YAGEO CA0508MZRY5V9BB473 Surface-mount ceramic multilayer capacitor Datasheet

DATA SHEET
SURFACE-MOUNT CERAMIC
MULTILAYER CAPACITORS
C-Array
NP0/X7R/Y5V
16 V TO 50 V
sizes 0508 (4 x 0402) / 0612 (4 x 0603)
Product Specification – Feb 05, 2010 V.1
RoHS compliant & Halogen Free
Product specification
Surface-Mount Ceramic Multilayer Capacitors
SCOPE
This specification describes
NP0/X7R/Y5V 4-capacitor Array
with lead-free terminations.
APPLICATIONS
Professional electronics
High density consumer
electronics
NP0/X7R/Y5V
16 V to 50 V
2
17
ORDERING INFORMATION - GLOBAL PART NUMBER, PHYCOMP
CTC & 12NC
All part numbers are identified by the series, size, tolerance, TC material,
packing style, voltage, process code, termination and capacitance value.
Please note that 12 digits ordering code will expire at the end of 2010.
YAGEO BRAND ordering code
GLOBAL PART NUMBER (PREFERRED )
CA
XXXX X X XXX X
(1)
FEATURES
Supplied in tape on reel
Nickel-barrier end termination
0508 (4x0402) / 0612 (4x0603)
capacitors (of the same
capacitance value) per array
Less than 50% board space of
an equivalent discrete
component
High volumetric efficiency
Increased throughout, by time
saved in mounting
RoHS compliant
Halogen Free compliant
4C-Array
(2) (3)
(4)
(5)
B
X XXX
(6) (7)
(1) SIZE – INCH BASED (METRIC)
0508 (1220)
0612 (1632)
(2) TOLERANCE
J = ±5%
K = ±10%
M = ±20%
Z = -20% to +80%
(3) PACKING STYLE
R = Paper/PE taping reel; Reel 7 inch
(4) TC MATERIAL
NPO
X7R
Y5V
(5) RATED VOLTAGE
7 = 16 V
8 = 25 V
9 = 50 V
(6) PROCESS
N = NP0
B = X7R / Y5V
(7) CAPACITANCE VALUE
2 significant digits+number of zeros
The 3rd digit signifies the multiplying factor, and letter R is decimal point
Example: 121 = 12 x 101 = 120 pF
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
3
17
16 V to 50 V
NP0/X7R/Y5V
PHYCOMP BRAND ordering codes
GLOBAL PART NUMBER (preferred), PHYCOMP CTC (for North America) and 12NC (traditional) codes are
acceptable to order Phycomp brand products.
GLOBAL PART NUMBER
( PREFERRED )
For detailed information of GLOBAL PART NUMBER and ordering example, please refer to page 2.
12NC
CODE
2 2 XX
XX
X
X
X
X
XX
Capacitance value(1)
Carrier type
55 = Paper/PE
Tolerance
5 = ±5%
6 = ±10%
7 = ±20%
8 = -20% to +80%
Voltage
10 = 16 V
12 = 25 V
14 = 50 V
Size
7 = 0508 (4 x 0402)
6 = 0612 (4 x 0603)
YNM0030
Temperature characteristic
1 = NP0
5 = X7R
9 = Y5V
Packaging(2)
1 = reel: ∅180 mm; 7"
(1) Refer to “Conversion table of capacitance & last 2-digit of 12NC”
(2) Quantity on reel depends on thickness classification; see table 5
PHYCOMP CTC
CODE ( FOR NORTH AMERICA )
Example: 0508CG220K9B200
0508
CG
220
K
Size code
Temp.
Char.
Capacitance
in pF
Tolerance
0508
CG = NP0 101 = 100 pF;
(4 x 0402) 2R = X7R the third digit
signifies the
2F = Y5V
0612
multiplying factor:
(4 x 0603)
0=×1
9
B
Voltage Termination
J = ±5%
7 = 16 V B = NiSn
K = ±10%
8 = 25 V
M = ±20%
9 = 50 V
2
0
0
Packing
Marking
Range identifier
2 = 180 mm
0 = no marking 0 = conv. Ceramic
7” Paper/PE
D = Class 2 MLCC
Z = -20% to +80%
1 = × 10
2 = × 100
3 = × 1,000
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
16 V to 50 V
NP0/X7R/Y5V
4
17
CONSTRUCTION
The capacitor consists of a rectangular
block of ceramic dielectric in which
a number of interleaved metal
electrodes are contained. This
structure gives rise to a high
capacitance per unit volume.
The inner electrodes are connected
to the two end terminations and
finally covered with a layer of
plated tin (NiSn).
The terminations are lead-free.
An outline of the structure is
shown in Fig.1.
CCA833
Fig. 1 Simplified outline
DIMENSIONS
OUTLINES
Table 1
TYPE
0508
(4 X 0402)
0612
(4 X 0603)
L (mm)
2.0 ±0.15
3.2 ±0.15
W (mm)
1.25 ±0.15
1.60 ±0.15
Tmin. (mm)
0.50
0.70
Tmax. (mm)
0.70
0.90
A (mm)
0.28 ±0.10
0.4 ±0.10
B (mm)
0.2 ±0.10
0.3 ±0.20
P (mm)
0.5 ±0.10
0.8 ±0.10
For dimensions see Table 1
L
W
B
P
A
T
HBK092
Fig. 2 Surface mounted multilayer ceramic capacitor dimension
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
NP0/X7R/Y5V
16 V to 50 V
5
17
CAPACITANCE RANGE & THICKNESS FOR 4C-ARRAY
Table 2 Temperature characteristic material from NP0
CAPACITANCE
Last 2-digit of
12NC
10 pF
23
15 pF
25
18 pF
26
22 pF
27
33 pF
29
39 pF
31
47 pF
32
56 pF
33
68 pF
34
82 pF
35
100 pF
36
120 pF
37
150 pF
38
180 pF
39
220 pF
41
270 pF
42
330 pF
43
390 pF
44
470 pF
45
560 pF
46
680 pF
47
820 pF
48
1.0 nF
49
0508 (4 x 0402)
0612 (4 x 0603)
50 V
50 V
0.6±0.1
0.8±0.1
NOTE
Values in shaded cells indicate thickness class in mm
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
NP0/X7R/Y5V
16 V to 50 V
6
17
CAPACITANCE RANGE & THICKNESS FOR 4C-ARRAY
Table 3 Temperature characteristic material from X7R
CAPACITANCE
Last 2-digit of
0508 (4 x 0402)
0612 (4 x 0603)
16 V
16 V
12NC
180 pF
13
220 pF
14
270 pF
15
330 pF
16
390 pF
17
470 pF
18
560 pF
19
680 pF
21
820 pF
22
1.0 nF
23
1.2 nF
24
1.5 nF
25
1.8 nF
26
2.2 nF
27
2.7 nF
28
3.3 nF
29
3.9 nF
31
4.7 nF
32
5.6 nF
33
6.8 nF
34
8.2 nF
35
10 nF
36
12 nF
37
15 nF
38
18 nF
39
22 nF
41
27 nF
42
33 nF
43
47 nF
45
56 nF
46
68 nF
47
82 nF
48
100 nF
49
25 V
50 V
0.8±0.1
0.8±0.1
0.6±0.1
0.8±0.1
NOTE
Values in shaded cells indicate thickness class in mm
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
NP0/X7R/Y5V
16 V to 50 V
7
17
CAPACITANCE RANGE & THICKNESS FOR 4C-ARRAY
Table 4 Temperature characteristic material from Y5V
0612 (4 x 0603)
CAPACITANCE Last 2-digit of
12NC
10 nF
36
22 nF
41
47 nF
45
100 nF
49
25 V
0.6±0.1
NOTE
Values in shaded cells indicate thickness class in mm
THICKNESS CLASSES AND PACKING QUANTITY
Table 5
THICKNESS
TAPE WIDTH QUANTITY
Ø180 MM / 7 INCH
CLASSIFICATION
PER REEL
Paper
0508
0.6 ±0.1 mm
8 mm
4,000
0612
0.8 ±0.1 mm
8 mm
4,000
SIZE
CODE
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
NP0/X7R/Y5V
16 V to 50 V
8
17
ELECTRICAL CHARACTERISTICS
4C-ARRAY DIELECTRIC CAPACITORS; NISN TERMINATIONS
Unless otherwise stated all electrical values apply at an ambient temperature of 20±1 °C, an atmospheric
pressure of 86 to 106 kPa, and a relative humidity of 63 to 67%.
Table 6
VALUE
DESCRIPTION
Capacitance range
10 pF to 100 nF
Rated voltage
NP0
50 V
X7R
0508: 16 V, 0612: 16 V to 50 V
Y5V
0612: 25 V
NP0
±5%, ±10%
X7R
±10%, ±20%
Y5V
–20% to +80%
NP0
≤ 0.1%
X7R
16 V ≤ 3.5%, 25V ≤ 2.5%, 50V ≤ 2.5%
Y5V
0508 ≤ 9%, 0612 ≤ 7%
Capacitance tolerance
Dissipation factor (D.F.)
Insulation resistance after 1 minute at Ur (DC)
Rins ≥ 10 GΩ or Rins × Cr ≥ 500 seconds whichever is less
Maximum capacitance change as a function of temperature
(temperature characteristic/coefficient):
NP0
±30 ppm/°C
X7R
±15%
Y5V
+22% to –82%
NP0
–55 °C to +125 °C
X7R
–55 °C to +125 °C
Y5V
–30 °C to +85 °C
Operating temperature range:
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
16 V to 50 V
NP0/X7R/Y5V
9
17
NP0 0508/0612 50 V
Sample limits (broken lines)
Requirement levels (dotted lines)
MEA607
MEA608
10
tan δ
(x 10 4)
40
TC
(x10 6/K)
7.5
20
5
0
20
2.5
40
0
40
Fig. 3
0
40
80
120
o
T ( C)
Typical temperature coefficient as a function of
temperature
Fig. 4
40
0
40
80
120
T ( oC)
Typical tan δ as a function of temperature
MEA614
15
ΔC
C
(%) 10
5
0
–5
– 10
– 15
0
Fig. 5
10
20
30
40
50
V DC (V)
Typical capacitance change with respect to the
capacitance at 1 V as a function of DC voltage
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
NP0/X7R/Y5V
16 V to 50 V
10
17
X7R 0508 16 V
CCB966
0
CCB965
600
ΔC
C
(%)
tan δ
(× 10−4)
−20
400
−40
200
−60
−80
Fig. 6
ΔC
C
(%)
0
20
40
0
100
80
VDC (V)
60
Typical capacitance change with respect to the
capacitance at 1 V as a function of DC voltage
at 20 °C
Fig. 7
−40
0
40
80
120
T (°C)
Typical tan δ as a function of temperature
YNM0013
15
10
5
0
−5
−10
−15
−55
Fig. 8
−25
5
40
65
95
125
T (oC)
Typical capacitance change as a function of
temperature
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
16 V to 50 V
NP0/X7R/Y5V
11
17
X7R 0612 16 V to 50 V
Curve 1 = 16 V product
Curve 2 = 25 V product
Curve 3 = 50 V product
Curve 1 = 16 V product
Curve 2 = 25 V product
Curve 3 = 50 V product
CCB558
0
CCB559
600
handbook, halfpage
handbook, halfpage
ΔC
C
(%)
tan δ
(× 10−4)
1
−20
400
1
2
2
3
3
−40
−60
200
0
Fig. 9
ΔC
C
(%)
20
40
VDC (V)
60
Typical capacitance change with respect to the
capacitance at 1 V as a function of DC voltage
at 25 °C
0
−60
−20
20
60
100
140
T (°C)
Fig. 10 Typical tan δ as a function of temperature
YNM0013
15
10
5
0
−5
−10
−15
−55
−25
5
40
65
95
125
T (oC)
Fig. 11 Typical capacitance change as a function of
temperature
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
NP0/X7R/Y5V
16 V to 50 V
12
17
Y5V 0612 25 V
CCB401
0
C
C
(%)
−20
tan δ
(× 10−4)
4000
−40
3000
−60
2000
−80
1000
−100
0
10
20
30
40
50
VDC (V)
Fig. 12 Typical capacitance change with respect to the
capacitance at 1 V as a function of DC voltage
at 25 °C
0
−40
−20
0
20
40
60
80
100
T (°C)
Fig. 13 Typical tan δ as a function of temperature
CCB403
40
C
C
(%)
CCB402
5000
20
0
−20
−40
−60
−80
−40
−20
0
20
40
60
80
100
T (°C)
Fig. 14 Typical capacitance change as a function of
temperature
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
NP0/X7R/Y5V
16 V to 50 V
13
17
TESTS AND REQUIREMENTS
Table 7 Test procedures and requirements
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
Mounting
IEC 6038421/22
4.3
The capacitors may be mounted on printed-circuit boards or
ceramic substrates
No visible damage
Visual
inspection
and
dimension
check
4.4
Any applicable method using × 10 magnification
In accordance with specification
Capacitance
4.5.1
Class 1:
f = 1 MHz for C ≤ 1 nF, measuring at voltage 1 Vrms at 20 °C
Within specified tolerance
f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C
Class 2:
f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C
f = 120 Hz for C >10 µF, measuring at voltage 0.5 Vrms at 20 °C
Dissipation
factor (D.F.)
4.5.2
Class 1:
f = 1 MHz for C ≤ 1 nF , measuring at voltage 1 Vrms at 20 °C
In accordance with specification
f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C
Class 2:
f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C
f = 120 Hz for C > 10 µF, measuring at voltage 0.5 Vrms at 20 °C
Insulation
resistance
4.5.3
At Ur (DC) for 1 minute
In accordance with specification
Temperature
coefficient
4.6
Class 1:
Between minimum and maximum temperature
NP0: -55 °C to +125 °C
Normal Temperature: 20 °C
<General purpose series>
Class 2:
Between minimum and maximum temperature
X5R: -55 °C to +85 °C
X7R: -55 °C to +125 °C
Y5V: -30 °C to +85 °C
Normal Temperature: 20 °C
<General purpose series>
Class 2: X5R/X7R: ±15%
Y5V: 22% to -82%
A force applied for 10 seconds to the line joining the terminations
and in a plane parallel to the substrate
Force
size ≥ 0603: 5N
size = 0402: 2.5N
size = 0201: 1N
Temperature
characteristic
Adhesion
4.7
ΔC/C:
Class 1: NP0: ±30 ppm/°C
<High Capacitance series>
Class 2: X5R/X7R: ±15%
Y5V: 22% to - 82%
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
NP0/X7R/Y5V
16 V to 50 V
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
Bond
strength of
plating on
end face
IEC 6038421/22
Mounting in accordance with IEC 60384-22
paragraph 4.3
No visible damage
Conditions: bending 1 mm at a rate of 1 mm/s,
radius jig 340 mm
<General purpose series>
4.8
14
17
∆C/C
Class 1:
NP0: within ±1% or 0.5 pF, whichever is greater
Class2:
X5R/X7R/Y5V: ±10%
<High Capacitance series>
∆C/C
Class2:
X5R/X7R/Y5V: ±10%
Resistance to
soldering
heat
4.9
Precondition: 150 +0/–10 °C for 1 hour, then
keep for 24 ±1 hours at room temperature
Preheating: for size ≤ 1206: 120 °C to 150 °C for
1 minute
Preheating: for size >1206: 100 °C to 120 °C for
1 minute and 170 °C to 200 °C for 1 minute
Solder bath temperature: 260 ±5 °C
Dipping time: 10 ±0.5 seconds
Recovery time: 24 ±2 hours
Dissolution of the end face plating shall not
exceed 25% of the length of the edge
concerned
<General purpose series>
∆C/C
Class 1:
NP0: within ±0.5% or 0.5 pF, whichever is greater
Class2:
X5R/X7R: ±10%
Y5V: ±20%
<High Capacitance series>
∆C/C
Class2:
X5R/X7R: ±10%
Y5V: ±20%
D.F. within initial specified value
Rins within initial specified value
Solderability
4.10
Preheated the temperature of 80 °C to 140 °C
and maintained for 30 seconds to 60 seconds.
The solder should cover over 95% of the critical
area of each termination
Test conditions for lead containing solder alloy
Temperature: 235 ±5 °C
Dipping time: 2 ±0.2 seconds
Depth of immersion: 10 mm
Alloy Composition: 60/40 Sn/Pb
Number of immersions: 1
Test conditions for leadfree containing solder alloy
Temperature: 245 ±5 °C
Dipping time: 3 ±0.3 seconds
Depth of immersion: 10 mm
Alloy Composition: SAC305
Number of immersions: 1
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
NP0/X7R/Y5V
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
Rapid change
of
temperature
IEC 6038421/22
Preconditioning;
150 +0/–10 °C for 1 hour, then keep for
24 ±1 hours at room temperature
No visual damage
4.11
16 V to 50 V
15
17
<General purpose series>
∆C/C
5 cycles with following detail:
30 minutes at lower category temperature
30 minutes at upper category temperature
Recovery time 24 ±2 hours
Class 1:
NP0: within ±1% or 1 pF, whichever is greater
Class2:
X5R/X7R: ±15%
Y5V: ±20%
<High Capacitance series>
∆C/C
Class2:
X5R/X7R: ±15%
Y5V: ±20%
D.F. meet initial specified value
Rins meet initial specified value
Damp heat
with Ur load
4.13
1. Preconditioning, class 2 only:
150 +0/-10 °C /1 hour, then keep for
24 ±1 hour at room temp
2. Initial measure:
Spec: refer initial spec C, D, IR
3. Damp heat test:
500 ±12 hours at 40 ±2 °C;
90 to 95% R.H. 1.0 Ur applied
4. Recovery:
Class 1: 6 to 24 hours
Class 2: 24 ±2 hours
5. Final measure: C, D, IR
P.S. If the capacitance value is less than the
minimum value permitted, then after the
other measurements have been made the
capacitor shall be precondition according to
“IEC 60384 4.1” and then the requirement
shall be met.
No visual damage after recovery
<General purpose series>
∆C/C
Class 1:
NP0: within ±2% or 1 pF, whichever is greater
Class2:
X5R/X7R: ±15%; Y5V: ±30%
D.F.
Class 1: NP0: ≤ 2 x specified value
Class2:
X5R/X7R: ≤ 16V: ≤ 7%
≥ 25V: ≤ 5%
Y5V: ≤ 15%
Rins
Class 1:
NP0: ≥ 2,500 MΩ or Rins x Cr ≥ 25s whichever is less
Class2:
X5R/X7R/Y5V: ≥ 500 MΩ or Rins x Cr ≥ 25s
whichever is less
<High Capacitance series>
∆C/C
Class2: X5R/X7R: ±20%; Y5V: ±30%
D.F.
Class2: 2 x initial value max
Rins
Class2: 500 MΩ or Rins x Cr ≥ 25s, whichever is less
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
NP0/X7R/Y5V
TEST
TEST METHOD
PROCEDURE
REQUIREMENTS
Endurance
IEC 6038421/22
1. Preconditioning, class 2 only:
No visual damage
4.14
150 +0/-10 °C /1 hour, then keep for
24 ±1 hour at room temp
2. Initial measure:
Spec: refer initial spec C, D, IR
3. Endurance test:
Temperature: NP0/X7R: 125 °C
X5R/Y5V: 85 °C
Specified stress voltage applied for 1,000 hours:
Applied 2.0 x Ur for general product.
Applied 1.5 x Ur for high cap. product.
High voltage series follows with below stress
condition:
Applied 1.3 x Ur for 500V series
Applied 1.2 x Ur for 1KV, 2KV, 3KV series
4. Recovery time: 24 ±2 hours
5. Final measure: C, D, IR
P.S. If the capacitance value is less than the
minimum value permitted, then after the other
measurements have been made the capacitor shall
be precondition according to “IEC 60384 4.1” and
then the requirement shall be met.
16 V to 50 V
16
17
<General purpose series>
∆C/C
Class1:
NP0: within ±2% or 1 pF, whichever is greater
Class2:
X5R/X7R: ±15%; Y5V: ±30%
D.F.
Class1:
NP0: ≤ 2 x specified value
Class2:
X5R/X7R: ≤ 16V: ≤ 7%
≥ 25V: ≤ 5%
Y5V: ≤ 15%
Rins
Class1:
NP0: ≥ 4,000 MΩ or
Rins x Cr ≥ 40s whichever is less
Class2:
X5R/X7R/Y5V: ≥ 1,000 MΩ or
Rins x Cr ≥ 50s whichever is less
<High Capacitance series>
∆C/C
Class 2:
X5R/X7R: ±20%; Y5V: ±30%
D.F.
Class 2:
2 x initial value max
Rins
Class 2:
1,000 MΩ or Rins x Cr ≥ 50s, whichever is less
Voltage proof
IEC 60384-1 4.6
Specified stress voltage applied for 1 minute
Ur ≤ 100 V: series applied 2.5 Ur
100 V < Ur ≤ 200 V series applied (1.5 Ur + 100)
200 V < Ur ≤ 500 V series applied (1.3 Ur + 100)
Ur > 500 V: 1.3 Ur
I: 7.5 mA
No breakdown or flashover
www.yageo.com
Feb 05, 2010 V.1
Product specification
Surface-Mount Ceramic Multilayer Capacitors
4C-Array
NP0/X7R/Y5V
16 V to 50 V
17
17
REVISION HISTORY
REVISION DATE
CHANGE NOTIFICATION
DESCRIPTION
Version 1
Feb 05, 2010
-
- The statement of "Halogen Free" on the cover added
Version 0
Jun 22, 2009
-
- New datasheet for 4C-Array series with RoHS compliant
- Replace from pdf files: 0508_16V to 50V_1, 0612_16V to 50V_0,
C-Array_NP0_50V_0508_7, C-Array_NP0_50V_0612_7,
C-Array_X7R_16V_25V_50V_0612_6, C-Array_X7R_16V_0508_5,
C-Array_Y5V_25V_0508_0, C-Array_Y5V_25V_0612_5
- Define global part number
- Description of "Halogen Free compliant" added
- Test method and procedure updated
www.yageo.com
Feb 05, 2010 V.1