DATA SHEET SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS High-Voltage NP0/X7R 1 KV TO 3 KV 10 pF to 33 nF Product Specification – December 19, 2012 V.6 RoHS compliant & Halogen Free Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R 2 15 1 KV to 3 KV SCOPE ORDERING INFORMATION - GLOBAL PART NUMBER, PHYCOMP This specification describes HighVoltage NP0/X7R series chip capacitors with lead-free terminations. All part numbers are identified by the series, size, tolerance, TC material, packing style, voltage, process code, termination and capacitance value. APPLICATIONS PCs, Hard disk, Game PCs Power supplies LCD panel ADSL, Modem FEATURES Supplied in tape on reel Nickel-barrier end termination RoHS compliant Halogen Free compliant CTC & 12NC YAGEO BRAND ordering code GLOBAL PART NUMBER (PREFERRED ) CC XXXX X X XXX X (1) (2) (3) (4) (5) B X XXX (6) (7) (1) SIZE – INCH BASED (METRIC) 0805 (2012) / 1206 (3216) / 1210 (3225) / 1808 (4520) / 1812 (4532) (2) TOLERANCE C = ±0.25 pF D = ±0.5 pF G = ±2% J = ±5% K = ±10% (3) PACKING STYLE R = Paper/PE taping reel; Reel 7 inch K = Blister taping reel; Reel 7 inch P = Paper/PE taping reel; Reel 13 inch F = Blister taping reel; Reel 13 inch C = Bulk case (4) TC MATERIAL NPO X7R (5) RATED VOLTAGE C = 1 KV D = 2 KV E = 3 KV (6) PROCESS N = NP0 B = Class 2 MLCC (7) CAPACITANCE VALUE 2 significant digits+number of zeros The 3rd digit signifies the multiplying factor, and letter R is decimal point Example: 121 = 12 x 101 = 120 pF www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R 3 15 1 KV to 3 KV PHYCOMP BRAND ordering codes GLOBAL PART NUMBER (preferred), PHYCOMP CTC (for North America) and 12NC (traditional) codes are acceptable to order Phycomp brand products. GLOBAL PART NUMBER ( PREFERRED ) For detailed information of GLOBAL PART NUMBER and ordering example, please refer to page 2. 12NC CODE Ordering information for NP0 1 KV to 3 KV, C ≥ 10 pF 2 2 XX XX X X 1 X XX Capacitance value(1) Carrier type 22 = blister 38 = paper/PE 50 = blister 54 = bulk Tolerance 4 = ±2% 5 = ±5% Voltage 00 = 1 KV 02 = 2 KV 04 = 3 KV TC material 1 = NP0 Size 0 = 0805 1 = 1206 2 = 1210 3 = 1808 4 = 1812 Packaging(3) 1 = reel: ∅180 mm; 7" 5 = reel: ∅330 mm; 13" 4 = bulk case YNM0038 Ordering information for NP0 1 KV to 3 KV, C < 10 pF 2 2 XX XX X X X XXX Capacitance value(2) Carrier type 92 = paper/PE 97 = bulk case Tolerance 4 = ±0.25 pF for 5 pF ≤ C < 10 pF ±2% for C ≥ 10 pF 5 = ±0.25 pF for C < 5 pF ±0.5 pF for 5 pF ≤ C < 10 pF ±5% for C ≥ 10 pF Voltage 00 = 1 KV 02 = 2 KV 04 = 3 KV Size 3 = 1206 2 = 1210 4 = 1808 5 = 1812 YNM0039 Packaging(3) 1 = reel: ∅180 mm; 7" 7 = reel: ∅330 mm; 13" 4 = bulk case (1) Please refer to "Last 2-digit of 12NC" in "CAPACITANCE RANGE & THICKNESS FOR NP0" (2) Please refer to "Last 3-digit of 12NC" in "CAPACITANCE RANGE & THICKNESS FOR NP0" (3) Quantity on reel depends on thickness classification; see table 5 www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors NP0/X7R High-Voltage 4 15 1 KV to 3 KV Ordering information for X7R 1 KV to 3 KV 2 2 XX XX X X X X XX Capacitance value(1) Carrier type 50 = Blister 55 = Paper/PE 54 = Bulk Tolerance 5 = ±5%(2) 6 = ±10% Rated voltage - Termination 00 = 1 KV 02 = 2 KV 04 = 3 KV Temperature characteristic 5 = X7R Size 1 = 1206 2 = 1210 3 = 1808 4 = 1812 YNM0040 Packaging(3) 1 = reel: ∅180 mm; 7" 5 = reel: ∅330 mm; 13" 4 = bulk case (1) Please refer to "Last 2-digit of 12NC" in "CAPACITANCE RANGE & THICKNESS FOR X7R" (2) Tolerance ±5% is not available for full product range, please contact local sales force before ordering (3) Quantity on reel depends on thickness classification; see table 5 PHYCOMP CTC CODE ( FOR NORTH AMERICA ) Example: 12102R102KFBB00 1210 2R 102 K F B B 0 0 Size code Temp. Char. Capacitance in pF Tolerance Voltage Termination Packing Marking Range identifier C = ±0.25 pF E = 1 KV D = ±0.5 pF F = 2 KV G = ±2% G = 3 KV 0805 CG = NP0 1206 2R = X7R 1210 1808 1812 101 = 100 pF; the third digit signifies the multiplying factor: 8 = × 0.01 9 = × 0.1 0=×1 J = ±5% K = ±10% B = NiSn 2 = 180 mm 7” Paper/PE 0 = no marking 0 = conv. Ceramic D = Class 2 MLCC 3 = 330 mm 13” Paper/PE B = 180 mm 7” Blister 1 = × 10 F = 330 mm 13” Blister 2 = × 100 P = Bulk case 3 = × 1,000 www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R 5 15 1 KV to 3 KV CONSTRUCTION The capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. This structure gives rise to a high capacitance per unit volume. The inner electrodes are connected to the two end terminations and finally covered with a layer of plated tin (NiSn). The terminations are lead-free. A cross section of the structure is shown in Fig.1. terminations electrodes MLB457 ceramic material Fig. 1 Surface mounted multilayer ceramic capacitor construction DIMENSION Table 1 For outlines see fig. 2 TYPE L1 (mm) W (mm) 0805 2.0 ±0.20 1206 3.2 ±0.30 OUTLINES T (MM) L2 / L3 (mm) L4 (mm) min. max. min. 1.25 ±0.20 0.25 0.75 0.55 1.6 ±0.20 0.25 0.75 1.40 0.25 0.75 1.40 Refer to table 2 to 4 1210 3.2 ±0.30 2.5 ±0.20 1808 4.5 ±0.40 2.0 ±0.30 0.25 0.75 2.20 1812 4.5 ±0.40 3.2 ±0.20 0.25 0.75 2.20 For dimension see Table 1 W T L2 L4 L1 L3 MBB211 Fig. 2 Surface mounted multilayer ceramic capacitor dimension www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R 6 15 1 KV to 3 KV CAPACITANCE RANGE & THICKNESS FOR NP0 Table 2 Sizes from 0805 to 1812 0805 1206 CAP. Last 2-digit of 12NC 10 pF 23 12 pF 24 15 pF 25 18 pF 26 22 pF 27 27 pF 28 33 pF 29 39 pF 31 47 pF 32 56 pF 33 68 pF 34 82 pF 35 100 pF 36 120 pF 37 150 pF 38 180 pF 39 220 pF 41 270 pF 42 330 pF 43 390 pF 44 470 pF 45 560 pF 46 680 pF 47 820 pF 48 1.0 nF 49 1.2 nF 51 1.5 nF 52 1.8 nF 53 2.2 nF 54 2.7 nF 55 3.3 nF 56 1 KV 1 KV 1808 1210 2 KV 1 KV 2 KV 1 KV 1812 2 KV 3 KV 1 KV 2 KV 3 KV 0.85±0.1 1.6±0.2 1.25±0.2 1.25±0.2 1.25±0.2 1.25±0.2 1.25±0.2 1.25±0.2 1.25±0.2 1.25±0.2 1.25±0.2 2.0±0.2 NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-12 series is on request www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R 7 15 1 KV to 3 KV CAPACITANCE RANGE & THICKNESS FOR X7R Table 3 Sizes from 0805 to 1812 CAP. Last 2-digit of 12NC 100 pF 09 150 pF 12 220 pF 14 330 pF 16 470 pF 18 680 pF 21 1.0 nF 23 1.5 nF 25 2.2 nF 27 3.3 nF 29 4.7 nF 32 6.8 nF 34 10 nF 36 15 nF 38 22 nF 41 33 nF 43 47 nF 45 68 nF 47 100 nF 49 0805 1206 1 KV 1 KV 1808 1210 2 KV 1 KV 2 KV 1 KV 1812 2 KV 3 KV 1 KV 2 KV 3 KV 1.6±0.2 0.85±0.1 1.25±0.2 1.35±0.15 1.25±0.2 1.25±0.2 1.35±0.15 1.6±0.2 2.0±0.2 1.35±0.15 1.6±0.2 1.25±0.2 1.35±0.15 1.6±0.2 1.6±0.2 2.0±0.2 1.6±0.2 1.6±0.2 NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-6 series is on request 3. For products with 5% tolerance, please contact local sales force before ordering www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R 1 KV to 3 KV 8 15 THICKNESS CLASSES AND PACKING QUANTITY Table 5 SIZE CODE THICKNESS CLASSIFICATION TAPE WIDTH QUANTITY PER REEL 0201 0.3 ±0.03 mm 0402 0603 0805 1206 Ø180 MM / 7 INCH Ø330 MM / 13 INCH Paper Blister Paper Blister QUANTITY PER BULK CASE 8 mm 15,000 --- 50,000 --- --- 0.5 ±0.05 mm 8 mm 10,000 --- 50,000 --- 50,000 0.8 ±0.1 mm 8 mm 4,000 --- 15,000 --- 15,000 0.6 ±0.1 mm 8 mm 4,000 --- 20,000 --- 10,000 0.8 / 0.85 ±0.1 mm 8 mm 4,000 --- 15,000 --- 8,000 1.00 ±0.1 mm 8 mm --- 3,000 --- 10,000 --- 1.25 ±0.2 mm 8 mm --- 3,000 --- 10,000 5,000 0.6 ±0.1 mm 8 mm 4,000 --- 20,000 --- --- 0.8 / 0.85 ±0.1 mm 8 mm 4,000 --- 15,000 --- --- 1.00 / 1.15 ±0.1 mm 8 mm --- 3,000 --- 10,000 --- 1.25 ±0.2 mm 8 mm --- 3,000 --- 10,000 --- 1.6 ±0.15 mm 8 mm --- 2,500 --- 10,000 --- 1.6 ±0.2 mm 8 mm --- 2,000 --- 8,000 --- 0.6 / 0.7 ±0.1 mm 8 mm --- 4,000 --- 15,000 --- 0.85 ±0.1 mm 8 mm --- 4,000 --- 10,000 --- 1.15 ±0.1 mm 8 mm --- 3,000 --- 10,000 --- 1.15 ±0.15 mm 8 mm --- 3,000 --- 10,000 --- 1.25 ±0.2 mm 8 mm --- 3,000 --- --- --- 1.5 ±0.1 mm 8 mm --- 2,000 --- --- --- 1.6 / 1.9 ±0.2 mm 8 mm --- 2,000 --- --- --- 2.0 ±0.2 mm 8 mm --- 2,000 1,000 --- --- --- 2.5 ±0.2 mm 8 mm --- 1,000 500 --- --- --- 1.15 ±0.15 mm 12 mm --- 3,000 --- --- --- 1.25 ±0.2 mm 12 mm --- 3,000 --- --- --- 1.35 ±0.15 mm 12 mm --- 2,000 --- --- --- 1.5 ±0.1 mm 12 mm --- 2,000 --- --- --- 1.6 ±0.2 mm 12 mm --- 2,000 --- --- --- 1210 1808 2.0 ±0.2 mm 12 mm --- 2,000 --- --- --- 0.6 / 0.85 ±0.1 mm 12 mm --- 2,000 --- --- --- 1.15 ±0.1 mm 12 mm --- 1,000 --- --- --- 1.15 ±0.15 mm 12 mm --- 1,000 --- --- --- 1.25 ±0.2 mm 12 mm --- 1,000 --- --- --- 1.35 ±0.15 mm 12 mm --- 1,000 --- --- --- 1.5 ±0.1 mm 12 mm --- 1,000 --- --- --- 1.6 ±0.2 mm 12 mm --- 1,000 --- --- --- 2.0 ±0.2 mm 12 mm --- 1,000 --- --- --- 2.5 ±0.2 mm 12 mm --- 500 --- --- --- 1812 www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R 9 15 1 KV to 3 KV ELECTRICAL CHARACTERISTICS NP0/X7R DIELECTRIC CAPACITORS; NISN TERMINATIONS Unless otherwise stated all electrical values apply at an ambient temperature of 20±1 °C, an atmospheric pressure of 86 to 106 kPa, and a relative humidity of 63 to 67%. Table 6 VALUE DESCRIPTION Capacitance range 10 pF to 33 nF Capacitance tolerance NP0 C < 10 pF ±0.25 pF, ±0.5 pF C ≥ 10 pF ±2%, ±5% X7R ±5% (1), ±10% Dissipation factor (D.F.) NP0 C < 30 pF ≤ 1 / ( 400 + 20C ) C ≥ 30 pF ≤ 0.1 % X7R Insulation resistance after 1 minute at Ur (DC) ≤ 2.5 % Rins ≥ 10 GΩ or Rins × C ≥ 500 seconds whichever is less Maximum capacitance change as a function of temperature (temperature characteristic/coefficient): NP0 ±30 ppm/°C X7R ±15% Operating temperature range: NP0/X7R –55 °C to +125 °C NOTE 1. ±5% tolerance of capacitance value isn't available for X7R full product range, please contact local sales force before ordering www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R 10 15 1 KV to 3 KV HIGH - VOLTAGE NP0 Sample limits (broken lines). Requirement levels (dotted lines) MEA607 CCA044 10 tan δ (× 10−4) 40 TC (x10 6/K) 7.5 20 5 0 20 2.5 40 0 40 0 40 80 120 T ( oC) Fig. 3 Typical temperature coefficient as a function of temperature −40 0 40 80 120 T (oC) Fig. 4 Typical tan δ as a function of temperature HIGH - VOLTAGE X7R ΔC C (%) YNM0013 15 YNM0041 300 tan δ (× 10−4) 10 200 5 1 KV product 0 2 KV product 100 −5 3 KV product −10 −15 −55 0 −25 5 40 65 95 125 T (oC) Fig. 5 Typical capacitance change as a function of temperature −40 0 40 80 120 T (°C) Fig. 6 Typical tan δ as a function of temperature www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R 11 15 1 KV to 3 KV SOLDERING RECOMMENDATION Table 7 SOLDERING METHOD SIZE 0402 0603 0805 1206 ≥ 1210 Reflow ≥ 0.1 µF ≥ 1.0 µF ≥ 2.2 µF ≥ 4.7 µF Reflow only Reflow/Wave < 0.1 µF < 1.0 µF < 2.2 µF < 4.7 µF --- TESTS AND REQUIREMENTS Table 8 Test procedures and requirements TEST TEST METHOD PROCEDURE REQUIREMENTS Mounting IEC 6038421/22 4.3 The capacitors may be mounted on printed-circuit boards or ceramic substrates No visible damage Visual Inspection and Dimension Check 4.4 Any applicable method using × 10 magnification In accordance with specification Capacitance 4.5.1 Class 1: f = 1 MHz for C ≤ 1 nF, measuring at voltage 1 Vrms at 20 °C Within specified tolerance f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C Class 2: f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C Dissipation Factor (D.F.) 4.5.2 Class 1: f = 1 MHz for C ≤ 1 nF , measuring at voltage 1 Vrms at 20 °C In accordance with specification f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C Class 2: f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C Insulation Resistance 4.5.3 Temperature Coefficient 4.6 Temperature Characteristic Ur ≤ 500 V: At Ur for 1 minute In accordance with specification Ur > 500 V: At 500 V for 1 minute Class 1: Between minimum and maximum temperature NP0: -55 °C to +125 °C Normal Temperature: 20 °C C/C: Class 2: Between minimum and maximum temperature X7R: -55 °C to +125 °C Normal Temperature: 20 °C Class 2 X7R: ±15% Class 1: NP0: ±30 ppm/°C www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R TEST TEST METHOD PROCEDURE REQUIREMENTS Adhesion IEC 6038421/22 4.7 A force applied for 10 seconds to the line joining the terminations and in a plane parallel to the substrate Force size ≥ 0603: 5N 4.8 Mounting in accordance with IEC 60384-22 paragraph 4.3 No visible damage Conditions: bending 1 mm at a rate of 1 mm/s, radius jig 340 mm ∆C/C Bond Strength of Plating on End Face 12 15 1 KV to 3 KV Class 1: NP0: within ±1% or 0.5 pF, whichever is greater Class2: X7R: ±10% Resistance to Soldering Heat 4.9 Precondition: 150 +0/–10 °C for 1 hour, then keep for 24 ±1 hours at room temperature Preheating: for size ≤ 1206: 120 °C to 150 °C for 1 minute Preheating: for size >1206: 100 °C to 120 °C for 1 minute and 170 °C to 200 °C for 1 minute Solder bath temperature: 260 ±5 °C Dipping time: 10 ±0.5 seconds Recovery time: 24 ±2 hours Dissolution of the end face plating shall not exceed 25% of the length of the edge concerned ∆C/C Class 1: NP0: within ±0.5% or 0.5 pF, whichever is greater Class2: X7R: ±10% D.F. within initial specified value Rins within initial specified value Solderability 4.10 Preheated to a temperature of 80 °C to 140 °C and maintained for 30 seconds to 60 seconds. The solder should cover over 95% of the critical area of each termination 1. Temperature: 235±5°C / Dipping time: 2 ±0.5 s 2. Temperature: 245±5°C / Dipping time: 3 ±0.5 s (lead free)Depth of immersion: 10mm www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R TEST TEST METHOD PROCEDURE REQUIREMENTS Rapid Change of Temperature IEC 6038421/22 Preconditioning; 150 +0/–10 °C for 1 hour, then keep for 24 ±1 hours at room temperature No visual damage 4.11 5 cycles with following detail: 30 minutes at lower category temperature 30 minutes at upper category temperature Recovery time 24 ±2 hours 13 15 1 KV to 3 KV ∆C/C Class 1: NP0: within ±1% or 1 pF, whichever is greater Class2: X7R: ±15% D.F. meet initial specified value Rins meet initial specified value Damp Heat 4.13 1. Preconditioning, class 2 only: 150 +0/-10 °C /1 hour, then keep for 24 ±1 hour at room temp 2. Initial measure: Spec: refer to initial spec C, D, IR 3. Damp heat test: 500 ±12 hours at 40 ±2 °C; 90 to 95% R.H. 4. Recovery: Class 1: 6 to 24 hours Class 2: 24 ±2 hours 5. Final measure: C, D, IR P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be preconditioned according to “IEC 60384 4.1” and then the requirement shall be met. No visual damage after recovery ∆C/C Class 1: NP0: within ±2% or 1 pF, whichever is greater Class2: X7R: ±15% D.F. Class 1: NP0: ≤ 2 x specified value Class2: X7R: ≥ 25 V: ≤ 5% Rins Class 1: NP0: ≥ 2,500 MΩ or Rins x Cr ≥ 25s whichever is less Class2: X7R: ≥ 500 MΩ or Rins x Cr ≥ 25s whichever is less www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R TEST TEST METHOD PROCEDURE REQUIREMENTS Endurance IEC 6038421/22 1. Preconditioning, class 2 only: No visual damage 4.14 150 +0/-10 °C /1 hour, then keep for 24 ±1 hour at room temp 2. Initial measure: Spec: refer to initial spec C, D, IR 3. Endurance test: Temperature: NP0/X7R: 125 °C Specified stress voltage applied for 1,000 hours. High-Voltage series follows the stress conditions below: Applied 2.0 x Ur for < 500 V series Applied 1.3 x Ur for 500 V, 630 V series Applied 1.2 x Ur for 1 KV, 2 KV, 3 KV series 4. Recovery time: 24 ±2 hours 5. Final measure: C, D, IR P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be preconditioned according to “IEC 60384 4.1” and then the requirement shall be met. Voltage Proof IEC 60384-1 4.6 Specified stress voltage applied for 1 minute Ur ≤ 100 V: series applied 2.5 Ur 100 V < Ur ≤ 200 V series applied (1.5 Ur + 100) 200 V < Ur ≤ 500 V series applied (1.3 Ur + 100) Ur > 500 V: 1.3 Ur I: 7.5 mA 14 15 1 KV to 3 KV ∆C/C Class1: NP0: within ±2% or 1 pF, whichever is greater Class2: X7R: ±15% D.F. Class1: NP0: ≤ 2 x specified value Class2: X7R: ≥ 25 V: ≤ 5% Rins Class1: NP0: ≥ 4,000 MΩ or Rins x Cr ≥ 40s whichever is less Class2: X7R: ≥ 1,000 MΩ or Rins x Cr ≥ 50s whichever is less No breakdown or flashover www.yageo.com Dec. 19, 2012 V.6 Product specification Surface-Mount Ceramic Multilayer Capacitors High-Voltage NP0/X7R 15 15 1 KV to 3 KV REVISION HISTORY REVISION DATE CHANGE NOTIFICATION DESCRIPTION Version 6 Dec. 19, 2012 - - Product range updated Version 5 Sep 25, 2012 - - Product range updated Version 4 Aug 08, 2011 - - Product range updated Version 3 Jan 19, 2011 - - Dimension updated - Add NP0 0805 1KV Version 2 Feb 02, 2010 - - Change to dual brand datasheet that describe High-Voltage NP0/X7R series with RoHS compliant - Replace the high voltage part of pdf files: UP-NP0X7R_HV_1K-to-4KV_1 and UY-NP0X7R_HV_1K-to-4KV_1 - Description of "Halogen Free compliant" added - Product range updated - Define global part number - Test method and procedure updated Version 1 Sep 30, 2005 - - Thickness revised Version 0 Sep 12, 2005 - - New www.yageo.com Dec. 19, 2012 V.6