Analog 5-wire PET-On-Glass Touch Screen Specification 1. Mechanical Dimensions and Construction 1.1 1.2 General: Analog Resistive touch screen is laminated by ITO PET to ITO glass. Construction : Item 1 2 3 4 5 6 7 8 9 10 Description ITO PET (Top layer) Material Remarks 0.188mm ITO PET Film Antiglare coating Surface hardness: 3H Resistance:300~600Ω/□ ITO Patterned Glass (Bottom 2.36mm ITO Glass Resistance:300~600Ω/□ layer) Tail Base Kapton Separated Tail Tail Coverlay Kapton Connector AMP Compatible Pitch:2.54mm Top layer circuit Silver ink Bottom layer circuit Silver ink Layer to layer contacted Silver ink Dot spacer UV Cure ink Isolation Layer Isolation Adhesive Touch screen side view: Changes that contribute to technical improvement are subject to alternations 2002 Datum Name Bearb. 24.10. Maurer Gepr. 24.10. Maurer TOUCHSCREEN 15“, 5-Wire Vert. EDV-Datasheet SPECIFICATIONS OF ANALOG RESISTIVE don’t change manually Manufactured bei Apex Material Technology Corp. PET-ON-GLASS TOUCH SCREEN H Zu Änd. Datum Name D 79346 Endingen 1070.0442 Blatt 1 von 3 Index: - 1.3 Input Method and Activation Force Input Method 1.6mm dia. Delrin stylus 16mm dia. Silicon "finger" Average Activation Force 10~70 grams 10~ 80 grams 2. Typical Optical Characteristics 2.1 2.2 Visible Light Transmission: >80% Haze: 3~7% (JIS K-7105) 3. Electrical Specifications 3.1 3.2 3.3 3.4 3.5 3.6 Operating Voltage: 5.5V or less Contact current: 20mA (maximum) Circuit close resistance: 30~300Ω Circuit open resistance: > 10MΩ at 25VDC Contact bounce: < 15ms Linear Test : <1.5 % 4. Environment Specification 4.1 4.2 Operating Temperature - 10° C ~ + 60° C Storage Temperature - 20° C ~ + 80° C Humidity less than 90% RH at Ambient Humidity 5. Reliability Test 5.1 Exposure to high temperature Touch panel is put into a test machine at the condition of 80 for 120 hours. Then it is left at the room temperature for 24 hours or more. The measurement must satisfy the following: - Circuit close resistance: as Sec. 3.3 - Circuit open resistance: as Sec. 3.4 - Contact bounce: as Sec. 3.5 - Linearity test: as Sec. 3.6 5.2 Exposure to low temperature Touch panel is put into a test machine at the condition of -20 for 120 hours. Then it is left at the room temperature for 24 hours or more. The measurement must satisfy the following: - Circuit close resistance: as Sec. 3.3 - Circuit open resistance: as Sec. 3.4 - Contact bounce: as Sec. 3.5 - Linearity test: as Sec. 3.6 Changes that contribute to technical improvement are subject to alternations 2002 Datum Name Bearb. 24.10. Maurer Gepr. 24.10. Maurer TOUCHSCREEN 15“, 5-Wire Vert. EDV-Datasheet SPECIFICATIONS OF ANALOG RESISTIVE don’t change manually Manufactured bei Apex Material Technology Corp. PET-ON-GLASS TOUCH SCREEN H Zu Änd. Datum Name D 79346 Endingen 1070.0442 Blatt 2 von 3 Index: - 5.3 Exposure to constant temperature and humidity Touch panel is put into a test machine at the condition of 60 , 90%RH for 120 hours. Then it is left at the room temperature for 24 hours or more. The measurement must satisfy the following: - Circuit close resistance: as Sec. 3.3 - Circuit open resistance: as Sec. 3.4 - Contact bounce: as Sec. 3.5 - Linearity test: as Sec. 3.6 5.4 Thermal Shock Touch panel is put into a test machine at the condition of -20 for 30 minutes, and then 80 for 30 minutes. The process is repeated by 10 cycles. Then it is left at the room temperature for 24 hours or more. The measurement must satisfy the following: - Circuit close resistance: as Sec. 3.3 - Circuit open resistance: as Sec. 3.4 - Contact bounce: as Sec. 3.5 - Linearity test: as Sec. 3.6 6. Durability test: 6.1 Finger touches Touch panel is hit 36 millions times with a silicone rubber of R8 finger, hitting rate is by 250g at 2 times per second. The measurement must satisfy the following: - Circuit close resistance: as Sec. 3.3 - Circuit open resistance: as Sec. 3.4 - Contact bounce: as Sec. 3.5 - Linearity test: as Sec. 3.6 6.2 Stylus writing Touch panel is drawn by R0.8 Derlin stylus pen, at 250g forces, repeat one inch by 100K times. The measurement must satisfy the following: - Circuit close resistance: as Sec. 3.3 - Circuit open resistance: as Sec. 3.4 - Contact bounce: as Sec. 3.5 - Linearity test: as Sec. 3.6 7. Optical Performance: 7.1 Optical inspection method and optical defect standards refer to document. A001-2 Touch Screen Optical Quality Standard. 7.2 Outside to Active Area : any optical defected in this area need to be ignored if no effected to touch screen function. 7.3 Glass defects such as edge chips and scratches refer to A001-2, Touch Screen Optical Quality Standard. 7.4 Others 7.4.1 7.4.2 7.4.3 Folding line should be avoided on the pressure sensitive adhesive. Refer to document A001-2, Touch Screen Optical Quality Standard. Always store the touch screen in its original shipping container under normal Conditions (20~25°C, 65% RH) Changes that contribute to technical improvement are subject to alternations 2002 Datum Name Bearb. 24.10. Maurer Gepr. 24.10. Maurer TOUCHSCREEN 15“, 5-Wire Vert. EDV-Datasheet SPECIFICATIONS OF ANALOG RESISTIVE don’t change manually Manufactured bei Apex Material Technology Corp. PET-ON-GLASS TOUCH SCREEN H Zu Änd. Datum Name D 79346 Endingen 1070.0442 Blatt 3 von 3 Index: -