YAGEO CC1210DKNPODBN121 Surface-mount ceramic multilayer capacitor Datasheet

DATA SHEET
SURFACE-MOUNT CERAMIC
MULTILAYER CAPACITORS
High-Voltage
NP0/X7R
1 KV TO 3 KV
10 pF to 33 nF
Product Specification – January 16, 2017 V.9
RoHS compliant & Halogen Free
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
SCOPE
ORDERING INFORMATION - GLOBAL PART NUMBER, PHYCOMP
This specification describes HighVoltage NP0/X7R series chip
capacitors with lead-free
terminations.
CTC & 12NC
APPLICATIONS
PCs, Hard disk, Game PCs
Power supplies
LCD panel
ADSL, Modem
FEATURES
Supplied in tape on reel
Nickel-barrier end termination
RoHS compliant
Halogen Free compliant
2
13
1 KV to 3 KV
All part numbers are identified by the series, size, tolerance, TC material,
packing style, voltage, process code, termination and capacitance value.
YAGEO BRAND ordering code
GLOBAL PART NUMBER (PREFERRED )
CC
XXXX X X XXX X
(1)
(2) (3) (4)
(5)
B
X XXX
(6) (7)
(1) SIZE – INCH BASED (METRIC)
0805 (2012) / 1206 (3216) / 1210 (3225) / 1808 (4520) / 1812 (4532)
(2) TOLERANCE
C = ± 0.25 pF
D = ± 0.5 pF
G = ± 2%
J = ± 5%
K = ± 10%
(3) PACKING STYLE
R = Paper/PE taping reel; Reel 7 inch
K = Blister taping reel; Reel 7 inch
P = Paper/PE taping reel; Reel 13 inch
F = Blister taping reel; Reel 13 inch
C = Bulk case
(4) TC MATERIAL
NPO
X7R
(5) RATED VOLTAGE
C = 1 KV
D = 2 KV
S = 2.5KV
E = 3 KV
(6) PROCESS
N = NP0
B = Class 2 MLCC
(7) CAPACITANCE VALUE
2 significant digits+number of zeros
The 3rd digit signifies the multiplying factor, and letter R is decimal point
Example: 121 = 12 x 101 = 120 pF
www.yageo.com
Jan. 16, 2017 V.9
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
3
13
1 KV to 3 KV
CONSTRUCTION
The capacitor consists of a
rectangular block of ceramic
dielectric in which a number of
interleaved metal electrodes are
contained. This structure gives
rise to a high capacitance per
unit volume.
The inner electrodes are
connected to the two end
terminations and finally covered
with a layer of plated tin (NiSn).
The terminations are lead-free. A
cross section of the structure is
shown in Fig.1.
Fig. 1 Surface mounted multilayer ceramic capacitor construction
DIMENSION
OUTLINES
Table 1 For outlines see fig. 2
T (MM)
L2 / L3 (mm)
min.
max.
L4 (mm)
min.
TYPE
L1 (mm)
W (mm)
0805
2.0 ± 0.20
1.25 ± 0.20
0.25
0.75
0.55
1206
3.2 ± 0.30
1.6 ± 0.20
0.25
0.75
1.40
1210
3.2 ± 0.30
2.5 ± 0.20
0.25
0.75
1.40
1808
4.5 ± 0.40
2.0 ± 0.30
0.25
0.75
2.20
1812
4.5 ± 0.40
3.2 ± 0.20
0.25
0.75
2.20
Refer to
table 2 to 4
For dimension see Table 1
Fig. 2 Surface mounted multilayer
ceramic capacitor dimension
www.yageo.com
Jan. 16, 2017 V.9
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
4
13
1 KV to 3 KV
CAPACITANCE RANGE & THICKNESS FOR NP0
Table 2 Sizes from 0805 to 1812
0805
1206
CAP.
1 KV
1 KV
2 KV
10 pF
0.85± 0.1
1.25± 0.2
12 pF
0.85± 0.1
15 pF
1808
1210
1 KV
2 KV
1 KV
1812
2 KV
3 KV
1 KV
2 KV
3 KV
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
0.85± 0.1
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
18 pF
0.85± 0.1
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
22 pF
0.85± 0.1
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
27 pF
0.85± 0.1
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
33 pF
0.85± 0.1
1.25± 0.2
1.25± 0.2 1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
39 pF
0.85± 0.1
1.25± 0.2
1.25± 0.2 1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
47 pF
0.85± 0.1
1.25± 0.2
1.25± 0.2 1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
56 pF
1.25± 0.2
1.25± 0.2 1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
68 pF
1.25± 0.2
1.25± 0.2 1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
82 pF
1.25± 0.2
1.25± 0.2 1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
100 pF
1.25± 0.2
1.25± 0.2 1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
120 pF
1.25± 0.2
1.25± 0.2 1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
150 pF
1.25± 0.2
1.25± 0.2 1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
180 pF
1.25± 0.2
1.25± 0.2 1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
2.0± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
220 pF
1.25± 0.2
1.25± 0.2 1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
2.0± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
270 pF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
330 pF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
390 pF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
470 pF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
560 pF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
680 pF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
820 pF
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.25± 0.2
1.0 nF
1.25± 0.2
1.25± 0.2
2.0± 0.2
1.25± 0.2
1.25± 0.2
1.2 nF
1.25± 0.2
1.5 nF
1.25± 0.2
1.8 nF
2.2 nF
2.7 nF
3.3 nF
NOTE
1. Values in shaded cells indicate thickness class in mm
2. Capacitance value of non E-12 series is on request
www.yageo.com
Jan. 16, 2017 V.9
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
5
13
1 KV to 3 KV
CAPACITANCE RANGE & THICKNESS FOR X7R
Table 3 Sizes from 0805 to 1812
CAP.
0805
1206
1 KV
1 KV
1808
1210
2 KV
2.5KV
1 KV
2 KV
1 KV
1812
2 KV
3 KV
1 KV
2 KV
3 KV
100 pF
150 pF 0.85± 0.1
1.6± 0.2
220 pF 0.85± 0.1 1.25± 0.2 1.25± 0.2
1.25± 0.2 1.25± 0.2
1.6± 0.2
330 pF 0.85± 0.1 1.25± 0.2 1.25± 0.2
1.25± 0.2 1.25± 0.2
1.35± 0.15 1.6± 0.2
470 pF 0.85± 0.1 1.25± 0.2 1.25± 0.2
1.25± 0.2 1.25± 0.2 1.35± 0.15 1.35± 0.15 1.6± 0.2
680 pF 0.85± 0.1 1.25± 0.2 1.25± 0.2
1.25± 0.2 1.25± 0.2 1.35± 0.15 1.35± 0.15 1.6± 0.2
1.0 nF 0.85± 0.1 1.25± 0.2 1.25± 0.2
1.6± 0.2 1.25± 0.2 1.25± 0.2 1.35± 0.15 1.35± 0.15 2.0± 0.2 1.35± 0.15 1.35± 0.15 1.6± 0.2
1.5 nF
1.25± 0.2 1.25± 0.2
1.25± 0.2 1.25± 0.2 1.35± 0.15 1.35± 0.15 2.0± 0.2 1.35± 0.15 1.35± 0.15
2.2 nF
1.25± 0.2
1.25± 0.2 1.60± 0.2 1.35± 0.15
3.3 nF
1.25± 0.2
1.25± 0.2
1.35± 0.15
1.35± 0.15 1.35± 0.15
4.7 nF
1.25± 0.2
1.25± 0.2
1.35± 0.15
1.35± 0.15 1.35± 0.15
6.8 nF
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.35± 0.15
1.6± 0.2
10 nF
1.25± 0.2
1.25± 0.2
1.6± 0.2
1.35± 0.15
2.0± 0.2
1.6± 0.2
1.35± 0.15 1.35± 0.15
15 nF
1.25± 0.2
1.35± 0.15
22 nF
1.6± 0.2
1.35± 0.15
33 nF
1.6± 0.2
47 nF
68 nF
100 nF
NOTE
1. Values in shaded cells indicate thickness class in mm
2. Capacitance value of non E-6 series is on request
3. For products with 5% tolerance, please contact local sales force before ordering
www.yageo.com
Jan. 16, 2017 V.9
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
1 KV to 3 KV
6
13
THICKNESS CLASSES AND PACKING QUANTITY
Table 5
SIZE
CODE
Ø 180 MM / 7 INCH
Paper
Blister
Ø 330 MM / 13 INCH
Paper
Blister
THICKNESS
CLASSIFICATION
TAPE WIDTH
QUANTITY PER REEL
0201
0.3 ± 0.03 mm
8 mm
15,000
---
50,000
---
---
0402
0.5 ± 0.05 mm
8 mm
10,000
---
50,000
---
50,000
0603
0.8 ± 0.1 mm
8 mm
4,000
---
15,000
---
15,000
0.6 ± 0.1 mm
8 mm
4,000
---
20,000
---
10,000
0.8 / 0.85 ± 0.1 mm
8 mm
4,000
---
15,000
---
8,000
1.00 ± 0.1 mm
8 mm
---
3,000
---
10,000
---
1.25 ± 0.2 mm
8 mm
---
3,000
---
10,000
5,000
0.6 ± 0.1 mm
8 mm
4,000
---
20,000
---
---
0805
1206
QUANTITY
PER BULK CASE
0.8 / 0.85 ± 0.1 mm
8 mm
4,000
---
15,000
---
---
1.00 / 1.15 ± 0.1 mm
8 mm
---
3,000
---
10,000
---
1.25 ± 0.2 mm
8 mm
---
3,000
---
10,000
---
1.6 ± 0.15 mm
8 mm
---
2,500
---
10,000
---
1.6 ± 0.2 mm
8 mm
---
2,000
---
8,000
---
0.6 / 0.7 ± 0.1 mm
8 mm
---
4,000
---
15,000
---
0.85 ± 0.1 mm
8 mm
---
4,000
---
10,000
---
1.15 ± 0.1 mm
8 mm
---
3,000
---
10,000
---
1.15 ± 0.15 mm
8 mm
---
3,000
---
10,000
---
1.25 ± 0.2 mm
8 mm
---
3,000
---
---
---
1.5 ± 0.1 mm
8 mm
---
2,000
---
---
---
1.6 / 1.9 ± 0.2 mm
8 mm
---
2,000
---
---
---
---
---
---
1210
2.0 ± 0.2 mm
8 mm
---
2,000
1,000
2.5 ± 0.2 mm
8 mm
---
1,000
500
---
---
---
1.15 ± 0.15 mm
12 mm
---
3,000
---
---
---
1.25 ± 0.2 mm
12 mm
---
3,000
---
---
---
1.35 ± 0.15 mm
12 mm
---
2,000
---
---
---
1.5 ± 0.1 mm
12 mm
---
2,000
---
---
---
1.6 ± 0.2 mm
12 mm
---
2,000
---
---
---
2.0 ± 0.2 mm
12 mm
---
2,000
---
---
---
0.6 / 0.85 ± 0.1 mm
12 mm
---
2,000
---
---
---
1.15 ± 0.1 mm
12 mm
---
1,000
---
---
---
1.15 ± 0.15 mm
12 mm
---
1,000
---
---
---
1808
1812
1.25 ± 0.2 mm
12 mm
---
1,000
---
---
---
1.35 ± 0.15 mm
12 mm
---
1,000
---
---
---
1.5 ± 0.1 mm
12 mm
---
1,000
---
---
---
1.6 ± 0.2 mm
12 mm
---
1,000
---
---
---
2.0 ± 0.2 mm
12 mm
---
1,000
---
---
---
2.5 ± 0.2 mm
12 mm
---
500
---
---
---
www.yageo.com
Jan. 16, 2017 V.9
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
7
13
1 KV to 3 KV
ELECTRICAL CHARACTERISTICS
NP0/X7R DIELECTRIC CAPACITORS; NISN TERMINATIONS
Unless otherwise stated all electrical values apply at an ambient temperature of 20± 1 °C, an atmospheric
pressure of 86 to 106 kPa, and a relative humidity of 63 to 67%.
Table 6
VALUE
DESCRIPTION
Capacitance range
10 pF to 33 nF
Capacitance tolerance
NP0
C < 10 pF
± 0.25 pF, ± 0.5 pF
C ≥ 10 pF
± 2%, ± 5%
X7R
± 5% (1), ± 10%
Dissipation factor (D.F.)
NP0
C < 30 pF
≤ 1 / ( 400 + 20C )
C ≥ 30 pF
≤ 0.1 %
X7R
Insulation resistance after 1 minute at Ur (DC)
≤ 2.5 %
Rins ≥ 10 GΩ or Rins × C ≥ 500 seconds whichever is less
Maximum capacitance change as a function of temperature
(temperature characteristic/coefficient):
NP0
± 30 ppm/°C
X7R
± 15%
Operating temperature range:
NP0/X7R
–55 °C to +125 °C
NOTE
1. ±5% tolerance of capacitance value isn't available for X7R full product range, please contact local sales force before ordering
www.yageo.com
Jan. 16, 2017 V.9
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
8
13
1 KV to 3 KV
HIGH - VOLTAGE NP0
Sample limits (broken lines).
Requirement levels (dotted lines)
Fig. 3 Typical temperature coefficient as a function of
temperature
Fig. 4 Typical tan δ as a function of temperature
HIGH - VOLTAGE X7R

X
Fig. 5 Typical capacitance change as a function of
temperature
Fig. 6 Typical tan δ as a function of temperature
www.yageo.com
Jan. 16, 2017 V.9
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
9
13
1 KV to 3 KV
SOLDERING RECOMMENDATION
Table 7
SOLDERING
METHOD
Reflow
SIZE
0402
0603
0805
1206
≥ 1210
Reflow only
≥ 1.0 µF
≥ 2.2 µF
≥ 4.7 µF
Reflow only
---
< 1.0 µF
< 2.2 µF
< 4.7 µF
---
Reflow/Wave
TESTS AND REQUIREMENTS
Table 8 Test procedures and requirements
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
Mounting
IEC 6038421/22
4.3
The capacitors may be mounted on printed-circuit boards or
ceramic substrates
No visible damage
Visual
Inspection and
Dimension
Check
4.4
Any applicable method using × 10 magnification
In accordance with specification
Capacitance
4.5.1
Class 1:
f = 1 MHz for C ≤ 1 nF, measuring at voltage 1 Vrms at 20 °C
Within specified tolerance
f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C
Class 2:
f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C
Dissipation
Factor (D.F.)
4.5.2
Class 1:
f = 1 MHz for C ≤ 1 nF , measuring at voltage 1 Vrms at 20 °C
In accordance with specification
f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C
Class 2:
f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C
Insulation
Resistance
4.5.3
Ur ≤ 500 V: At Ur for 1 minute
In accordance with specification
Ur > 500 V: At 500 V for 1 minute
www.yageo.com
Jan. 16, 2017 V.9
Product specification
Surface-Mount Ceramic Multilayer Capacitors
TEST
TEST METHOD
Temperature
Coefficient
4.6
High-Voltage
NP0/X7R
1 KV to 3 KV
PROCEDURE
REQUIREMENTS
Capacitance shall be measured by the steps shown
in the following table.
<General purpose series>
Class1:
∆ C/C: ± 30ppm
The capacitance change should be measured after
5 min at each specified temperature stage.
Step
Temperature(℃)
a
25± 2
b
Lower temperature± 3℃
c
25± 2
d
Upper Temperature± 2℃
e
25± 2
10
13
Class2:
X7R: ∆ C/C: ±15%
Y5V: ∆ C/C: 22~-82%
<High Capacitance series>
Class2:
X7R/X5R: ∆ C/C: ±15%
Y5V: ∆ C/C: 22~-82%
(1) Class I
Temperature Coefficient shall be calculated from
the formula as below
C2 - C1
106 [ppm/℃]
Temp, Coefficient =
C1 xΔT
C1: Capacitance at step c
C2: Capacitance at 125℃
∆T: 100℃(=125℃-25℃)
(2) Class II
Capacitance Change shall be calculated from the
formula as below
C2 - C1
∆C =
x 100%
C1
C1: Capacitance at step c
C2: Capacitance at step b or d
Adhesion
Bending
Strength
IEC 6038421/22
4.7
A force applied for 10 seconds to the line joining
the terminations and in a plane parallel to the
substrate
Force
size ≥ 0603: 5N
4.8
Mounting in accordance with IEC 60384-22
paragraph 4.3
No visible damage
Conditions: bending 1 mm at a rate of 1 mm/s,
radius jig 5 mm
∆C/C
Class 1:
NP0: within ± 1% or 0.5 pF, whichever is greater
Class2:
X7R: ± 10%
www.yageo.com
Jan. 16, 2017 V.9
Product specification
Surface-Mount Ceramic Multilayer Capacitors
TEST
Resistance to
Soldering
Heat
TEST METHOD
4.9
High-Voltage
NP0/X7R
PROCEDURE
REQUIREMENTS
Precondition: 150 +0/–10 °C for 1 hour, then
keep for 24 ± 1 hours at room temperature
Dissolution of the end face plating shall not
exceed 25% of the length of the edge
concerned
Preheating: for size ≤ 1206: 120 °C to 150 °C for
1 minute
Preheating: for size >1206: 100 °C to 120 °C for
1 minute and 170 °C to 200 °C for 1 minute
Solder bath temperature: 260 ± 5 °C
Dipping time: 10 ± 0.5 seconds
Recovery time: 24 ± 2 hours
11
13
1 KV to 3 KV
∆C/C
Class 1:
NP0: within ± 0.5% or 0.5 pF, whichever is greater
Class2:
X7R: ± 10%
D.F. within initial specified value
Rins within initial specified value
Solderability
4.10
Preheated to a temperature of 80 °C to 140 °C
and maintained for 30 seconds to 60 seconds.
The solder should cover over 95% of the critical
area of each termination
1. Temperature: 235± 5°C / Dipping time: 2 ± 0.5 s
2. Temperature: 245± 5°C / Dipping time: 3 ± 0.5 s
(lead free)Depth of immersion: 10mm
Rapid Change
of
Temperature
IEC 6038421/22
4.11
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for
24 ± 1 hours at room temperature
5 cycles with following detail:
30 minutes at lower category temperature
30 minutes at upper category temperature
Recovery time 24 ± 2 hours
No visual damage
∆C/C
Class 1:
NP0: within ± 1% or 1 pF, whichever is greater
Class2:
X7R: ± 15%
D.F. meet initial specified value
Rins meet initial specified value
Damp Heat
4.13
1. Preconditioning, class 2 only:
150 +0/-10 °C /1 hour, then keep for
24 ± 1 hour at room temp
2. Initial measure:
Spec: refer to initial spec C, D, IR
3. Damp heat test:
500 ± 12 hours at 40 ± 2 °C;
90 to 95% R.H.
4. Recovery:
Class 1: 6 to 24 hours
Class 2: 24 ± 2 hours
5. Final measure: C, D, IR
P.S. If the capacitance value is less than the
minimum value permitted, then after the other
measurements have been made the capacitor shall
be preconditioned according to “IEC 60384 4.1”
and then the requirement shall be met.
No visual damage after recovery
∆C/C
Class 1:
NP0: within ± 2% or 1 pF, whichever is greater
Class2:
X7R: ± 15%
D.F.
Class 1:
NP0: ≤ 2 x specified value
Class2:
X7R: ≥ 25 V: ≤ 5%
Rins
Class 1:
NP0: ≥ 2,500 MΩ or Rins x Cr ≥ 25s whichever is
less
Class2:
X7R: ≥ 500 MΩ or Rins x Cr ≥ 25s whichever is
less
www.yageo.com
Jan. 16, 2017 V.9
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
Endurance
IEC 6038421/22
1. Preconditioning, class 2 only:
No visual damage
4.14
150 +0/-10 °C /1 hour, then keep for
24 ± 1 hour at room temp
2. Initial measure:
Spec: refer to initial spec C, D, IR
∆C/C
Class1:
NP0: within ± 2% or 1 pF, whichever is greater
Endurance test:
Temperature: NP0/X7R: 125 °C
Specified stress voltage applied for 1,000 hours.
High-Voltage series follows the stress conditions
below:
Class2:
X7R: ± 15%
Voltage
NPO
X7R
≤ 100V
2.0 x Ur
2.0 x Ur
Class2:
X7R: ≥ 25 V: ≤ 5%
200/250V
1.5 x Ur
1.5 x Ur
Rins
500/630V
1.3 x Ur
1.2 x Ur
≥ 1KV
1.2 x Ur
1.1 x Ur
Class1:
NP0: ≥ 4,000 MΩ or
Rins x Cr ≥ 40s whichever is less
3. Recovery time: 24 ± 2 hours
4. Final measure: C, D, IR
12
13
1 KV to 3 KV
D.F.
Class1:
NP0: ≤ 2 x specified value
Class2:
X7R: ≥ 1,000 MΩ or
Rins x Cr ≥ 50s whichever is less
P.S. If the capacitance value is less than the
minimum value permitted, then after the other
measurements have been made the capacitor shall
be preconditioned according to “IEC 60384 4.1”
and then the requirement shall be met.
Voltage Proof
Specified stress voltage applied for 1~5 seconds
No breakdown or flashover
Ur ≤ 100 V: series applied 2.5 Ur
100 V < Ur ≤ 200 V series applied
(1.5 Ur + 100)
200 V < Ur ≤ 500 V series applied
(1.3 Ur + 100)
Ur > 500 V: 1.3 Ur
Ur ≥ 1KV: 1.2 Ur
Charge/Discharge current less than 50mA
www.yageo.com
Jan. 16, 2017 V.9
Product specification
Surface-Mount Ceramic Multilayer Capacitors
High-Voltage
NP0/X7R
13
13
1 KV to 3 KV
REVISION HISTORY
REVISION DATE
CHANGE NOTIFICATION
DESCRIPTION
Version 9
Jan. 16, 2017
-
- Product range updated
Version 8
Oct. 12, 2015
-
- Product range updated
Version 7
May 21, 2014
-
- Product range updated
Version 6
Jun. 17, 2012
-
- Product range updated
Version 5
Sep 25, 2012
-
- Product range updated
Version 4
Aug 08, 2011
-
- Product range updated
Version 3
Jan 19, 2011
-
- Dimension updated
- Add NP0 0805 1KV
Version 2
Feb 02, 2010
-
- Change to dual brand datasheet that describe High-Voltage NP0/X7R
series with RoHS compliant
- Replace the high voltage part of pdf files:
UP-NP0X7R_HV_1K-to-4KV_1 and UY-NP0X7R_HV_1K-to-4KV_1
- Description of "Halogen Free compliant" added
- Product range updated
- Define global part number
- Test method and procedure updated
Version 1
Sep 30, 2005
-
- Thickness revised
Version 0
Sep 12, 2005
-
- New
www.yageo.com
Jan. 16, 2017 V.9