Y5V Dielectric General Specifications Y5V formulations are for general-purpose use in a limited temperature range. They have a wide temperature characteristic of +22% –82% capacitance change over the operating temperature range of –30°C to +85°C. These characteristics make Y5V ideal for decoupling applications within limited temperature range. PART NUMBER (see page 2 for complete part number explanation) 3 G 104 Z A T 2 A Size (L" x W") Voltage 6.3V = 6 10V = Z 16V = Y 25V = 3 50V = 5 Dielectric Y5V = G Capacitance Code (In pF) 2 Sig. Digits + Number of Zeros Capacitance Tolerance Z = +80 –20% Failure Rate A = Not Applicable Terminations T = Plated Ni and Sn Packaging 2 = 7" Reel 4 = 13" Reel Special Code A = Std. Product Capacitance Change vs. DC Bias Voltage +20 +10 0 -10 -20 -30 -40 -50 -60 -70 -80 +40 +20 ⌬ c/c (%) 0 -20 -40 -60 -80 -55 -35 -15 -100 0 +5 +25 +45 +65 +85 +105 +125 Temperature °C 10,000 80 100 100 10 1 1,000,000 Frequency (Hz) +20 10,000,000 +40 +50 +60 +70 +80 +90 1 F - 1206 Impedance vs. Frequency 1,000 100 100 10 1 0.01 10,000 +30 Temperature °C 10 1 0.1 0.1 0.1 100,000 0 1,000 |Z| (Ohms) |Z| (Ohms) 60 100 0.22 F - 0805 Impedance vs. Frequency 1,000 26 40 1,000 % DC Bias Voltage 0.1 F - 0603 Impedance vs. Frequency 0.01 10,000 20 Insulation Resistance vs. Temperature 10,000 |Z| (Ohms) % ⌬ Capacitance Temperature Coefficient Insulation Resistance (Ohm-Farads) 0805 100,000 1,000,000 Frequency (Hz) 10,000,000 0.01 10,000 100,000 1,000,000 Frequency (Hz) 10,000,000 Y5V Dielectric Specifications and Test Methods Parameter/Test Operating Temperature Range Capacitance Insulation Resistance Y5V Specification Limits -30ºC to +85ºC Within specified tolerance ≤ 5.0% for ≥ 50V DC rating ≤ 7.0% for 25V DC rating ≤ 9.0% for 16V DC rating ≤ 12.5% for ≤ 10V DC rating 100,000MΩ or 500MΩ - μF, whichever is less Dielectric Strength No breakdown or visual defects Dissipation Factor Resistance to Flexure Stresses Appearance Capacitance Variation Dissipation Factor Insulation Resistance Solderability Resistance to Solder Heat Thermal Shock Load Life Load Humidity Appearance Capacitance Variation Dissipation Factor Insulation Resistance Dielectric Strength Appearance Capacitance Variation Dissipation Factor Insulation Resistance Dielectric Strength Appearance Capacitance Variation Dissipation Factor Insulation Resistance Dielectric Strength Appearance Capacitance Variation Dissipation Factor Insulation Resistance Dielectric Strength No defects ≤ ±30% Measuring Conditions Temperature Cycle Chamber Freq.: 1.0 kHz ± 10% Voltage: 1.0Vrms ± .2V For Cap > 10 μF, 0.5Vrms @ 120Hz Charge device with rated voltage for 120 ± 5 secs @ room temp/humidity Charge device with 300% of rated voltage for 1-5 seconds, w/charge and discharge current limited to 50 mA (max) Deflection: 2mm Test Time: 30 seconds 1mm/sec Meets Initial Values (As Above) ≥ Initial Value x 0.1 ≥ 95% of each terminal should be covered with fresh solder No defects, <25% leaching of either end terminal 90 mm Dip device in eutectic solder at 230 ± 5ºC for 5.0 ± 0.5 seconds ≤ ±20% Meets Initial Values (As Above) Dip device in eutectic solder at 260ºC for 60 seconds. Store at room temperature for 24 ± 2 hours before measuring electrical properties. Meets Initial Values (As Above) Meets Initial Values (As Above) No visual defects Step 1: -30ºC ± 2º 30 ± 3 minutes ≤ ±20% Step 2: Room Temp ≤ 3 minutes Meets Initial Values (As Above) Step 3: +85ºC ± 2º 30 ± 3 minutes Meets Initial Values (As Above) Step 4: Room Temp ≤ 3 minutes Meets Initial Values (As Above) Repeat for 5 cycles and measure after 24 ±2 hours at room temperature No visual defects ≤ ±30% ≤ Initial Value x 1.5 (See Above) ≥ Initial Value x 0.1 (See Above) Meets Initial Values (As Above) No visual defects ≤ ±30% Charge device with twice rated voltage in test chamber set at 85ºC ± 2ºC for 1000 hours (+48, -0) Remove from test chamber and stabilize at room temperature for 24 ± 2 hours before measuring. Store in a test chamber set at 85ºC ± 2ºC/ 85% ± 5% relative humidity for 1000 hours (+48, -0) with rated voltage applied. ≤ Initial Value x 1.5 (See above) ≥ Initial Value x 0.1 (See Above) Remove from chamber and stabilize at room temperature and humidity for 24 ± 2 hours before measuring. Meets Initial Values (As Above) 27 Y5V Dielectric Capacitance Range PREFERRED SIZES ARE SHADED SIZE 0201 0402 0603 0805 1206 1210 Soldering Packaging Reflow Only All Paper Reflow Only All Paper Reflow Only All Paper Reflow/Wave Paper/Embossed Reflow/Wave Paper/Embossed Reflow Only Paper/Embossed 0.60 ± 0.03 (0.024 ± 0.001) 0.30 ± 0.03 (0.011 ± 0.001) 0.15 ± 0.05 (0.006 ± 0.002) 6.3 10 1.00 ± 0.10 (0.040 ± 0.004) 0.50 ± 0.10 (0.020 ± 0.004) 0.25 ± 0.15 (0.010 ± 0.006) 25 1.60 ± 0.15 (0.063 ± 0.006) .81 ± 0.15 (0.032 ± 0.006) 0.35 ± 0.15 (0.014 ± 0.006) 16 25 3.20 ± 0.20 (0.126 ± 0.008) 1.60 ± 0.20 (0.063 ± 0.008) 0.50 ± 0.25 (0.020 ± 0.010) 16 25 3.20 ± 0.20 (0.126 ± 0.008) 2.50 ± 0.20 (0.098 ± 0.008) .50 ± 0.25 (0.020 ± 0.010) 16 25 Cap (μF) 50 A A A A C A C C C C Letter Max. Thickness C C G G G G G J N G G 28 K N N K N N N 16 C 0.56 (0.022) 25 50 10 0402 E 0.71 (0.028) PAPER G 0.90 (0.035) 16 25 50 0603 J 0.94 (0.037) W K 1.02 (0.040) M 1.27 (0.050) T 10 16 25 t N 50 10 0805 N 1.40 (0.055) 50 M M Q Q 10 L G N 6.3 10 䉲 N 0201 A 0.33 (0.013) 50 G G 4.7 10.0 22.0 47.0 WVDC 10 A A 0.47 1.0 2.2 SIZE 50 䉲 10 䉲 0.047 0.10 0.22 50 䉲 4700 0.010 0.022 16 䉲 Cap (pF) 䉲 (t) Terminal 2.01 ± 0.20 (0.079 ± 0.008) 1.25 ± 0.20 (0.049 ± 0.008) 0.50 ± 0.25 (0.020 ± 0.010) 10 16 25 䉲 (W) Width MM (in.) MM (in.) MM (in.) WVDC 820 1000 2200 䉲 (L) Length P Q 1.52 1.78 (0.060) (0.070) EMBOSSED M P Q 16 25 50 10 1206 X 2.29 (0.090) N Q Q X Y 2.54 (0.100) 16 1210 Z 2.79 (0.110) 25 50