again note the C0G 0603 4.7nF 100V part had very few failures except at 175ºC. This shows the robustness of this part type to the testing, indicating a highly reliable part. Analysis of the time-to-failure data was conducted by plotting the data on log plots. Linear fits were applied to the data to determine the MTTF. Figures 3 and 4 show the time-to-failure plots for both the X7R 0402 100nF 16V and C0G 1206 100nF 25V parts. Note that in most cases a linear correlation fit well for all data in the time distribution using regression analysis. However, in some cases there was limited data because less the 50% of the parts failed after 200 hours. For these cases, advanced regression analysis was completed by right-censoring the data with time of 12,000 minutes (parts did not fail in 200 hours). In other cases, where the time distribution showed multi- SMTA Medical Electronics Symposium – Anaheim, California – 2008 Time to Failure (X7R 0402 100nF 16V) Time to Failure (C0G 1206 100nF 25V) Lognormal Temperature (°C) = 105 Lognormal Temperature (°C) = 125 Test voltage (V) 25 50 75 100 125 95 90 70 60 50 40 30 10 5 5 1000 TTF (mins) 1 10000 90 80 70 60 50 40 30 20 10 5 5 1000 TTF (mins) 1 10000 0.01 0.10 1.00 10.00 100.00 TTF (mins) 1000.00 10000.00 Time to Failure (X7R 0402 100nF 16V) Time to Failure (C0G 1206 100nF 25V) Lognormal Temperature (°C) = 140 Lognormal Temperature (°C) = 155 Test voltage (V) 25 50 75 100 125 95 90 80 70 60 50 40 30 99 90 80 70 60 50 40 30 20 20 10 10 5 5 1000 TTF (mins) Test voltage (V) 250 300 350 400 450 500 550 600 95 Percent 99 1 10000 0.01 0.10 1.00 10.00 100.00 TTF (mins) 1000.00 10000.00 Time to Failure (X7R 0402 100nF 16V) Time to Failure (C0G 1206 100nF 25V) Lognormal Temperature (°C) = 155 Lognormal Temperature (°C) = 175 99 Test voltage (V) 25 50 75 100 125 95 90 80 70 60 50 40 30 99 90 80 70 60 50 40 30 20 10 10 5 5 1000 TTF (mins) 10000 Figure 3: Time-to-failure plots at various temperatures and voltages showing linear estimation fits for the X7R 0402 100nF part. Test voltage (V) 250 300 350 400 450 500 550 600 95 20 100 Test voltage (V) 250 300 350 400 450 500 550 600 95 10 1 1000.00 10000.00 99 20 100 10.00 100.00 TTF (mins) Lognormal Temperature (°C) = 140 70 60 50 40 30 1 1.00 Time to Failure (C0G 1206 100nF 25V) Test voltage (V) 25 50 75 100 125 100 0.10 Lognormal Temperature (°C) = 125 80 1 0.01 Time to Failure (X7R 0402 100nF 16V) Percent 100 90 Percent 70 60 50 40 30 20 95 Percent 80 10 99 Percent 90 20 1 Test voltage (V) 250 300 350 400 450 500 550 600 95 Percent Percent 80 99 Percent 99 1 0.01 0.10 1.00 10.00 100.00 TTF (mins) 1000.00 10000.00 Figure 4: Time-to-failure plots at various temperatures and voltage showing linear estimation fits for the C0G 1206 100nF part. SMTA Medical Electronics Symposium – Anaheim, California – 2008 Part No. Time to Failure (C0G 0603 4.7nF 100V) Lognormal 100 1000 125 10000 140 90 Percent 50 10 155 Test voltage (V) 500 525 550 575 600 175 90 50 10 100 1000 10000 TTF (mins) Panel variable: Temperature (°C) Figure 5: Time-to-failure plots at various temperatures and voltages for the C0G 0603 4.7nF 100V part. Linear estimation fits could not be completed since there were few HALT failures. Table 3: MTTF for each part type based on linear estimation fits. Part No. X7R 0402 0.1000µF 16V (time in min) VOLT Part No. VOLT 125 100 75 50 25 500 450 400 350 300 200 X7R 0603 0.1000µF 50V (time in min) Part No. VOLT 450 425 400 375 350 320 X7R 1210 1.0000µF 100V (time in min) Part No. VOLT 105 6473 14600 105 66383 0 fail 2 fail 0 fail 0 fail 125 600 575 550 525 500 150 C0G 0402 0.0010µF 25V (time in min) Part No. C0G 0603 0.0047µF 100V (time in min) 105 5070 13586 0 fail VOLT 600 575 550 525 500 Temperature (ºC) 125 140 2726 6140 0 fail 662 1921 11495 Temperature (ºC) 125 140 786 287 2246 467 5055 990 9973 2600 3 fail Temperature (ºC) 125 140 10639 3 fail 13043 3 fail 16288 1 fail 27230 1 fail Temperature (ºC) 140 155 365 139 437 381 1515 663 3747 0 fail 125 0 fail 0 fail Temperature (ºC) 140 155 0 fail 0 fail 0 fail 0 fail 0 fail 0 fail 0 fail VOLT 550 500 450 400 350 300 250 C0G 1206 0.1000µF 25V (time in min) Temperature (ºC) 140 155 125 0.31 4.1 208 447 2.73 40.7 110 1286 75 208 4129 175 98 153 13445 Multiple regression fit of the MTTF data for each part type was conducted to estimate the model coefficients (Table 4). Overall the r2 was greater than 90% showing a good fit to the P-V model. Only the X7R 1210 1.0µF 100V part had a low r2, mainly due to the limited amount of MTTF data collected at lower temperatures. Generally, the Ea and n were consistent with those reported by others9-12. The C0G dielectrics had high voltage exponents indicating a large voltage dependence. They also had an extremely large time constant suggesting these parts have a long lifetime at benign conditions. The X7R had both time constant and voltage exponents that correlated to the voltage rating. In turn, this correlates well with the dielectric thickness of the corresponding part types (0402: 3.2µm, 0603: 5.1µm, 1210: 10.4µm). 155 307 584 3638 0 fail 155 248 507 1558 8555 155 4966 10220 35619 175 69 60 193 432 760 175 0 fail 2 fail 1 fail 0 fail 0 fail Table 4: Model Coefficients Part Number 0402 100nF 0603 100nF 1210 1μF 0402 1nF 1206 100nF Dielectric Family X7R X7R X7R C0G C0G Rated Voltage 16 50 100 25 25 A (mins) 1.16E-03 4.43E+01 1.31E+13 1.11E+37 1.02E+30 n 3.8 5.4 8.4 16.4 17.3 Ea (eV) 1.1 1.27 1.05 0.91 1.39 r2 98.3% 97.5% 75.4% 94.9% 89.7% The P-V model was used to predict the MTTF at standard conditions (125ºC, 2xVr and 1xVr) and in-vitro conditions (37ºC, 1xVr and 0.5xVr) shown in Table 5. For X7R, the lifetime is strongly a function of voltage rating (i.e., dielectric thickness). The lifetime at 125ºC and 2xVr is reasonable, but is greatly increased when the voltage is reduced to 1xVr. More importantly, the lifetime at 37ºC at either voltage is nearly infinite compared to the life expectancy of a typical medical device. The lifetime at any conditions for the C0G are realistically infinite. In summary, the likelihood of any of these parts failing under in-vitro conditions is extremely remote. Table 5: Predicted Median Time to Failure MTTF (Yrs) 125C 1xVr MTTF MTTF (Yrs) (Yrs) 85C MTTF (Yrs) 37C 0.5xVr 37C 1xVr 0.5xVr Dielectric Family Rated Voltage 0402 100nF X7R 16 4.9 2,500 4.4.E+04 0603 100nF 1210 1µF X7R 50 599 1,600,000 2.2.E+07 9.4.E+08 X7R 100 7,734 8.0E+07 4.6.E+07 1.5.E+10 0402 1nF C0G 25 8.3E+19 1.4E+26 1.5.E+23 1.3.E+28 1206 100nF C0G 25 5.0E+17 7.5E+24 4.9.E+22 8.0.E+27 Part Number 6.2.E+05 In addition to HALT testing, load life tests were conducted under standard environmental conditions of twice rated voltage and 125ºC for 1000 hours. A large sample size ranging from 460 to 1000 pieces was tested for each part type. The limit was set for each part type based on EIA specification. This data will be used in the FIT model for each part type. SMTA Medical Electronics Symposium – Anaheim, California – 2008 Table 6: Load life failures at 125oC and 2xVr. Part Type C0G X7R X7R C0G C0G X7R 0402 0402 0603 0603 1206 1210 Qty 1nF 25V 100nF 16V 100nF 50V 4.7nF 100V 100nF 25V 1μF 100V 500 500 500 500 500 500 Test Voltage 50 32 100 200 50 200 100 hrs. 0 1 0 0 0 0 250 hrs. 2 0 1 0 0 2 500 hrs. 1 1 0 0 1 2 1000 hrs. 1 5 0 0 1 1 Total 4 7 1 0 2 5 Estimated Reliability Since we have developed constants for activation energy and voltage coefficients for each of the selected part types, we can begin to predict FIT rates based on the formula in Equation 4. A high sample size life test of 500 pieces per batch was performed at two times rated voltage and rated temperature (125°C) on capacitors that were voltage conditioned. The accelerated life test failures were noted and included in the calculations using the FIT formula. Reliability engineers commonly use FIT rates to estimate reliability. FIT rates are expressed in failures per billion piece hours. Using estimated FIT rates, we can make reliability predictions at the parts-per-billion and parts-permillion levels into future years of device service given application use conditions. dielectric system for a medical implantable application. At elevated temperatures and half rated voltage, the ceramic capacitors are predicted not to fail at the ppb level with two significant figures. Table 9 data depicts the predicted reliability of the BME X7R dielectric system. For all three scenarios, the one-year projected failure rate for 50V and 100V rated devices is less than one part per million (ppm) per device. For the 0402 case size 16V rated component, scenario 3 demonstrates a predicted ppm level of 17.5 in the first year. The Scenario 2 failure rate performance below 1ppm at 10 years of service life and at 50% rated voltage conditions and human body temperature demonstrates the robust nature of this dielectric system for a medical implantable application. Table 9: X7R FIT and Predicted Reliability X7R Dielectric System Projected Projected Projected Failure Failure Rate Failure Rate Rate in 1 Year, in 10 Years, in 50 Years, FIT (Discrete) Device (ppm) Device (ppm) Device (ppm) X7R 0402 100nF 16V X7R 1210 1.0µF 100V Table 7 depicts a summary of the application scenarios chosen to make reliability predictions. The application conditions used in the prediction model represent several potential use conditions in medical implantable and general medical electronic applications. Table 7: Application Scenarios Scenario Application Voltage Tem perature 1 Medical Implantable Vr 2 Medical Implantable 50% Vr 37°C 37°C 3 Elevated Temperature 50% Vr 85°C Vr = Rated Voltage Given the varying scenarios, we can predict projected failure rates for the selected dielectric systems and their associated part numbers. Table 8 summarizes the C0G dielectric system reliability predictions. Table 8: C0G FIT and Predicted Reliability C0G Dielectric System KEMET Part Number C0G 1206 100nF 25V C0G 0402 1nF 25V Scenario Projected Projected Projected Failure Failure Rate Failure Rate Rate in 1 Year, in 10 Years, in 50 Years, FIT (Discrete) Device (ppb) Device (ppb) Device (ppb) 1 2.49E-07 0.002 0.02 0.11 2 1.54E-12 0.000 0.00 0.00 0.00 3 1.66E-09 0.000 0.00 1 4.94E-05 0.433 4.3 22 2 5.72E-10 0.000 0.000 0.000 3 5.51E-08 0.000 0.005 0.024 For all three scenarios, the one-year projected failure rate is less than one part per billion (ppb) per device. The model requires 10 years for scenario one on the 0402 case size part number in order to reach a single digit ppb level of 4.3. This performance under rated voltage conditions and human body temperature demonstrates the robust reliability of this X7R 0603 100nF 50V 1 1.31E-01 1.153 11.527 2 9.44E-03 0.083 0.828 57.636 4.138 3 2.14E+00 18.726 187.256 936.280 1 4.97E-03 0.044 0.435 2.176 2 1.47E-05 0.000 0.001 0.006 3 2.86E-03 0.025 0.251 1.254 1 3.04E-05 0.000 0.003 0.013 2 7.21E-07 0.000 0.000 0.000 3 4.23E-04 0.004 0.037 0.186 Conclusions Previous studies on ceramic capacitor reliability point out the importance of defining voltage coefficients for accurate reliability modeling [12]. In this study there was a wide range of voltage coefficients varying from 3.8 to 17.3. In order to effectively predict reliability, it is important to develop the voltage coefficients to model capacitor behavior over known application conditions. The activation energy (Ea) values demonstrated a smaller range from 0.91 to 1.39. The effect of temperature is less significant than voltage on the time-to-failure for the capacitors modeled. For the devices tested in this study, projected median timeto-failure is well in excess of 100,000 years for medical implantable application conditions at 50% rated voltage and 37°C. Projected failure rates for this application condition in the observed C0G dielectric system were practically zero ppb even up to 50 years of device use. Projected failure rates for this application condition in the observed X7R dielectric system were less than 1 ppm up to 10 years and less than 3.5 ppm up to 50 years. As the pressure for higher reliability continues to increase for the Medical Electronics market, device manufacturers and capacitor suppliers must work in tandem to design-in the right capacitors under the known application conditions. When used under the proper application conditions, highcapacitance BME ceramic capacitors demonstrate excellent long-term reliability performance. SMTA Medical Electronics Symposium – Anaheim, California – 2008 ACKNOWLEDGEMENTS The authors would like to express gratitude to Ella Jones for conducting all the HALT tests, Jose Luis del Angel for preparing the samples, and Alicia Cruz for completing the Load Life testing. Special thanks to Bob Willoughby and Abhijit Gurav for their technical guidance and advice. REFERENCES [1] B. S. Rawal, M. Kahn, and W. R. Buessem, Grain Boundary Phenomena in Electronics Ceramics in Advances in Ceramics, Vol. 1, p. 172-188, 1981. [2] D. Hennings and G. Rosenstein, J. Am. Ceram. Soc., 67, 249-254 (1984). [3] Y. Mizuno, T. Hagiwara, H. Chazono, and H. Kishi, J. Euro.Ceram. Soc., 21, 1649-1652 (2001). [4] X. Xu, P. Pinceloup, J. Beeson, A. Gurav, and G.Y. Yang, p373-376, 12th US-Japan Seminar on Dielectric and Piezoelectric Ceramics, Nov. 6-9, 2005, Annapolis, MD, USA. [5] X. Xu, et al., p179-188, CARTS USA 2007, Alburquerque, NM, USA. [6] P. Pinceloup, et al., p459-466, CARTS USA 2006, Orlando, FL, USA. [7] A. S. Gurav, X. Xu, P. Pinceloup, M. Sato, A. Tajuddin, C. Randall and G. Yang, 13th US-Japan Seminar on Dielectric and Piezoelectric Ceramics, Nov. 2-5, 2007, Awaji Island, Japan. [8] T. Prokopowicz and A. Vaskas, “Research and Development, Intrinsic Reliability, Subminiature Ceramic Capacitors,” Final Report, ECOM-9705-F, 1969 NTIS AD864068 [9] G. Maher, “Highly Accelerated Life Testing of K-4500 Low Fired X7R Dielectric,” Proceedings of the Passive Components for Power Electronics Workshop. April 26-27, 2000, Penn State University. Also presented in parts at the US-Japan Seminar on Dielectric Studies November, 1999, Okinawa, Japan. [10] M.J. Cozzolino, B. Wong, L.S. Rosenheck, “Investigation of Insulation Resistance Degradation in BG Dielectric Characteristic, MIL-PRF-55681 Capacitors,” CARTS 2001 pp. 254-264. [11] J.L. Paulsen, E.K. Reed, “Highly Accelerated Life Testing of KEMET Base Metal Electrode (BME) Ceramic Chip Capacitors,” CARTS 2001, pp. 265-270. [12] M. Randall, A. Gurav, D. Skamser, J. Beeson, “Lifetime Modeling of Sub 2 Micron Dielectric Thickness BME MLCC,” CARTS 2003. SMTA Medical Electronics Symposium – Anaheim, California – 2008

- Similar pages
- KEMET C052T102M2R5CS
- Ceramic Molded Axial/Radial Leaded MIL-C-11015/ MIL-PRF-39014 X7R
- KEMET C340
- AVX TAZG686004C
- Ceramic Molded Axial/Radial Leaded X7R
- Ceramic Molded Axial/Radial Leaded MIL-PRF-20 C0G
- Ceramic Molded Axial/Radial Leaded C0G
- KEMET C512
- Reliability Management of Tantalum Capacitors
- Electromigration Performance of WLCSP Solder Joints
- 2003-01 CARTS Ceramic Life Model Sub-2-Micron 01/03 (245.2K PDF)
- 2007-11 CARTS - BME C0G MLCCs: The High Capacitance Class-I Solution 11/07 (229K PDF)
- FAIRCHILD MSX532
- an1283
- C24 - Wittig
- OxiCap NLJ Series Datasheet