DATA SHEET SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS General Purpose & High Capacitance Class 2, X7R 6.3 V TO 50 V 100 pF to 22 µF Product Specification – May 31, 2016 V.14 RoHS compliant & Halogen Free Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V SCOPE ORDERING INFORMATION - GLOBAL PART NUMBER, PHYCOMP This specification describes X7R series chip capacitors with leadfree terminations. CTC & 12NC APPLICATIONS PCs, Hard disk, Game PCs DVDs, Video cameras Mobile phones Data processing FEATURES Supplied in tape on reel Nickel-barrier end termination RoHS compliant Halogen Free compliant 2 2 All part numbers are identified by the series, size, tolerance, TC material, packing style, voltage, process code, termination and capacitance value. YAGEO BRAND ordering code GLOBAL PART NUMBER (PREFERRED ) CC XXXX X X (1) X7R (2) (3) X BB XXX (4) (5) (1) SIZE – INCH BASED (METRIC) 0201 (0603) 0402 (1005) 0603 (1608) 0805 (2012) 1206 (3216) 1210 (3225) 1812 (4532) (2) TOLERANCE J = ± 5% (1) K = ± 10% M = ± 20% (3) PACKING STYLE R = Paper/PE taping reel; Reel 7 inch K = Blister taping reel; Reel 7 inch P = Paper/PE taping reel; Reel 13 inch F = Blister taping reel; Reel 13 inch (4) RATED VOLTAGE 5 = 6.3 V 6 = 10 V 7 = 16 V 8 = 25 V 9 = 50 V (5) CAPACITANCE VALUE 2 significant digits+number of zeros The 3rd digit signifies the multiplying factor, and letter R is decimal point Example: 103 = 10 x 103 = 10,000 pF = 10 nF NOTE 1. Tolerance ±5% is not available for full product range, please contact local sales force before ordering www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V 3 3 CONSTRUCTION The capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. This structure gives rise to a high capacitance per unit volume. The inner electrodes are connected to the two end terminations and finally covered with a layer of plated tin (NiSn). The terminations are lead-free. A cross section of the structure is shown in Fig.1. Fig. 1 Surface mounted multilayer ceramic capacitor construction DIMENSION Table 1 For outlines see fig. 2 TYPE 0201 0402 W (mm) 0.6 ± 0.03 0.3 ± 0.03 0.10 0.20 0.20 1.0 ± 0.05 0.5 ± 0.05 0.15 0.30 0.40 0.20 0.60 0.40 0.25 0.75 0.55 0.25 0.75 1.40 0.25 0.75 1.40 0.25 0.75 2.20 1.6 ± 0.10 0603 1206 1210 1812 0.8 ± 0.10 0.8 ± 0.15 (2) (3) (3) 0.8 ± 0.20 2.0 ± 0.10 (1) 1.25 ± 0.10 (1) (2) 1.25 ± 0.20 (2) 2.0 ± 0.20 3.2 ± 0.15 (1) 1.6 ± 0.15 (1) (2) 1.6 ± 0.20 (2) 3.2 ± 0.30 (3) 1.6 ± 0.30 (3) (1) 2.5 ± 0.20 (1) 3.2 ± 0.40 (2) 2.5 ± 0.30 (2) 4.5 ± 0.20 (1) 3.2 ± 0.20 (1) 4.5 ± 0.40 (2) 3.2 ± 0.40 (2) 3.2 ± 0.20 3.2 ± 0.20 OUTLINES For dimension see Table 1 (1) 1.6 ± 0.15 (2) 1.6 ± 0.20 0805 L4 (mm) min. L1 (mm) (1) T (MM) L2 / L3 (mm) min. max. Refer to table 2 to 4 Fig. 2 Surface mounted multilayer ceramic capacitor dimension NOTE 1. Dimension for size 0603, C < 2.2 µF; 0805 to 1812, C ≤ 100nF 2. Dimension for size 0603, C = 1µF; 50V; 0805 to 1812, C > 100 nF 3. Dimension for size 0603, C = 4.7µF, 6.3V; 0603, C = 2.2 µF, 16V; 1206, C = 22 µF, 16V www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors CAPACITANCE RANGE & THICKNESS FOR X7R Table 2 Sizes from 0201 to 0402 0201 CAP. General Purpose & High Cap. X7R 6.3 V to 50 V 4 4 0402 6.3 V 10 V 16 V 25 V 50 V 6.3 V 10 V 16 V 25 V 50 V 100 pF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 150 pF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 220 pF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 330 pF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 470 pF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 680 pF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 1.0 nF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 1.5 nF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 2.2 nF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 3.3 nF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 4.7 nF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 6.8 nF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 10 nF 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.3± 0.03 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 15 nF 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 22 nF 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 33 nF 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 47 nF 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 68 nF 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 100 nF 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 0.5± 0.05 150 nF 220 nF 330 nF 470 nF 680 nF 1.0 µF 0.5± 0.05 2.2 µF 4.7 µF 10 µF 22 µF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-6 series is on request 3. For product with 5% tolerance, please contact local sales force before ordering www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors CAPACITANCE RANGE & THICKNESS FOR X7R Table 3 Sizes from 0603 to 0805 0603 CAP. General Purpose & High Cap. X7R 6.3 V to 50 V 5 5 0805 6.3 V 10 V 16 V 25 V 50 V 6.3 V 10 V 16 V 25 V 50 V 100 pF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 150 pF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 220 pF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 330 pF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 470 pF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 680 pF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 1.0 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 1.5 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 2.2 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 3.3 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 4.7 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 6.8 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 10 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 15 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 22 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 0.6± 0.1 33 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 47 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 68 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 100 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 150 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 220 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.25± 0.2 330 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 470 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 680 nF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.0 µF 0.8± 0.1 0.8± 0.1 0.8± 0.1 0.8± 0.1 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 2.2 µF 0.8± 0.1 0.8± 0.1 0.8± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 4.7 µF 0.8± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 0.8± 0.1 0.8± 0.15 10 µF 22 µF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-6 series is on request 3. For product with 5% tolerance, please contact local sales force before ordering www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V 6 6 CAPACITANCE RANGE & THICKNESS FOR X7R Table 4 Size 1206 1206 CAP. 6.3 V 10 V 16 V 25 V 50 V 220 pF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 330 pF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 470 pF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 680 pF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.0 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.5 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 2.2 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 3.3 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 4.7 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 6.8 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 10 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 15 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 22 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 33 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 47 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 68 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 100 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 150 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.15± 0.1 220 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.15± 0.1 330 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 470 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.0± 0.1 680 nF 1.15± 0.1 1.15± 0.1 1.15± 0.1 1.15± 0.1 1.6± 0.2 1.0 µF 1.15± 0.1 1.15± 0.1 1.15± 0.1 1.15± 0.1 1.6± 0.2 2.2 µF 1.15± 0.1 1.15± 0.1 1.15± 0.1 1.15± 0.1 1.6± 0.2 4.7 µF 1.6± 0.2 1.6± 0.2 1.6± 0.2 1.6± 0.2 1.6± 0.2 10 µF 1.6± 0.2 1.6± 0.2 1.6± 0.2 1.6± 0.2 22 µF 1.6± 0.2 1.6± 0.2 1.6± 0.3 100 pF 150 pF 47 µF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-6 series is on request 3. For product with 5% tolerance, please contact local sales force before ordering 4. Please contact local sales force for special ordering code before ordering www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V 7 7 CAPACITANCE RANGE & THICKNESS FOR X7R Table 5 Sizes from 1210 to 1812 1210 CAP. 1812 6.3 V 10 V 16 V 25 V 50 V 50 V 2.2 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 3.3 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 4.7 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 6.8 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 10 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 15 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 22 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 33 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 47 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 68 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 100 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.15± 0.1 150 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.15± 0.1 1.15± 0.1 220 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.15± 0.1 1.15± 0.1 330 nF 0.85± 0.1 0.85± 0.1 0.85± 0.1 0.85± 0.1 1.15± 0.1 1.15± 0.1 470 nF 1.15± 0.1 1.15± 0.1 1.15± 0.1 1.15± 0.1 1.25± 0.2 1.15± 0.1 680 nF 1.15± 0.1 1.15± 0.1 1.15± 0.1 1.15± 0.1 1.25± 0.2 1.6± 0.2 1.0 µF 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.25± 0.2 1.6± 0.2 100 pF 150 pF 220 pF 330 pF 470 pF 680 pF 1.0 nF 1.5 nF 2.2 µF 1.9± 0.2 4.7 µF 1.9± 0.2 1.9± 0.2 1.9± 0.2 1.9± 0.2 10 µF 1.9± 0.2 1.9± 0.2 1.9± 0.2 1.9± 0.2 22 µF 2.5± 0.2 2.5± 0.2 2.5± 0.2 2.5± 0.2 47 µF 2.5± 0.2 2.5± 0.2 2.5± 0.3 NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-6 series is on request 3. For product with 5% tolerance, please contact local sales force before ordering 4. Please contact local sales force for special ordering code before ordering www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V 8 8 THICKNESS CLASSES AND PACKING QUANTITY Table 6 SIZE CODE Ø 180 MM / 7 INCH Paper Blister Ø 330 MM / 13 INCH Paper Blister THICKNESS CLASSIFICATION TAPE WIDTH QUANTITY PER REEL 0201 0.3 ± 0.03 mm 8 mm 15,000 --- 50,000 --- --- 0402 0.5 ± 0.05 mm 8 mm 10,000 --- 50,000 --- 50,000 0603 0.8 ± 0.1 mm 8 mm 4,000 --- 15,000 --- 15,000 0.6 ± 0.1 mm 8 mm 4,000 --- 20,000 --- 10,000 0.85 ± 0.1 mm 8 mm 4,000 --- 15,000 --- 8,000 1.25 ± 0.2 mm 8 mm --- 3,000 --- 10,000 5,000 0.6 ± 0.1 mm 8 mm 4,000 --- 20,000 --- --- 0.85 ± 0.1 mm 8 mm 4,000 --- 15,000 --- --- 1.00 / 1.15 ± 0.1 mm 8 mm --- 3,000 --- 10,000 --- 1.25 ± 0.2 mm 8 mm --- 3,000 --- 10,000 --- 1.6 ± 0.15 mm 8 mm --- 2,500 --- 10,000 --- 1.6 ± 0.2 mm 8 mm --- 2,000 --- 8,000 --- 0.6 / 0.7 ± 0.1 mm 8 mm --- 4,000 --- 15,000 --- 0.85 ± 0.1 mm 8 mm --- 4,000 --- 10,000 --- 1.15 ± 0.1 mm 8 mm --- 3,000 --- 10,000 --- 1.15 ± 0.15 mm 8 mm --- 3,000 --- 10,000 --- 1.25 ± 0.2 mm 8 mm --- 3,000 --- --- --- 1.5 ± 0.1 mm 8 mm --- 2,000 --- --- --- 1.6 / 1.9 ± 0.2 mm 8 mm --- 2,000 --- --- --- --- --- --- 0805 1206 1210 QUANTITY PER BULK CASE 2.0 ± 0.2 mm 8 mm --- 2,000 1,000 2.5 ± 0.2 mm 8 mm --- 1,000 500 --- --- --- 1.15 ± 0.15 mm 12 mm --- 3,000 --- --- --- 1.25 ± 0.2 mm 12 mm --- 3,000 --- --- --- 1.35 ± 0.15 mm 12 mm --- 2,000 --- --- --- 1.5 ± 0.1 mm 12 mm --- 2,000 --- --- --- 1.6 ± 0.2 mm 12 mm --- 2,000 --- 8,000 --- 2.0 ± 0.2 mm 12 mm --- 2,000 --- --- --- 0.6 / 0.85 ± 0.1 mm 12 mm --- 2,000 --- --- --- 1.15 ± 0.1 mm 12 mm --- 1,000 --- --- --- 1.25 ± 0.2 mm 12 mm --- 1,000 --- --- --- 1.5 ± 0.1 mm 12 mm --- 1,000 --- --- --- 1.6 ± 0.2 mm 12 mm --- 1,000 --- --- --- 2.0 ± 0.2 mm 12 mm --- 1,000 --- --- --- 2.5 ± 0.2 mm 12 mm --- 500 --- --- --- 1808 1812 www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. 9 6.3 V to 50 V X7R 9 ELECTRICAL CHARACTERISTICS X7R DIELECTRIC CAPACITORS; NISN TERMINATIONS Unless otherwise specified, all test and measurements shall be made under standard atmospheric conditions for testing as given in 5.3 of IEC 60068-1: - Temperature: 15 °C to 35 °C Relative humidity: 25% to 75% Air pressure: 86 kPa to 106 kPa Before the measurements are made, the capacitor shall be stored at the measuring temperature for a time sufficient to allow the entire capacitor to reach this temperature. The period as prescribed for recovery at the end of a test is normally sufficient for this purpose. Table 7 VALUE DESCRIPTION Capacitance range 100 pF to 47 µF Capacitance tolerance ± 5%, ± 10%, ± 20% Dissipation factor (D.F.) X7R 0201 ≤10V 0402 100pF to 10nF 100pF to 100nF 220nF to 470nF 0603 1206 1210 100pF to 1uF 150pF to 2.2uF 220pF to 2.2uF 2.2nF to 2.2uF ≤5% 4.7uF to 47uF ≤10% 2.2uF to 4.7uF 0805 4.7uF to 10uF 4.7uF to 22uF 1uF 16V ≤12.5% 100pF to 1.2nF 100pF to 22nF 100pF to 220nF 150pF to 470nF 220pF to 1μF 2.2nF to 1μF ≤ 3.5% 1.5nF to 10nF 27nF to 100nF 470nF to 2.2uF 680 nF to 2.2μF 2.2uF 2.2uF to 10uF ≤ 5% 220nF 25V 4.7uF to 22uF 22uF ≤10% 100pF to 470pF 100pF to 10nF 100pF to 39nF 150pF to 180nF 220pF to 680nF 4.7uF to 10uF 2.2nF to 1μF ≤ 2.5% 12 nF to 47nF 47nF to 220nF 220nF to 470nF 1uF 560pF to 10nF 56nF to 100nF 680nF to 1μF 2.2uF 2.2uF ≤ 5% 2.2uF to 4.7uF 4.7uF to 22uF 4.7uF to 22uF ≤10% 100pF to 10nF 100pF to 39nF 150pF to 180nF 220pF to 470nF 2.2nF to 1μF 12 nF to 47nF 47nF to 220nF 220nF to 470nF 270nF to 1uF 50V 100pF to 1nF ≤ 3.5% 680nF to 1μF 680nF 100nF 470nF to 1uF Insulation resistance after 1 minute at Ur (DC) 1uF to 2.2uF ≤2.5% ≤ 3.5% ≤ 5% 2.2uF to 4.7uF 2.2uF to 10uF ≤10% Rins ≥ 10 GΩ or Rins × Cr ≥ 500(100) seconds whichever is less Maximum capacitance change as a function of temperature (temperature characteristic/coefficient): Operating temperature range: ± 15% –55 °C to +125 °C NOTE Capacitance tolerance ±5% is not available for full product range, please contact local sales force before ordering www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V 10 10 Fig. 3 Typical capacitance change as a function of temperature www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V 11 11 Size 0201 10 nF / 16 V Solid lines: Impedance / Dotted lines: ESR Fig. 4 Impedance ESR vs. frequency characteristics for multilayer chip capacitors Size 0402 100 nF / 16 V Solid lines: Impedance / Dotted lines: ESR Fig. 5 Impedance ESR vs. frequency characteristics for multilayer chip capacitors www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V 12 12 Size 0603 1 µF / 16 V Solid lines: Impedance / Dotted lines: ESR Fig. 6 Impedance ESR vs. frequency characteristics for multilayer chip capacitors Size 0805 1 µF / 16 V Solid lines: Impedance / Dotted lines: ESR Fig. 7 Impedance ESR vs. frequency characteristics for multilayer chip capacitors www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V 13 13 Size 1206 1 µF / 25 V Solid lines: Impedance / Dotted lines: ESR Fig. 8 Impedance ESR vs. frequency characteristics for multilayer chip capacitors Size 1206 10 µF / 10 V Solid lines: Impedance / Dotted lines: ESR Fig. 9 Impedance ESR vs. frequency characteristics for multilayer chip capacitors www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V 14 14 SOLDERING RECOMMENDATION Table 8 SOLDERING METHOD SIZE 0402 0603 0805 1206 ≥ 1210 Reflow ≥ 0.1 µF ≥ 1.0 µF ≥ 2.2 µF ≥ 4.7 µF Reflow only Reflow/Wave < 0.1 µF < 1.0 µF < 2.2 µF < 4.7 µF --- TESTS AND REQUIREMENTS Table 9 Test procedures and requirements TEST TEST METHOD PROCEDURE REQUIREMENTS Mounting IEC 6038421/22 4.3 The capacitors may be mounted on printed-circuit boards or ceramic substrates No visible damage Visual Inspection and Dimension Check 4.4 Any applicable method using × 10 magnification In accordance with specification Capacitance (1) 4.5.1 Class 2: At 20 °C, 24 hrs after annealing Within specified tolerance f = 1 KHz for C ≤ 10 µF, rated voltage > 6.3 V, measuring at voltage 1 Vrms at 20 °C f = 1 KHz, for C ≤ 10 µF, rated voltage ≤ 6.3 V, measuring at voltage 0.5 Vrms at 20 °C f = 120 Hz for C > 10 µF, measuring at voltage 0.5 Vrms at 20 °C Dissipation Factor (D.F.) (1) 4.5.2 Class 2: At 20 °C, 24 hrs after annealing In accordance with specification f = 1 KHz for C ≤ 10 µF, rated voltage > 6.3 V, measuring at voltage 1 Vrms at 20 °C f = 1 KHz, for C ≤ 10 µF, rated voltage ≤ 6.3 V, measuring at voltage 0.5 Vrms at 20 °C f = 120 Hz for C > 10 µF, measuring at voltage 0.5 Vrms at 20 °C Insulation Resistance 4.5.3 At Ur (DC) for 1 minute In accordance with specification NOTE: 1. For individual product specification, please contact local sales. www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V TEST TEST METHOD PROCEDURE REQUIREMENTS Temperature Characteristic IEC 6038421/22 Capacitance shall be measured by the steps shown in the following table. <General purpose series> Class1: ∆ C/C: ± 30ppm 4.6 The capacitance change should be measured after 5 min at each specified temperature stage. Step Temperature(℃) a 25± 2 b Lower temperature± 3℃ c 25± 2 d Upper Temperature± 2℃ e 25± 2 15 15 Class2: X7R: ∆ C/C: ±15% Y5V: ∆ C/C: 22~-82% <High Capacitance series> Class2: X7R/X5R: ∆ C/C: ±15% Y5V: ∆ C/C: 22~-82% (1) Class I Temperature Coefficient shall be calculated from the formula as below C2 - C1 106 [ppm/℃] Temp, Coefficient = C1 xΔT C1: Capacitance at step c C2: Capacitance at 125℃ ∆T: 100℃(=125℃-25℃) (2) Class II Capacitance Change shall be calculated from the formula as below C2 - C1 ∆C = x 100% C1 C1: Capacitance at step c C2: Capacitance at step b or d Adhesion 4.7 A force applied for 10 seconds to the line joining the terminations and in a plane parallel to the substrate Force size ≥ 0603: 5N size = 0402: 2.5N size = 0201: 1N www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors TEST Bond Strength General Purpose & High Cap. TEST METHOD PROCEDURE 4.8 6.3 V to 50 V X7R 16 16 REQUIREMENTS Mounting in accordance with IEC 60384-22 paragraph 4.3 No visible damage Conditions: bending 1 mm at a rate of 1 mm/s, radius jig 5 mm <General Purpose series> ∆C/C Class2: X7R: ± 10% <High Capacitance series> ∆C/C Class2: X7R: ± 10% Test Substrate: b 4.5 C 40 4.9 Type a b c 0201 0.3 0.9 0.3 0402 0.4 1.5 0.5 a 0603 1.0 3.0 1.2 100 0805 1.2 4.0 1.65 1206 2.2 5.0 1.65 1210 2.2 5.0 2.0 1808 3.5 7.0 3.7 unit:mm Resistance to Soldering Heat Dimension(mm) YNSC147 Precondition: 150 +0/–10 °C for 1 hour, then keep for 24 ± 1 hours at room temperature Preheating: for size ≤ 1206: 120 °C to 150 °C for 1 minute Preheating: for size >1206: 100 °C to 120 °C for 1 minute and 170 °C to 200 °C for 1 minute Dissolution of the end face plating shall not exceed 25% of the length of the edge concerned <General Purpose series> Dipping time: 10 ± 0.5 seconds ∆C/C Class2: X7R: ± 10% Recovery time: 24 ± 2 hours <High Capacitance series> Solder bath temperature: 260 ± 5 °C ∆C/C Class2: X7R: ± 10% D.F. within initial specified value Rins within initial specified value www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors TEST Solderability General Purpose & High Cap. TEST METHOD PROCEDURE IEC 60384- 4.10 21/22 X7R 6.3 V to 50 V 17 17 REQUIREMENTS Preheated to a temperature of 80 °C to 140 °C and The solder should cover over 95% of the critical area of each termination maintained for 30 seconds to 60 seconds. Test conditions for lead containing solder alloy Temperature: 235 ± 5 °C Dipping time: 2 ± 0.2 seconds Depth of immersion: 10 mm Alloy Composition: 60/40 Sn/Pb Number of immersions: 1 Test conditions for lead-free containing solder alloy Temperature: 245 ± 5 °C Dipping time: 3 ± 0.3 seconds Depth of immersion: 10 mm Alloy Composition: SAC305 Number of immersions: 1 Rapid Change of Temperature 4.11 Preconditioning; 150 +0/–10 °C for 1 hour, then keep for 24 ± 1 hours at room temperature No visual damage <General Purpose series> ∆C/C 5 cycles with following detail: 30 minutes at lower category temperature 30 minutes at upper category temperature Class2: X7R: ± 15% <High Capacitance series> Recovery time 24 ± 2 hours ∆C/C Class2: X7R: ± 15% D.F. meet initial specified value Rins meet initial specified value www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors TEST Damp Heat with Ur Load General Purpose & High Cap. X7R 6.3 V to 50 V TEST METHOD PROCEDURE REQUIREMENTS IEC 6038421/22 1. Preconditioning, class 2 only: 150 +0/-10 °C /1 hour, then keep for 24 ± 1 hour at room temp No visual damage after recovery 2. Initial measure: Spec: refer to initial spec C, D, IR ∆C/C 4.13 3. Damp heat test: 500 ± 12 hours at 40 ± 2 °C; 90 to 95% R.H. 1.0 Ur applied 18 <General Purpose series> Class2: X7R: ± 15% D.F. 4. Recovery: Class 2: 24 ± 2 hours Class2: X7R: ≤ 16V: ≤ 7% ≥ 25V: ≤ 5% 5. Final measure: C, D, IR Rins P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be preconditioned according to “IEC 60384 4.1” and then the requirement shall be met. 18 Class2: X7R: ≥ 500 MΩ or Rins x Cr ≥ 25s whichever is less <High Capacitance series(≥ 1uF) and CC0402xRX7R9BB104> ∆C/C Class2: X7R: ± 20% D.F. Class2: X7R: 2 x initial value max Rins Class2: X7R: 500 MΩ or Rins x Cr ≥ 25(5)s whichever is less www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors TEST Endurance General Purpose & High Cap. X7R TEST METHOD PROCEDURE REQUIREMENTS IEC 6038421/22 1. Preconditioning, class 2 only: 150 +0/-10 °C /1 hour, then keep for 24 ± 1 hour at room temp No visual damage 2. Initial measure: Spec: refer to initial spec C, D, IR ∆C/C 4.14 3. Endurance test: Temperature: X7R: 125 °C Specified stress voltage applied for 1,000 hours: Applied 2.0 x Ur for general products Applied 1.5(1.0) x Ur for high cap. products 4. Recovery time: 24 ± 2 hours 5. Final measure: C, D, IR P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be preconditioned according to “IEC 60384 4.1” and then the requirement shall be met. 6.3 V to 50 V 19 19 <General Purpose series> Class2: X7R: ± 15% D.F. Class2: X7R: ≤ 16V: ≤ 7% ≥ 25V: ≤ 5% Rins Class2: X7R: ≥ 1,000 MΩ or Rins x Cr ≥ 50s whichever is less <High Capacitance series(≥ 1uF) and CC0402xRX7R9BB104> ∆C/C Class 2: X7R: ± 20% D.F. Class 2: X7R: 2 x initial value max Rins Class 2: X7R: 1,000 MΩ or Rins x Cr ≥ 50(10)s whichever is less Voltage Proof IEC 603841 4.6 Specified stress voltage applied for 1~5 seconds No breakdown or flashover Ur ≦ 100 V: series applied 2.5 Ur Charge/Discharge current is less than 50 mA www.yageo.com May. 31, 2016 V.14 Product specification Surface-Mount Ceramic Multilayer Capacitors General Purpose & High Cap. X7R 6.3 V to 50 V 20 20 REVISION HISTORY REVISION DATE CHANGE NOTIFICATION DESCRIPTION Version 13 Dec. 30, 2015 - - Dimension on 0603 and 1206 case size updated Version 12 May 26, 2015 - - 1210, 25V dissipation factor updated Version 11 Jan. 06, 2015 - - 0402, 100nF, 50V Dissipation factor (D.F.) updated. Version 10 Jul. 08, 2014 - - Dimension updated Version 9 Aug. 19, 2013 - - Dimension updated Version 8 Oct 13, 2011 - - Dimension updated - 50V Dissipation factor(D.F) updated Version 7 Jan 13, 2011 - - Dimension updated Version 6 Oct 13, 2010 - - Rated voltage of 0201 extend to 50 V - Capacitance range of 0201 X7R 6.3V to 16V extend to 100 pF - Capacitance range of 0805 X7R 10V extend to 10 µF - Capacitance range of 0805 X7R 50V extend to 1 µF - Capacitance range of 1210 X7R 10V extend to 22 µF - Figures of impedance ESR updated Version 5 Jul 27, 2010 - Version 4 Apr 21, 2010 - Version 3 Oct 26, 2009 - - Dimension on 0603 and 1206 case size updated - 16V to 25V Dissipation factor(D.F) updated - The statement of "Halogen Free" on the cover added - Dimension updated - Capacitance range of 0402 X7R 25 V extend to 100 nF - 16V Dissipation factor updated Version 2 May 11, 2009 - - Product range updated Version 1 Apr 24, 2009 - - Ordering code updated Version 0 Apr 15, 2009 - - New datasheet for general purpose and high capacitance X7R series with RoHS compliant - Replace the "6.3V to 50V" part of pdf files: X7R_10V_9, X7R_16V-to100V_9, X7R_16-to-500V_9, UP-X5R_X7R_HighCaps_6.3-to-25V_11, UY-X5R_X7R_HighCaps_6.3-to-25V_11 - Combine 0201 from pdf files: UP-NP0X5RX7RY5V_0201_6.3-to-50V_2 and UY-NPOX5RX7RY5V_0201_6.3-to-50V_2 - Define global part number - Description of "Halogen Free compliant" added - Test method and procedure updated www.yageo.com May. 31, 2016 V.14