ZTTWS4.19MG 1. SCOPE This specification shall cover the characteristics of the ceramic resonator with the type ZTTWS4.19MG. 2. PART NO: PART NUMBER CUSTOMER PART NO SPECIFICATION NO ZTTWS4.19MG 3. OUTLINE DRAWING AND STRUCTURE 3.1 Appearance: No visible damage and dirt. 3.2 Construction: Leads are soldered on electrode and body is molded by resin. 3.3 Except the chip(ceramic element, ceramic base, capacitance slice), the materials don’t contain lead. 3.4 Dimensions 9.5max 0.5±0.1 ③ ② 2.5±0.3 ① 5.0±1.0 5.5max 5.0max 2.5±0.3 0.3±0.1 ① Iuput ② Ground ③ Output * EIAJ MONTHLY CODE http://www.luguang.cn Email:[email protected] ZTTWS4.19MG 4 RATING AND ELECTRICAL SPECIFICATIONS 4.1 RATING Items Content Withstanding Voltage (V) 50 (DC，1min) Insulation Resistance Ri,（MΩ）min. 100 （100V，1min） Operating Temperature Range (℃) -20～+80 Storage Temperature Range (℃) -40～+85 4.2 ELECTRICAL SPECIFICATIONS Items Oscillation Frequency Fosc（MHz） Frequency Accuracy （%） Resonant Impedance Ro（Ω）max. Temperature Coefficient of Oscillation Frequency （%） max. Rating Voltage UR（V）max. Aging Rate （%）max. 5 Content 4.190 ±0.5 30 ±0.3 （Oscillation Frequency drift，-25℃～+85℃） 6V DC 15V p-p ±0.3 （For Ten Years） MEASUREMENT 5.1 Measurement Conditions: Parts shall be measured under a condition ( Temp.： 20±15℃,Humidity ：65±20% R.H.) unless the standard condition(Temp.：25±3 ℃,Humidity ：65±5% R.H.) is regulated to measure. 5.2 Test Circuit IC：1/6TC4069UBP×2 X：CERAMIC RESONATOR C1，C2：15pF(1±20%) http://www.luguang.cn Email:[email protected] ZTTWS4.19MG 6 PHYSICAL AND ENVIRONMENTAL CHARACTERISTICS No. 6.1 6.2 6.3 6.4 6.5 6.6 6.7 6.8 Item Humidity High Temperature Exposure Low Temperature Exposure Condition of Test Subject the resonator at +40℃±2℃ and 90%-95% R.H. for 500h, resonator shall be measured after being placed in natural conditions for 1h. Subject the resonator to +85℃±5℃ for 500h, resonator shall be measured after being placed in natural conditions for 1hr. Performance Requirements It shall fulfill the specifications in Table 1. It shall fulfill the specifications in Table 1. Subject the resonator to –25℃±5℃ for It shall fulfill the 500h, resonator shall be measured after specifications in being placed in natural conditions for 1h. Table 1. Subject the resonator to －25℃ for 30 min. followed by a high temperature of +85℃ It shall fulfill the Temperature for 30 min. Cycling shall be repeated 5 specifications in Cycling times. Resonator shall be measured after Table 1. being placed in natural conditions for 1h. Subject the resonator to vibration for 2h each in x y and z axis with the amplitude of It shall fulfill the 1.5mm, the frequency shall be varied specifications in Vibration uniformly between the limits of 10Hz-55Hz Table 1. and then resonator shall be measured. No visible Resonator shall be measured after 3 times' damage and it Mechanical random dropping from the height of 100cm shall fulfill the Shock on concrete floor. specifications in Table 1. Lead terminals are immersed up to 2 mm Resistance from resonator’s body in soldering bath of It shall fulfill the to Soldering 260℃±5℃ for 5s±1s and then resonator specifications in shall be measured after being placed in Table 1. Heat natural conditions for 1h More than 95% of the terminal Lead terminals are immersed up to 2mm surface of the Solderability from resonator’s body in soldering bath of resonator shall 250℃±5℃ for 2s±0.5s. be covered with fresh solder. http://www.luguang.cn Email:[email protected] ZTTWS4.19MG 6 PHYSICAL AND ENVIRONMENTAL CHARACTERISTICS 6.9 Terminal Strength 6.9.1 Terminal Force of 5N is applied to each lead in axial Pulling direction for 10s±1s. 6.9.2 Terminal When force of 5N is applied to each lead in Bending axial direction,the lead shall folded up 90° from the axial direction and folded back to the axial direction. The speed of folding shall be each 3s. No visible damage and it shall fulfill the specifications in Table 1. Table 1 Item Specification after test Oscillation Frequency Change Δfosc/fosc （%）max ±0.3（Refer to the initial value） Resonant Impedance Ro（Ω）max http://www.luguang.cn 30 Email:[email protected] ZTTWS4.19MG 7 PACKAGE To protect the products in storage and transportation，it is necessary to pack them(outer and inner package).On paper pack, the following requirements are requested. 7.1 Section of package Package is made of corrugated paper with thickness of 0.8cm.Package has 2 inner packages, each has 20 inner boxes (each box for plastic bag). 7.2 Quantity of package Per plastic bag 500 pieces Per inner box 3 plastic bags Per inner package 20 inner boxes Per package 2 inner packages (60000 pieces of piezoelectric ceramic part) 7.3 Dimensions and Mark At the end of package, the warning (moisture proof, upward put) should be stick to it(see below) ③ ④ ① ⑤ 300mm ② ⑦ 34 0m m ⑥ 450mm ① Belt(2.9m) ③ Label(1) ⑤ Package(1) ② Certificate of ④ Adhesive ⑥ Box(2) proval(1) tape(1.2m) ⑦ Inner box(40) http://www.luguang.cn Email:[email protected] ZTTWS4.19MG 7.4 Inner package 0mm ① 135mm 32 ② ③ 435mm ① Label ② Inner package ③ Package tack 7.5 Inner box Dimensions ① 82 mm 52mm ② ③ 152mm Pars shall be packaged in box with hold down tape upside. Part No., quantity and lot No. http://www.luguang.cn Email:[email protected] ZTTWS4.19MG 8 EIAJ Monthly Code 2003 / 2005 / 2007 / 2009 MONTH CODE JAN A FEB B MAR C APR D MAY E JUN F JUL G AUG H SEP J OCT K NOV L DEC M 2004 / 2006 / 2008 / 2010 MONTH CODE JAN N FEB P MAR Q APR R MAY S JUN T JUL U AUG V SEP W OCT X NOV Y DEC Z 9 OTHER 9.1 Caution of use 9.1.1 Do not clean or wash the component for it is not hermetically sealed. 9.1.2 Don’t be close to fire 9.1.3 Don’t apply excess mechanical stress to the component. 9.1.4 Don’t bend terminals of the component 9.1.5 This specification mentions the quality of the component as a single unit. Please insure the component is thoroughly evaluated in your application circuit. 9.2 Notice 9.2.1 Please return one of this specification after your signature of acceptance. 9.2.2 When something gets doubtful with this specifications, we shall jointly work to get an agreement. http://www.luguang.cn Email:[email protected]