ROITHNER LASERTECHNIK B5b-436-30 DESCRIPTION zSuper bright LED Lamp zRound type zT1-3/4 (5mm) diameter zLens color: Water Clear zWith Flange zSolder leads without stand-off 5.9 ± 0.3 5.0 ± 0.3 4.7 ± 0.2 8.6 ± 0.3 1.0 ± 0.2 1 MAX. FEATURES zEmitted color: Super Red zHigh Luminous intensity zTechnology: GaAlAs zPeak wavelength λp = 660 nm □ 0.5 26.4 MIN. zViewing angle: 8 ° ANODE 1.0 MIN. 2.54 Notes: 1. All dimensions are in millimeter. 2. Lead spacing is measured where the lead emerge from the package. SELECTION GUIDE Chip Material Chip Emitted Lens Color Viewing Angle GaAlAs Super Red Water Clear 8° Schoenbrunner Strasse 7, Vienna, Austria, Tel.: +43-1-586 52 43 – 0 Fax.: +43-1-586 52 43 44 [email protected], http://www.roithner-laser.com REV.2004/01/10 1/3 ROITHNER LASERTECHNIK B5b-436-30 (Ta=25 °C) ABSOLUTE MAXIMUM RATINGS PARAMETER SYMBOL MAX. RATING Unit Power Dissipation PD 80 mW Peak Forward Current (1/10 Duty Cycle @1KHz ) IPF 50 mA Continuous Forward Current IAF 30 mA Reverse Voltage VR 5.0 V Operating Temperature Range TOPR -40~+85 °C Storage Temperature Range TSTG -40~+85 °C Solder temperature 1.6 mm from body for 3 seconds at 260 °C OPTICAL-ELECTRICAL CHARACTERISTICS SYMBOL TEST CONDITION MIN TYP Luminous Intensity IV IF = 20mA 2300 3500 Forward Voltage VF IF = 20mA Reverse Current IR VR = 5V 2θ1/2 IF = 20mA 8 deg. Peak Wavelength λP IF = 20mA 660 nm Dominant Wavelength λD IF = 20mA 645 nm Spectrum Radiation Bandwidth ∆λ IF = 20mA 25 nm PARAMETER Viewing Angle 1.9 MAX UNIT mcd 2.4 V 10 uA *Tolerance of Viewing Angle: -10 / +5 deg. Schoenbrunner Strasse 7, Vienna, Austria, Tel.: +43-1-586 52 43 – 0 Fax.: +43-1-586 52 43 44 [email protected], http://www.roithner-laser.com REV.2004/01/10 2/3 ROITHNER LASERTECHNIK B5b-436-30 0° 10° 20° 30° 40° 50° 60° 70° 80° 90° 1.0 0.9 0.7 0.5 0.3 0.1 0.2 0.4 0.6 0.8 60 40 20 0 630 640 650 660 670 680 690 700 λ - Wavclength (nm) 50 Forward Current -If(mA) 2.0 Relative Luminous Intensity 80 RELATIVE LUMINOUS INTENSITY Vs. WAVELENGTH RADIATION DIAGRAM 1.0 0.5 0.2 0.1 0 100 Relative Luminous Intensity (%) Normalized at If=20mA Relative Luminous Intensity TYPICAL OPTICAL-ELECTRICAL CHARACTERISTIC CURVES 40 30 20 10 0 -30 -10 10 30 50 70 Ambient Temperature -TA( ) 40 4.0 30 20 10 2.0 2.4 2.8 3.0 Luminous Intensity Relative Volue at If=10mA Forward Current-I F (mA) 5.0 1.6 40 60 80 100 FORWARD CURRENT Vs. AMBIENT TEMPERATURE 50 1.2 20 Ambient Temperature -TA( ) LUMINOUS INTENSITY Vs. AMBIENT TEMPERATURE 0 0 3.0 2.0 1.0 0 60 80 100 LUMINOUS INTENSITY Vs. FORWARD CURRENT Schoenbrunner Strasse 7, Vienna, Austria, Tel.: +43-1-586 52 43 – 0 Fax.: +43-1-586 52 43 44 [email protected], http://www.roithner-laser.com 40 Forward Current-IF (mA) Forward Voltage -VF (V) FORWARD CURRENT Vs. FORWARD VOLTAGE 20 REV.2004/01/10 3/3