YAGEO CC1210KPNPOCBN103 Surface-mount ceramic multilayer capacitor Datasheet

DATA SHEET
SURFACE-MOUNT CERAMIC
MULTILAYER CAPACITORS
High-Voltage
NP0/X7R
1 KV TO 3 KV
10 pF to 33 nF
Product Specification – December 19, 2012 V.6
RoHS compliant & Halogen Free
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
2
15
1 KV to 3 KV
SCOPE
ORDERING INFORMATION - GLOBAL PART NUMBER, PHYCOMP
This specification describes HighVoltage NP0/X7R series chip
capacitors with lead-free
terminations.
All part numbers are identified by the series, size, tolerance, TC material,
packing style, voltage, process code, termination and capacitance value.
APPLICATIONS
PCs, Hard disk, Game PCs
Power supplies
LCD panel
ADSL, Modem
FEATURES
Supplied in tape on reel
Nickel-barrier end termination
RoHS compliant
Halogen Free compliant
CTC & 12NC
YAGEO BRAND ordering code
GLOBAL PART NUMBER (PREFERRED )
CC
XXXX X X XXX X
(1)
(2) (3) (4)
(5)
B
X XXX
(6) (7)
(1) SIZE – INCH BASED (METRIC)
0805 (2012) / 1206 (3216) / 1210 (3225) / 1808 (4520) / 1812 (4532)
(2) TOLERANCE
C = ±0.25 pF
D = ±0.5 pF
G = ±2%
J = ±5%
K = ±10%
(3) PACKING STYLE
R = Paper/PE taping reel; Reel 7 inch
K = Blister taping reel; Reel 7 inch
P = Paper/PE taping reel; Reel 13 inch
F = Blister taping reel; Reel 13 inch
C = Bulk case
(4) TC MATERIAL
NPO
X7R
(5) RATED VOLTAGE
C = 1 KV
D = 2 KV
E = 3 KV
(6) PROCESS
N = NP0
B = Class 2 MLCC
(7) CAPACITANCE VALUE
2 significant digits+number of zeros
The 3rd digit signifies the multiplying factor, and letter R is decimal point
Example: 121 = 12 x 101 = 120 pF
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
3
15
1 KV to 3 KV
PHYCOMP BRAND ordering codes
GLOBAL PART NUMBER (preferred), PHYCOMP CTC (for North America) and 12NC (traditional) codes are
acceptable to order Phycomp brand products.
GLOBAL PART NUMBER
( PREFERRED )
For detailed information of GLOBAL PART NUMBER and ordering example, please refer to page 2.
12NC
CODE
Ordering information for NP0 1 KV to 3 KV, C ≥ 10 pF
2 2 XX
XX
X
X
1
X
XX
Capacitance value(1)
Carrier type
22 = blister
38 = paper/PE
50 = blister
54 = bulk
Tolerance
4 = ±2%
5 = ±5%
Voltage
00 = 1 KV
02 = 2 KV
04 = 3 KV
TC material
1 = NP0
Size
0 = 0805
1 = 1206
2 = 1210
3 = 1808
4 = 1812
Packaging(3)
1 = reel: ∅180 mm; 7"
5 = reel: ∅330 mm; 13"
4 = bulk case
YNM0038
Ordering information for NP0 1 KV to 3 KV, C < 10 pF
2 2 XX
XX
X
X
X
XXX
Capacitance value(2)
Carrier type
92 = paper/PE
97 = bulk case
Tolerance
4 = ±0.25 pF for 5 pF ≤ C < 10 pF
±2% for C ≥ 10 pF
5 = ±0.25 pF for C < 5 pF
±0.5 pF for 5 pF ≤ C < 10 pF
±5% for C ≥ 10 pF
Voltage
00 = 1 KV
02 = 2 KV
04 = 3 KV
Size
3 = 1206
2 = 1210
4 = 1808
5 = 1812
YNM0039
Packaging(3)
1 = reel: ∅180 mm; 7"
7 = reel: ∅330 mm; 13"
4 = bulk case
(1) Please refer to "Last 2-digit of 12NC" in "CAPACITANCE RANGE & THICKNESS FOR NP0"
(2) Please refer to "Last 3-digit of 12NC" in "CAPACITANCE RANGE & THICKNESS FOR NP0"
(3) Quantity on reel depends on thickness classification; see table 5
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
NP0/X7R
High-Voltage
4
15
1 KV to 3 KV
Ordering information for X7R 1 KV to 3 KV
2 2 XX
XX
X
X
X
X
XX
Capacitance value(1)
Carrier type
50 = Blister
55 = Paper/PE
54 = Bulk
Tolerance
5 = ±5%(2)
6 = ±10%
Rated voltage - Termination
00 = 1 KV
02 = 2 KV
04 = 3 KV
Temperature characteristic
5 = X7R
Size
1 = 1206
2 = 1210
3 = 1808
4 = 1812
YNM0040
Packaging(3)
1 = reel: ∅180 mm; 7"
5 = reel: ∅330 mm; 13"
4 = bulk case
(1) Please refer to "Last 2-digit of 12NC" in "CAPACITANCE RANGE & THICKNESS FOR X7R"
(2) Tolerance ±5% is not available for full product range, please contact local sales force before ordering
(3) Quantity on reel depends on thickness classification; see table 5
PHYCOMP CTC
CODE ( FOR NORTH AMERICA )
 Example: 12102R102KFBB00
1210
2R
102
K
F
B
B
0
0
Size
code
Temp.
Char.
Capacitance
in pF
Tolerance
Voltage
Termination
Packing
Marking
Range identifier
C = ±0.25 pF
E = 1 KV
D = ±0.5 pF
F = 2 KV
G = ±2%
G = 3 KV
0805
CG = NP0
1206
2R = X7R
1210
1808
1812
101 = 100 pF;
the third digit
signifies the
multiplying factor:
8 = × 0.01
9 = × 0.1
0=×1
J = ±5%
K = ±10%
B = NiSn
2 = 180 mm
7” Paper/PE
0 = no marking 0 = conv. Ceramic
D = Class 2 MLCC
3 = 330 mm
13” Paper/PE
B = 180 mm
7” Blister
1 = × 10
F = 330 mm
13” Blister
2 = × 100
P = Bulk case
3 = × 1,000
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
5
15
1 KV to 3 KV
CONSTRUCTION
The capacitor consists of a
rectangular block of ceramic
dielectric in which a number of
interleaved metal electrodes are
contained. This structure gives
rise to a high capacitance per
unit volume.
The inner electrodes are
connected to the two end
terminations and finally covered
with a layer of plated tin (NiSn).
The terminations are lead-free. A
cross section of the structure is
shown in Fig.1.
terminations
electrodes
MLB457
ceramic material
Fig. 1 Surface mounted multilayer ceramic capacitor construction
DIMENSION
Table 1 For outlines see fig. 2
TYPE
L1 (mm)
W (mm)
0805
2.0 ±0.20
1206
3.2 ±0.30
OUTLINES
T (MM)
L2 / L3 (mm)
L4 (mm)
min.
max.
min.
1.25 ±0.20
0.25
0.75
0.55
1.6 ±0.20
0.25
0.75
1.40
0.25
0.75
1.40
Refer to
table 2 to 4
1210
3.2 ±0.30
2.5 ±0.20
1808
4.5 ±0.40
2.0 ±0.30
0.25
0.75
2.20
1812
4.5 ±0.40
3.2 ±0.20
0.25
0.75
2.20
For dimension see Table 1
W
T
L2
L4
L1
L3
MBB211
Fig. 2 Surface mounted multilayer
ceramic capacitor dimension
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
6
15
1 KV to 3 KV
CAPACITANCE RANGE & THICKNESS FOR NP0
Table 2 Sizes from 0805 to 1812
0805
1206
CAP. Last 2-digit of
12NC
10 pF
23
12 pF
24
15 pF
25
18 pF
26
22 pF
27
27 pF
28
33 pF
29
39 pF
31
47 pF
32
56 pF
33
68 pF
34
82 pF
35
100 pF
36
120 pF
37
150 pF
38
180 pF
39
220 pF
41
270 pF
42
330 pF
43
390 pF
44
470 pF
45
560 pF
46
680 pF
47
820 pF
48
1.0 nF
49
1.2 nF
51
1.5 nF
52
1.8 nF
53
2.2 nF
54
2.7 nF
55
3.3 nF
56
1 KV
1 KV
1808
1210
2 KV
1 KV
2 KV
1 KV
1812
2 KV
3 KV
1 KV
2 KV
3 KV
0.85±0.1
1.6±0.2
1.25±0.2
1.25±0.2
1.25±0.2 1.25±0.2
1.25±0.2
1.25±0.2
1.25±0.2
1.25±0.2
1.25±0.2
2.0±0.2
NOTE
1. Values in shaded cells indicate thickness class in mm
2. Capacitance value of non E-12 series is on request
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
7
15
1 KV to 3 KV
CAPACITANCE RANGE & THICKNESS FOR X7R
Table 3 Sizes from 0805 to 1812
CAP.
Last 2-digit
of 12NC
100 pF
09
150 pF
12
220 pF
14
330 pF
16
470 pF
18
680 pF
21
1.0 nF
23
1.5 nF
25
2.2 nF
27
3.3 nF
29
4.7 nF
32
6.8 nF
34
10 nF
36
15 nF
38
22 nF
41
33 nF
43
47 nF
45
68 nF
47
100 nF
49
0805
1206
1 KV
1 KV
1808
1210
2 KV
1 KV
2 KV
1 KV
1812
2 KV
3 KV
1 KV
2 KV
3 KV
1.6±0.2
0.85±0.1
1.25±0.2
1.35±0.15
1.25±0.2
1.25±0.2
1.35±0.15
1.6±0.2
2.0±0.2
1.35±0.15
1.6±0.2
1.25±0.2
1.35±0.15
1.6±0.2
1.6±0.2
2.0±0.2
1.6±0.2
1.6±0.2
NOTE
1. Values in shaded cells indicate thickness class in mm
2. Capacitance value of non E-6 series is on request
3. For products with 5% tolerance, please contact local sales force before ordering
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
1 KV to 3 KV
8
15
THICKNESS CLASSES AND PACKING QUANTITY
Table 5
SIZE
CODE
THICKNESS
CLASSIFICATION
TAPE WIDTH
QUANTITY PER REEL
0201
0.3 ±0.03 mm
0402
0603
0805
1206
Ø180 MM / 7 INCH
Ø330 MM / 13 INCH
Paper
Blister
Paper
Blister
QUANTITY
PER BULK CASE
8 mm
15,000
---
50,000
---
---
0.5 ±0.05 mm
8 mm
10,000
---
50,000
---
50,000
0.8 ±0.1 mm
8 mm
4,000
---
15,000
---
15,000
0.6 ±0.1 mm
8 mm
4,000
---
20,000
---
10,000
0.8 / 0.85 ±0.1 mm
8 mm
4,000
---
15,000
---
8,000
1.00 ±0.1 mm
8 mm
---
3,000
---
10,000
---
1.25 ±0.2 mm
8 mm
---
3,000
---
10,000
5,000
0.6 ±0.1 mm
8 mm
4,000
---
20,000
---
---
0.8 / 0.85 ±0.1 mm
8 mm
4,000
---
15,000
---
---
1.00 / 1.15 ±0.1 mm
8 mm
---
3,000
---
10,000
---
1.25 ±0.2 mm
8 mm
---
3,000
---
10,000
---
1.6 ±0.15 mm
8 mm
---
2,500
---
10,000
---
1.6 ±0.2 mm
8 mm
---
2,000
---
8,000
---
0.6 / 0.7 ±0.1 mm
8 mm
---
4,000
---
15,000
---
0.85 ±0.1 mm
8 mm
---
4,000
---
10,000
---
1.15 ±0.1 mm
8 mm
---
3,000
---
10,000
---
1.15 ±0.15 mm
8 mm
---
3,000
---
10,000
---
1.25 ±0.2 mm
8 mm
---
3,000
---
---
---
1.5 ±0.1 mm
8 mm
---
2,000
---
---
---
1.6 / 1.9 ±0.2 mm
8 mm
---
2,000
---
---
---
2.0 ±0.2 mm
8 mm
---
2,000
1,000
---
---
---
2.5 ±0.2 mm
8 mm
---
1,000
500
---
---
---
1.15 ±0.15 mm
12 mm
---
3,000
---
---
---
1.25 ±0.2 mm
12 mm
---
3,000
---
---
---
1.35 ±0.15 mm
12 mm
---
2,000
---
---
---
1.5 ±0.1 mm
12 mm
---
2,000
---
---
---
1.6 ±0.2 mm
12 mm
---
2,000
---
---
---
1210
1808
2.0 ±0.2 mm
12 mm
---
2,000
---
---
---
0.6 / 0.85 ±0.1 mm
12 mm
---
2,000
---
---
---
1.15 ±0.1 mm
12 mm
---
1,000
---
---
---
1.15 ±0.15 mm
12 mm
---
1,000
---
---
---
1.25 ±0.2 mm
12 mm
---
1,000
---
---
---
1.35 ±0.15 mm
12 mm
---
1,000
---
---
---
1.5 ±0.1 mm
12 mm
---
1,000
---
---
---
1.6 ±0.2 mm
12 mm
---
1,000
---
---
---
2.0 ±0.2 mm
12 mm
---
1,000
---
---
---
2.5 ±0.2 mm
12 mm
---
500
---
---
---
1812
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
9
15
1 KV to 3 KV
ELECTRICAL CHARACTERISTICS
NP0/X7R DIELECTRIC CAPACITORS; NISN TERMINATIONS
Unless otherwise stated all electrical values apply at an ambient temperature of 20±1 °C, an atmospheric
pressure of 86 to 106 kPa, and a relative humidity of 63 to 67%.
Table 6
VALUE
DESCRIPTION
Capacitance range
10 pF to 33 nF
Capacitance tolerance
NP0
C < 10 pF
±0.25 pF, ±0.5 pF
C ≥ 10 pF
±2%, ±5%
X7R
±5% (1), ±10%
Dissipation factor (D.F.)
NP0
C < 30 pF
≤ 1 / ( 400 + 20C )
C ≥ 30 pF
≤ 0.1 %
X7R
Insulation resistance after 1 minute at Ur (DC)
≤ 2.5 %
Rins ≥ 10 GΩ or Rins × C ≥ 500 seconds whichever is less
Maximum capacitance change as a function of temperature
(temperature characteristic/coefficient):
NP0
±30 ppm/°C
X7R
±15%
Operating temperature range:
NP0/X7R
–55 °C to +125 °C
NOTE
1. ±5% tolerance of capacitance value isn't available for X7R full product range, please contact local sales force before ordering
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
10
15
1 KV to 3 KV
HIGH - VOLTAGE NP0
Sample limits (broken lines).
Requirement levels (dotted lines)
MEA607
CCA044
10
tan δ
(× 10−4)
40
TC
(x10 6/K)
7.5
20
5
0
20
2.5
40
0
40
0
40
80
120
T ( oC)
Fig. 3 Typical temperature coefficient as a function of
temperature
−40
0
40
80
120
T (oC)
Fig. 4 Typical tan δ as a function of temperature
HIGH - VOLTAGE X7R
ΔC
C
(%)
YNM0013
15
YNM0041
300
tan δ
(× 10−4)
10
200
5
1 KV product
0
2 KV product
100
−5
3 KV product
−10
−15
−55
0
−25
5
40
65
95
125
T (oC)
Fig. 5 Typical capacitance change as a function of
temperature
−40
0
40
80
120
T (°C)
Fig. 6 Typical tan δ as a function of temperature
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
11
15
1 KV to 3 KV
SOLDERING RECOMMENDATION
Table 7
SOLDERING
METHOD
SIZE
0402
0603
0805
1206
≥ 1210
Reflow
≥ 0.1 µF
≥ 1.0 µF
≥ 2.2 µF
≥ 4.7 µF
Reflow only
Reflow/Wave
< 0.1 µF
< 1.0 µF
< 2.2 µF
< 4.7 µF
---
TESTS AND REQUIREMENTS
Table 8 Test procedures and requirements
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
Mounting
IEC 6038421/22
4.3
The capacitors may be mounted on printed-circuit boards or
ceramic substrates
No visible damage
Visual
Inspection and
Dimension
Check
4.4
Any applicable method using × 10 magnification
In accordance with specification
Capacitance
4.5.1
Class 1:
f = 1 MHz for C ≤ 1 nF, measuring at voltage 1 Vrms at 20 °C
Within specified tolerance
f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C
Class 2:
f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C
Dissipation
Factor (D.F.)
4.5.2
Class 1:
f = 1 MHz for C ≤ 1 nF , measuring at voltage 1 Vrms at 20 °C
In accordance with specification
f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C
Class 2:
f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C
Insulation
Resistance
4.5.3
Temperature
Coefficient
4.6
Temperature
Characteristic
Ur ≤ 500 V: At Ur for 1 minute
In accordance with specification
Ur > 500 V: At 500 V for 1 minute
Class 1:
Between minimum and maximum temperature
NP0: -55 °C to +125 °C
Normal Temperature: 20 °C
C/C:
Class 2:
Between minimum and maximum temperature
X7R: -55 °C to +125 °C
Normal Temperature: 20 °C
Class 2
X7R: ±15%
Class 1:
NP0: ±30 ppm/°C
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
Adhesion
IEC 6038421/22
4.7
A force applied for 10 seconds to the line joining
the terminations and in a plane parallel to the
substrate
Force
size ≥ 0603: 5N
4.8
Mounting in accordance with IEC 60384-22
paragraph 4.3
No visible damage
Conditions: bending 1 mm at a rate of 1 mm/s,
radius jig 340 mm
∆C/C
Bond
Strength of
Plating on
End Face
12
15
1 KV to 3 KV
Class 1:
NP0: within ±1% or 0.5 pF, whichever is greater
Class2:
X7R: ±10%
Resistance to
Soldering
Heat
4.9
Precondition: 150 +0/–10 °C for 1 hour, then
keep for 24 ±1 hours at room temperature
Preheating: for size ≤ 1206: 120 °C to 150 °C for
1 minute
Preheating: for size >1206: 100 °C to 120 °C for
1 minute and 170 °C to 200 °C for 1 minute
Solder bath temperature: 260 ±5 °C
Dipping time: 10 ±0.5 seconds
Recovery time: 24 ±2 hours
Dissolution of the end face plating shall not
exceed 25% of the length of the edge
concerned
∆C/C
Class 1:
NP0: within ±0.5% or 0.5 pF, whichever is greater
Class2:
X7R: ±10%
D.F. within initial specified value
Rins within initial specified value
Solderability
4.10
Preheated to a temperature of 80 °C to 140 °C
and maintained for 30 seconds to 60 seconds.
The solder should cover over 95% of the critical
area of each termination
1. Temperature: 235±5°C / Dipping time: 2 ±0.5 s
2. Temperature: 245±5°C / Dipping time: 3 ±0.5 s
(lead free)Depth of immersion: 10mm
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
Rapid Change
of
Temperature
IEC 6038421/22
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for
24 ±1 hours at room temperature
No visual damage
4.11
5 cycles with following detail:
30 minutes at lower category temperature
30 minutes at upper category temperature
Recovery time 24 ±2 hours
13
15
1 KV to 3 KV
∆C/C
Class 1:
NP0: within ±1% or 1 pF, whichever is greater
Class2:
X7R: ±15%
D.F. meet initial specified value
Rins meet initial specified value
Damp Heat
4.13
1. Preconditioning, class 2 only:
150 +0/-10 °C /1 hour, then keep for
24 ±1 hour at room temp
2. Initial measure:
Spec: refer to initial spec C, D, IR
3. Damp heat test:
500 ±12 hours at 40 ±2 °C;
90 to 95% R.H.
4. Recovery:
Class 1: 6 to 24 hours
Class 2: 24 ±2 hours
5. Final measure: C, D, IR
P.S. If the capacitance value is less than the
minimum value permitted, then after the
other measurements have been made the
capacitor shall be preconditioned according
to “IEC 60384 4.1” and then the
requirement shall be met.
No visual damage after recovery
∆C/C
Class 1:
NP0: within ±2% or 1 pF, whichever is greater
Class2:
X7R: ±15%
D.F.
Class 1:
NP0: ≤ 2 x specified value
Class2:
X7R: ≥ 25 V: ≤ 5%
Rins
Class 1:
NP0: ≥ 2,500 MΩ or Rins x Cr ≥ 25s whichever is less
Class2:
X7R: ≥ 500 MΩ or Rins x Cr ≥ 25s whichever is less
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
Endurance
IEC 6038421/22
1. Preconditioning, class 2 only:
No visual damage
4.14
150 +0/-10 °C /1 hour, then keep for
24 ±1 hour at room temp
2. Initial measure:
Spec: refer to initial spec C, D, IR
3. Endurance test:
Temperature: NP0/X7R: 125 °C
Specified stress voltage applied for 1,000 hours.
High-Voltage series follows the stress conditions
below:
Applied 2.0 x Ur for < 500 V series
Applied 1.3 x Ur for 500 V, 630 V series
Applied 1.2 x Ur for 1 KV, 2 KV, 3 KV series
4. Recovery time: 24 ±2 hours
5. Final measure: C, D, IR
P.S. If the capacitance value is less than the
minimum value permitted, then after the other
measurements have been made the capacitor shall
be preconditioned according to “IEC 60384 4.1”
and then the requirement shall be met.
Voltage Proof
IEC 60384-1 4.6
Specified stress voltage applied for 1 minute
Ur ≤ 100 V: series applied 2.5 Ur
100 V < Ur ≤ 200 V series applied (1.5 Ur + 100)
200 V < Ur ≤ 500 V series applied (1.3 Ur + 100)
Ur > 500 V: 1.3 Ur
I: 7.5 mA
14
15
1 KV to 3 KV
∆C/C
Class1:
NP0: within ±2% or 1 pF, whichever is greater
Class2:
X7R: ±15%
D.F.
Class1:
NP0: ≤ 2 x specified value
Class2:
X7R: ≥ 25 V: ≤ 5%
Rins
Class1:
NP0: ≥ 4,000 MΩ or
Rins x Cr ≥ 40s whichever is less
Class2:
X7R: ≥ 1,000 MΩ or
Rins x Cr ≥ 50s whichever is less
No breakdown or flashover
www.yageo.com
Dec. 19, 2012 V.6
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
15
15
1 KV to 3 KV
REVISION HISTORY
REVISION DATE
CHANGE NOTIFICATION
DESCRIPTION
Version 6
Dec. 19, 2012
-
- Product range updated
Version 5
Sep 25, 2012
-
- Product range updated
Version 4
Aug 08, 2011
-
- Product range updated
Version 3
Jan 19, 2011
-
- Dimension updated
- Add NP0 0805 1KV
Version 2
Feb 02, 2010
-
- Change to dual brand datasheet that describe High-Voltage NP0/X7R
series with RoHS compliant
- Replace the high voltage part of pdf files:
UP-NP0X7R_HV_1K-to-4KV_1 and UY-NP0X7R_HV_1K-to-4KV_1
- Description of "Halogen Free compliant" added
- Product range updated
- Define global part number
- Test method and procedure updated
Version 1
Sep 30, 2005
-
- Thickness revised
Version 0
Sep 12, 2005
-
- New
www.yageo.com