Samsung CL31C332FBFNNNE Multi-layer ceramic capacitor Datasheet

SPECIFICATION
• Samsung P/N : CL31C332FBFNNNE
CAP, 3.3㎋
㎋, 50V, ±1%, C0G, 1206
• Description :
• Supplier : Samsung electro-mechanics
• Product : Multi-layer Ceramic Capacitor
A. Samsung Part Number
① Series
② Size
③ Dielectric
④ Capacitance
⑤ Capacitance
tolerance
⑥ Rated Voltage
⑦ Thickness
CL
31
C
332
F
B
F
N
N
N
E
①
②
③
④
⑤
⑥
⑦
⑧
⑨
⑩
⑪
Samsung Multi-layer Ceramic Capacitor
1206
(inch code)
L: 3.2
± 0.15
mm
W:
⑧ Inner electrode
Termination
C0G
3.3 ㎋
±1 %
50 V
1.25 ± 0.15 mm
Plating
⑨ Product
⑩ Special
⑪ Packaging
1.6 ± 0.15 mm
Ni
Cu
Sn 100%
(Pb Free)
Normal
Reserved for future use
Embossed Type, 7" reel
B. Samsung Reliablility Test and Judgement condition
Performance
Test condition
Within specified tolerance
1000 min
1㎑±10%
0.5~5Vrms
10,000Mohm or 500Mohm⋅㎌
Whichever is Smaller
Rated Voltage
60~120 sec.
Withstanding
No abnormal exterior appearance
No dielectric breakdown or
Microscope (×10)
300% of the rated voltage
Voltage
Temperature
mechanical breakdown
C0G
Characterisitcs
Adhesive Strength
(From -55℃ to 125℃, Capacitance change shoud be within ±30PPM/℃)
No peeling shall be occur on the
500g⋅F, for 10±1 sec.
terminal electrode
Capacitance
Q
Insulation
Resistance
Appearance
of Termination
Bending Strength
Solderability
Resistance to
Soldering heat
Capacitance change :
within ±5% or ±0.5㎊ whichever is larger
More than 75% of terminal surface
is to be soldered newly
Capacitance change :
within ±2.5% or ±0.25㎊ whichever is larger
Tan δ, IR : initial spec.
Bending to the limit (1mm)
with 1.0mm/sec.
SnAg3.0Cu0.5 solder
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Solder pot : 270±5℃, 10±1sec.
Performance
Vibration Test
Moisture
Resistance
Capacitance change :
within ±7.5% or ±0.75㎊ whichever is larger 40±2℃, 90~95%RH, 500+12/-0hrs
Q:
200 min
Cycling
500Mohm or 25Mohm ⋅ ㎌
Whichever is Smaller
Capacitance change :
within ±3% or ±0.3㎊ whichever is larger
Q:
350 min
IR :
Temperature
Amplitude : 1.5mm
within ±2.5% or ±0.25㎊ whichever is larger From 10㎐ to 55㎐ (return : 1min.)
Tan δ, IR : initial spec.
2hours × 3 direction (x, y, z)
Capacitance change :
With rated voltage
IR :
High Temperature
Resistance
Test condition
With 200% of the rated voltage
Max. operating temperature
1000+48/-0hrs
1000Mohm or 50Mohm ⋅ ㎌
Whichever is Smaller
Capacitance change :
1 cycle condition
25℃
within ±2.5% or ±0.25㎊ whichever is larger Min. operating temperature
→
Tan δ, IR : initial spec.
→ Max. operating temperature → 25℃
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.