Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Overview KEMET’s High Temperature 200ºC epoxy molded radial through-hole ceramic capacitors in X7R dielectric feature a robust and proprietary dielectric system that offers industryleading performance in extreme high pressure and high temperature environments up to 200°C. These capacitors are designed specifically to withstand the severe shock and vibration conditions associated with deep-well and horizontal drilling activities and are well suited for use in aerospace engine compartments, geophysical probes, hybrid and electric automotive motor drives and defense applications. These epoxy molded radial through-hole ceramic capacitors in X7R dielectric achieve high dielectric breakdown, low leakage current and minimal parametric shift while maintaining predictable performance characteristics with respect to variations in temperature, applied voltage and time. These devices are suited for bypass and decoupling applications or for frequency discriminating circuits where Q and stability of capacitance characteristics are not critical. Capacitance change is limited to ±15% from -55°C to +125°C and +15% / -55% at +200°C. As high temperature electronic module complexity increases, the size reduction of components becomes more and more critical. These devices are significantly smaller by volume than most competitor radial molded capacitors, allowing for downsizing and replacement opportunities of larger high temperature precious metal electrode (PME) and base metal electrode (BME) dielectric system devices. They feature goldplated lead wires for temperature resistance and an epoxy molded case for environmental protection and mechanical durability. Click image above for interactive 3D content Open PDF in Adobe Reader for full functionality Ordering Information C 062 Ceramic Style/Size 052 062 H 105 Specification/ Series Capacitance Code (pF) K 5 R Capacitance Rated Voltage Dielectric Tolerance1 (VDC) H = High Temp 2 significant digits + J = ±5% 200ºC number of zeros K = ±10% Use 9 for 1.0 – 9.9 pF M = ±20% ex. 2.2 pF = 229 5 = 50 1 = 100 2 = 200 5 G A 7303 Design Lead Finish2 Failure Rate Packaging C-Spec3 R = X7R 5 = Multilayer G = Gold (Au) A = N/A Blank = Bulk Bag T250 = 250 pcs / 12" Reel T500 = 500 pcs / 12" Reel T1K0 = 1,000 pcs / 12" Reel 7301 = Full Reel Qty / 12" Reel 7303 = Full Reel Qty / 12" Reel 7061 = Bulk Tray Additional capacitance tolerance offerings may be available. Contact KEMET for details. Wire lead materials and finishes: Alternative lead materials and finishes may be available. Contact KEMET for details. 3 Default packaging for this product series is "Bulk Bag". KEMET will assume "Bulk Bag" packaging is required when the 15th thru 18th character positions are left blank. 3 C-Spec 7301 can only be used when ordering 052 style/size. 3 C-Spec 7303 can only be used when ordering 062 style/size. 1 2 One world. One KEMET © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 1 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Dimensions – Inches (Millimeters) C052H C062H L 0.045 (1.143) Maximum T L H H LL LD LL LD S Series T S S Lead Spacing L Length H Height T Thickness LD Lead Diameter LL Lead Length Minimum 0.20 ±0.015 (5.08 ±0.38) 0.19 ±0.01 (4.83 ±0.25) 0.29 ±0.01 (7.37 ±0.25) 0.19 ±0.01 (4.83 ±0.25) 0.29 ±0.01 (7.37 ±0.25) 0.09 ±0.01 (2.29 ±0.25) 0.09 ±0.01 (2.29 ±0.25) 0.025 +0.004/ -0.002 (0.635 +0.102/ -0.051) 1.25 (31.75) C052H C062H Benefits • Operating temperature range of -55°C to +200°C • X7R temperature stable dielectric • High shock and vibration capability • Radial through-hole form factor • Gold (Au) plated wire lead finish • Base metal electrode (BME) and precious metal electrode (PME) dielectric systems. • RoHS and REACH compliant (most select values) • Military designation styles CK/CKR05 and CK/CKR06 • Molded case • High breakdown voltage strength • DC voltage ratings of 50 V, 100 V & 200 V • Capacitance offerings ranging from 1,000 pF to 1.0 μF • Available capacitance tolerances of ±5%, ±10% & ±20% • Low ESR and ESL • Predictable performance characteristics with respect to variations in temperature, applied voltage and time • Non-polar device, minimizing installation concerns • Encapsulation meets flammability standard UL 94V-0 • Halogen-free Applications Typical applications include decoupling, bypass, smoothing circuits, DC/DC converters, power supplies (input/output filters), noise reduction (piezoelectric/mechanical), circuits with a direct battery or power source connection, critical and safety relevant circuits without (integrated) current limitation and any application that is subject to extreme environments such as high shock and vibration, high temperature, high levels of board flexure and/or temperature cycling. Markets include military, industrial, aerospace, and automotive. © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 2 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Qualification These devices are subject to internal qualification. Details regarding test methods and conditions are referenced in Table 2, Performance & Reliability. Environmental Compliance RoHS compliance is dependent upon series and rated capacitance value. 1 Series Rated Capacitance RoHS Compliant RoHS Exemption Code1 Halogen Free C052H All Yes 7(a) Yes C062H < 0.27µF Yes 7(a) Yes C062H ≥ 0.27µF No n/a Yes 7(a): Lead in high melting temperature type solders Electrical Parameters/Characteristics Item Parameters/Characteristics Operating Temperature Range -55°C to +200°C Capacitance Change with Reference to +25°C and 0 VDC Applied (TCC) ±15% (-55°C to +125°C), +15% / -55% (200°C) Capacitance Change with Reference to +25°C and 100% Rated VDC Applied +15% / -30% (-55°C to +125°C), +15% / -60% (200°C) Aging Rate (Maximum % Cap Loss/Decade Hour) Dielectric Withstanding Voltage Dissipation Factor (DF) Maximum Limit at 25ºC Insulation Resistance (IR) Limit at 25°C 3% 250% of rated voltage (5 ±1 seconds and charge/discharge not exceeding 50 mA at 25°C) 2.50% 1,000 MΩ microfarads or 100 GΩ (Rated voltage applied for 120 ±5 seconds) Regarding aging rate: Capacitance measurements (including tolerance) are indexed to a referee time of 1,000 hours. To obtain IR limit, divide MΩ-µF value by the capacitance and compare to GΩ limit. Select the lower of the two limits. Capacitance and dissipation factor (DF) measured under the following conditions: 1 kHz ±50 Hz and 1.0 ±0.2 Vrms if capacitance ≤ 10 µF 120 Hz ±10 Hz and 0.5 ±0.1 Vrms if capacitance > 10 µF Note: When measuring capacitance it is important to ensure the set voltage level is held constant. The HP4284 and Agilent E4980 have a feature known as Automatic Level Control (ALC). The ALC feature should be switched to "ON." Post Environmental Limits High Temperature Life, Biased Humidity, Moisture Resistance Dielectric Rated DC Voltage Capacitance Value DF (%) Capacitance Shift IR X7R > 25 All 3.0 ±20% 10% of Initial Limit © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 3 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Table 1A – C052 Style/Size (0.20" Lead Spacing), Capacitance Range Waterfall C052 Style/Size (0.20" Lead Spacing) Rated Voltage (VDC) 50 100 200 Voltage Code 5 1 2 Capacitance Tolerance Capacitance 1,000 pF 1,200 pF 1,500 pF 1,800 pF 2,200 pF 2,700 pF 3,300 pF 3,900 pF 4,700 pF 5,600 pF 6,800 pF 8,200 pF 0.01 µF 0.012 µF 0.015 µF 0.018 µF 0.022 µF 0.027 µF 0.033 µF 0.039 µF 0.047 µF 0.056 µF 0.068 µF 0.082 µF 0.1 µF Capacitance Code (Available Capacitance) C052H102(1)5R5GA(2) C052H122(1)5R5GA(2) C052H152(1)5R5GA(2) C052H182(1)5R5GA(2) C052H222(1)5R5GA(2) C052H272(1)5R5GA(2) C052H332(1)5R5GA(2) C052H392(1)5R5GA(2) C052H472(1)5R5GA(2) C052H562(1)5R5GA(2) C052H682(1)5R5GA(2) C052H822(1)5R5GA(2) C052H103(1)5R5GA(2) C052H123(1)5R5GA(2) C052H153(1)5R5GA(2) C052H183(1)5R5GA(2) C052H223(1)5R5GA(2) C052H273(1)5R5GA(2) C052H333(1)5R5GA(2) C052H393(1)5R5GA(2) C052H473(1)5R5GA(2) C052H563(1)5R5GA(2) C052H683(1)5R5GA(2) C052H823(1)5R5GA(2) C052H104(1)5R5GA(2) C052H102(1)1R5GA(2) C052H122(1)1R5GA(2) C052H152(1)1R5GA(2) C052H182(1)1R5GA(2) C052H222(1)1R5GA(2) C052H272(1)1R5GA(2) C052H332(1)1R5GA(2) C052H392(1)1R5GA(2) C052H472(1)1R5GA(2) C052H562(1)1R5GA(2) C052H682(1)1R5GA(2) C052H822(1)1R5GA(2) C052H103(1)1R5GA(2) C052H123(1)1R5GA(2) C052H153(1)1R5GA(2) C052H183(1)1R5GA(2) C052H223(1)1R5GA(2) C052H273(1)1R5GA(2) C052H333(1)1R5GA(2) C052H393(1)1R5GA(2) C052H473(1)1R5GA(2) C052H102(1)2R5GA(2) C052H122(1)2R5GA(2) C052H152(1)2R5GA(2) C052H182(1)2R5GA(2) C052H222(1)2R5GA(2) C052H272(1)2R5GA(2) C052H332(1)2R5GA(2) Rated Voltage (VDC) 50 100 200 Voltage Code 5 1 2 J = ±5% K = ±10% M = ±20% (1) To complete ordering code, insert the proper character for capacitance tolerance: (See table above for character definitions) (1) Available capacitance tolerances: J, K, M (2) To complete ordering code, enter the four-digit numeric or alphanumeric "Packaging C-Spec Ordering Code." See details below: Blank = Bulk Bag T250 = 250 pcs / 12" Reel T500 = 500pcs / 12" Reel T1K0 = 1,000 pcs / 12" reel 7301 = Full Reel Qty / 12" reel 7303 = Full Reel Qty / 12" reel 7061 = Bulk Tray These products are protected under U.S. Patents 7172985 & 7670981, other patents pending, and any foreign counterparts. © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 4 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Table 1B – C062 Style/Size (0.20" Lead Spacing), Capacitance Range Waterfall C062 Style/Size (0.20" Lead Spacing) Rated Voltage (VDC) 50 100 200 Voltage Code 5 1 2 Capacitance Tolerance Capacitance 4,700 pF 5,600 pF 6,800 pF 0.056 µF 0.068 µF 0.082 µF 0.1 µF 0.12 µF 0.15 µF 0.18 µF 0.22 µF 0.27 µF 0.33 µF 0.39 µF 0.47 µF 0.56 µF 0.68 µF 0.82 µF 1.0 µF Capacitance Code (Available Capacitance) C062H563(1)1R5GA(2) C062H683(1)1R5GA(2) C062H823(1)1R5GA(2) C062H104(1)1R5GA(2) C062H124(1)1R5GA(2) C062H124(1)5R5GA(2) C062H154(1)5R5GA(2) C062H184(1)5R5GA(2) C062H224(1)5R5GA(2) C062H274(1)5R5GA(2) C062H334(1)5R5GA(2) C062H394(1)5R5GA(2) C062H474(1)5R5GA(2) C062H564(1)5R5GA(2) C062H684(1)5R5GA(2) C062H824(1)5R5GA(2) C062H105(1)5R5GA(2) J = ±5% K = ±10% M = ±20% C062H472(1)2R5GA(2) C062H562(1)2R5GA(2) C062H682(1)2R5GA(2) Rated Voltage (VDC) 50 100 200 Voltage Code 5 1 2 (1) To complete ordering code, insert the proper character for capacitance tolerance: (See table above for character definitions) (1) Available capacitance tolerances: J, K, M (2) To complete ordering code, enter the four-digit numeric or alphanumeric "Packaging C-Spec Ordering Code." See details below: Blank = Bulk Bag T250 = 250 pcs / 12" Reel T500 = 500pcs / 12" Reel T1K0 = 1,000 pcs / 12" reel 7301 = Full Reel Qty / 12" reel 7303 = Full Reel Qty / 12" reel 7061 = Bulk Tray These products are protected under U.S. Patents 7172985 & 7670981, other patents pending, and any foreign counterparts. Packaging Quantities Packaging Options Bulk Bag (default) 1 Bulk Tray Tape and Reel Packaging Quantities 3 Ordering Code C-Spec 2 Style/ Series n/a 7061 T250 T500 T1K0 7301 7303 C052H 100 pcs / bag 50 pcs / tray 250 500 1,000 2,000 n/a C062H 100 pcs / bag 40 pcs / tray 250 500 1,000 n/a 1,500 Default packaging for this product series is "Bulk Bag". KEMET will assume " Bulk Bag" packaging is required unless a valid C-spec is included in the 15th thru 18th character positions of the ordering code. For more information see "Ordering Information" section of this document. 1, 2 The " Ordering Code C-Spec" is a four-digit code that follows the KEMET part number and identifies any special packaging or processing requirements. Failure to include a C-Spec when ordering will result in the default packaging option. Default packaging for this product series is "Bulk Bag". 3 Packaging quantities reported above are considered "minimum order quantities" and are mandatory. 1 © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 5 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Soldering Process Recommended Soldering Technique: • Solder Wave • Hand Soldering (Manual) Recommended Soldering Profile: • Optimum Wave Solder Profile • Hand Soldering (Manual) Manual Solder Profile with Pre -heating Soldering Gradual Cooling Max 3 seconds Delta T <= 120 °C Gradual Preheat 60-120 Seconds Recommend 2.5 °C/sec KEMET recommends following the guidelines and techniques outlined in technical bulletins F2103 and F9207. © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 6 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Table 2 – Performance & Reliability: Test Methods and Conditions Stress Reference Test or Inspection Method Solderability J–STD–002 Temperature Cycling JESD22 Method JA–104 Biased Humidity MIL–STD–202 Method 103 Immersion MIL–STD–202 Method 104 Test condition B Storage Life MIL–STD–202 Method 108 Unpowered 1,000 hours at 200°C. Measurement at 24 hours ±4 hours after test conclusion. IR Measurement at 150°C High Temperature Life MIL–STD–202 Method 108 1,000 hours at 200°C with rated voltage applied. High Temperature Lead Pull KEMET Defined Test Vibration MIL–STD–202 Method 204 Resistance to Soldering Heat 5g for 20 minutes, 12 cycles each of 3 orientations. Note: Use 8" X 5" PCB. 031" thick 7 secure points on one long side and 2 secure points at corners of opposite sides. Parts mounted within 2" from any secure point. Test from 10 – 2000 Hz. MIL–STD–202 Method 210 Test Condition B, Solder dip. Note: no preheat of samples. Terminal Strength MIL–STD–202 Method 211 Test Condition A. 454g 5 – 10 s; Bend test © 227g, 3 bends Mechanical Shock MIL–STD–202 Method 213 Test Condition D. Figure 1 of Method 213. Resistance to Solvents MIL–STD–202 Method 215 Add aqueous wash chemical – OKEM Clean or equivalent. Method A at 235°C, category 3 50 cycles (-55°C to 220°C), measurement at 24 ±4 hours after test conclusion. 30 minutes maximum dwell time at each temperature extreme. 8 minutes maximum transition time. Load humidity: 1,000 hours 85°C/85% RH and rated voltage. Add 100 K ohm resistor. Measurement at 24 hours ±4 hours after test conclusion. Low volt humidity: 1,000 hours 85°C/85% RH and 1.5 V. Add 100 K ohm resistor. Measurement at 24 hours ±4 hours after test conclusion. Peel to Failure (25ºC and 200ºC): 4 lbs (1.84 kg) minimum Storage & Handling The un-mounted storage life of a through-hole (leaded) ceramic capacitor is dependent upon storage and atmospheric conditions as well as packaging materials. While the ceramic chips enveloped under the epoxy coating themselves are quite robust in most environments, solderability of the wire lead on the final epoxy-coated product will be degraded by exposure to high temperatures, high humidity, corrosive atmospheres, and long term storage. In addition, packaging materials will be degraded by high temperature and exposure to direct sunlight – reels may soften or warp, and tape peel force may increase. KEMET recommends storing the un-mounted capacitors in their original packaging, in a location away from direct sunlight, and where the temperature and relative humidity do not exceed 40 degrees centigrade and 70% respectively. For optimum solderability, capacitor stock should be used promptly, preferably within 18 months of receipt. For applications requiring pre-tinning of components, storage life may be extended if solderability is verified. Before cleaning, bonding or molding these devices, it is important to verify that your process does not affect product quality and performance. KEMET recommends testing and evaluating the performance of a cleaned, bonded or molded product prior to implementing and/or qualifying any of these processes. © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 7 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Application Notes Working Voltage: Application voltage (Vp-p or Vo-p) must not exceed the voltage rating of the capacitor. Irregular voltages can be generated for a transient period of time when voltage is initially applied and/or removed from a circuit. It is important to choose a capacitor with a voltage rating greater than or equal to these irregular voltages. Operating Temperature and Self-Generating Heat: The surface temperature of a capacitor should be kept below the upper limit of its rated operating temperature range. Be sure to take into account the heat generated by the capacitor itself. When the capacitor is used in a high-frequency current, pulse current or similar current, it may self-generate heat due to dielectric loss. Temperature rise due to self-generated heating should not exceed 20°C (while operated at an atmosphere temperature of 25°C). FAILURE TO FOLLOW THE ABOVE CAUTIONS MAY RESULT, WORST CASE, IN A SHORT CIRCUIT AND CAUSE FUMING OR PARTIAL DISPERSION WHEN THE PRODUCT IS USED. © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 8 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Construction Base Metal Electrode Epoxy Encapsulation Finish Layer (Sn10/Pb88/Ag2) Detailed Cross Section Barrier Layer (Ni) Base Metal (Cu) Lead Attach Solder (Sn10/Pb88/Ag2) Lead Attach Solder (Sn10/Pb88/Ag2) Dielectric Material (CaZrO3) Inner Electrodes (Ni) Finish Layer (Sn10/Pb88/Ag2) Barrier Layer (Ni) Base Metal (Cu) Lead Wire Base Metal Cu Clad Steel Core Ni Barrier Layer Au Finish Layer Precious Metal Electrode Inner Electrodes (Ni) Epoxy Encapsulation Detailed Cross Section Epoxy Encapsulation Chip End Metalization (Solderable Silver) Lead Attach Solder (Sn10/Pb88/Ag2) Lead Attach Solder (Sn10/Pb88/Ag2) Dielectric Material (BaTiO3) Inner Electrodes (PdAg) Lead Wire Chip End Metalization (Solderable Silver) Base Metal Cu Clad Steel Core Ni Barrier Layer Au Finish Layer Inner Electrodes (PdAg) Epoxy Encapsulation © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 9 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Marking FRONT BACK Rated Voltage (VDC) Style/Size Dielectric Specification/Series KEMET ID Rated Capacitance Capacitance Tolerance Code Date Code Date Code 14 20 Manufacturing Year: 14 = 2014 Manufacturing Week: 20 = Week 20 (of mfg. calendar year) © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 10 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Lead Tape & Reel Packaging Information KEMET offers standard reeling of Molded Radial Leaded Capacitors in accordance with EIA standard 468. Parts are taped to a tag board carrier strip, and wound on a reel as shown in Figure 1. Kraft paper interleaving is inserted between the layers of capacitors on the reel. t © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 11 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Table 3 – Ceramic Radial Tape and Reel Dimensions Metric will govern Constant Dimensions — Millimeters (Inches) D0 ±0.2 (0.008) P0 P P2 ±0.3 (0.012) ±0.3 (0.012) ±0.7 (0.028) ΔH Maximum L1 Maximum t Maximum T Maximum W + 1.0/- 0.5 (+0.039/-0.020) W0 Minimum W2 Maximum 4.00 (0.157) 12.7 (0.500) 12.7 (0.500) 6.35 (0.250) 1.0 (0.039) 1.0 (0.039) 0.9 (0.035) 2.0 (0.079) 18.0 (0.709) 5.0 (0.197) 3.0 (0.118) Variable Dimensions — Millimeters (Inches) F +0.6 (0.024) -0.2 (0.008) Note 1 P1 ±0.7 (0.028) Note 1 2.54 (0.100) 5.08 (0.200) 4.32 (0.170) 3.89 (0.153) 5.08 (0.200) 3.81 (0.150) 5.59 (0.220) 3.25 (0.128) 6.98 (0.275) 2.54 (0.100) 7.62 (0.300) 2.24 (0.088) 9.52 (0.375) 7.62 (0.300) 10.16 (0.400) 7.34 (0.290) 12.06 (0.475) 6.35 (0.250) 14.60 (0.575) 5.08 (0.200) 17.14 (0.675) 3.81 (0.15) H Minimum Note 2 H0 ±0.5 (0.630) Note 3 18.0 (0.709) 16.0 (0.024) Symbol Reference Table D0 P0 P F P1 P2 H H0 H1 ΔH L1 t W W0 W2 Sprocket Hole Diameter Sprocket Hole Pitch Component Pitch Lead Spacing Sprocket Hole Center to Adjacent Component Lead Sprocket Hole Center to Component Center Height to Seating Plane (Straight Leads Only) Height to Seating Plane (Formed Leads Only) Component Height Above Tape Center Component Alignment Lead Protrusion Composite Tape Thickness Carrier Tape Width Hold-Down Tape Width Hold-Down Tape Location 1. Measured at the egress from the carrier tape, on the component side. 2. Straight Lead configuration part types only. 3. Formed (bent) lead configuration part types only. © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 12 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) KEMET Corporation World Headquarters Europe Asia Southern Europe Sasso Marconi, Italy Tel: 39-051-939111 Northeast Asia Hong Kong Tel: 852-2305-1168 Mailing Address: P.O. Box 5928 Greenville, SC 29606 Skopje, Macedonia Tel: 389-2-55-14-623 Shenzhen, China Tel: 86-755-2518-1306 www.kemet.com Tel: 864-963-6300 Fax: 864-963-6521 Central Europe Landsberg, Germany Tel: 49-8191-3350800 Corporate Offices Fort Lauderdale, FL Tel: 954-766-2800 Kamen, Germany Tel: 49-2307-438110 North America Northern Europe Wyboston, United Kingdom Tel: 44-1480-273082 Taipei, Taiwan Tel: 886-2-27528585 Espoo, Finland Tel: 358-9-5406-5000 Southeast Asia Singapore Tel: 65-6701-8033 2835 KEMET Way Simpsonville, SC 29681 Northeast Wilmington, MA Tel: 978-658-1663 Southeast Lake Mary, FL Tel: 407-855-8886 Central Novi, MI Tel: 248-994-1030 Beijing, China Tel: 86-10-5877-1075 Shanghai, China Tel: 86-21-6447-0707 Seoul, South Korea Tel: 82-2-6294-0550 Penang, Malaysia Tel: 60-4-6430200 Bangalore, India Tel: 91-806-53-76817 Irving, TX Tel: 972-915-6041 West Milpitas, CA Tel: 408-433-9950 Mexico Guadalajara, Jalisco Tel: 52-33-3123-2141 Note: KEMET reserves the right to modify minor details of internal and external construction at any time in the interest of product improvement. KEMET does not assume any responsibility for infringement that might result from the use of KEMET Capacitors in potential circuit designs. KEMET is a registered trademark of KEMET Electronics Corporation. © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 13 Radial Through-Hole Multilayer Ceramic Capacitors High Temperature 200°C, Radial, Molded, X7R Dielectric, 50 – 200 VDC (Industrial Grade) Disclaimer All product specifications, statements, information and data (collectively, the “Information”) in this datasheet are subject to change. The customer is responsible for checking and verifying the extent to which the Information contained in this publication is applicable to an order at the time the order is placed. All Information given herein is believed to be accurate and reliable, but it is presented without guarantee, warranty, or responsibility of any kind, expressed or implied. Statements of suitability for certain applications are based on KEMET Electronics Corporation’s (“KEMET”) knowledge of typical operating conditions for such applications, but are not intended to constitute – and KEMET specifically disclaims – any warranty concerning suitability for a specific customer application or use. The Information is intended for use only by customers who have the requisite experience and capability to determine the correct products for their application. Any technical advice inferred from this Information or otherwise provided by KEMET with reference to the use of KEMET’s products is given gratis, and KEMET assumes no obligation or liability for the advice given or results obtained. Although KEMET designs and manufactures its products to the most stringent quality and safety standards, given the current state of the art, isolated component failures may still occur. Accordingly, customer applications which require a high degree of reliability or safety should employ suitable designs or other safeguards (such as installation of protective circuitry or redundancies) in order to ensure that the failure of an electrical component does not result in a risk of personal injury or property damage. Although all product–related warnings, cautions and notes must be observed, the customer should not assume that all safety measures are indicted or that other measures may not be required. © KEMET Electronics Corporation • P.O. Box 5928 • Greenville, SC 29606 (864) 963-6300 • www.kemet.com C1074_HT_X7R_RADIAL_MOLDED • 8/27/2015 14