AVX 0402ZG103ZAT2A

Y5V Dielectric
General Specifications
Y5V formulations are for general-purpose use in a limited
temperature range. They have a wide temperature
characteristic of +22% –82% capacitance change over the
operating temperature range of –30°C to +85°C.
These characteristics make Y5V ideal for decoupling
applications within limited temperature range.
PART NUMBER (see page 2 for complete part number explanation)
3
G
104
Z
A
T
2
A
Size
(L" x W")
Voltage
6.3V = 6
10V = Z
16V = Y
25V = 3
50V = 5
Dielectric
Y5V = G
Capacitance
Code (In pF)
2 Sig. Digits +
Number of
Zeros
Capacitance
Tolerance
Z = +80 –20%
Failure
Rate
A = Not
Applicable
Terminations
T = Plated Ni
and Sn
Packaging
2 = 7" Reel
4 = 13" Reel
Special
Code
A = Std.
Product
Capacitance Change
vs. DC Bias Voltage
+20
+10
0
-10
-20
-30
-40
-50
-60
-70
-80
+40
+20
⌬ c/c (%)
0
-20
-40
-60
-80
-55
-35 -15
-100
0
+5 +25 +45 +65 +85 +105 +125
Temperature °C
10,000
80
100
100
10
1
1,000,000
Frequency (Hz)
+20
10,000,000
+40
+50
+60
+70
+80
+90
1 ␮F - 1206
Impedance vs. Frequency
1,000
100
100
10
1
0.01
10,000
+30
Temperature °C
10
1
0.1
0.1
0.1
100,000
0
1,000
|Z| (Ohms)
|Z| (Ohms)
60
100
0.22 ␮F - 0805
Impedance vs. Frequency
1,000
26
40
1,000
% DC Bias Voltage
0.1 ␮F - 0603
Impedance vs. Frequency
0.01
10,000
20
Insulation Resistance vs. Temperature
10,000
|Z| (Ohms)
% ⌬ Capacitance
Temperature Coefficient
Insulation Resistance (Ohm-Farads)
0805
100,000
1,000,000
Frequency (Hz)
10,000,000
0.01
10,000
100,000
1,000,000
Frequency (Hz)
10,000,000
Y5V Dielectric
Specifications and Test Methods
Parameter/Test
Operating Temperature Range
Capacitance
Insulation Resistance
Y5V Specification Limits
-30ºC to +85ºC
Within specified tolerance
≤ 5.0% for ≥ 50V DC rating
≤ 7.0% for 25V DC rating
≤ 9.0% for 16V DC rating
≤ 12.5% for ≤ 10V DC rating
10,000MΩ or 500MΩ - μF,
whichever is less
Dielectric Strength
No breakdown or visual defects
Dissipation Factor
Resistance to
Flexure
Stresses
Appearance
Capacitance
Variation
Dissipation
Factor
Insulation
Resistance
Solderability
Resistance to
Solder Heat
Thermal
Shock
Load Life
Load
Humidity
Appearance
Capacitance
Variation
Dissipation
Factor
Insulation
Resistance
Dielectric
Strength
Appearance
Capacitance
Variation
Dissipation
Factor
Insulation
Resistance
Dielectric
Strength
Appearance
Capacitance
Variation
Dissipation
Factor
Insulation
Resistance
Dielectric
Strength
Appearance
Capacitance
Variation
Dissipation
Factor
Insulation
Resistance
Dielectric
Strength
No defects
≤ ±30%
Measuring Conditions
Temperature Cycle Chamber
Freq.: 1.0 kHz ± 10%
Voltage: 1.0Vrms ± .2V
For Cap > 10 μF, 0.5Vrms @ 120Hz
Charge device with rated voltage for
120 ± 5 secs @ room temp/humidity
Charge device with 300% of rated voltage for
1-5 seconds, w/charge and discharge current
limited to 50 mA (max)
Deflection: 2mm
Test Time: 30 seconds
1mm/sec
Meets Initial Values (As Above)
≥ Initial Value x 0.1
≥ 95% of each terminal should be covered
with fresh solder
No defects, <25% leaching of either end terminal
90 mm
Dip device in eutectic solder at 230 ± 5ºC
for 5.0 ± 0.5 seconds
≤ ±20%
Meets Initial Values (As Above)
Dip device in eutectic solder at 260ºC for 60
seconds. Store at room temperature for 24 ± 2
hours before measuring electrical properties.
Meets Initial Values (As Above)
Meets Initial Values (As Above)
No visual defects
Step 1: -30ºC ± 2º
30 ± 3 minutes
≤ ±20%
Step 2: Room Temp
≤ 3 minutes
Meets Initial Values (As Above)
Step 3: +85ºC ± 2º
30 ± 3 minutes
Meets Initial Values (As Above)
Step 4: Room Temp
≤ 3 minutes
Meets Initial Values (As Above)
Repeat for 5 cycles and measure after
24 ±2 hours at room temperature
No visual defects
≤ ±30%
≤ Initial Value x 1.5 (See Above)
≥ Initial Value x 0.1 (See Above)
Meets Initial Values (As Above)
No visual defects
≤ ±30%
Charge device with twice rated voltage in
test chamber set at 85ºC ± 2ºC
for 1000 hours (+48, -0)
Remove from test chamber and stabilize
at room temperature for 24 ± 2 hours
before measuring.
Store in a test chamber set at 85ºC ± 2ºC/
85% ± 5% relative humidity for 1000 hours
(+48, -0) with rated voltage applied.
≤ Initial Value x 1.5 (See above)
≥ Initial Value x 0.1 (See Above)
Remove from chamber and stabilize at
room temperature and humidity for
24 ± 2 hours before measuring.
Meets Initial Values (As Above)
27
Y5V Dielectric
Capacitance Range
PREFERRED SIZES ARE SHADED
SIZE
0201
0402
0603
0805
1206
1210
Soldering
Packaging
Reflow Only
All Paper
Reflow/Wave
All Paper
Reflow/Wave
All Paper
Reflow/Wave
Paper/Embossed
Reflow/Wave
Paper/Embossed
Reflow Only
Paper/Embossed
0.60 ± 0.03
(0.024 ± 0.001)
0.30 ± 0.03
(0.011 ± 0.001)
0.15 ± 0.05
(0.006 ± 0.002)
6.3
10
1.00 ± 0.10
(0.040 ± 0.004)
0.50 ± 0.10
(0.020 ± 0.004)
0.25 ± 0.15
(0.010 ± 0.006)
10
16
25
1.60 ± 0.15
(0.063 ± 0.006)
.81 ± 0.15
(0.032 ± 0.006)
0.35 ± 0.15
(0.014 ± 0.006)
16
25
3.20 ± 0.20
(0.126 ± 0.008)
1.60 ± 0.20
(0.063 ± 0.008)
0.50 ± 0.25
(0.020 ± 0.010)
16
25
3.20 ± 0.20
(0.126 ± 0.008)
2.50 ± 0.20
(0.098 ± 0.008)
.50 ± 0.25
(0.020 ± 0.010)
16
25
Cap
(μF)
50
50
A
A
A
A
A
C
C
C
G
C
C
G
K
C
G
G
G
G
28
T
t
G
N
C
N
N
M
M
M
Q
P
Q
X
Q
6.3
10
6
C
0.56
(0.022)
10
16
25
50
10
0402
E
0.71
(0.028)
PAPER
N
N
N
N
0201
A
0.33
(0.013)
W
L
50
G
22.0
47.0
Letter
Max.
Thickness
10
䉲
2.2
4.7
10.0
WVDC
50
A
A
0.33
0.47
1.0
SIZE
10
䉲
10
䉲
0.047
0.10
0.22
50
䉲
4700
0.010
0.022
6
䉲
Cap
(pF)
䉲
(t) Terminal
2.01 ± 0.20
(0.079 ± 0.008)
1.25 ± 0.20
(0.049 ± 0.008)
0.50 ± 0.25
(0.020 ± 0.010)
10
16
25
䉲
(W) Width
mm
(in.)
mm
(in.)
mm
(in.)
WVDC
820
1000
2200
䉲
(L) Length
G
0.90
(0.035)
16
25
50
0603
J
0.94
(0.037)
K
1.02
(0.040)
M
1.27
(0.050)
10
16
25
50
10
0805
N
1.40
(0.055)
P
Q
1.52
1.78
(0.060)
(0.070)
EMBOSSED
N
Q
X
16
25
50
10
1206
X
2.29
(0.090)
N
Q
Y
2.54
(0.100)
16
25
1210
Z
2.79
(0.110)
50