http://www.luguang.cn Email: [email protected] 1 SCOPE This specification shall cover the characteristics of the ceramic resonator with the type ZTA6.0MT. 2 PART NO. PART NUMBER CUSTOMER PART NO SPECIFICATION NO ZTA6.0MT 3 OUTLINE DRAWING AND DIMENSIONS 3.1 Appearance: No visible damage and dirt. 3.2 Construction: Leads are soldered on electrode and body is molded by resin. 3.3 Except the chip(ceramic element, ceramic base, capacitance slice), the materials don’t contain lead. 3.4 Dimensions ZTA 6.00MT UNIT：mm SHENZHEN LUGUANG ELECTRONIC TECHNOLOGY CO.,LTD. 1 http://www.luguang.cn Email: [email protected] 4 RATING AND ELECTRICAL SPECIFICATIONS 4.1 RATING Items Content Withstanding Voltage (V) 50 (DC，1min) Insulation Resistance Ri,（MΩ）min. 100 （100V，1min） Operating Temperature Range (℃) -20～+80 Storage Temperature Range (℃) -35～+85 4.2 ELECTRICAL SPECIFICATIONS Items Content Oscillation Frequency Fosc（MHz） 6.000 Frequency Accuracy （%） ±0.5 Resonant Impedance Ro（Ω）max. 30 ±0.3 Temperature Coefficient of Oscillation （Oscillation Frequency Frequency （%） max. drift，-20℃～+80℃） 6V DC Rating Voltage UR（V）max. 15V p-p Aging Rate （%）max. ±0.5（For Ten Years） 5 MEASUREMENT 5.1 Measurement Conditions Parts shall be measured under a condition ( Temp. ： 20 ℃ ±15 ℃ ,Humidity ： 65%±20% R.H.) unless the standard condition(Temp.：25℃±3℃,Humidity ：65%±5% R.H.) is regulated to measure. 5.2 Test Circuit IC：1/6TC4069UBP×2 X：CERAMIC RESONATOR C1 C2：30pF SHENZHEN LUGUANG ELECTRONIC TECHNOLOGY CO.,LTD. 2 6 No 6.1 6.2 6.3 6.4 6.5 6.6 6.7 http://www.luguang.cn Email: [email protected] PHYSICAL AND ENVIRONMENTAL CHARACTERISTICS Performance Item Condition of Test Requirements Subject the resonator at +40℃±2℃ It shall fulfill and 90%~95% R.H. for 500h, the Humidity resonator shall be measured after specifications being placed in natural conditions for in Table 1. 1h. Subject the resonator to +85℃±5℃ It shall fulfill High for 500h, resonator shall be measured the Temperature after being placed in natural specifications Exposure conditions for 1h. in Table 1. Subject the resonator to–25℃±5℃ It shall fulfill Low for 500h, resonator shall be measured the Temperature after being placed in natural specifications Exposure conditions for 1h. in Table 1. Subject the resonator to －25℃ for 30min. followed by a high It shall fulfill temperature of +85 ℃ for 30min. Temperature the Cycling shall be repeated 5 times. Cycling specifications Resonator shall be measured after in Table 1. being placed in natural conditions for 1h. Subject the resonator to vibration for 2h each in x y and z axis with the It shall fulfill amplitude of 1.5mm, the frequency the Vibration shall be varied uniformly between the specifications limits of 10Hz~55Hz and then in Table 1. resonator shall be measured. No visible Resonator shall be measured after 3 damage and it Mechanical times' random dropping from the shall fulfill the Shock height of 100cm on concrete floor. specifications in Table 1. Lead terminals are immersed up to 2mm from resonator’s body in It shall fulfill Resistance soldering bath of +260℃±5℃ for 5s the to Soldering ± 1s and then resonator shall be specifications Heat measured after being placed in natural in Table 1. conditions for 1h. (To be continued) SHENZHEN LUGUANG ELECTRONIC TECHNOLOGY CO.,LTD. 3 http://www.luguang.cn Email: [email protected] 6 PHYSICAL AND ENVIRONMENTAL CHARACTERISTICS More than 95% of the Lead terminals are immersed up to terminal 2mm from resonator’s body in surface of the 6.8 Solderability soldering bath of +250℃±5℃ for resonator shall be covered 2s±0.5s. with fresh solder. Terminal 6.9 Strength Force of 5N is applied to each lead in No any visible Terminal 6.9.1 Pulling axial direction for 10s±1s. damage and it When force of 5N is applied to each shall fulfill the Terminal lead in axial direction,the lead shall specifications Bending folded up 90 ° from the axial in Table1. 6.9.2 direction and folded back to the axial direction. The speed of folding shall be each 3s Table 1 Item Oscillation Frequency Change Δfosc/fosc （%）max. Resonant Impedance Ro（Ω）max. Specification after test ±0.5 25 The limits in the above table are referenced to the initial measurements. SHENZHEN LUGUANG ELECTRONIC TECHNOLOGY CO.,LTD. 4