MOLDED PARTS Qualtek Electronics QCB HEAT SHRINKABLE CONDUCTIVE BREAKOUT UP TO 36kV Features/Applications The conductive breakouts are made from radiation cross-linked polyolefin. The electrically semi-conductive of the breakout provides effective conductive screen and sealing protection to the cable terminations. The breakout can be used for cable terminations up to 36kV. Operating temperature: -55°C to +105°C Minimum shrink temperature: 110°C Full Recovery Temperature: 130°C Standard color: Black RoHS Compliant Technical Data Property Test Method Typical Data Operating Temperature IEC 216 -55°C to +105°C Tensile Strength ASTM D 2671 12 MPa min. Tensile Strength After Thermal Aging (120°C, 168 hrs.) ASTM D 2671 10 MPa min. Elongation at Break ASTM D 2671 250% min. Elongation at Break After Thermal Aging (120°C, 168 hrs.) ASTM D 2671 200% min. Water Absorption ISO 62 1% max. Volume Resistance IEC 93 10 Ω.cm (max.) 4 Product Dimensions Part Number D (mm) a (Min.) b (Max.) a (Min.) QCB320-60/24 60 24 QCB330-80/38 80 38 QCB340-110/50 110 QCB350-125/57 QCB360-140/70 Notes: (a) as supplied (b) after recovery ISO-9001 Company Recovered Length ± 10% l (mm) Recovered Wall ± 10% b (Max.) L (mm) F (mm) Dw (mm) lw (mm) 25 8 183 45 3.0 2.5 35 11 215 57 4.0 4.0 50 46 17.5 250 65 4.0 4.0 125 57 55 20 260 57 4.0 4.0 140 70 62 26 280 70 4.0 4.0 www.qualtekusa.com QCB-200C