EPCOS B65517D0000R048

PM/P/P Cores Halves/EP/TT/PR Cores
Series/Type: B65522
The following products presented in this data sheet are being withdrawn.
Ordering Code
B65522A5000X000
Substitute Product
Date of Withdrawal
18.10.2004
Deadline Last
Orders
31.03.2005
Last Shipments
30.09.2005
For further information please contact your nearest EPCOS sales office, which will also support you in selecting a
suitable substitute. The addresses of our worldwide sales network are presented at www.epcos.com/sales.
P9×5
Core
B65517
mm–1
mm
mm2
mm2
mm3
1.13
13.4
11.9
9.3
159
M1.4
ø2+0.1
Approx. weight (per set)
m
2.1+0.3
1.25
12.5
10
—
125
3.6+0.3
Σl/A
le
Ae
Amin
Ve
9.3 _ 0.3
7.5+0.25
with center without
hole
center hole
5.4 _ 0.2
Magnetic characteristics (per set)
s
5.8 _ 0.3
■ To IEC 60133
■ Delivery mode: sets
0.8
ø3.9 _ 0.2
1.0
g
FPK0356-F
Gapped
Material
AL value
nH
µe
s
approx.
mm
Ordering code 1)
-D with center hole
-T with threaded sleeve
K1
25 ±3%
40 ±3%
0.45
0.26
25
40
B65517+0025A001
B65517+0040A001
M33
63 ±3%
0.20
63
B65517D0063A033
N48
100 ±3%
160 ±3%
200 ±3%
250 ±5%
0.10
0.06
0.04
0.03
100
159
200
249
B65517+0100A048
B65517+0160A048
B65517D0200A048
B65517D0250J048
µe
Ordering code
-D with center hole
-W without center hole
Ungapped
Material
AL value
nH
N48
1300 +30/–20%
1290
B65517D0000R048
N30
2500 +30/–20%
2490
B65517D0000R030
T38
5500 +40/–30%
4930
B65517W0000Y038
1) Replace the + by the code letter ”D“ or ”T“ for the required version.
Please read Cautions and warnings and
Important notes at the end of this document.
2
09/06
P9×5
Accessories
B65522
Coil former
Standard:
Material:
to IEC 60133
GFR polyterephthalate (UL 94 V-0, insulation class to IEC 60085:
F max. operating temperature 155 °C), color code black
Valox 420-SE0 ® [E45329 (M)], GE PLASTICS B V
see Data Book 2007, chapter “Processing notes, 2.1”
Winding:
Insulating washer between core and coil former
■ For tolerance compensation and for insulation
■ Polycarbonate spring washer (UL 94 V-0, insulation class to IEC 60085: E
120 °C), 0.08 mm thick
Aryphan F685, [E167358 (M)], natural color, LOFO HIGH TECH FILM GMBH
Coil former
Ordering code
Sections
AN
mm2
lN
mm
AR value
µΩ
1
3.6
19.2
183
Insulating washer (reel packing, PU = 1 reel)
B65522A5000X000
Coil former
ø7.4 _ 0.15
ø4.8 _ 0.1
ø4+0.1
AN
1.5+0.3
0.35
3.5 _ 0.1
FPK0349-X
ø3,7±0,2
ø7,6±0,2
1,9
Insulating washer
(preliminary data)
0,8±0,15
FPK0054-F
Please read Cautions and warnings and
Important notes at the end of this document.
B65522B0000T001
3
09/06
P9×5
Accessories
B65524
SMD coil former with gullwing terminals
Material:
GFR liquid crystal polymer (UL 94 V-0, insulation class to IEC 60085:
F max. operating temperature 155 °C), color code black
Zenite 7130 ® [E41938 (M)], E I DUPONT DE NEMOURS & CO INC
Solderability: to IEC 60068-2-58, test Td, method 6 (Group 3): 245 °C, 3 s
Resistance to soldering heat: to IEC 60068-2-58, test Td, method 6 (Group 3): 255 °C, 10 s
permissible soldering temperature for wire-wrap connection on coil former: 400 °C, 1 s
Winding:
see Data Book 2007, chapter “Processing notes, 2.1”
lN
mm
AR value
µΩ
Terminals
Ordering code
1
3.4
3.4
19.2
19.2
194
194
4
8
B65524C1004T001
B65524C1008T001
ø4,8 _ 0,15
7
3
6
4
5
10,7 _ 0,2
_ 0,2
16,6 +0,1
10,16
2
2,54
8
6+0,2
1
Recommended
Empfehlung für das
Leiterplattenlayout
PCB
layout
0,65±0,05
2,54
1,6 _ 0,2
9,35+0,15
3,95+0,15
4 x 2,54 = 10,16
12,2 _ 0,3
0,3±0,2
ø10,35±0,15
0,75±0,1
4,7 _ 0,1
0,5±0,05
ø7,45 _ 0,2
1,2
0,35±0,05
AN
mm2
3,5 _ 0,15
Sections
2,5
17,8
FPK0234-D
In the 4-terminal version terminals 2, 3, 6 and 7 are omitted.
Please read Cautions and warnings and
Important notes at the end of this document.
4
09/06
P9×5
Accessories
B65518
Mounting assembly for printed circuit boards
■ The set comprises a terminal carrier and a yoke
■ For snap-in connection
Terminal carrier
■ With thread for the adjusting screw (to be combined with core version ”D“)
Material:
GFR polyterephthalate (UL 94 V-0, insulation class to IEC 60085:
F max. operating temperature 155 °C), color code black
Pocan B4235 ® [E245249 (M)], LANXESS AG
Solderability: to IEC 60068-2-20, test Ta, method 1 (aging 3): 235 °C, 2 s
Resistance to soldering heat: to IEC 60068-2-20, test Tb, method 1B: 350 °C, 3.5 s
Yoke
Spring yoke, made of tinned nickel silver (0.25 mm), with ground terminal
Complete mounting assembly
(4 solder terminals)
Ordering code: B65518D2001X000
Complete mounting assembly
(6 solder terminals)
Ordering code: B65518D2002X000
4 solder terminals
6 solder terminals
9,9 max.
3 4
1 2
9,9 max.
1
4
5
6
M1,4
M1,4
Thread for
Gewindeadjusting
führung
fürscrew
Abgleichschraube
Hole arrangement
View in mounting
direction
c
3,5 _ 0,4
2,54
2,54
1,25
ø0,5
1+0,1
3
1
1+0,1
4
6
1)
1)
ø0,5
Hole arrangement
View in mounting
direction
8,3 max.
a
3,5 _ 0,4
b
2
9,9 max.
8,3 max.
a
3
12,3 max.
M1,4
M1,4
Thread for
Gewindeadjusting
führung
fürscrew
Abgleichschraube
Erdungspunkt
Ground
FPK0057-S
1)
a)
b)
c)
Ground
Erdungspunkt
1.3 hole also permissible
Yoke
Terminal carrier with 4 solder terminals
Terminal carrier with 6 solder terminals
Please read Cautions and warnings and
Important notes at the end of this document.
FPK0056-W
5
09/06
Ferrites and accessories
Cautions and warnings
Mechanical stress and mounting
Ferrite cores have to meet mechanical requirements during assembling and for a growing number
of applications. Since ferrites are ceramic materials one has to be aware of the special behavior
under mechanical load.
As valid for any ceramic material, ferrite cores are brittle and sensitive to any shock, fast changing
or tensile load. Especially high cooling rates under ultrasonic cleaning and high static or cyclic loads
can cause cracks or failure of the ferrite cores.
For detailed information see Data Book 2007, chapter “General – Definitions, 8.1”.
Effects of core combination on AL value
Stresses in the core affect not only the mechanical but also the magnetic properties. It is apparent
that the initial permeability is dependent on the stress state of the core. The higher the stresses are
in the core, the lower is the value for the initial permeability. Thus the embedding medium should
have the greatest possible elasticity.
For detailed information see Data Book 2007, chapter “General – Definitions, 8.2”.
Heating up
Ferrites can run hot during operation at higher flux densities and higher frequencies.
NiZn-materials
The magnetic properties of NiZn-materials can change irreversible in high magnetic fields.
Processing notes
– The start of the winding process should be soft. Else the flanges may be destroid.
– To strong winding forces may blast the flanges or squeeze the tube that the cores can no more
be mount.
– To long soldering time at high temperature (>300 °C) may effect coplanarity or pin arrangement.
– Not following the processing notes for soldering of the J-leg terminals may cause solderability
problems at the transformer because of pollution with Sn oxyd of the tin bath or burned insulation
of the wire. For detailed information see Data Book 2007, chapter “Processing notes, 2.2”.
– The dimensions of the hole arrangement have fixed values and should be understood as a
recommendation for drilling the printed circuit board. For dimensioning the pins, the group of
holes can only be seen under certain conditions, as they fit into the given hole arrangement. To
avoid problems when mounting the transformer, the manufacturing tolerances for positioning the
customers’ drilling process must be considered by increasing the hole diameter.
6
09/06
Important notes
The following applies to all products named in this publication:
1. Some parts of this publication contain statements about the suitability of our products for
certain areas of application. These statements are based on our knowledge of typical
requirements that are often placed on our products in the areas of application concerned. We
nevertheless expressly point out that such statements cannot be regarded as binding
statements about the suitability of our products for a particular customer application. As
a rule, EPCOS is either unfamiliar with individual customer applications or less familiar with them
than the customers themselves. For these reasons, it is always ultimately incumbent on the
customer to check and decide whether an EPCOS product with the properties described in the
product specification is suitable for use in a particular customer application.
2. We also point out that in individual cases, a malfunction of passive electronic components
or failure before the end of their usual service life cannot be completely ruled out in the
current state of the art, even if they are operated as specified. In customer applications
requiring a very high level of operational safety and especially in customer applications in which
the malfunction or failure of a passive electronic component could endanger human life or health
(e.g. in accident prevention or life-saving systems), it must therefore be ensured by means of
suitable design of the customer application or other action taken by the customer (e.g.
installation of protective circuitry or redundancy) that no injury or damage is sustained by third
parties in the event of malfunction or failure of a passive electronic component.
3. The warnings, cautions and product-specific notes must be observed.
4. In order to satisfy certain technical requirements, some of the products described in this
publication may contain substances subject to restrictions in certain jurisdictions (e.g.
because they are classed as “hazardous”). Useful information on this will be found in our
Material Data Sheets on the Internet (www.epcos.com/material). Should you have any more
detailed questions, please contact our sales offices.
5. We constantly strive to improve our products. Consequently, the products described in this
publication may change from time to time. The same is true of the corresponding product
specifications. Please check therefore to what extent product descriptions and specifications
contained in this publication are still applicable before or when you place an order.
We also reserve the right to discontinue production and delivery of products.
Consequently, we cannot guarantee that all products named in this publication will always be
available.
6. Unless otherwise agreed in individual contracts, all orders are subject to the current version
of the “General Terms of Delivery for Products and Services in the Electrical Industry”
published by the German Electrical and Electronics Industry Association (ZVEI).
7. The trade names EPCOS, EPCOS-JONES, Baoke, Alu-X, CeraDiode, CSSP, MLSC,
PhaseCap, PhaseMod, SIFI, SIFERRIT, SIKOREL, SilverCap, SIMID, SIOV, SIP5D, SIP5K,
UltraCap, WindCap are trademarks registered or pending in Europe and in other countries.
Further information will be found on the Internet at www.epcos.com/trademarks.
7
09/06