Rohm MCH555FN107MP Multi-layer ceramic chip capacitor Datasheet

MCH55
Ceramic capacitors
Multi-layer ceramic chip capacitors
MCH55 (5750 (2220) size, chip capacitor)
zFeatures
1) High capacitance
2) Achieved high capacitance by thin and multi layer technology
3) Lead-free plating terminal
4) No polarity
zQuick Reference
The design and specifications are subject to change without prior notice. Please check the most recent technical
specifications prior to placing orders or using the product. For more detail information regarding packaging style code,
please check product designation.
zHigh dielectric constant
Part No.
Size code
Temperature characteristics
code
Operating temp. range
(°C)
Rated voltage
(V)
50
±10%
(B)
−25 to +85
25
16
50
CN
MCH55
±15%
(R) (X7R)
−55 to +125
5750
(2220)
25
16
±15%
(X5R)
−55 to +85
+30% , −80%
(F)
−25 to +85
+22% , −82%
(Y5V)
−30 to +85
FN
16
6.3
50
25
16
50
25
16
Capacitance (pF)
4,700,000 (E6 Series)
6,800,000 (E6 Series)
10,000,000 (E6 Series)
15,000,000 (E6 Series)
22,000,000 (E6 Series)
4,700,000 (E6 Series)
6,800,000 (E6 Series)
10,000,000 (E6 Series)
15,000,000 (E6 Series)
22,000,000 (E6 Series)
33,000,000 (E6 Series)
47,000,000 (E6 Series)
68,000,000 (E6 Series)
22,000,000 (E3 Series)
47,000,000 (E3 Series)
100,000,000 (E3 Series)
22,000,000 (E3 Series)
47,000,000 (E3 Series)
100,000,000 (E3 Series)
Capacitance
tolerance
K(±10%)
M(±20%)
Thickness
(mm)
2.0 ± 0.2
2.5 ± 0.3
2.0 ± 0.2
2.3 ± 0.2
2.5 ± 0.3
2.0 ± 0.2
2.5 ± 0.3
2.0 ± 0.2
2.3 ± 0.2
2.5 ± 0.3
2.0 ± 0.2
2.3 ± 0.2
2.0 ± 0.2
Z(+80% , −20%)
2.5 ± 0.3
2.0 ± 0.3
2.5 ± 0.3
zExternal dimensions (Unit : mm)
Product thickness(mm)
0.2Min.
T
2.0±0.2
2.3±0.2
2.5±0.3
T
5.7±0.4
5.0±0.4
1/9
MCH55
Ceramic capacitors
zProduct designation
Packing specification
Reel
Basic ordering unit (pcs.)
P
2.0mm
Plustic tape (width 8mm, pitch 4mm)
φ180mm (7in.)
500
P
2.3mm
Plustic tape (width 8mm, pitch 4mm)
φ180mm (7in.)
500
P
2.5mm
Plustic tape (width 8mm, pitch 4mm)
φ180mm (7in.)
500
Code Product thickness
Reel (φ180mm) : compatible with EIAJ ET-7200A
Packing Style
Part No.
M C H
5 5
Rated voltage
Code Voltage
8
6.3V
4
10V
3
16V
2
25V
5
50V
3
F N
1 0 7
Temperature characteristic code
: Refer to quick reference table.
Z
P
Nominal
capacitance
3-digit
designation
according
to IEC
Capacitance tolerance
Code
Tolerance
M
±10%
±20%
Z
+80%, −20%
K
zPerformance and test method
No.
Items
Performance
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
1
Appearance and
dimensions
No marked defects shall be allowed As per 4.4 of JIS C 5101-1.
As per 4.5 of JIS C 5101-10
for appearance.
Dimensions shall be as specified the Using a Magnifier.
clause 4.
2
Withstanding voltage
No dielectrical breakdown or other
damage shall be allowed.
As per 4.6 of JIS C 5101-1.
As per 4.6.4 of JIS C 5101-10
Voltage shall be applied as per Table1.
Table 1
CharacVoltage
teristic
CN
250% Rated voltage
FN
Voltage shall be applied for 1 to 5s with
50mA charging and discharging current.
3
Insulation resistance
Not less than 10000MΩ or
100MΩ µF, whichever is less.
As per 4.5 of JIS C 5101-1.
As per 4.6.3 of JIS C 5101-10
Measurements shall be made after
60+/−5s period of the rated voltage
applied.
4
Capacitance
Capacitance shall be
within specified tolerance range.
As per 4.7 of JIS C 5101-1.
As per 4.6.1 of JIS C 5101-10
Measurements shall be made under the
conditions specified in Table 2.
Table 2
Frequency Voltage
Characteristic
CN
FN
5 Dielectric loss tangent
CN
tan δ <
− 7.5%
FN
Rated voltage=16V
tan δ <
− 10.0%
<
− 10µF
> 10µF
1+/−0.1kHz
120+/−24Hz
1+/−0.2Vrms. 0.5+/−0.2Vrms.
As per 4.8 of JIS C 5101-1.
As per 4.6.2 of JIS C 5101-10
Measurements shall be made under the
conditions specified in Table 2.
2/9
MCH55
Ceramic capacitors
No.
Items
6 Temperature
characteristic
Performance
CN
FN
B
+/−10%
(−25°C to +85°C)
X5R
+/−15%
(−55°C to +85°C)
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
As per 4.24 of JIS C 5101-1.
As per 4.7 of JIS C 5101-10
If required, measurements shall be made
at a given temperature.
+30%, −80%
(−25°C to +85°C)
+22%, −82%
(−30°C to +85°C)
7 Solderability
More than 3/4 of each end
termination shall be covered with
new solder.
As per 4.15.2 of JIS C 5101-1.
As per 4.11 of JIS C 5101-10
The solder specified in JIS Z 3282 H63A
shall be used. Ans the flux containing 25%
rosin and ethanol solution shall be used.
The specimens shall be immersed into the
solder at 235+/−5°C for 2+/−0.5s
So that both end terminations are
completely under solder.
8 Resistance Appearance
to soldering
heat
Without mechanical damage.
As per 4.14 of JIS C 5101-1.
As per 4.10 of JIS C 5101-10
The solder specified in JIS Z 3282. H63A
shall be used.
The specimens shall be immersed into the
solder at 260+/−5°C for 5+/−0.5s so that
both end terminations are completely
under the solder.
Pre-heating at 150+/−10°C for 1 to 2min
Initial measurements prior to test shall be
performed after the thermal
Pre-conditioning specified in Remarks (1).
Final measurements shall be made after the
specimens have been left at room
temperature as per Table3.
Change
rate from
initial value
CN
Within +/−7.5%
FN
Within +/−20%
Dielectric
loss
tangent
Within specified initial value.
Insulation
resistance
Within specified initial value.
Withstanding No defects shall be allowed.
voltage
9 End termination
adherence
Without peeling or sign of
peeling shall be allowed
on the end terminations.
Table3
Characteristic
CN, FN
Time
48+/−4 h
As per 4.13 of JIS C 5101-1.
As per 4.8 ofJIS C 5101-10
A 5N weight for 10+/−1s shall be applied
to the soldered specimens as shown by the
arrow mark in the below sketch.
Applied pressure
Substrate
Capacitor
3/9
MCH55
Ceramic capacitors
No.
Items
Performance
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
10 Bending
strength
Appearance
Without mechanical damage.
As per 4.35 of JIS C 5101-1.
As per 4.9 of JIS C 5101-10
Glass epoxy board with soldered
specimens shall be bent till 1mm by
1.0mm/s.
11 Vibration
Appearance
Without mechanical damage.
As per 4.17 of JIS C 5101-1.
The specimens shall be soldered on the
specified test jig.
Initial measurements shall be made after
the thermal pre-conditioning specified in
Remarks(1).
Final measurements shall be made after the
specimens have been left at room
temperature as per Table3.
[Condition]
Directions : 2h each X, Y and Z directions
Total : 6h
Frequency range : 10 to 55 to 10Hz(1min)
Applitude : 1.5mm
(shall not exceed acceleration196m/s2)
Change
rate from
initial value
Dielectric
loss
tangent
CN
Within +/−7.5%
FN
Within +/−20%
Within specified initial value.
Table3
Characteristic
CN, FN
12 Temperature Appearance
cycling
Change
rate from
initial value
Dielectric
loss
tangent
Insulation
resistance
Without mechanical damage.
CN
Within +/−7.5%
FN
Within +/−20%
Within specified initial value.
Within specified initial value.
Withstanding No defects shall be allowed.
voltage
Time
48+/−4 h
As per 4.16 of JIS C 5101-1
As per 4.12 of JIS C 5101-10
The specimens shall be soldered on the test
jig shown in Remarks.
Temperature cycle : 100cycles Initial
measurements prior to test shall be
performed after the thermal
per-conditioning specified in Remarks (1).
Final measurements shall be made after the
specimens have been left at room
temperature as per Table3.
Test condition
Step
Temp. (°C)
Time (min)
1
Min operating temp.
2
Room temp.
30+/−3
<
−3
3
Max operating temp.
4
Room temp.
30+/−3
<
−3
Table3
Characteristic
CN, FN
Time
48+/−4 h
4/9
MCH55
Ceramic capacitors
No.
13 Humidity
(Steady)
Items
Performance
Appearance Without mechanical damage.
Change
rate from
initial value
CN
FN
Dielectric
tangent
CN
FN
Insulation
resistance
14 Humidity
life test
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
As per 4.22 of JIS C 5101-1
As per JIS C 5101-10
Test temperature : 60+/−2°C
Within +/−12.5%
Relative humidity : 90 to 95%
Test time
: 500 +24/−0 h
Initial measurements prior to test shall
Within +/−30%
be made after the voltage
pre-conditioning specified in
Less than 200% of Remarks (2).
initial spec.
Final measurements have been left at
room temperature as per Table3.
Less than 150% of
initial spec.
Table3
Not less than 1000MΩ or
10MΩ µF, whichever is less.
Characteristic
CN, FN
Time
48+/−4 h
Appearance Without mechanical damage.
Change
rate from
initial value
Dielectric
loss
tangent
Insulation
resistance
As per 4.22 of JIS C 5101-1
As per 4.14 of JIS C 5101-10
CN
Within +/−12.5% Test temperature : 60+/−2°C
Relative humidity : 90 to 95%
Voltage : Rated voltage
FN
Within +/−30%
Test time : 500 +24/−0 h
Less than 200% of Initial measurements prior to test shall
CN
be made after the voltage
initial spec.
pre-conditioning specified in
Less than 150% of Remarks (2).
FN
initial spec.
Final measurements shall be made after
the specimens have been left at room
Not less than 500MΩ or
temperature as per Table3.
5MΩ µF, whichever is less.
Table3
Characteristic
CN, FN
Time
48+/−4 h
5/9
MCH55
Ceramic capacitors
No.
Items
15 Heat life
test
Performance
Appearance Without mechanical damage.
Change
rate from
initial value
Dielectric
loss
tangent
Insulation
resistance
CN
Within +/−15%
FN
Within +/−30%
CN
Less than 200% of
initial spec.
FN
Less than 150% of
initial spec.
Not less than 1000MΩ or
10MΩ µF, whichever is less.
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
As per 4.23 of JIS C 5101-1.
As per 4.15 of JIS C 5101-10
Test
Voltage
temperature(°C)
CN
85
(B X5R)
FN
85
200%
Rated
voltage
200%
Rated
voltage
Test
time (h)
1000
+48/−0
1000
+48/−0
Initial measurements prior to test shall be
made after the voltage pre-conditioning
specified in Remarks (2).
Final measurements shall be made after
the specimens have been left at room
temperature
Table3
Characteristic
CN, FN
Time
48+/−4 h
[Remarks]
Pre-conditioning
If specified in test method of as per 3(Performance and test method), capacitors of CN, FN
characteristics shall be pre-conditionded as follows.
(1) Thermal pre-conditioning
Prior to initial measurements, specimens shall be conditioned at a temperature of 150 0/−10°C
for a period of 1hr., and shall be allowed to stabilize at room temperature for 48+/−4h
(2) Voltage pre-conditioning
Prior to initial measurements, voltage specified as a test condition shall be applied to specimens
for a period of 1hr., and the specimens shall be allowed to stabilize at room temperature for 48+/−4h
<Test jig>
Soldering
Glass epoxy
substrate
6/9
MCH55
Ceramic capacitors
zPackaging specifications
Taping dimensions
Reel dimensions
t
φJ
E
A
D
G
t1
H
P : Plastic tape
Pulling direction
C
Symbol
D
φ13.0 +
− 0.2
F
E
H
G
F
t
J
t1
Plastic
5.5 1.75
8.0
2.0
4.0
φ1.5
Dimensions 12.0
+/ −0.3 +/ −0.05 +/ −0.1 +/ −0.1 +/ −0.05 +/ −0.1 +0.1/ −0
0.6
MAX.
6.5
MAX.
(Unit : mm)
Symbol
Style
A
Label pasting
As per EIAJ ET−7200A
(Unit : mm)
B
5.4
MCH55
14.0 +
− 1.5
Pulling direction
+0
φ180 −1.5
C
φ60.0+1.0
−0
B
6.1
(Unit : mm)
(1) The quantity for one reel is as bellows.
Kind of reel
Series
φ180 reel
MCH55
Plastic tape
Quantity
Symbol
500 pcs.
P
(2) When the tape is pulled out towards the operator with the cover tape facing
upward, the feeding holes shall be found on the right portion of the tape.
(3) Specification of beginning and ending of the tape are as follows.
Ending(reel's center)
Beginning(reel's round)
: Approx. Over 160mm (no chips)
: Approx. Over 160mm (no chips)
: Approx. 240mm (cover tape only)
(4) No juncture of tape shall be allowed.
(5) The share strength of tape shall be more than 5N at the break down strength.
(6) The peel strength of the cover tape shall be 0.1 to 0.7(N) when the cover tape are
peeled 0 to 15 degree from the surface.
(7) The number of missing components shall not exceed 0.1% of the total number
of components (marked number) or one whichever is the larger, and no consecutive
missing exceeding two is allowed.
(8) The reels made from resin shall be used, as per EIAJ ET-7200A.
zMarking
No marking shall be performed on the chip.
Trademark, parts number, quantity, lot No. , and country of origin shall be labeled on each reel.
zNumbering system for LOT No.
Example
03
(1)
01
(2)
A0001
(3)
F
(4)
(1) The end of the Christian Era < two digits> of production finish.
(2) Week in completing part of production finish.
(3) Manufacture continuity number.
(4) The symbol of manufacturing plant.
7/9
MCH55
Ceramic capacitors
zLabel expression
The Figure below is label expression
< Label Example > Part Number : MCH553CN226MP
①
②
③
④
⑤
⑥
⑦
⑧
Part Number
Division cord
Quantity
Lot No.
The Country of origin
Inspector
QR code
Trademark
zPacking method
1) φ180mm Reel
EIAJ cole
B'
2
C'
(reel)
Label
A'
[width of 9mm : 5reel]
1
A
(interior box of R-26)
Packing slip
B
C
(R-26)
8/9
MCH55
Ceramic capacitors
< Packaging unit >
Symbol
Quantity of reel in
interior box
Quantity of reel in
box of R-26
K
Dimensions
R-26
3
12
Packaging
interior box of R-26
A (A’)
195
185
B (B’)
255
60
C (C’)
190
185
(Unit : mm)
< Appearance >
Carton
< Accumulation >
You must do accumulation by ten boxes
< Packaging slip >
1.
2.
3.
4.
5.
Customer
Parts number
Quantity
Box quantity
Trade mark
9/9
Appendix
Notes
No technical content pages of this document may be reproduced in any form or transmitted by any
means without prior permission of ROHM CO.,LTD.
The contents described herein are subject to change without notice. The specifications for the
product described in this document are for reference only. Upon actual use, therefore, please request
that specifications to be separately delivered.
Application circuit diagrams and circuit constants contained herein are shown as examples of standard
use and operation. Please pay careful attention to the peripheral conditions when designing circuits
and deciding upon circuit constants in the set.
Any data, including, but not limited to application circuit diagrams information, described herein
are intended only as illustrations of such devices and not as the specifications for such devices. ROHM
CO.,LTD. disclaims any warranty that any use of such devices shall be free from infringement of any
third party's intellectual property rights or other proprietary rights, and further, assumes no liability of
whatsoever nature in the event of any such infringement, or arising from or connected with or related
to the use of such devices.
Upon the sale of any such devices, other than for buyer's right to use such devices itself, resell or
otherwise dispose of the same, no express or implied right or license to practice or commercially
exploit any intellectual property rights or other proprietary rights owned or controlled by
ROHM CO., LTD. is granted to any such buyer.
Products listed in this document are no antiradiation design.
The products listed in this document are designed to be used with ordinary electronic equipment or devices
(such as audio visual equipment, office-automation equipment, communications devices, electrical
appliances and electronic toys).
Should you intend to use these products with equipment or devices which require an extremely high level of
reliability and the malfunction of with would directly endanger human life (such as medical instruments,
transportation equipment, aerospace machinery, nuclear-reactor controllers, fuel controllers and other
safety devices), please be sure to consult with our sales representative in advance.
About Export Control Order in Japan
Products described herein are the objects of controlled goods in Annex 1 (Item 16) of Export Trade Control
Order in Japan.
In case of export from Japan, please confirm if it applies to "objective" criteria or an "informed" (by MITI clause)
on the basis of "catch all controls for Non-Proliferation of Weapons of Mass Destruction.
Appendix1-Rev1.1