HEAT SHRINK MEDIUM VOLTAGE INSULATION TUBING Qualtek Electronics QDWT SEMI-CONDUCTING / INSULATION, DOUBLE LAYER, UP TO 36kV HEAT SHRINKABLE TUBING SHRINK RATIO 3:1 Features/Applications QDWT is double layer semi-conductive heat shrinkable tubing. The inner layer is made from insulation material to provide high insulation and the external layer is made from semi-conductive materials to provide electric shielding. The tubing is manufactured with technology very suitable for applications in power cable joints up to 36kV. Operating temperature: -45°C to +100°C Minimum shrink temperature: 100°C Full Recovery Temperature: 130°C Standard color: Black RoHS Compliant Two layer Semi-conductive Specification Values for Inner Layer Test Method Typical Data Tensile Strength ASTM D 2671 > 12 MPa min. Elongation at Break ASTM D 2671 > 300% min. Property Water Absorption ISO 62 < 0.5% max. Volume Resistance IEC 93 > 10 14 Ω.cm (min.) IEC 243 > 20kV / mm (min.) ASTM D 257-98 1.1 g/cm 3 Dielectric Strength Density Specification Values for External Layer Test Method Typical Data Tensile Strength ASTM D 638 > 14 MPa min. Elongation at Break ASTM D 638 > 300% min. Water Absorption ISO 62 < 0.5% max. Volume Resistance IEC 93 Property < 10 ASTM D 257-98 Density 4 Ω.cm (min.) 1.2 g/cm 3 Product Dimensions As Supplied (mm) After Recovered (mm) Standard Packaging *(QB) (mm) Inside Diameter (min.) Inside Diameter (max.) Total Wall Thickness (nom.) Inner Insulation Layer Wall Thickness (mm) 36/12 36 12 6.0 5.0 1000 45/15 45 15 6.0 5.0 1000 55/18 55 18 6.0 5.0 1000 62/18 62 18 6.5 5.5 1000 65/22 65 22 6.6 5.6 1000 73/26 73 26 6.6 5.6 1000 85/30 85 30 6.5 5.6 1000 100/38 100 38 6.6 5.6 1000 120/45 120 45 7.0 5.7 1000 140/50 140 50 7.0 5.7 1000 Size (mm) Notes: 1. * See Part Number Guide for standard packaging codes. 2. Special sizes, packaging, colors and cut pieces are available upon request. ISO-9001 Company www.qualtekusa.com QDWT-200C