ROHM MCH313FN106JK

MCH31
Ceramic capacitors
Multi-layer ceramic chip capacitors
MCH31 (3216 (1206) size, chip capacitor)
zFeatures
1) Miniature, high capacitance
2) Achieved high capacitance by thin and multi layer technology
3) Lead-free plating terminal
4) No polarity
zQuick Reference
The design and specifications are subject to change without prior notice. Please check the most recent technical
specifications prior to placing orders or using the product. For more detail information regarding packaging style code,
please check product designation.
zThermal compensation
Part No.
Size code
MCH31
3216
(1206)
Temperature characteristics
(ppm/°C)
code
A (AN)
0±30
(CG) (C0G)
Operating temp. range
(°C)
Rated voltage
(V)
−55 to +125
50
Operating temp. range
(°C)
Rated voltage
(V)
−25 to +85
50
Capacitance (pF)
4,700 to 6,800 (E12 Series)
8,200 to 10,000 (E12 Series)
15,000 to 22,000 (E12 Series)
33,000 (E12 Series)
Capacitance
tolerance
Thickness
(mm)
J(±5%)
0.6 ± 0.15
0.85 ± 0.15
1.15 ± 0.15
1.6 ± 0.2
zHigh dielectric constant
Part No.
Size code
Temperature characteristics
(ppm/°C)
code
±10%
(B)
25
CN
±15%
(R) (X7R)
−55 to +125
50
25
±15%
(X5R)
MCH31
16
−55 to +85
3216
(1206)
10
6.3
50
+30% , −80%
(F)
−25 to +85
FN
25
16
10
6.3
50
+22% , −82%
(Y5V)
−30 to +85
25
16
10
6.3
Capacitance (pF)
220 to 68,000 (E6 Series)
100,000 (E6 Series)
150,000 to 330,000 (E6 Series)
470,000 (E6 Series)
680,000 (E6 Series)
220 to 68,000 (E6 Series)
100,000 (E6 Series)
150,000 to 330,000 (E6 Series)
470,000 (E6 Series)
680,000 (E6 Series)
1,000,000 (E6 Series)
1,500,000 to 4,700,000 (E6 Series)
6,800,000 to 10,000,000 (E6 Series)
22,000,000 (E3 Series)
1,000,000 (E3 Series)
2,200,000 (E3 Series)
4,700,000 (E3 Series)
10,000,000 (E3 Series)
22,000,000 (E3 Series)
47,000,000 (E3 Series)
1,000,000 (E3 Series)
2,200,000 (E3 Series)
4,700,000 (E3 Series)
10,000,000 (E3 Series)
22,000,000 (E3 Series)
47,000,000 (E3 Series)
Capacitance
tolerance
K(±10%)
Thickness
(mm)
0.6 ± 0.15
0.85 ± 0.15
1.15 ± 0.15
1.6 +0.3
−0.1
0.85 ± 0.15
0.6 ± 0.15
0.85 ± 0.15
1.15 ± 0.15
1.6 +0.3
−0.1
0.85 ± 0.15
1.6 +0.3
−0.1
0.85 ± 0.15
1.15 ± 0.15
1.6 +0.3
−0.1
Z(+80% , −20%)
0.85 ± 0.15
1.15 ± 0.15
1.6 +0.3
−0.1
1/10
MCH31
Ceramic capacitors
zExternal dimensions (Unit : mm)
Product thickness(mm)
0.2Min.
0.6±0.15
0.85±0.15
1.15±0.15
T
1.0Min.
+0.3
1.6−0.1
∗1 : CN charac.
FN charac.
∗2 : CN charac.
CN charac.
FN charac.
3,300,000 to 22,000,000pF : 3.2+0.3/−0.1(mm)
10,300,000 to 22,000,000pF : 3.2+0.3/−0.1(mm)
2,200,000 to 4,700,000pF : 1.6±0.2(mm)
6,800,000 to 22,000,000pF : 1.6+0.3/−0.1(mm)
10,300,000 to 22,000,000pF : 1.6+0.3/−0.1(mm)
T
3.2±0.2 ∗1
1.6±0.2 ∗2
zProduct designation
Code Product thickness
Packing specification
Reel
Basic ordering unit (pcs.)
K
0.6mm
Paper tape (width 8mm, pitch 4mm)
φ180mm (7in.)
4,000
K
0.85mm
Paper tape (width 8mm, pitch 4mm)
φ180mm (7in.)
4,000
P
1.15mm
Plustic tape (width 8mm, pitch 4mm)
φ180mm (7in.)
2,000
P
1.60mm
Plustic tape (width 8mm, pitch 4mm)
φ180mm (7in.)
1,000
Reel (φ180mm) : compatible with EIAJ ET-7200A
Packing Style
Part No.
M C H
Rated voltage
Code Voltage
8
6.3V
4
10V
3
16V
2
25V
5
50V
3 1
3
F N
1 0 6
Temperature characteristic code
: Refer to quick reference table.
Z
K
Nominal
capacitance
3-digit
designation
according
to IEC
Capacitance tolerance
Code
Tolerance
K
±5% (11pF or more)
±10%
Z
+80%, −20%
J
2/10
MCH31
Ceramic capacitors
•Performance and test method
No.
Items
Performance
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
1
Appearance and
dimensions
No marked defects shall be allowed As per 4.4 of JIS C 5101-1.
As per 4.5 of JIS C 5101-10
for appearance.
Dimensions shall be as specified the Using a Magnifier.
clause 4.
2
Withstanding voltage
No dielectrical breakdown or other
damage shall be allowed.
As per 4.6 of JIS C 5101-1.
As per 4.6.4 of JIS C 5101-10
Voltage shall be applied as per Table1.
Table 1
CharacVoltage
teristic
A, AN 300% Rated voltage
CN
250% Rated voltage
FN
Voltage shall be applied for 1 to 5s with
50mA charging and discharging current.
3
Insulation resistance
Not less than 10000MΩ or
500MΩ µF, whichever is less.
(For products with rated voltage less
than 16V, it is not less than 10000MΩ
or 100MΩ µF, whichever is less.)
As per 4.5 of JIS C 5101-1.
As per 4.6.3 of JIS C 5101-10
Measurements shall be made after
60+/−5s period of the rated voltage
applied.
4
Capacitance
Capacitance shall be
within specified tolerance range.
As per 4.7 of JIS C 5101-1.
As per 4.6.1 of JIS C 5101-10
Measurements shall be made under the
conditions specified in Table 2.
Characteristic
A, AN
5 Dielectric loss tangent
A, A N
tan δ <
− 0.1%
CN
Rated voltage <
− 25V
tan δ <
− 3.0%
Rated voltage=16,10V
tan δ <
− 5.0%
Rated voltage=6.3V
tan δ <
− 10.0%
FN
Rated voltage=50V
tan δ <
− 5.0%
Rated voltage=25V
tan δ <
− 7.5%
Rated voltage=16V
tan δ <
− 10.0%
Rated voltage=10V,6.3V
tan δ <
− 12.5%
Table 2
Frequency Voltage
CN
<
− 1000pF
1+/−0.1MHz
1+/−0.1Vrms.
<
− 10µF
FN
1+/−0.1KHz
120+/−24Hz
1+/−0.1Vrms. 0.5+/−0.2Vrms.
> 1000pF
1+/−0.1kHz
1+/−0.1Vrms.
> 10µF
As per 4.8 of JIS C 5101-1.
As per 4.6.2 of JIS C 5101-10
Measurements shall be made under the
conditions specified in Table 2.
3/10
MCH31
Ceramic capacitors
No.
Items
6 Temperature
characteristic
Performance
A, A N
CN
FN
7 Solderability
0+/−30ppm / °C
(−55°C to +125°C)
X7R
R
+/−15%
(−55°C to +125°C)
B
+/−10%
(−25°C to +85°C)
X5R
+/−15%
(−55°C to +85°C)
8 Resistance Appearance Without mechanical damage.
to soldering
heat
A, A N
Within +/−2.5%
CN
Within +/−7.5%
FN
Within +/−20%
Dielectric
loss
tangent
Within specified initial value.
Insulation
resistance
Within specified initial value.
Withstanding No defects shall be allowed.
voltage
9 End termination
adherence
As per 4.24 of JIS C 5101-1.
As per 4.7 of JIS C 5101-10
Temperature coefficient shall be calculated
at 20°C and 85°C.
As per 4.24 of JIS C 5101-1.
As per 4.7 of JIS C 5101-10
If required, measurements shall be made
at a given temperature.
+30%, −80%
(−25°C to +85°C)
+22%, −82%
(−30°C to +85°C)
More than 3/4 of each end
termination shall be covered with
new solder.
Change
rate from
initial value
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
Without peeling or sign of
peeling shall be allowed
on the end terminations.
As per 4.15.2 of JIS C 5101-1.
As per 4.11 of JIS C 5101-10
The solder specified in JIS Z 3282 H63A
shall be used. Ans the flux containing 25%
rosin and ethanol solution shall be used.
The specimens shall be immersed into the
solder at 235+/−5°C for 2+/−0.5s
So that both end terminations are
completely under solder.
As per 4.14 of JIS C 5101-1.
As per 4.10 of JIS C 5101-10
The solder specified in JIS Z 3282. H63A
shall be used.
The specimens shall be immersed into the
solder at 260+/−5°C for 5+/−0.5s so that
both end terminations are completely
under the solder.
Pre-heating at 150+/−10°C for 1 to 2min
Initial measurements prior to test shall be
performed after the thermal
Pre-conditioning specified in Remarks (1).
Final measurements shall be made after the
specimens have been left at room
temperature as per Table3.
Table3
Characteristic
A, AN
CN, FN
Time
24+/−2 h
48+/−4 h
As per 4.13 of JIS C 5101-1.
As per 4.8 ofJIS C 5101-10
A 5N weight for 10+/−1s shall be applied
to the soldered specimens as shown by the
arrow mark in the below sketch.
Applied pressure
Substrate
Capacitor
4/10
MCH31
Ceramic capacitors
No.
Items
Performance
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
10 Bending
strength
Appearance
Without mechanical damage.
As per 4.35 of JIS C 5101-1.
As per 4.9 of JIS C 5101-10
Glass epoxy board with soldered
specimens shall be bent till 1mm by
1.0mm/s.
11 Vibration
Appearance
Without mechanical damage.
As per 4.17 of JIS C 5101-1.
The specimens shall be soldered on the
specified test jig.
Initial measurements shall be made after
the thermal pre-conditioning specified in
Remarks(1).
Final measurements shall be made after the
specimens have been left at room
temperature as per Table3.
[Condition]
Directions : 2h each X, Y and Z directions
Total : 6h
Frequency range : 10 to 55 to 10Hz(1min)
Applitude : 1.5mm
(shall not exceed acceleration196m/s2)
Change
rate from
initial value
Dielectric
loss
tangent
A, A N
Capacitance shall be
within specified
tolerance range.
CN
Within +/−7.5%
FN
Within +/−20%
Within specified initial value.
Table3
Characteristic
A, AN
CN, FN
12 Temperature Appearance Without mechanical damage.
cycling
Change
A, A N
Within +/−2.5%
rate from
initial value
Rated vcoltage
C N 25V,16V,10V Within +/−7.5%
Rated vcoltage
Within +/−15%
6.3V
FN
Dielectric
loss
tangent
Insulation
resistance
Within +/−20%
Within specified initial value.
Within specified initial value.
Withstanding No defects shall be allowed.
voltage
Time
24+/−2 h
48+/−4 h
As per 4.16 of JIS C 5101-1
As per 4.12 of JIS C 5101-10
The specimens shall be soldered on the test
jig shown in Remarks.
Temperature cycle : 100cycles Initial
measurements prior to test shall be
performed after the thermal
per-conditioning specified in Remarks (1).
Final measurements shall be made after the
specimens have been left at room
temperature as per Table3.
Test condition
Step
Temp. (°C)
Time (min)
1
Min operating temp.
2
Room temp.
30+/−3
<
−3
3
Max operating temp.
4
Room temp.
30+/−3
<
−3
Table3
Characteristic
A, AN
CN, FN
Time
24+/−2 h
48+/−4 h
5/10
MCH31
Ceramic capacitors
No.
13 Humidity
(Steady)
Items
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
Appearance Without mechanical damage.
Change
rate from
initial value
Dielectric
tangent
Insulation
resistance
14 Humidity
life test
Performance
As per 4.22 of JIS C 5101-1
JIS C 5101-10
Within +/−5.0%
A, A N
Test temperature : 60+/−2°C
Relative humidity : 90 to 95%
Rated voltaeg
: 500 +24/−0 h
25V,16V,10V Within +/−12.5% Test time
CN
Initial measurements prior to test shall
Rated voltaeg
Within
+/−25.0%
6.3V
be made after the voltage
pre-conditioning specified in
Within +/−30%
FN
Remarks (2).
Final measurements have been left at
tan δ <
A, A N
− 0.3%
room temperature as per Table3.
CN
Less than 200% of
initial spec.
FN
Less than 150% of
initial spec.
Not less than 1000MΩ or
50MΩ µF, whichever is less.
(For products with rated
voltage less than 16V, it is not less
than 1000MΩ or 10MΩ µF,
whichever is less.)
Table3
Characteristic
A, AN
CN, FN
Time
24+/−2 h
48+/−4 h
Appearance Without mechanical damage.
Change
rate from
initial value
Dielectric
loss
tangent
Insulation
resistance
As per 4.22 of JIS C 5101-1
As per 4.14 of JIS C 5101-10
Within +/−7.5%
A, A N
Test temperature : 60+/−2°C
Relative humidity : 90 to 95%
Rated voltaeg
25V,16V,10V Within +/−12.5% Voltage : Rated voltage
CN
Test time : 500 +24/−0 h
Rated voltaeg
Within +/−25.0% Initial measurements prior to test shall
6.3V
be made after the voltage
FN
Within +/−30%
pre-conditioning specified in
Remarks (2).
A, A N
tan δ <
− 0.5%
Final measurements shall be made after
the specimens have been left at room
Less than 200% of temperature as per Table3.
CN
initial spec.
Table3
Less than 150% of
FN
initial spec.
CharacTime
teristic
Not less than 500MΩ or
A, AN
24+/−2 h
25MΩ µF, whichever is less.
(For products with rated voltage less
CN, FN
48+/−4 h
than 16V, it is not less than 500mΩ
or 5MΩ µF, whichever is less.)
6/10
MCH31
Ceramic capacitors
No.
Items
15 Heat life
test
Performance
Appearance Without mechanical damage.
Change
rate from
initial value
A, A N
CN
Rated voltage
Within +/−25%
6.3V
A, A N
CN
FN
Insulation
resistance
As per 4.23 of JIS C 5101-1.
As per 4.15 of JIS C 5101-10
Test
Voltage
temperature(°C)
Rated voltage
25V,16V,10V Within +/−15%
FN
Dielectric
loss
tangent
Within +/−3.0%
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
Within +/−30%
A, AN
125
200%
Rated
voltage
1000
+48/−0
CN
85
(B X5R)
200%
Rated
voltage
1000
+48/−0
125
(B X5R)
200%
Rated
voltage
1000
+48/−0
85
200%
Rated
voltage
1000
+48/−0
tan δ <
− 0.5%
Less than 200% of
initial spec.
FN
Less than 150% of
initial spec.
Not less than 1000MΩ or
50MΩ µF, whichever is less.
(For products with rated voltage less
than 16V, it is not less than 1000mΩ
or 10MΩ µF, whichever is less.)
Test
time (h)
Initial measurements prior to test shall be
made after the voltage pre-conditioning
specified in Remarks (2).
Final measurements shall be made after
the specimens have been left at room
temperature
Table3
Characteristic
A, AN
CN, FN
Time
24+/−2 h
48+/−4 h
[Remarks]
Pre-conditioning
If specified in test method of as per 3(Performance and test merhod), capacitors of CN, FN
characteristics shall be pre-conditionded as follows.
(1) Thermal pre-conditioning
Prior to initial measurements, specimens shall be conditioned at a temperature of 150 0/−10°C
for a period of 1hr., and shall be allowed to stabilize at room temperature for 48+/−4h
(2) Voltage pre-conditioning
Prior to initial measurements, voltage specified as a test condition shall be applied to specimens
for a period of 1hr., and the specimens shall be allowed to stabilize at room temperature for 48+/−4h
<Test jig>
Soldering
Glass epoxy
substrate
7/10
MCH31
Ceramic capacitors
zPackaging specifications
Taping dimensions
Reel dimensions
t
t
φJ
E
A
G
t1
H
P : Plastic tape
Pulling direction
C
Symbol
Dimensions
D
E
H
G
F
J
t
t
Paper
t1
Plastic
3.5
1.1
8.0
1.75
4.0
2.0
4.0
φ1.5
+/ −0.3 +/ −0.05 +/ −0.1 +/ −0.1 +/ −0.05 +/ −0.1 +0.1/ −0 MAX.
2.5
0.3
MAX. MAX.
Label pasting
As per EIAJ ET−7200A
(Unit : mm)
Symbol
A
B
1.9+/−0.2
3.5+/−0.2
Style
MCH31
+0
φ180 −1.5
φ13.0 +
− 0.2
K : Paper tape
F
+1.0
9.0 −0
Pulling direction
C
φ60.0+1.0
−0
D
B
(Unit : mm)
(Unit : mm)
(1) The quantity for one reel is as bellows.
Kind of reel
φ180 reel
Series
Paper tape
Quantity
MCH31 4,000 pcs.
Plastic tape
Symbol
Quantity
Symbol
K
2,000 pcs.
P
(2) When the tape is pulled out towards the operator with the cover tape facing
upward, the feeding holes shall be found on the right portion of the tape.
(3) Specification of beginning and ending of the tape are as follows.
Ending(reel's center)
Beginning(reel's round)
: Approx. Over 160mm (no chips)
: Approx. Over 160mm (no chips)
: Approx. 240mm (cover tape only)
(4) No juncture of tape shall be allowed.
(5) The share strength of tape shall be more than 5N at the break down strength.
(6) The peel strength of the cover tape shall be 0.1 to 0.7(N) when the cover tape are
peeled 0 to 15 degree from the surface.
(7) The number of missing components shall not exceed 0.1% of the total number
of components (marked number) or one whichever is the larger, and no consecutive
missing exceeding two is allowed.
(8) The reels made from resin shall be used, as per EIAJ ET-7200A.
zMarking
No marking shall be performed on the chip.
Trademark, parts number, quantity, lot No. , and country of origin shall be labeled on each reel.
zNumbering system for LOT No.
Example
04
(1)
01
(2)
A0001
(3)
F
(4)
(1) The end of the Christian Era < two digits> of production finish.
(2) Week in completing part of production finish.
(3) Manufacture continuity number.
(4) The symbol of manufacturing plant.
8/10
MCH31
Ceramic capacitors
zLabel expression
The Figure below is label expression
< Label Example > Part Number : MCH315A103JK
①
Part Num ber
②
Divis ion cord
③
Quantity
④
Lot No.
⑤
The Country of origin
⑥
Ins pector
⑦
QR code
⑧
Tradem ark
zPacking method
1) φ180mm Reel
EIAJ cole
B'
2
C'
(reel)
Label
A'
[width of 9mm : 5reel]
1
A
(interior box of R-26)
Packing slip
B
C
(R-26)
9/10
MCH31
Ceramic capacitors
< Packaging unit >
Symbol
Quantity of reel in
interior box
Quantity of reel in
box of R-26
K
Dimensions
R-26
5
20
< Appearance >
Packaging
interior box of
R-26
185
A (A’)
195
B (B’)
255
60
C (C’)
190
185
(Unit : mm)
Carton
< Accumulation >
You must do accumulation by ten boxes
< Packaging slip >
1.
2.
3.
4.
5.
Customer
Parts number
Quantity
Box quantity
Trade mark
10/10
Appendix
Notes
No technical content pages of this document may be reproduced in any form or transmitted by any
means without prior permission of ROHM CO.,LTD.
The contents described herein are subject to change without notice. The specifications for the
product described in this document are for reference only. Upon actual use, therefore, please request
that specifications to be separately delivered.
Application circuit diagrams and circuit constants contained herein are shown as examples of standard
use and operation. Please pay careful attention to the peripheral conditions when designing circuits
and deciding upon circuit constants in the set.
Any data, including, but not limited to application circuit diagrams information, described herein
are intended only as illustrations of such devices and not as the specifications for such devices. ROHM
CO.,LTD. disclaims any warranty that any use of such devices shall be free from infringement of any
third party's intellectual property rights or other proprietary rights, and further, assumes no liability of
whatsoever nature in the event of any such infringement, or arising from or connected with or related
to the use of such devices.
Upon the sale of any such devices, other than for buyer's right to use such devices itself, resell or
otherwise dispose of the same, no express or implied right or license to practice or commercially
exploit any intellectual property rights or other proprietary rights owned or controlled by
ROHM CO., LTD. is granted to any such buyer.
Products listed in this document are no antiradiation design.
The products listed in this document are designed to be used with ordinary electronic equipment or devices
(such as audio visual equipment, office-automation equipment, communications devices, electrical
appliances and electronic toys).
Should you intend to use these products with equipment or devices which require an extremely high level of
reliability and the malfunction of with would directly endanger human life (such as medical instruments,
transportation equipment, aerospace machinery, nuclear-reactor controllers, fuel controllers and other
safety devices), please be sure to consult with our sales representative in advance.
About Export Control Order in Japan
Products described herein are the objects of controlled goods in Annex 1 (Item 16) of Export Trade Control
Order in Japan.
In case of export from Japan, please confirm if it applies to "objective" criteria or an "informed" (by MITI clause)
on the basis of "catch all controls for Non-Proliferation of Weapons of Mass Destruction.
Appendix1-Rev1.1