ILU-008-N

ILU - 008 series
Appearance
Application
LED Bulb(MR16,GU10,etc...)
LED Down-light , others ...
Recommended LED
CL-L400 series
Material : PMMA
Unit : [mm]
Outline
Layout
Cav.No.
Gate　(under　φ28)
Type
CL-L400
A-A section
< Attention in the handling >
・To fix the lens, the use of its flange with thickness of 0.8mm is recommended.
・The lens should be placed against the LED “CL-L400” as as shown in the figure above.
・The specification is subject to change without notice.
・The prism shape is not accurate.
・Do not use this product under the temperature condition exceeding 85℃.
CITIZEN ELECTRONICS CO.,LTD.
Ref.CE-P1810 02/12
ILU - 008 series
Luminous intensity
With CL-L400 Series
Lens
LED
ILU-008-N
ILU-008-M
ILU-008-W
FWHM 18[deg]
FWHM 32[deg]
FWHM 45[deg]
CL-L400-MC1N1-A
118 [lm]
710 [cd]
280 [cd]
165 [cd]
CL-L400-MC1W1-A
115 [lm]
690 [cd]
270 [cd]
160 [cd]
CL-L400-MC1WW1-A
110 [lm]
660 [cd]
260 [cd]
155 [cd]
CL-L400-MC1L1-A
106 [lm]
635 [cd]
250 [cd]
145 [cd]
CL-L400-MC1L2-A
100 [lm]
600 [cd]
235 [cd]
140 [cd]
CL-L400-C1N-A
137 [lm]
805 [cd]
315 [cd]
185 [cd]
Relative intensity
Directivity
1.1
1.0
0.9
0.8
0.7
0.6
0.5
0.4
0.3
0.2
0.1
0.0
-40
-30
-20
-10
ILU-008-N
ILU-008-M
ILU-008-W
0
10
20
30
40
Angle [degree]
< Attention in the handling >
・To fix the lens, the use of its flange with thickness of 0.8mm is recommended.
・The lens should be placed against the LED “CL-L400” as shown in the figure above.
・The specification is subject to change without notice.
・Do not use this product under the temperature condition exceeding 85℃.
CITIZEN ELECTRONICS CO.,LTD.
Ref.CE-P1810 02/12
ILU - 008 series
Physical properties
Property
Optical
Light transmission
Reflectiv Index
Mechanical
Tensile modulus
Tensile strength at yield
Nominal tensile strain at break
Flexual modulus
Flexual strength
Charpy impact strength
Izod impact strength
Rockwell hardness
Thermal
Heat deflection temperature
Vicat softening point
Test Method
Condition
Unit
ASTM D 1003
ASTM D 542
3.2mm
ND@23℃
%
---
92
1.49
Max.
-------
MPa
MPa
%
MPa
MPa
3100
70
6
3200
103
7.5
Noched (23℃)
M scale
kJ/m 2
---
1.2
93
1820kPa
(Rate A;1kg)
(Rate A;5kg)
-----
℃
℃
℃
g/10min
×10 -5
102
111
104
3.7
Ω/sq
Ωcm
-----
ASTM D 405
----60cycles
1,000,000cycles
volts/mil
60cycles
1,000,000cycles
---
ASTM D 792
ASTM D 570
UL94
-------
g/cm 3
%
class
ASTM
ASTM
ASTM
ASTM
ASTM
ASTM
ASTM
ASTM
D
D
D
D
D
D
D
D
638
790
638
790
790
256
256
785
ASTM D 648
ASTM D 1525
Melt volume flow rate
Coeffient of linear expansion
Electrical
Surface resistivity
Volume resistivity
ASTM D 1238
ASTM D 696
Specific Inductive capacity
ASTM D 150
Dielectric strength
ASTM D 149
Dielectric loss Factor
ASTM D 150
Tracking resistance
Other
Density
Water absorption
Flammability
ASTM D 257
ASTM D 257
seconds
Value
5.8
1.00E+18
1.00E+18
3.7
2.2
500
0.19
0.007
no track
1.19
0.3
HB
* Values reported are typical and should not be used for specification purpose.
< Attention in the handling >
・ The data on this document is the characteristics combining ILU-008 and CL-L400 series.
・ ILU-008 is the lens for CL-L400 series.
・Discussion will be needed separately if you combine it with LEDs other than these.
・Do not use this product under the temperature condition exceeding 85℃.
CITIZEN ELECTRONICS CO.,LTD.