Samsung CL32A106KA9LNNE Specification Datasheet

SPECIFICATION
• Samsung P/N : CL32A106KA9LNNE
㎌, 25V, ±10%, X5R, 1210
• Description : CAP, 10㎌
• Supplier : Samsung electro-mechanics
• Product : Multi-layer Ceramic Capacitor
A. Samsung Part Number
① Series
② Size
③ Dielectric
④ Capacitance
⑤ Capacitance
tolerance
⑥ Rated Voltage
⑦ Thickness
CL
32
A
106
K
A
9
L
N
N
E
①
②
③
④
⑤
⑥
⑦
⑧
⑨
⑩
⑪
Samsung Multi-layer Ceramic Capacitor
1210 (inch code)
L: 3.2 ± 0.3
2.5 ± 0.2
W:
⑧ Thickness division
Inner electrode
X5R
10 ㎌
±10 %
25 V
0.9 ± 0.1
mm
mm
mm
Low profile
Ni
Termination
Cu
Plating
Sn 100%
(Pb Free)
⑨ Product
⑩ Special
Normal
⑪ Packaging
Embossed Type, 7" reel
Reserved for future use
B. Samsung Reliablility Test and Judgement condition
Performance
Capacitance
Tan δ (DF)
Insulation
Within specified tolerance
Test condition
1㎑±10%
1.0±0.2 Vrms
60~120 sec.
0.1 max.
10,000Mohm or 100Mohm⋅㎌
Whichever is Smaller
Rated Voltage
Resistance
Appearance
No abnormal exterior appearance
Withstanding
No dielectric breakdown or
Microscope (×10)
250% of the rated voltage
Voltage
mechanical breakdown
Temperature
X5R
Characterisitcs
Adhesive Strength
(From -55℃ to 85℃, Capacitance change shoud be within ±15%)
No peeling shall be occur on the
500g⋅F, for 10±1 sec.
of Termination
terminal electrode
Bending Strength
Capacitance change :
within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability
More than 75% of terminal surface
SnAg3.0Cu0.5 solder
is to be soldered newly
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to
Capacitance change :
Soldering heat
Tan δ, IR : initial spec.
within ±7.5%
Solder pot : 270±5℃, 10±1sec.
Performance
Vibration Test
Capacitance change :
within ±5%
Tan δ, IR : initial spec.
Moisture
Capacitance change :
Resistance
Tan δ : 0.125 max
IR :
Amplitude : 1.5mm
From 10㎐ to 55㎐ (return : 1min.)
2hours × 3 direction (x, y, z)
within ±12.5% With rated voltage
40±2℃, 90~95%RH, 500+12/-0hrs
12.5㏁·㎌ or Over
High Temperature
Capacitance change :
Resistance
Tan δ : 0.125 max
IR :
Test condition
within ±12.5% With 150%
of the rated voltage
Max. operating temperature
25㏁·㎌ or Over
1000+48/-0hrs
Temperature
Capacitance change :
Cycling
Tan δ, IR : initial spec.
within ±7.5%
1 cycle condition
Min. operating temperature→
→
25℃
Max. operating temperature → 25℃
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.