PQFN 3X3 RoHS Compliance Document Contents: 1. Composition 2. Solder Reflow 3. Tin Whisker Report The information contained in this document is provided without any warranty, either expressed or implied, and IR specifically disclaims any and all liability, including but not limited to consequential or indirect damages. Dec. 2014 PQFN 3X3 BOM 1 Component Material Name Material Mass (g) Chip Silicon 0.00145 Encapsulant Epoxy Resin 0.01179 Lead Frame Copper 0.01089 Die Attach Silver Epoxy 0.00050 Wire Bond Lead Finish Copper Matte Tin* 0.00030 0.00012 Element Name Composition Si SiO2 Epoxy Resin Cu Fe Ag Epoxy Resin Cu Sn Total Weight (g) CAS # Substance Mass (g) 7440-21-3 60676-86-0 90598-46-2 7440-50-8 7439-89-6 7440-22-4 90598-46-2 7440-50-8 7440-31-5 0.00145 0.00766 0.00413 0.01056 0.00033 0.00043 0.00007 0.00030 0.00012 Material Analysis Weight (%) 100% 65% 35% 97% 3% 85% 15% 100% 100% % of Total Weight 5.8% 30.6% 16.5% 42.1% 1.3% 1.7% 0.3% 1.2% 0.5% 0.02505 *Tin whisker mitigation strategy is 150 °C, 1 hour anneal within 24 hours of tin plating. This part is compliant with EU Directive 2011/65/EU (RoHS Directive) and does not contain lead, mercury, cadmium (0.01%), hexavalent chromium, PBB or PBDE in concentrations greater than 0.1%, except as permitted by Annex III. Further part complies with 3 reflow cycles per JEDEC J-STD-020 The information contained in this document is provided without any warranty, either expressed or implied, and IR specifically disclaims any and all liability, including but not limited to consequential or indirect damages. 1 Dec. 2014 PQFN 3X3 BOM 2 Component Material Name Material Mass (g) Chip Silicon 0.00145 Encapsulant Epoxy Resin 0.01179 Lead Frame Copper 0.01089 Die Attach Silver Epoxy 0.00050 Wire Bond Copper 0.00030 Lead Finish Ni/Pd/Au 0.00012 Element Name Composition Si SiO2 Epoxy Resin Cu Fe Ag Epoxy Resin Cu Ni Pd Au Total Weight (g) CAS # Substance Mass (g) 7440-21-3 60676-86-0 90598-46-2 7440-50-8 7439-89-6 7440-22-4 90598-46-2 7440-50-8 7440-02-0 7440-05-3 7440-57-5 0.00145 0.00766 0.00413 0.01056 0.00033 0.00043 0.00007 0.00030 0.00011 0.00001 0.00000 Material Analysis Weight (%) 100% 89% 11% 97% 3% 86% 14% 100% 93% 6% 1% % of Total Weight 5.8% 30.6% 16.5% 42.1% 1.3% 1.7% 0.3% 1.2% 0.4% 0.1% 0.0% 0.02505 No tin whisker mitigation strategy This part is compliant with EU Directive 2011/65/EU (RoHS Directive) and does not contain lead, mercury, cadmium (0.01%), hexavalent chromium, PBB or PBDE in concentrations greater than 0.1%, except as permitted by Annex III. Further part complies with 3 reflow cycles per JEDEC J-STD-020 The information contained in this document is provided without any warranty, either expressed or implied, and IR specifically disclaims any and all liability, including but not limited to consequential or indirect damages. 2 Dec. 2014 PQFN 3X3 Test Definition Room Temperature Humidity Temperature Humidity Unbiase Temperature Cycling Test Conditions Inspection Total Interval Class Duration 1 and 2 Class 1 and 2 Products Products Maximum Whisker Length (µm) 30± 2°C/60± 3% RH 1000 hours 4000 hours 20 55± 3°C/85± 3% RH 1000 hours 4000 hours 20 500 cycles 1500 cycles 45 -40 to 55°C to 80 to 95°C, air to air, 10 min soak, approx 3 Tin Whisker testing per JESD201, Environmental Acceptance Requirements for Tin Whisker Susceptibility of Tin and Tin Alloy Surface Finish Tin Whisker Results (number of failing whiskers) Test Room Temperature Humidity Storage Temperature Humidity Test Temperature Cycling 1000 Hours 2000 Hours 3000 Hours 4000 Hours 0/24 0/24 0/24 0/24 0/24 0/24 0/24 0/24 500 Cycles 1000 Cycles 1500 Cycles 0/24 0/24 0/24 The information contained in this document is provided without any warranty, either expressed or implied, and IR specifically disclaims any and all liability, including but not limited to consequential or indirect damages. 3 Dec. 2014