SAMSUNG CL31B104KCFNNNE

SPECIFICATION
• Supplier : Samsung electro-mechanics
• Samsung P/N : CL31B104KCFNNNE
• Product : Multi-layer Ceramic Capacitor
• Description :
CAP, 100㎋, 100V, ±10%, X7R, 1206
A. Samsung Part Number
① Series
CL
31
B
104
K
C
F
N
N
N
E
①
②
③
④
⑤
⑥
⑦
⑧
⑨
⑩
⑪
Samsung Multi-layer Ceramic Capacitor
② Size
1206 (inch code)
③ Dielectric
X7R
④ Capacitance
⑤ Capacitance
L: 3.2 ± 0.15
mm
1.6
± 0.15 mm
⑧ Inner electrode
Ni
Termination
Cu
Plating
Sn 100%
100 ㎋
±10 %
(Pb Free)
Normal
⑥ Rated Voltage
100 V
⑨ Product
⑩ Special
⑦ Thickness
1.25 ± 0.15 mm
⑪ Packaging
tolerance
W:
Reserved for future use
Embossed Type, 7" reel
B. Samsung Reliablility Test and Judgement condition
Performance
1.0±0.2Vrms
Rated Voltage
60~120 sec.
Resistance
10,000Mohm or 500Mohm⋅㎌
Whichever is Smaller
Appearance
No abnormal exterior appearance
Withstanding
No dielectric breakdown or
Microscope (×10)
200% of the rated voltage
Voltage
mechanical breakdown
Temperature
X7R
Characterisitcs
Adhesive Strength
(From -55℃ to 125℃, Capacitance change shoud be within ±15%)
No peeling shall be occur on the
500g⋅F, for 10±1 sec.
of Termination
terminal electrode
Bending Strength
Capacitance change :
Tan δ (DF)
Insulation
Within specified tolerance
Test condition
1㎑±10%
Capacitance
0.025 max.
within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability
More than 75% of terminal surface
1) Sn63Pb37 solder
is to be soldered newly
235±5℃, 5±0.5sec.
2) SnAg3.0Cu0.5 solder
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to
Capacitance change :
Soldering heat
Tan δ, IR : initial spec.
within ±7.5%
Solder pot : 270±5℃, 10±1sec.
Performance
Vibration Test
Capacitance change :
within ±5%
Tan δ, IR : initial spec.
Moisture
Capacitance change :
Resistance
Tan δ :
IR :
Amplitude : 1.5mm
From 10㎐ to 55㎐ (return : 1min.)
2hours × 3 direction (x, y, z)
within ±12.5% With rated voltage
0.05 max
40±2℃, 90~95%RH, 500+12/-0hrs
500Mohm or 25Mohm ⋅ ㎌
Whichever is Smaller
High Temperature
Capacitance change :
Resistance
Tan δ :
IR :
Test condition
within ±12.5% With 200%
0.05 max
Max. operating temperature
1000Mohm or 50Mohm ⋅ ㎌
Whichever is Smaller
Temperature
Capacitance change :
Cycling
Tan δ, IR : initial spec.
of the rated voltage
within ±7.5%
1000+48/-0hrs
1 cycle condition
Min. operating temperature→
→
25℃
Max. operating temperature → 25℃
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.