Kemet C0805C226Z3VACTU Y5v dielectric, 6.3- 50 vdc (commercial grade) Datasheet

Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs)
Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Overview
KEMET’s Y5V dielectric features an 85°C maximum
operating temperature and is considered “general-purpose.”
The Electronics Components, Assemblies & Materials
Association (EIA) characterizes Y5V dielectric as a Class III
material. Components of this classification are fixed, ceramic
dielectric capacitors suited for bypass and decoupling or other
applications in which dielectric losses, high insulation resistance
and capacitance stability are not of major importance. Y5V exhibits
a predictable change in capacitance with respect to time and
voltage and displays wide variations in capacitance with reference
to ambient temperature. Capacitance change is limited to +22%,
−82% from −30°C to +85°C.
Benefits
Applications
•
•
•
•
•
•
•
•
Typical applications include limited temperature, decoupling and
bypass.
−30°C to +85°C operating temperature range
Lead (Pb)-Free, RoHS and REACH compliant
EIA 0402, 0603, 0805, 1206, and 1210 case sizes
DC voltage ratings of 6.3 V, 10 V, 16 V, 25 V, and 50 V
Capacitance offerings ranging from 0.022 μF to 22 μF
Available capacitance tolerance of +80%/−20%
Non-polar device, minimizing installation concerns
100% pure matte tin-plated termination finish that allowing for
excellent solderability
Click image above for interactive 3D content
Open PDF in Adobe Reader for full functionality
Ordering Information
C
1210
Case Size
Ceramic
(L" x W")
0402
0603
0805
1206
1210
1
C
226
Z
Specification/
Series
Capacitance
Code (pF)
Capacitance
Tolerance
C = Standard
Two significant
digits + number
of zeros
Z = +80%/-20%
M = ±20%
4
V
A
C
TU
Failure Rate/
Rated Voltage
Packaging/Grade
Termination Finish1
Dielectric
Design
(C-Spec)
(VDC)
9 = 6.3
8 = 10
4 = 16
3 = 25
5 = 50
V = Y5V
A = N/A
C = 100% Matte
Sn
See "Packaging
C-Spec Ordering
Options Table"
below
Additional termination finish options may be available. Contact KEMET for details.
One world. One KEMET
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
1
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Packaging C-Spec Ordering Options Table
Packaging/Grade
Ordering Code (C-Spec)
Packaging Type1
Bulk Bag / Unmarked
7" Reel / Unmarked
13" Reel / Unmarked
7" Reel / Marked
13" Reel / Marked
7" Reel / Unmarked / 2mm pitch2
13" Reel / Unmarked / 2mm pitch2
Not required (Blank)
TU
7411 (EIA 0603 and smaller case sizes)
7210 (EIA 0805 and larger case sizes)
TM
7040 (EIA 0603 and smaller case sizes)
7215 (EIA 0805 and larger case sizes)
7081
7082
Default packaging is "Bulk Bag". An ordering code C-Spec is not required for "Bulk Bag" packaging.
The terms "Marked" and "Unmarked" pertain to laser marking option of capacitors. All packaging options labeled as "Unmarked" will contain capacitors that have
not been laser marked. Please contact KEMET if you require a laser marked option. For more information see "Capacitor Marking".
2
The 2 mm pitch option allows for double the packaging quantity of capacitors on a given reel size. This option is limited to EIA 0603 (1608 metric) case size
devices. For more information regarding 2 mm pitch option see "Tape & Reel Packaging Information".
1
1
Dimensions – Millimeters (Inches)
L
W
B
T
S
EIA
Size
Code
Metric
Size
Code
B
Bandwidth
S
Separation
Minimum
Mounting
Technique
0402
1005
1.00 (0.040) ±0.05 (0.002) 0.50 (0.020) ±0.05 (0.002)
0.30 (0.012) ±0.10 (0.004)
0.30 (0.012)
Solder Reflow Only
0603
1608
1.60 (0.063) ±0.15 (0.006) 0.80 (0.032) ±0.15 (0.006)
0.70 (0.028)
3216
0.35 (0.014) ±0.15 (0.006)
See Table 2
2.00 (0.079) ±0.20 (0.008) 1.25 (0.049) ±0.20 (0.008)
0.50 (0.02) ±0.25 (0.010)
for Thickness
3.20 (0.126) ±0.20 (0.008) 1.60 (0.063) ±0.20 (0.008)
0.50 (0.02) ±0.25 (0.010)
0805
2012
1206
1210
3225
3.20 (0.126) ±0.20 (0.008) 2.50 (0.098) ±0.20 (0.008)
L
Length
W
Width
T
Thickness
0.50 (0.02) ±0.25 (0.010)
0.75 (0.030)
N/A
Solder Wave or
Solder Reflow
Solder Reflow Only
Qualification/Certification
Commercial Grade products are subject to internal qualification. Details regarding test methods and conditions are referenced in
Table 4, Performance & Reliability.
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
2
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Environmental Compliance
Lead (Pb)-Free, RoHS, and REACH compliant without exemptions.
Electrical Parameters/Characteristics
Item
Parameters/Characteristics
Operating Temperature Range
Capacitance Change with Reference to +25°C and 0 Vdc Applied (TCC)
Aging Rate (Maximum % Capacitance Loss/Decade Hour)
1
2
3
4
Dielectric Withstanding Voltage (DWV)
Dissipation Factor (DF) Maximum Limit @ 25°C
Insulation Resistance (IR) Minimum Limit @ 25°C
-30°C to +85°C +22%, -82%
7.0%
250% of rated voltage
(5 ± 1 seconds and charge/discharge not exceeding 50mA)
10% (6.3V & 10V), 7% (16V & 25V) and 5% (50V )
See Insulation Resistance Limit Table
(Rated voltage applied for 120 ± 5 secs @ 25°C)
Regarding Aging Rate: Capacitance measurements (including tolerance) are indexed to a referee time of 48 or 1,000 hours. Please refer to a part number specific
datasheet for referee time details.
2
DWV is the voltage a capacitor can withstand (survive) for a short period of time. It exceeds the nominal and continuous working voltage of the capacitor.
3
Capacitance and dissipation factor (DF) measured under the following conditions:
1kHz ± 50Hz and 1.0 ± 0.2 Vrms if capacitance ≤10µF
120Hz ± 10Hz and 0.5 ± 0.1 Vrms if capacitance >10µF
4
To obtain IR limit, divide MΩ-µF value by the capacitance and compare to GΩ limit. Select the lower of the two limits.
Note: When measuring capacitance it is important to ensure the set voltage level is held constant. The HP4284 & Agilent E4980 have a feature known as
Automatic Level Control (ALC). The ALC feature should be switched to "ON".
1
Post Environmental Limits
High Temperature Life, Biased Humidity, Moisture Resistance
Dielectric
Rated DC
Voltage
Capacitance
Value
Dissipation Factor
(Maximum %)
> 25
Y5V
16/25
Capacitance
Shift
Insulation
Resistance
±30% 10% of Initial Limit
7.5
All
< 16
10.0
15.0
Insulation Resistance Limit Table
EIA Case Size
100 Megohm
Microfarads or 10 GΩ
50 Megohm
Microfarads or 10 GΩ
All
≥ 16 V
≤ 10 V
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
3
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Table 1 – Capacitance Range/Selection Waterfall (0402 – 1210 Case Sizes)
5
9
8
4
3
5
50
3
16
4
25
8
10
9
6.3
5
50
16
3
25
10
FD
FD
FD
FD
FD
FD
FD
FF
FH
FD
FD
FD
FJ
FE
FT
FG
FH
FH²
FH
FT²
FD
FD
FD
FD
FD
FD
FD
FF
FH
FD
FD
FD
FJ
FE
FT
FG
FH
FH²
FH
FT²
FD
FD
FD
FD
FD
FD
FD
FF
FH
FD
FD
FD
FJ
FE
FT
FG
FH
FH²
FH
FS
FD
FD
FD
FD
FD
FD
FD
FF
FH
FD
FD
FD
FD
FD
FD
FD
FF
FH
C0402C
EH
FS
50
EH
25
EH
EC
EB
EB
EB
EC
EB
EB
EB
EP
16
EH
EC
EB
EB
EB
EC
EB
EB
EB
EP
EC
EC
ED
EC
EH
EM²
EJ
10
EC
EB
EB
EB
EC
EB
EB
EB
EP
EC
EC
ED
EC
EH
EM²
EJ
EJ
EH
6.3
EC
EB
EB
EB
EC
EB
EB
EB
DG EP
EC
EC
ED
EC
EH
EM²
EJ
EJ
EH
50
8
DG
25
9
DN
DN
DN
DP
DO
DP
DP
DP
DN
16
4
DN
DN
DN
DP
DO
DP
DP
DP
DN
DN
DN
DN
DN
DN
DG
DN
DG
DP
DG
DG
DG
10
8
DN
DN
DN
DP
DO
DP
DP
DP
DN
DN
DN
DN
DN
DN
DG
DN
DG
DP
DP
DG
DP
DN
DN
DP
DG
DG
DG
6.3
9
DN
DN
DN
DP
DO
DP
DP
DP
DN
DN
DN
DN
DN
DN
DG
DN
DG
DP
DP
DG
DP
DN
DN
DP
DG
DL
DG
DF
DG
DG
50
Voltage Code
DN
DN
DN
DP
DO
DP
DP
DP
DN
DN
DN
DN
DN
DN
DG
DN
DG
DP
DP
DG
CG CG DP
DN
DN
DP
DG
DL
DG
DF
DG
DG
25
BB
CF
CF
CF
CF
CF
CF
CF
CF
CG
CG
CG
CG
CG
CG
CG
16
BB
10
BB
6.3
BB
CF
CF
CF
CF
CF
CF
CF
CF
CG
CG
CG
CG
CG
CG
CG
CG
CG
10
BB
CF
CF
CF
CF
CF
CF
CF
CF
CG
CG
CG
CG
CG
CG
CG
CG
CG
CG
CG
CG
CG
6.3
BB
CF
CF
CF
CF
CF
CF
CF
CF
CG
CG
CG
CG
CG
CG
CG
CG
CG
CG
CG
CG
CG
16
BB
BB
BB
BB
BB
BB
BB
BB
BB
25
BB
BB
BB
BB
BB
BB
BB
BB
BB
Rated Voltage (VDC)
Case Size/
Series
4
16
6.3
BB
BB
BB
BB
BB
BB
BB
BB
BB
16
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
Z
10
Capacitance
Code
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
M
6.3
Capacitance
223
273
333
393
473
563
683
823
104
124
154
184
224
274
334
394
474
564
684
824
105
125
155
185
225
335
475
565
685
106
156
226
8
C1210C
Product Availability and Chip Thickness Codes
See Table 2 for Chip Thickness Dimensions
Capacitance Tolerance
22,000 pF
27,000 pF
33,000 pF
39,000 pF
47,000 pF
56,000 pF
68,000 pF
82,000 pF
0.10 µF
0.12 µF
0.15 µF
0.18 µF
0.22 µF
0.27 µF
0.33 µF
0.39 µF
0.47 µF
0.56 µF
0.68 µF
0.82 µF
1.0 µF
1.2 µF
1.5 µF
1.8 µF
2.2 µF
3.3 µF
4.7 µF
5.6 µF
6.8 µF
10 µF
15 µF
22 µF
9
10
Rated Voltage (VDC)
3
6.3
4
50
8
25
9
16
4
10
8
C1206C
25
9
C0805C
6.3
Voltage Code
16
C0603C
10
Capacitance
Code
C0402C
6.3
Capacitance
Case Size/
Series
4
3
9
8
4
3
5
9
8
4
3
5
9
8
4
3
5
C0603C
C0805C
C1206C
C1210C
xx² Only available in Z tolerance.
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
4
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Table 2A – Chip Thickness/Tape & Reel Packaging Quantities
Thickness
Code
Case
Size1
Thickness ±
Range (mm)
BB
CF
CG
DN
DO
DP
DL
DF
DG
EB
EC
ED
EP
EM
EH
EJ
FD
FE
FF
FG
FH
FJ
FT
FS
0402
0603
0603
0805
0805
0805
0805
0805
0805
1206
1206
1206
1206
1206
1206
1206
1210
1210
1210
1210
1210
1210
1210
1210
0.50 ± 0.05
0.80 ± 0.07*
0.80 ± 0.10*
0.78 ± 0.10*
0.80 ± 0.10*
0.90 ± 0.10*
0.95 ± 0.10
1.10 ± 0.10
1.25 ± 0.15
0.78 ± 0.10
0.90 ± 0.10
1.00 ± 0.10
1.20 ± 0.20
1.25 ± 0.15
1.60 ± 0.20
1.70 ± 0.20
0.95 ± 0.10
1.00 ± 0.10
1.10 ± 0.10
1.25 ± 0.15
1.55 ± 0.15
1.85 ± 0.20
1.90 ± 0.20
2.50 ± 0.30
Thickness
Code
Case
Size1
Thickness ±
Range (mm)
Paper Quantity1
Plastic Quantity
7" Reel
13" Reel
7" Reel
13" Reel
7" Reel
13" Reel
7" Reel
13" Reel
10,000
4,000
4,000
4,000
4,000
4,000
0
0
0
4,000
0
0
0
0
0
0
0
0
0
0
0
0
0
0
50,000
15,000
15,000
15,000
15,000
15,000
0
0
0
10,000
0
0
0
0
0
0
0
0
0
0
0
0
0
0
Paper Quantity1
0
0
0
0
0
0
4,000
2,500
2,500
4,000
4,000
2,500
2,500
2,500
2,000
2,000
4,000
2,500
2,500
2,500
2,000
2,000
2,000
1,000
0
0
0
0
0
0
10,000
10,000
10,000
10,000
10,000
10,000
10,000
10,000
8,000
8,000
10,000
10,000
10,000
10,000
8,000
8,000
8,000
4,000
Plastic Quantity
Package quantity based on finished chip thickness specifications.
1
If ordering using the 2 mm Tape and Reel pitch option, the packaging quantity outlined in the table above will be doubled. This option is limited to EIA 0603 (1608 metric)
case size devices. For more information regarding 2 mm pitch option see “Tape & Reel Packaging Information”.
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
5
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Table 2B – Bulk Packaging Quantities
Loose Packaging
Packaging Type
Bulk Bag (default)
Packaging C-Spec
N/A 2
Case Size
Packaging Quantities (pieces/unit packaging)
1
EIA (in)
Metric (mm)
0402
0603
0805
1206
1210
1808
1812
1825
2220
2225
1005
1608
2012
3216
3225
4520
4532
4564
5650
5664
Minimum
Maximum
50,000
1
20,000
The "Packaging C-Spec" is a 4 to 8 digit code which identifies the packaging type and/or product grade. When ordering, the proper code must be included in the 15th
through 22nd character positions of the ordering code. See "Ordering Information" section of this document for further details. Commercial Grade product ordered without
a packaging C-Spec will default to our standard "Bulk Bag" packaging. Contact KEMET if you require a bulk bag packaging option for Automotive Grade products.
2
A packaging C-Spec (see note 1 above) is not required for "Bulk Bag" packaging (excluding Anti-Static Bulk Bag and Automotive Grade products). The 15th through
22nd character positions of the ordering code should be left blank. All product ordered without a packaging C-Spec will default to out standard "Bulk Bag" packaging.
1
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
6
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Table 3 – Chip Capacitor Land Pattern Design Recommendations per IPC-7351
EIA
Size
Code
Metric
Size
Code
0402
Density Level A:
Maximum (Most)
Land Protrusion (mm)
Density Level B:
Median (Nominal)
Land Protrusion (mm)
Density Level C:
Minimum (Least)
Land Protrusion (mm)
C
Y
X
V1
V2
C
Y
X
V1
V2
C
Y
X
V1
V2
1005
0.50
0.72
0.72
2.20
1.20
0.45
0.62
0.62
1.90
1.00
0.40
0.52
0.52
1.60
0.80
0603
1608
0.90
1.15
1.10
4.00
2.10
0.80
0.95
1.00
3.10
1.50
0.60
0.75
0.90
2.40
1.20
0805
2012
1.00
1.35
1.55
4.40
2.60
0.90
1.15
1.45
3.50
2.00
0.75
0.95
1.35
2.80
1.70
1206
3216
1.60
1.35
1.90
5.60
2.90
1.50
1.15
1.80
4.70
2.30
1.40
0.95
1.70
4.00
2.00
1210
3225
1.60
1.35
2.80
5.65
3.80
1.50
1.15
2.70
4.70
3.20
1.40
0.95
2.60
4.00
2.90
12101
3225
1.50
1.60
2.90
5.60
3.90
1.40
1.40
2.80
4.70
3.30
1.30
1.20
2.70
4.00
3.00
Only for capacitance values ≥ 22 µF
Density Level A: For low-density product applications. Recommended for wave solder applications and provides a wider process window for reflow solder
processes. KEMET only recommends wave soldering of EIA 0603, 0805, and 1206 case sizes.
Density Level B: For products with a moderate level of component density. Provides a robust solder attachment condition for reflow solder processes.
Density Level C: For high component density product applications. Before adapting the minimum land pattern variations the user should perform qualification
testing based on the conditions outlined in IPC Standard 7351 (IPC–7351).
1
Image below based on Density Level B for an EIA 1210 case size.
V1
Y
Y
X
X
C
C
V2
Grid Placement Courtyard
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
7
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Soldering Process
Recommended Soldering Technique:
• Solder wave or solder reflow for EIA case sizes 0603, 0805 and 1206
• All other EIA case sizes are limited to solder reflow only
Recommended Reflow Soldering Profile:
KEMET’s families of surface mount multilayer ceramic capacitors (SMD MLCCs) are compatible with wave (single or dual), convection,
IR or vapor phase reflow techniques. Preheating of these components is recommended to avoid extreme thermal stress. KEMET’s
recommended profile conditions for convection and IR reflow reflect the profile conditions of the IPC/J-STD-020 standard for moisture
sensitivity testing. These devices can safely withstand a maximum of three reflow passes at these conditions.
Preheat/Soak
Temperature Minimum (TSmin)
Temperature Maximum (TSmax)
Time (tS) from TSmin to TSmax
Ramp-Up Rate (TL to TP)
Termination Finish
SnPb
100% Matte Sn
100°C
150°C
60 – 120 seconds
150°C
200°C
60 – 120 seconds
183°C
217°C
Time Above Liquidous (tL)
60 – 150 seconds
60 – 150 seconds
Peak Temperature (TP)
235°C
260°C
Time Within 5°C of Maximum
Peak Temperature (tP)
20 seconds maximum
30 seconds maximum
Time 25°C to Peak
Temperature
TL
tP
Maximum Ramp Up Rate = 3°C/sec
Maximum Ramp Down Rate = 6°C/sec
tL
Tsmax
Tsmin
tS
3°C/second maximum 3°C/second maximum
Liquidous Temperature (TL)
Ramp-Down Rate (TP to TL)
TP
Temperature
Profile Feature
25
25° C to Peak
Time
6°C/second maximum 6°C/second maximum
6 minutes maximum
8 minutes maximum
Note 1: All temperatures refer to the center of the package, measured on the
capacitor body surface that is facing up during assembly reflow.
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
8
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Table 4 – Performance & Reliability: Test Methods and Conditions
Stress
Reference
Test or Inspection Method
Terminal Strength
JIS–C–6429
Appendix 1, Note: Force of 1.8 kg for 60 seconds.
Board Flex
JIS–C–6429
Appendix 2, Note: Standard termination system – 2.0 mm (minimum) for all except 3 mm for C0G.
Flexible termination system – 3.0 mm (minimum).
Magnification 50 X. Conditions:
Solderability
J–STD–002
a) Method B, 4 hours @ 155°C, dry heat @ 235°C
b) Method B @ 215°C category 3
c) Method D, category 3 @ 260°C
Temperature Cycling
JESD22 Method JA–104
Biased Humidity
MIL–STD–202 Method 103
Moisture Resistance
MIL–STD–202 Method 106
1,000 Cycles (−55°C to +125°C). Measurement at 24 hours +/- 4 hours after test conclusion.
Load Humidity: 1,000 hours 85°C/85% RH and rated voltage. Add 100 K ohm resistor. Measurement
at 24 hours +/- 4 hours after test conclusion.
Low Volt Humidity: 1,000 hours 85°C/85% RH and 1.5 V. Add 100 K ohm resistor.
Measurement at 24 hours +/- 4 hours after test conclusion.
t = 24 hours/cycle. Steps 7a and 7b not required.
Measurement at 24 hours +/- 4 hours after test conclusion.
−55°C/+125°C. Note: Number of cycles required – 300, maximum transfer time – 20 seconds, dwell
time – 15 minutes. Air – Air.
Thermal Shock
MIL–STD–202 Method 107
High Temperature Life
MIL–STD–202 Method 108
/EIA–198
Storage Life
MIL–STD–202 Method 108
150°C, 0 VDC for 1,000 hours.
Vibration
MIL–STD–202 Method 204
5 g's for 20 min., 12 cycles each of 3 orientations. Note: Use 8" X 5" PCB 0.031" thick 7 secure
points on one long side and 2 secure points at corners of opposite sides. Parts mounted within 2"
from any secure point. Test from 10 – 2,000 Hz
Mechanical Shock
MIL–STD–202 Method 213
Figure 1 of Method 213, Condition F.
Resistance to Solvents
MIL–STD–202 Method 215
Add aqueous wash chemical, OKEM Clean or equivalent.
1,000 hours at 125°C (85°C for X5R, Z5U and Y5V) with 2 X rated voltage applied.
Storage and Handling
Ceramic chip capacitors should be stored in normal working environments. While the chips themselves are quite robust in other
environments, solderability will be degraded by exposure to high temperatures, high humidity, corrosive atmospheres, and long term
storage. In addition, packaging materials will be degraded by high temperature– reels may soften or warp and tape peel force may
increase. KEMET recommends that maximum storage temperature not exceed 40ºC and maximum storage humidity not exceed 70%
relative humidity. Temperature fluctuations should be minimized to avoid condensation on the parts and atmospheres should be free of
chlorine and sulfur bearing compounds. For optimized solderability chip stock should be used promptly, preferably within 1.5 years of
receipt.
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
9
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Construction (Typical)
Detailed Cross Section
Dielectric Material
(BaTiO3)
Dielectric Material
(BaTiO3)
Barrier Layer
(Ni)
Termination Finish
(100% Matte Sn)
End Termination/
External Electrode
(Cu)
Inner Electrodes
(Ni)
End Termination/
External Electrode
(Cu)
Barrier Layer
(Ni)
Termination Finish
(100% Matte Sn)
Inner Electrodes
(Ni)
Capacitor Marking (Optional):
Laser marking option is not available on:
•
•
•
•
C0G, Ultra Stable X8R and Y5V dielectric devices
EIA 0402 case size devices
EIA 0603 case size devices with Flexible Termination option.
KPS Commercial and Automotive grade stacked devices.
These capacitors are supplied unmarked only.
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
10
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Tape & Reel Packaging Information
KEMET offers multilayer ceramic chip capacitors packaged in 8, 12 and 16 mm tape on 7" and 13" reels in accordance with EIA
Standard 481. This packaging system is compatible with all tape-fed automatic pick and place systems. See Table 2 for details on
reeling quantities for commercial chips.
Bar Code Label
Anti-Static Reel
®
Embossed Plastic* or
Punched Paper Carrier.
ET
KEM
Chip and KPS Orientation in Pocket
(except 1825 Commercial, and 1825 and 2225 Military)
Sprocket Holes
Embossment or Punched Cavity
8 mm, 12 mm
or 16 mm Carrier Tape
178 mm (7.00")
or
330 mm (13.00")
Anti-Static Cover Tape
(.10 mm (.004") Maximum Thickness)
*EIA 01005, 0201, 0402 and 0603 case sizes available on punched paper carrier only.
Table 5 – Carrier Tape Configuration, Embossed Plastic & Punched Paper (mm)
EIA Case Size
Tape
Size
(W)*
Embossed Plastic
7" Reel
13" Reel
Punched Paper
7" Reel
Pitch (P1)*
13" Reel
Pitch (P1)*
01005 – 0402
8
2
2
0603
8
2/4
2/4
0805
8
4
4
4
4
1206 – 1210
8
4
4
4
4
1805 – 1808
12
4
4
≥ 1812
12
8
8
KPS 1210
12
8
8
KPS 1812 & 2220
16
12
12
Array 0508 & 0612
8
4
4
*Refer to Figures 1 & 2 for W and P1 carrier tape reference locations.
*Refer to Tables 6 & 7 for tolerance specifications.
New 2 mm Pitch Reel Options*
Packaging
Ordering Code
(C-Spec)
C-3190
C-3191
C-7081
C-7082
Packaging Type/Options
Automotive grade 7" reel unmarked
Automotive grade 13" reel unmarked
Commercial grade 7" reel unmarked
Commercial grade 13" reel unmarked
* 2 mm pitch reel only available for 0603 EIA case size.
2 mm pitch reel for 0805 EIA case size under development.
Benefits of Changing from 4 mm to 2 mm Pitching Spacing
• Lower placement costs
• Double the parts on each reel results in fewer reel
changes and increased efficiency
• Fewer reels result in lower packaging, shipping and
storage costs, reducing waste
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
11
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Figure 1 – Embossed (Plastic) Carrier Tape Dimensions
P2
T
T2
ØDo
[10 pitches cumulative
tolerance on tape ± 0.2 mm]
Po
E1
Ao
F
Ko
B1
E2
Bo
S1
W
P1
T1
Center Lines of Cavity
ØD 1
Cover Tape
B 1 is for tape feeder reference only,
including draft concentric about B o.
Embossment
For cavity size,
see Note 1 Table 4
User Direction of Unreeling
Table 6 – Embossed (Plastic) Carrier Tape Dimensions
Metric will govern
Constant Dimensions — Millimeters (Inches)
Tape Size
D0
8 mm
12 mm
1.5 +0.10/-0.0
(0.059 +0.004/-0.0)
16 mm
D1 Minimum
Note 1
1.0
(0.039)
1.5
(0.059)
E1
P0
1.75 ±0.10
(0.069 ±0.004)
4.0 ±0.10
(0.157 ±0.004)
R Reference S1 Minimum
Note 2
Note 3
25.0
(0.984)
2.0 ±0.05
0.600
(0.079 ±0.002)
(0.024)
30
(1.181)
P2
T
Maximum
T1
Maximum
0.600
(0.024)
0.100
(0.004)
Variable Dimensions — Millimeters (Inches)
Tape Size
Pitch
8 mm
Single (4 mm)
12 mm
Single (4 mm) &
Double (8 mm)
16 mm
Triple (12 mm)
B1 Maximum
Note 4
4.35
(0.171)
8.2
(0.323)
12.1
(0.476)
E2
Minimum
6.25
(0.246)
10.25
(0.404)
14.25
(0.561)
F
P1
3.5 ±0.05
(0.138 ±0.002)
5.5 ±0.05
(0.217 ±0.002)
7.5 ±0.05
(0.138 ±0.002)
4.0 ±0.10
(0.157 ±0.004)
8.0 ±0.10
(0.315 ±0.004)
12.0 ±0.10
(0.157 ±0.004)
T2
Maximum
2.5
(0.098)
4.6
(0.181)
4.6
(0.181)
W
Maximum
8.3
(0.327)
12.3
(0.484)
16.3
(0.642)
A0,B0 & K0
Note 5
1. The embossment hole location shall be measured from the sprocket hole controlling the location of the embossment. Dimensions of embossment location and
hole location shall be applied independent of each other.
2. The tape with or without components shall pass around R without damage (see Figure 6).
3. If S1 < 1.0 mm, there may not be enough area for cover tape to be properly applied (see EIA Standard 481 paragraph 4.3 section b).
4. B1 dimension is a reference dimension for tape feeder clearance only.
5. The cavity defined by A0, B0 and K0 shall surround the component with sufficient clearance that:
(a) the component does not protrude above the top surface of the carrier tape.
(b) the component can be removed from the cavity in a vertical direction without mechanical restriction, after the top cover tape has been removed.
(c) rotation of the component is limited to 20° maximum for 8 and 12 mm tapes and 10° maximum for 16 mm tapes (see Figure 3).
(d) lateral movement of the component is restricted to 0.5 mm maximum for 8 and 12 mm wide tape and to 1.0 mm maximum for 16 mm tape (see Figure 4).
(e) for KPS Series product, A0 and B0 are measured on a plane 0.3 mm above the bottom of the pocket.
(f) see Addendum in EIA Standard 481 for standards relating to more precise taping requirements.
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
12
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Figure 2 – Punched (Paper) Carrier Tape Dimensions
P2
T
Po
ØDo
[10 pitches cumulative
tolerance on tape ± 0.2 mm]
A0
F
P1
T1
T1
Top Cover Tape
W
E2
B0
Bottom Cover Tape
E1
G
Cavity Size,
See
Note 1, Table 7
Center Lines of Cavity
Bottom Cover Tape
User Direction of Unreeling
Table 7 – Punched (Paper) Carrier Tape Dimensions
Metric will govern
Constant Dimensions — Millimeters (Inches)
Tape Size
D0
E1
P0
P2
8 mm
1.5 +0.10 -0.0
(0.059 +0.004 -0.0)
1.75 ±0.10
(0.069 ±0.004)
4.0 ±0.10
(0.157 ±0.004)
2.0 ±0.05
(0.079 ±0.002)
G Minimum
0.10
(0.004)
Maximum
R Reference
Note 2
0.75
(0.030)
25
(0.984)
T Maximum
W Maximum
A0 B 0
1.1
(0.098)
8.3
(0.327)
8.3
(0.327)
T1 Maximum
Variable Dimensions — Millimeters (Inches)
Tape Size
Pitch
8 mm
Half (2 mm)
8 mm
Single (4 mm)
E2 Minimum
6.25
(0.246)
F
3.5 ±0.05
(0.138 ±0.002)
P1
2.0 ±0.05
(0.079 ±0.002)
4.0 ±0.10
(0.157 ±0.004)
Note 1
1. The cavity defined by A0, B0 and T shall surround the component with sufficient clearance that:
a) the component does not protrude beyond either surface of the carrier tape.
b) the component can be removed from the cavity in a vertical direction without mechanical restriction, after the top cover tape has been removed.
c) rotation of the component is limited to 20° maximum (see Figure 3).
d) lateral movement of the component is restricted to 0.5 mm maximum (see Figure 4).
e) see Addendum in EIA Standard 481 for standards relating to more precise taping requirements.
2. The tape with or without components shall pass around R without damage (see Figure 6).
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
13
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Packaging Information Performance Notes
1. Cover Tape Break Force: 1.0 Kg minimum.
2. Cover Tape Peel Strength: The total peel strength of the cover tape from the carrier tape shall be:
Tape Width
Peel Strength
8 mm
0.1 to 1.0 Newton (10 to 100 gf)
12 and 16 mm
0.1 to 1.3 Newton (10 to 130 gf)
The direction of the pull shall be opposite the direction of the carrier tape travel. The pull angle of the carrier tape shall be 165° to 180°
from the plane of the carrier tape. During peeling, the carrier and/or cover tape shall be pulled at a velocity of 300 ±10 mm/minute.
3. Labeling: Bar code labeling (standard or custom) shall be on the side of the reel opposite the sprocket holes. Refer to EIA
Standards 556 and 624.
Figure 3 – Maximum Component Rotation
°
T
Maximum Component Rotation
Top View
Maximum Component Rotation
Side View
Typical Pocket Centerline
Tape
Width (mm)
8,12
16 – 200
Bo
Maximum
Rotation (
20
10
°
T)
Typical Component Centerline
Ao
Figure 4 – Maximum Lateral Movement
8 mm & 12 mm Tape
0.5 mm maximum
0.5 mm maximum
16 mm Tape
°
s
Tape
Maximum
Width (mm) Rotation (
8,12
20
16 – 56
10
72 – 200
5
°
S)
Figure 5 – Bending Radius
Embossed
Carrier
Punched
Carrier
1.0 mm maximum
1.0 mm maximum
R
Bending
Radius
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
R
C1005_Y5V_SMD • 2/29/2016
14
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Figure 6 – Reel Dimensions
Full Radius,
See Note
W3 (Includes
Access Hole at
Slot Location
(Ø 40 mm minimum)
flange distortion
at outer edge)
W2 (Measured at hub)
D
A
(See Note)
N
C
(Arbor hole
diameter)
B
(see Note)
W1 (Measured at hub)
If present,
tape slot in core
for tape start:
2.5 mm minimum width x
10.0 mm minimum depth
Note: Drive spokes optional; if used, dimensions B and D shall apply.
Table 8 – Reel Dimensions
Metric will govern
Constant Dimensions — Millimeters (Inches)
Tape Size
A
B Minimum
C
D Minimum
8 mm
178 ±0.20
(7.008 ±0.008)
or
330 ±0.20
(13.000 ±0.008)
1.5
(0.059)
13.0 +0.5/-0.2
(0.521 +0.02/-0.008)
20.2
(0.795)
12 mm
16 mm
Variable Dimensions — Millimeters (Inches)
Tape Size
N Minimum
W1
W2 Maximum
W3
50
(1.969)
8.4 +1.5/-0.0
(0.331 +0.059/-0.0)
12.4 +2.0/-0.0
(0.488 +0.078/-0.0)
16.4 +2.0/-0.0
(0.646 +0.078/-0.0)
14.4
(0.567)
18.4
(0.724)
22.4
(0.882)
Shall accommodate tape width
without interference
8 mm
12 mm
16 mm
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
15
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Figure 7 – Tape Leader & Trailer Dimensions
Embossed Carrier
Carrier Tape
Punched Carrier
8 mm & 12 mm only
END
Round Sprocket Holes
START
Top Cover Tape
Elongated Sprocket Holes
(32 mm tape and wider)
Trailer
160 mm Minimum
Components
100 mm
Minimum Leader
400 mm Minimum
Top Cover Tape
Figure 8 – Maximum Camber
Elongated sprocket holes
(32 mm & wider tapes)
Carrier Tape
Round Sprocket Holes
1 mm Maximum, either direction
Straight Edge
250 mm
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
16
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
KEMET Corporation
World Headquarters
Europe
Asia
Southern Europe
Sasso Marconi, Italy
Tel: 39-051-939111
Northeast Asia
Hong Kong
Tel: 852-2305-1168
Mailing Address:
P.O. Box 5928
Greenville, SC 29606
Skopje, Macedonia
Tel: 389-2-55-14-623
Shenzhen, China
Tel: 86-755-2518-1306
www.kemet.com
Tel: 864-963-6300
Fax: 864-963-6521
Central Europe
Landsberg, Germany
Tel: 49-8191-3350800
Corporate Offices
Fort Lauderdale, FL
Tel: 954-766-2800
Kamen, Germany
Tel: 49-2307-438110
North America
Northern Europe
Wyboston, United Kingdom
Tel: 44-1480-273082
Taipei, Taiwan
Tel: 886-2-27528585
Espoo, Finland
Tel: 358-9-5406-5000
Southeast Asia
Singapore
Tel: 65-6701-8033
2835 KEMET Way
Simpsonville, SC 29681
Northeast
Wilmington, MA
Tel: 978-658-1663
Southeast
Lake Mary, FL
Tel: 407-855-8886
Central
Novi, MI
Tel: 248-994-1030
Beijing, China
Tel: 86-10-5877-1075
Shanghai, China
Tel: 86-21-6447-0707
Seoul, South Korea
Tel: 82-2-6294-0550
Penang, Malaysia
Tel: 60-4-6430200
Bangalore, India
Tel: 91-806-53-76817
Irving, TX
Tel: 972-915-6041
West
Milpitas, CA
Tel: 408-433-9950
Mexico
Guadalajara, Jalisco
Tel: 52-33-3123-2141
Note: KEMET reserves the right to modify minor details of internal and external construction at any time in the interest of product improvement. KEMET does not
assume any responsibility for infringement that might result from the use of KEMET Capacitors in potential circuit designs. KEMET is a registered trademark of
KEMET Electronics Corporation.
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016
17
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – Y5V Dielectric, 6.3 – 50 VDC (Commercial Grade)
Disclaimer
All product specifications, statements, information and data (collectively, the “Information”) in this datasheet are subject to change. The customer is responsible for checking and
verifying the extent to which the Information contained in this publication is applicable to an order at the time the order is placed.
All Information given herein is believed to be accurate and reliable, but it is presented without guarantee, warranty, or responsibility of any kind, expressed or implied.
Statements of suitability for certain applications are based on KEMET Electronics Corporation’s (“KEMET”) knowledge of typical operating conditions for such applications, but are
not intended to constitute – and KEMET specifically disclaims – any warranty concerning suitability for a specific customer application or use. The Information is intended for use only
by customers who have the requisite experience and capability to determine the correct products for their application. Any technical advice inferred from this Information or otherwise
provided by KEMET with reference to the use of KEMET’s products is given gratis, and KEMET assumes no obligation or liability for the advice given or results obtained.
Although KEMET designs and manufactures its products to the most stringent quality and safety standards, given the current state of the art, isolated component failures may still
occur. Accordingly, customer applications which require a high degree of reliability or safety should employ suitable designs or other safeguards (such as installation of protective
circuitry or redundancies) in order to ensure that the failure of an electrical component does not result in a risk of personal injury or property damage.
Although all product–related warnings, cautions and notes must be observed, the customer should not assume that all safety measures are indicted or that other measures may not
be required.
© KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com
C1005_Y5V_SMD • 2/29/2016