KOA FBA1J4ATE102P Multilayer ferrite chip bead array Datasheet

KOA SPEER ELECTRONICS, INC.
SS-224 R5
AHA 10/27/04
Multilayer Ferrite Chip Bead Array
Type FBA
CERTIFIED
1. Scope of Application
Noise suppression in signal I/O lines and other circuits that require
multiple chip beads for noise suppression.
1.1 Applications
■
■
■
Computers
Peripherals
■
Telecommunications equipment
Data communications
2. Features
The Multilayer Ferrite Chip Bead Array retains all the features of Multilayer Ferrite Chip Beads.
In addition, it provides multiple circuits in a single package, which reduce the required land space
on PCB and reduce the cost for assembly.
3. Dimension and Structure
a
L
p
b
W
t
Protective
Coating
Solder
Plating
Type
(Inch Size Code)
L
W
1J
(0603)
.126±.008
(3.2±0.2)
.063±.008
(1.6±0.2)
Dimensions inches (mm)
t
a
.031±.008
(0.8±0.2)
.014±.008
(0.35±0.2)
b
p
.012±.008
(0.3±0.2)
.031±.008
(0.8±0.2)
3.1 Circuit
PAGE 1 OF 8
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
4. Ordering and Specifying Information*
FBA
1J
4
A
T
TE
300
P
Type
Size
Circuits
Characteristics
Termination
Material
Packaging
Impedance
Tolerance
1J
(0603)
Number of
Circuits
A: Standard
B: High Speed
T: Sn
L: SnPb
TE: 7" Embossed
Plastic
3000 pcs/reel
2 significant
figure + 1
multipler
Ex: 300 = 30Ω
P: ±25%
* Please note: KSE’s part numbers do not contain any spaces or hyphens.
5. Standard Applications
Impedance
@ 100MHz
Ω
Maximum DC
Resistance
Ω
Allowable
DC Current
(mA)
FBA1J4ATE300P
FBA1J4ATE600P
FBA1J4ATE121P
FBA1J4ATE221P
FBA1J4ATE301P
FBA1J4ATE601P
30
60
120
220
300
600
0.1
0.25
0.3
0.3
0.4
0.5
200
400
350
250
250
100
FBA1J4ATE102P
1,000
0.7
200
FBA1J4BTE100P
FBA1J4BTE220P
10
22
0.15
0.25
200
200
FBA1J4BTE470P
FBA1J4BTE600P
FBA1J4BTE121P
FBA1J4BTE221P
FBA1J4BTE471P
47
60
120
220
470
0.3
0.3
0.5
0.55
0.55
150
350
100
100
100
FBA1J4BTE601P
600
0.65
100
Ordering
Code
Operating
Temperature
-55°C
to
125°C
PAGE 2 OF 8
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
6. Graphs*
*
Bolivar Drive
|Z|
XL
R
■
P.O. Box 547
PAGE 3 OF 8
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
6. Graphs* (continued)
*
Bolivar Drive
|Z|
XL
R
■
P.O. Box 547
PAGE 4 OF 8
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
6. Graphs* (continued)
*
Bolivar Drive
|Z|
XL
R
■
P.O. Box 547
PAGE 5 OF 8
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
6. Packaging Specifications
KOA’s multilayer components are provided on tape-and-reel
for use in pick-and-place machines. The reel size is 7 inch.
7. Dimensions - inches (mm)
Do
Tape
1J4
Ao
Bo
Ko
P2
Po
t
E
0.071±0.002 0.138±0.002 0.048±0.002
(1.8±0.1)
(3.5±0.1)
(1.2±0.1)
W
F
Bo
Tape
1J4
E
W
0.069±0.004 0.138±0.002 0.318±0.002
(1.75±0.10) (3.50±.005)
(8.1±0.1)
Tape
1J4
F
P1
Po
P2
D1
Do
D1
0.157±0.004 0.157±0.004 0.079±0.002 0.059±0.004 0.039 min.
(4.0±0.1)
(4.0±0.1)
(2.00±0.05) (1.5+0.1/-0.0) (1.0 min.)
Ao
P1
Ko
t
0.009±0.001
(0.23±0.02)
8. Chip Quantities Per Reel
Chip Size
Parts on 7 inch (178mm) Reel
1J4
3,000
9. Characteristics
Item
Requirement
Conditions
Operating Temperature
-55°C ~ +125°C
Storage Temperature
40°C @ 70% Humidity
Sealed plastic bags with desiccant shall be
used to reduce the potential of oxidation on
the terminations during storage.
Resistance to Solder
Heat
Change in Impedance: Relative to value before
test ±20%.
Appearance: There shall be no cracking
Solder Coverage: More than 75% of the terminal
electrode shall be covered with solder.
Flux: 5-10 sec dip
After Flux: Air dry for 15 sec
Preheat: 150°C ±10°C
Preheat Time: 60 sec
Solder Temp: 260°C ±5°C
Dip Time: 10 ±1 sec
PAGE 6 OF 8
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
9. Characteristics (continued)
Item
Requirement
Conditions
Solderability
Solder Coverage: More than 95% of the
termination shall be covered with solder.
Flux: 5-10 sec dip
After Flux: Air dry for 15 sec
Solder Temp: 245°C ±5°C
Dip Time: 5 ±0.5 sec
Leach Resistance
Appearance: There shall be no visible signs of
physical or mechanical damage (i.e. no cracks)
Terminations: Termination must not be leached
away for more than 5%.
The bead shall be subjected to the following
5 steps for the period of time shown below.
The 5 steps constitute one (1) rotation.
4 rotations shall be carried out.
1) Flux: 5-10 sec
2) After Flux: Air dry for 15 sec
3) Solder Temp: 230°C ±5°C
4) Dip Time: 5 ±0.5 sec
5) Cool: Air cool for 60 seconds
Insulation Resistance
Insulation Resistance: Min 1G ohms
Solvent Resistance
Change in Impedance: Relative to value before
test ±10%.
Terminal Strength
(hanging test)
Appearance: The terminal electrode shall not
break off, nor shall there be damage to the body.
Type
1206
W(kgf)
1.5
Time
30 sec ±2 sec
Terminal Strength
(push test)
Appearance: There shall be no evidence of
mechanical degradations to terminals or body.
Type
1206
W(kgf)
2.3
Time
60 sec
Bending Strength
Appearance: There shall be no physical or
mechanical damage
Impedance: Relative to initial value before
test ±10%
Board: 90x40x1.6mm
Bend: 1mm
Time: 5 sec
Mechanical Shock
Appearance: There shall be no physical or
mechanical damage
Impedance: Relative to initial value before test
±10%
Force: 50G
Time: 11 msec
There shall be 3 shocks in each of 6 directions
(18 shocks total).
Vibration
Impedance: Relative to initial value ±10%
Only endurance conditioning by sweeping shall
be made. The entire frequency range from
10-2,000Hz and return to 10Hz in 20
minutes (this shall constitute one cycle).
Amplitude: 1.5mm
The test shall have a 15G peak and shall be
applied for a period of 4 hours (12 cycles)
in each of 3 mutually perpendicular directions
(a total of 36 cycles within a total of 12 hours).
Cleaning by:
Washer: Ultrasonic washer (100W)
Solvent: Isopropyl alcohol
Time: 3 minutes
PAGE 7 OF 8
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.
KOA SPEER ELECTRONICS, INC.
SS-224 R5
9. Characteristics (continued)
Item
Requirement
Conditions
Thermal Shock
Appearance: There shall be no physical or
mechanical damage.
Impedance: Relative to initial value ±20%.
DCR: The DCR shall not exceed initial specified
value.
Testing of the parts will be made at 0 hours, 250
hours and 500 hours. Before testing the parts
shall be allowed to cool to room temperature for
24 hours.
Load Humidity
Appearance: There shall be no physical or
mechanical damage
Impedance: Relative to initial value ±15%
Step
1-start
2-hold
3-transfer
4-hold
5-transfer
Temperature
-40°C ±2°C
-40°C ±2°C
—
+105°C ±2°C
—
Time
—
30 min ±5 min
0.5 min max.
30 min ±5 min
0.5 min max.
Steps 1 thru 5 constitute one complete cycle
and the test shall consist of a total of 500
cycles.
Temperature: 85°C ±2°C
Relative Humidity: 85%
Time: 1,000 hours total
Apply: 100% rated current
Measurements shall be taken at 0 hours, 250
hours, 500 hours and 1,000 hours and shall meet
the conditions stated above.
Life Test
Appearance: There shall be no physical or
mechanical damage
Impedance: Relative to initial value ±15%
Temperature: 85°C ±2°C
Time: 1,000 hours total
Apply: 100% rated current
Measurements shall be taken at 0 hours, 250
hours, 500 hours and 1,000 hours and shall meet
the conditions stated above.
10. Recommended PC Board Land Patterns - inches (mm)
Chip Component Size
Size
L
W
Soldering
Pad
B W
A
Chip
Component
1206
(3216)
.126
(3.2)
.063
(1.6)
A
B
C
E
.030
.120
.016
.031
(0.762) (3.048) (0.406) (0.787)
E
C
L
PAGE 8 OF 8
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.koaspeer.com
Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.