DATA SHEET SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS Mid-voltage NP0/X7R 100 V TO 630 V 0.47 pF to 2.2 µF Product Specification – April 25, 2016 V.16 RoHS compliant & Halogen Free Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 630 V SCOPE ORDERING INFORMATION - GLOBAL PART NUMBER, PHYCOMP This specification describes Midvoltage NP0/X7R series chip capacitors with lead-free terminations. CTC & 12NC APPLICATIONS PCs, Hard disk, Game PCs Power supplies LCD panel ADSL, Modem FEATURES Supplied in tape on reel Nickel-barrier end termination RoHS compliant Halogen Free compliant 2 18 All part numbers are identified by the series, size, tolerance, TC material, packing style, voltage, process code, termination and capacitance value. YAGEO BRAND ordering code GLOBAL PART NUMBER (PREFERRED ) CC XXXX X X XXX X (1) (2) (3) (4) (5) B X XXX (6) (7) (1) SIZE – INCH BASED (METRIC) 0402 (1005) / 0603 (1608) / 0805 (2012) / 1206 (3216) / 1210 (3225) 1808 (4520) / 1812 (4532) (2) TOLERANCE C = ± 0.25 pF D = ± 0.5 pF F = ± 1% G = ± 2% J = ± 5% K = ± 10% M = ± 20% (3) PACKING STYLE R = Paper/PE taping reel; Reel 7 inch K = Blister taping reel; Reel 7 inch P = Paper/PE taping reel; Reel 13 inch F = Blister taping reel; Reel 13 inch C = Bulk case (4) TC MATERIAL NPO X7R (5) RATED VOLTAGE 0 = 100 V A = 200 V Y = 250 V B = 500 V Z = 630 V (6) PROCESS N = NP0 B = Class 2 MLCC (7) CAPACITANCE VALUE 2 significant digits+number of zeros The 3rd digit signifies the multiplying factor, and letter R is decimal point Example: 121 = 12 x 101 = 120 pF www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 630 V 3 18 CONSTRUCTION The capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. This structure gives rise to a high capacitance per unit volume. The inner electrodes are connected to the two end terminations and finally covered with a layer of plated tin (NiSn). The terminations are lead-free. A cross section of the structure is shown in Fig.1. Fig. 1 Surface mounted multilayer ceramic capacitor construction DIMENSION Table 1 For outlines see fig. 2 OUTLINES T (MM) L2 / L3 (mm) min. max. L4 (mm) min. TYPE L1 (mm) W (mm) 0402 1.0 ± 0.10 0.5 ± 0.05 0.15 0.30 0.40 0603 1.6 ± 0.10 0.8 ± 0.10 0.20 0.60 0.40 0805 2.0 ± 0.20 1.25 ± 0.20 0.25 0.75 0.55 0.25 0.75 1.40 Refer to table 2 to 13 1206 3.2 ± 0.30 1.6 ± 0.20 1210 3.2 ± 0.30 2.5 ± 0.20 0.25 0.75 1.40 1808 4.5 ± 0.40 2.0 ± 0.30 0.25 0.75 2.20 1812 4.5 ± 0.40 3.2 ± 0.30 0.25 0.75 2.20 For dimension see Table 1 Fig. 2 Surface mounted multilayer ceramic capacitor dimension www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors CAPACITANCE RANGE & THICKNESS FOR NP0 Table 2 Sizes from 0603 to 0805 0402 0603 CAP. Mid-voltage NP0/X7R 100 V to 630 V 4 18 0805 100V 100 V 200 V 250 V 100 V 200 V 250 V 500 V 630V 0.5± 0.05 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.47 pF 0.56 pF 0.68 pF 0.82 pF 1.0 pF 1.2 pF 1.5 pF 1.8 pF 2.2 pF 2.7 pF 3.3 pF 3.9 pF 4.7 pF 5.6 pF 6.8 pF 8.2 pF Table 3 Sizes from 0402 to 0805 0402 0603 100 V 100 V 200 V 250 V 100 V 200 V 250 V 500 V 630V 0.5± 0.05 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 CAP. 0805 10 pF 12 pF 15 pF 18 pF 22 pF 27 pF 33 pF 39 pF 47 pF 56 pF 68 pF 82 pF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-12 series is on request www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors CAPACITANCE RANGE & THICKNESS FOR NP0 Table 4 Sizes from 0402 to 0805 (continued) 0402 0603 CAP. 100 V 100 pF 100 V 200 V 250 V Mid-voltage NP0/X7R 100 V to 630 V 5 18 0805 100 V 200 V 250 V 500 V 630 V 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.85± 0.1 0.85± 0.1 1.25± 0.2 1.25± 0.2 0.5± 0.05 120 pF 150 pF 180 pF 220 pF 270 pF 0.8± 0.1 330 pF 0.8± 0.1 0.6± 0.1 390 pF 470 pF 560 pF 0.85± 0.1 0.85± 0.1 0.8± 0.1 680 pF 820 pF 1.0 nF 1.2 nF 1.5 nF 0.85± 0.1 1.8 nF 2.2 nF 1.25± 0.2 2.7 nF 3.3 nF 1.25± 0.2 1.25± 0.2 3.9 nF 4.7 nF 5.6 nF 6.8 nF 8.2 nF 10 nF 12 nF 15 nF 18 nF 22 nF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-12 series is on request www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors CAPACITANCE RANGE & THICKNESS FOR NP0 Table 5 Sizes from 1206 to 1210 1206 CAP. 100 V 200 V 250 V 0.6± 0.1 0.6± 0.1 0.6± 0.1 500 V Mid-voltage NP0/X7R 100 V to 630 V 6 18 1210 630 V 100 V 200 V 250 V 500 V 630 V 200 V 250 V 500 V 630 V 0.47 pF 0.56 pF 0.68 pF 0.82 pF 1.0 pF 1.2 pF 1.5 pF 1.8 pF 2.2 pF 2.7 pF 3.3 pF 3.9 pF 4.7 pF 5.6 pF 6.8 pF 8.2 pF Table 6 Sizes from 1206 to 1210 1206 CAP. 1210 100 V 200 V 250 V 500 V 630 V 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 1.25± 0.2 100 V 10 pF 12 pF 15 pF 18 pF 22 pF 27 pF 33 pF 39 pF 47 pF 56 pF 68 pF 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 82 pF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-12 series is on request www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors CAPACITANCE RANGE & THICKNESS FOR NP0 Table 7 Sizes from 1206 to 1210 (continued) 1206 CAP. 100 V 200 V 250 V 500 V Mid-voltage NP0/X7R 100 V to 630 V 7 18 1210 630 V 100 V 200 V 250 V 500 V 630 V 100 pF 120 pF 150 pF 1.25± 0.2 180 pF 220 pF 270 pF 0.6± 0.1 0.6± 0.1 0.6± 0.1 330 pF 390 pF 470 pF 560 pF 1.25± 0.2 0.6± 0.1 680 pF 1.25± 0.2 1.25± 0.2 1.25± 0.2 820 pF 1.0 nF 0.85± 0.1 1.2 nF 0.85± 0.1 0.85± 0.1 1.25± 0.2 1.5 nF 1.8 nF 1.25± 0.2 2.2 nF 2.7 nF 1.25± 0.2 1.25± 0.2 3.3 nF 3.9 nF 4.7 nF 0.85± 0.1 5.6 nF 6.8 nF 8.2 nF 10 nF 1.25± 0.2 12 nF 15 nF 18 nF 22 nF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-12 series is on request www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors CAPACITANCE RANGE & THICKNESS FOR NP0 Table 8 Sizes 1812 1812 CAP. 100 V 200 V 500 V CAP. 630V 12 pF 120 pF 15 pF 150 pF 18 pF 180 pF 22 pF 220 pF 27 pF 270 pF 33 pF 330 pF 39 pF 390 pF 47 pF 470 pF 56 pF 560 pF 82 pF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-12 series is on request 100 V to 630 V 8 18 1.25± 0.2 1812 100 V 100 pF 1.25± 0.2 NP0/X7R Table 9 Sizes 1812 (continued) 10 pF 68 pF Mid-voltage 200 V 500 V 630V 1.25± 0.2 680 pF 1.25± 0.2 820 pF 1 nF 1.2 nF 1.5 nF 1.25± 0.2 1.25± 0.2 1.8 nF 2.2 nF 2.7 nF 3.3 nF 3.9 nF 4.7 nF 5.6 nF 6.8 nF 8.2 nF 10 nF 12 nF 15 nF 18 nF 22 nF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-12 series is on request www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors CAPACITANCE RANGE & THICKNESS FOR X7R Table 10 Sizes from 0603 to 0805 0402 0603 CAP. 100 V 100 V Mid-voltage NP0/X7R 100 V to 630 V 9 18 0805 100 V 200 V 250 V 500 V 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.25± 0.2 1.25± 0.2 100 pF 150 pF 220 pF 330 pF 470 pF 680 pF 1.0 nF 0.5± 0.05 1.5 nF 0.6± 0.1 2.2 nF 3.3 nF 0.8± 0.1 4.7 nF 6.8 nF 10 nF 15 nF 22 nF 1.25± 0.2 0.85± 0.1 33 nF 47 nF 68 nF 1.25± 0.2 100 nF 150 nF 220 nF 330 nF 470 nF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-6 series is on request 3. For special ordering code, please contact local sales force before order 4. For product with 5% tolerance, please contact local sales force before order www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors CAPACITANCE RANGE & THICKNESS FOR X7R Table 11 Sizes from 1206 to 1210 1206 CAP. 100 V 200 V 250 V 0.85± 0.1 0.85± 0.1 500 V Mid-voltage NP0/X7R 100 V to 630 V 10 18 1210 630 V 100 V 200 V 250 V 0.85± 0.1 0.85± 0.1 500 V 630V 100 pF 150 pF 220 pF 330 pF 470 pF 680 pF 1.0 nF 1.5 nF 2.2 nF 3.3 nF 1.25± 0.2 1.25± 0.2 0.85± 0.1 4.7 nF 6.8 nF 10 nF 15 nF 33 nF 1.25± 0.2 47 nF 1.25± 0.2 1.6± 0.2 1.6± 0.2 68 nF 100 nF 150 nF 1.25± 0.2 1.25± 0.2 1.6± 0.2 470 nF 1.25± 0.2 1.6± 0.2 220 nF 330 nF 1.25± 0.2 0.85± 0.1 22 nF 1.25± 0.2 1.25± 0.2 1.6± 0.2 680 nF 1 µF 1.6± 0.2 2.0± 0.2 2.2 µF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-6 series is on request 3. For product with 5% tolerance, please contact local sales force before order www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors CAPACITANCE RANGE & THICKNESS FOR X7R Table 12 Sizes from 1808 to 1812 1808 CAP. 100 V 200 V 250 V 500 V Mid-voltage NP0/X7R 100 V to 630 V 11 18 1812 100 V 200 V 250 V 500 V 630 V 100 pF 150 pF 220 pF 330 pF 470 pF 680 pF 1.0 nF 1.5 nF 2.2 nF 3.3 nF 4.7 nF 1.35± 0.2 6.8 nF 10 nF 15 nF 22 nF 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.25± 0.2 33 nF 1.6± 0.2 47 nF 68 nF 100 nF 150 nF 220 nF 1.25± 0.2 1.25± 0.2 1.6± 0.2 1.6± 0.2 1.6± 0.2 1.25± 0.2 330 nF 470 nF 680 nF 1.6± 0.2 1 µF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-6 series is on request 3. For product with 5% tolerance, please contact local sales force before order www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 630 V 12 18 THICKNESS CLASSES AND PACKING QUANTITY Table 13 SIZE CODE Ø 180 MM / 7 INCH Paper Blister Ø 330 MM / 13 INCH Paper Blister THICKNESS CLASSIFICATION TAPE WIDTH QUANTITY PER REEL 0201 0.3 ± 0.03 mm 8 mm 15,000 --- 50,000 --- --- 0402 0.5 ± 0.05 mm 8 mm 10,000 --- 50,000 --- 50,000 0603 0.8 ± 0.1 mm 8 mm 4,000 --- 15,000 --- 15,000 0.6 ± 0.1 mm 8 mm 4,000 --- 20,000 --- 10,000 0.8 / 0.85 ± 0.1 mm 8 mm 4,000 --- 15,000 --- 8,000 1.25 ± 0.2 mm 8 mm --- 3,000 --- 10,000 5,000 0.6 ± 0.1 mm 8 mm 4,000 --- 20,000 --- --- 0.8 / 0.85 ± 0.1 mm 8 mm 4,000 --- 15,000 --- --- 1.00 / 1.15 ± 0.1 mm 8 mm --- 3,000 --- 10,000 --- 1.25 ± 0.2 mm 8 mm --- 3,000 --- 10,000 --- 1.6 ± 0.15 mm 8 mm --- 2,500 --- 10,000 --- 1.6 ± 0.2 mm 8 mm --- 2,000 --- 8,000 --- 0.6 / 0.7 ± 0.1 mm 8 mm --- 4,000 --- 15,000 --- 0.85 ± 0.1 mm 8 mm --- 4,000 --- 10,000 --- 0805 1206 QUANTITY PER BULK CASE 1.15 ± 0.1 mm 8 mm --- 3,000 --- 10,000 --- 1.15 ± 0.15 mm 8 mm --- 3,000 --- 10,000 --- 1.25 ± 0.2 mm 8 mm --- 3,000 --- --- --- 1.5 ± 0.1 mm 8 mm --- 2,000 --- --- --- 1.6 / 1.9 ± 0.2 mm 8 mm --- 2,000 --- --- --- 2.0 ± 0.2 mm 8 mm --- 2,000 1,000 --- --- --- 2.5 ± 0.2 mm 8 mm --- 1,000 500 --- --- --- 1.15 ± 0.15 mm 12 mm --- 3,000 --- --- --- 1.25 ± 0.2 mm 12 mm --- 3,000 --- --- --- 1.35 ± 0.15 mm 12 mm --- 2,000 --- --- --- 1.5 ± 0.1 mm 12 mm --- 2,000 --- --- --- 1.6 ± 0.2 mm 12 mm --- 2,000 --- 8,000 --- 2.0 ± 0.2 mm 12 mm --- 2,000 --- --- --- 0.6 / 0.85 ± 0.1 mm 12 mm --- 2,000 --- --- --- 1.15 ± 0.1 mm 12 mm --- 1,000 --- --- --- 1.15 ± 0.15 mm 12 mm --- 1,000 --- --- --- 1.25 ± 0.2 mm 12 mm --- 1,000 --- --- --- 1.35 ± 0.15 mm 12 mm --- 1,000 --- --- --- 1.5 ± 0.1 mm 12 mm --- 1,000 --- --- --- 1.6 ± 0.2 mm 12 mm --- 1,000 --- --- --- 2.0 ± 0.2 mm 12 mm --- 1,000 --- --- --- 2.5 ± 0.2 mm 12 mm --- 500 --- --- --- 1210 1808 1812 www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 13 18 100 V to 630 V ELECTRICAL CHARACTERISTICS NP0/X7R DIELECTRIC CAPACITORS; NISN TERMINATIONS Unless otherwise specified, all test and measurements shall be made under standard atmospheric conditions for testing as given in 5.3 of IEC 60068-1: - Temperature: 15 °C to 35 °C Relative humidity: 25% to 75% Air pressure: 86 kPa to 106 kPa Before the measurements are made, the capacitor shall be stored at the measuring temperature for a time sufficient to allow the entire capacitor to reach this temperature. The period as prescribed for recovery at the end of a test is normally sufficient for this purpose. Table 14 VALUE DESCRIPTION Capacitance range 0.47 pF to 2.2 µF Capacitance tolerance NP0 C < 10 pF ± 0.25 pF, ± 0.5 pF C ≥ 10 pF ±2%, ± 5%, ± 10% X7R ± 5% (1), ± 10%, ± 20% Dissipation factor (D.F.) NP0 C < 30 pF ≤ 1 / ( 400 + 20C ) C ≥ 30 pF ≤ 0.1 % X7R Exception Insulation resistance after 1 minute at Ur (DC) ≤ 2.5 % X7R/0603/100V, 12nF ≤ C ≤ 100nF ≤ 5% X7R/1206/100V/1uF; X7R/1210/100V/1uF and 2.2uF; ≤ 3.5% Rins ≥ 10 GΩ or Rins × C ≥ 500(100) seconds whichever is less Maximum capacitance change as a function of temperature (temperature characteristic/coefficient): NP0 ± 30 ppm/°C X7R ± 15% Operating temperature range: NP0/X7R –55 °C to +125 °C NOTE 1. Capacitance tolerance ±5% doesn't available for X7R full product range, please contact local sales force before order www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 14 18 100 V to 630 V SOLDERING RECOMMENDATION Table 15 SOLDERING METHOD SIZE 0402 0603 0805 1206 ≥ 1210 Reflow ≥ 0.1 µF ≥ 1.0 µF ≥ 2.2 µF ≥ 4.7 µF Reflow only Reflow/Wave < 0.1 µF < 1.0 µF < 2.2 µF < 4.7 µF --- TESTS AND REQUIREMENTS Table 16 Test procedures and requirements TEST TEST METHOD PROCEDURE REQUIREMENTS Mounting IEC 60384- 4.3 21/22 The capacitors may be mounted on printed-circuit boards or ceramic substrates No visible damage Visual Inspection and Dimension Check 4.4 Any applicable method using × 10 magnification In accordance with specification Capacitance 4.5.1 Class 1: f = 1 MHz for C ≤ 1 nF, measuring at voltage 1 Vrms at 20 °C Within specified tolerance f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C Class 2: f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C Dissipation Factor (D.F.) 4.5.2 Class 1: f = 1 MHz for C ≤ 1 nF , measuring at voltage 1 Vrms at 20 °C In accordance with specification f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C Class 2: f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C Insulation Resistance 4.5.3 Ur ≤ 500 V: At Ur for 1 minute In accordance with specification Ur > 500 V: At 500 V for 1 minute www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors TEST TEST METHOD Temperature coefficient 4.6 Mid-voltage NP0/X7R 100 V to 630 V PROCEDURE REQUIREMENTS Capacitance shall be measured by the steps shown in the following table. <General purpose series> Class1: ∆ C/C: ± 30ppm The capacitance change should be measured after 5 min at each specified temperature stage. Step Temperature(℃) a 25± 2 b Lower temperature± 3℃ c 25± 2 d Upper Temperature± 2℃ e 25± 2 15 18 Class2: X7R: ∆ C/C: ±15% Y5V: ∆ C/C: 22~-82% <High Capacitance series> Class2: X7R/X5R: ∆ C/C: ±15% Y5V: ∆ C/C: 22~-82% (1) Class I Temperature Coefficient shall be calculated from the formula as below C2 - C1 106 [ppm/℃] Temp, Coefficient = C1 xΔT C1: Capacitance at step c C2: Capacitance at 125℃ ∆T: 100℃(=125℃-25℃) (2) Class II Capacitance Change shall be calculated from the formula as below C2 - C1 ∆C = x 100% C1 C1: Capacitance at step c C2: Capacitance at step b or d Adhesion Bending Strength IEC 6038421/22 4.7 A force applied for 10 seconds to the line joining the terminations and in a plane parallel to the substrate Force size ≥ 0603: 5N 4.8 Mounting in accordance with IEC 60384-22 paragraph 4.3 No visible damage Conditions: bending 1 mm at a rate of 1 mm/s, radius jig 5 mm ∆C/C Class 1: NP0: within ± 1% or 0.5 pF, whichever is greater Class2: X7R: ± 10% www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors TEST TEST METHOD Resistance to Soldering Heat 4.9 Mid-voltage NP0/X7R 100 V to 630 V 16 18 PROCEDURE REQUIREMENTS Precondition: 150 +0/–10 °C for 1 hour, then keep for 24 ± 1 hours at room temperature Dissolution of the end face plating shall not exceed 25% of the length of the edge concerned Preheating: for size ≤ 1206: 120 °C to 150 °C for 1 minute Class 1: NP0: within ± 0.5% or 0.5 pF, whichever is greater ∆C/C Preheating: for size >1206: 100 °C to 120 Class2: °C for 1 minute and 170 °C to 200 °C for 1 X7R: ± 10% minute D.F. within initial specified value Solder bath temperature: 260 ± 5 °C Dipping time: 10 ± 0.5 seconds Rins within initial specified value Recovery time: 24 ± 2 hours Solderability 4.10 Preheated the temperature of 80 °C to 140 °C and maintained for 30 seconds to 60 seconds. The solder should cover over 95% of the critical area of each termination Test conditions for lead containing solder alloy Temperature: 235 ± 5 °C Dipping time: 2 ± 0.2 seconds Depth of immersion: 10 mm Alloy Composition: 60/40 Sn/Pb Number of immersions: 1 Test conditions for leadfree containing solder alloy Temperature: 245 ± 5 °C Dipping time: 3 ± 0.3 seconds Depth of immersion: 10 mm Alloy Composition: SAC305 Number of immersions: 1 Rapid Change of Temperature IEC 6038421/22 4.11 Preconditioning; 150 +0/–10 °C for 1 hour, then keep for 24 ± 1 hours at room temperature 5 cycles with following detail: 30 minutes at lower category temperature 30 minutes at upper category temperature Recovery time 24 ± 2 hours No visual damage ∆C/C Class 1: NP0: within ± 1% or 1 pF, whichever is greater Class2: X7R: ± 15% D.F. meet initial specified value Rins meet initial specified value www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors TEST TEST METHOD Damp Heat 4.13 Mid-voltage REQUIREMENTS 1. Preconditioning, class 2 only: No visual damage after recovery 2. Initial measure: Spec: refer initial spec C, D, IR 3. Damp heat test: 500 ± 12 hours at 40 ± 2 °C; 90 to 95% R.H. 4. Recovery: Class 1: 6 to 24 hours Class 2: 24 ± 2 hours 5. Final measure: C, D, IR P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be precondition according to “IEC 60384 4.1” and then the requirement shall be met. IEC 6038421/22 4.14 1. Preconditioning, class 2 only: 2. 3. 4. 5. 6. 150 +0/-10 °C /1 hour, then keep for 24 ± 1 hour at room temp Initial measure: Spec: refer initial spec C, D, IR Endurance test: Temperature: NP0/X7R: 125 °C Specified stress voltage applied for 1,000 hours: High voltage series follows with below stress condition: Applied 2.0 x Ur for 100 V series Applied 1.5 x Ur for 200/250 V series Applied 1.3 x Ur for 500 V, 630 V series Applied 1.2 x Ur for 1 KV, 2 KV, 3 KV series Recovery time: 24 ± 2 hours Final measure: C, D, IR P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be precondition according to “IEC 60384 4.1” and then the requirement shall be met. Voltage Proof 4.6 100 V to 630 V PROCEDURE 150 +0/-10 °C /1 hour, then keep for 24 ± 1 hour at room temp Endurance NP0/X7R Specified stress voltage applied for 1~5 seconds Ur ≤ 100 V: series applied 2.5 Ur 17 18 ∆C/C Class 1: NP0: within ± 2% or 1 pF, whichever is greater Class2: X7R: ± 15% D.F. Class 1: NP0: ≤ 2 x specified value Class2: X7R: ≥ 25 V: ≤ 5% Rins Class 1: NP0: ≥ 2,500 MΩ or Rins x Cr ≥ 25s whichever is less Class2: X7R: ≥ 500 MΩ or Rins x Cr ≥ 25s whichever is less No visual damage ∆C/C Class1: NP0: within ± 2% or 1 pF, whichever is greater Class2: X7R: ± 15% D.F. Class1: NP0: ≤ 2 x specified value Class2: X7R: ≥ 25 V: ≤ 5% Rins Class1: NP0: ≥ 4,000 MΩ or Rins x Cr ≥ 40s whichever is less Class2: X7R: ≥ 1,000 MΩ or Rins x Cr ≥ 50s whichever is less No breakdown or flashover 100 V < Ur ≤ 200 V series applied (1.5 Ur + 100) 200 V < Ur ≤ 500 V series applied (1.3 Ur + 100) Ur > 500 V: 1.3 Ur Ur ≧ 1000 V: 1.2 Ur Charge/Discharge current is less than 50 mA www.yageo.com Apr. 25, 2016 V.16 Product specification Surface-Mount Ceramic Multilayer Capacitors Mid-voltage NP0/X7R 100 V to 630 V 18 18 REVISION HISTORY REVISION DATE CHANGE NOTIFICATION DESCRIPTION Version 16 Apr. 16, 2015 - - Capacitance range & thickness Version 15 Apr. 16, 2015 - - Electrical characteristics update Version 14 Sep. 25, 2014 - - Electrical characteristics update Version 13 Apr. 21, 2014 - - Electrical characteristics update Version 12 Dec. 12, 2013 - - Electrical characteristics update Version 11 Jun. 17, 2013 - - Test method and procedure updated Version 10 Nov 22, 2012 - - Test method and procedure updated Version 9 Feb 02, 2012 - - Test method and procedure updated Version 8 Apr 22, 2011 - - NP0 0402 100V added Version 7 Mar 01, 2011 - - Dimension updated Version 6 Sep 30, 2010 - - Update the thickness of 0805 100V Version 5 Sep 28, 2010 - - Product range updated - Thickness classes and packing quantity table updated Version 4 Jun 17, 2010 - - Update the dimension of 0805, 1206 and 1812 Version 3 Mar 25, 2010 - - Product range update Version 2 Mar 15, 2010 - - Product range update Version 1 Oct 30, 2009 - - Change to dual brand datasheet that describe Mid-voltage NP0/X7R series with RoHS compliant - Replace the "100V to 630V" part of pdf files: UP-NP0X7R_MV_100-to500V_0, UY-NP0X7R_MV_100-to-500V_0, NP0_16V-to-100V_6, NP0_50-to-500V_10, X7R_16-to-500V_9 and X7R_16V-to-100V_9 - Define global part number - Description of "Halogen Free compliant" added - Test method and procedure updated Version 0 Sep 08, 2005 - - New www.yageo.com Apr. 25, 2016 V.16