RoHS ZTA16.0MX/ZTT16.0MX CERAMIC RESONATOR 1. SCOPE This specification is applied to the ceramics resonator used for the clock Oscillation of Microprocessor. 2. MODEL NAME Customer Part Name s Part number D T ,. L Drawing No. ZTA16.0MX ZTT16.0MX 3. DIMENSIONS R T J E E C E L MARK 1 ZTA16.0MX O IC C O N MARK 2 ZTT16.0MX W WEJ ELECTRONIC CO. Http:// www.wej.cn E-mail:[email protected] RoHS ZTA16.0MX/ZTT16.0MX CERAMIC RESONATOR 4. TEST CIRCUIT Parts shall be measured under a condition Temp.:3 35 .Hum.:45 85 unless any Necessity to measure under a standard condition Temp.:20±2 .Humi.: 65±5 is occurred. X1 ZTA16.0MX C1=C2=30PF IC: 1/674HCU04 VDD=+5V 5. ELECTRICAL CHARACTERISTICS R T Item 5-1 Frequency Accuracy C E L 5-2 5-3 5-4 5-5 J E 5-6 5-7 X2 ZTT16.0MX O IC N 16.0M±0.5% 30 Operating Temperature Range Storage Temperature Range E O Requirements Resonant Impedance Stability Temperature C D T ,. L max -20 to +80 -30 to +85 ±0.3% max. Withstanding Voltage DC 100V. Insulation Resistance 100 M Aging for 10 Years 20 +80 less than 5 sec min ±0.5± DC 10V max W WEJ ELECTRONIC CO. Http:// www.wej.cn E-mail:[email protected] RoHS ZTA16.0MX/ZTT16.0MX CERAMIC RESONATOR 6.PHYSICAL AND ENVIRONMENTAL CHARCTERISTICS Test Item 6-1 Condition of Test Lead strength Lead Bending Requirements D T ,. L Force of 1 Kg is applied for 10 second to each lead in No mechanical damage axial direction. and Firmed the terminal up to 2mm. Resonator lead values shall meet Item shall be subjected to withstand against 90º bending 5. the its stem. This operation shall be done toward both direction. The terminals of the Resonator shall be immersion 6-2 in a soldering bath 230±5 Solder ability for 3±0.5sec. refer to IC Resonator shall be measured after being Applied vibration as below. Vibration Freq: 10-55Hz Vibration Amplitude: 1.5 mm O Directions: 3 axial directions Time: 2 hour/each direction R T N Shall meet table l Random dropping from the height of 1m. Random Drop Concrete floor C E L Dipped in 6-5 Resistance to Soldering Heat J E C at least 95% of the The measured values Resonator shall be measured after 3 times 6-4 O The solder shall for coat terminal. Mil-STD-202E-208C 6-3 measured E 350±10 measured solder to a point 1.5mm from Resonator body for 3±0.5 sec or dipped in 260±5 melted solder for 10±1 sec. Resonator shall be measured after being placed in natural condition for 1 hour. W WEJ ELECTRONIC CO. Http:// www.wej.cn E-mail:[email protected] RoHS ZTA16.0MX/ZTT16.0MX CERAMIC RESONATOR 6. PHYSICAL AND ENVIRONMENTAL CHARACTERISTICS Test Item Condition of Test Humidity After being placed in a chamber 6-6 90-95 RH Temp:40±2 D T ,. L Requirements Humi: for 96 hours Resonator shall be measured after placed in natural condition for 1 hour. Life Test 6-7 After being placed in a chamber 85±2 (High 96 hours, Resonator shall be measured after temperature) being placed in natural condition for 1 hour. Life Test Low Stored in a chamber 6-8 for IC Temp:-20±2 for 1000 hours, Resonator shall be measured temperature N C O The measured values Shall meet table l after being placed in natural condition for 1 hour. O Thermal shock After temperature cycling of -20 6-9 to +80 R T 30min 30min was performed 5 times the Resonator shall be measured after being placed in natural condition for 1 hour. C E L Table 1 Item Frequency shift E Resonant Impedance Limit Value F/FO ±0.3% Zr 5 Note: The limits in the above table are referenced to the initial Measurements. J E W WEJ ELECTRONIC CO. Http:// www.wej.cn E-mail:[email protected] RoHS ZTA16.0MX/ZTT16.0MX CERAMIC RESONATOR 7. 7.1 7.2 7.3 NOTICE Ceramic Resonator should be stored in storeroom. And the surrounding atmosphere is acid less, alkali-free and no other harmful impurity. The package for ceramic damage. This specification limits the quality of the component as a single unit. Please make sure that the component is evaluated and confirmed the drawing When it is mounted to your product. R T J E O IC C D T ,. L O N C E L E W WEJ ELECTRONIC CO. Http:// www.wej.cn E-mail:[email protected]