SAMSUNG CL10A105KA8NNNC

SPECIFICATION
 Supplier : Samsung electro-mechanics
 Samsung P/N : CL10A105KA8NNNC
 Product : Multi-layer Ceramic Capacitor
 Descriptiont :
CAP, 1㎌, 25V, ±10%, X5R, 0603
A. Samsung Part Number
① Series
CL
10
A
105
K
A
8
N
N
N
C
①
②
③
④
⑤
⑥
⑦
⑧
⑨
⑩
⑪
Samsung Multi-layer Ceramic Capacitor
② Size
0603 (inch code)
③ Dielectric
X5R
④ Capacitance
⑤ Capacitance
L: 1.6 ± 0.1
⑥ Rated Voltage
25 V
⑦ Thickness
0.8 ± 0.1
mm
0.8 ± 0.1
W:
⑧ Inner electrode
Ni
Termination
Cu
Plating
Sn 100%
1㎌
±10 %
tolerance
mm
mm
(Pb Free)
⑨ Product
Normal
⑩ Special
Reserved for future use
⑪ Packaging
Cardboard Type, 7" reel
B. Samsung Reliability Test and Judgement condition
Performance
1.0±0.2Vrms
Rated Voltage
60~120 sec.
Resistance
10,000Mohm or 500Mohm㎌
Whichever is Smaller
Appearance
No abnormal exterior appearance
Withstanding
No dielectric breakdown or
Microscope (10)
250% of the rated voltage
Voltage
mechanical breakdown
Temperature
X5R
Characteristics
Adhesive Strength
(From -55℃ to 85℃, Capacitance change should be within ±15%)
No peeling shall be occur on the
500gF, for 10±1 sec.
of Termination
terminal electrode
Bending Strength
Capacitance change :
Tan δ (DF)
Insulation
Within specified tolerance
Test condition
1㎑±10%
Capacitance
0.1 max.
within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability
More than 75% of terminal surface
SnAg3.0Cu0.5 solder
is to be soldered newly
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to
Capacitance change :
Soldering heat
Tan δ, IR : initial spec.
within ±7.5%
Solder pot : 270±5℃, 10±1sec.
Performance
Vibration Test
Capacitance change :
within ±5%
Tan δ, IR : initial spec.
Moisture
Capacitance change :
Resistance
Tan δ :
IR :
Amplitude : 1.5mm
From 10㎐ to 55㎐ (return : 1min.)
2hours  3 direction (x, y, z)
within ±12.5% With rated voltage
0.125 max
40±2℃, 90~95%RH, 500+12/-0hrs
12.5㏁·㎌ or Over
High Temperature
Capacitance change :
Resistance
Tan δ :
IR :
Test condition
within ±12.5% With 150%
0.125 max
of the rated voltage
Max. operating temperature
25㏁·㎌ or Over
1000+48/-0hrs
Temperature
Capacitance change :
Cycling
Tan δ, IR : initial spec.
within ±7.5%
1 cycle condition
Min. operating temperature
25℃
→
25℃
→
Max. operating temperature →
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.