KOA SPEER ELECTRONICS, INC. SS-224 R5 AHA 10/27/04 Multilayer Ferrite Chip Bead Array Type FBA CERTIFIED 1. Scope of Application Noise suppression in signal I/O lines and other circuits that require multiple chip beads for noise suppression. 1.1 Applications ■ ■ ■ Computers Peripherals ■ Telecommunications equipment Data communications 2. Features The Multilayer Ferrite Chip Bead Array retains all the features of Multilayer Ferrite Chip Beads. In addition, it provides multiple circuits in a single package, which reduce the required land space on PCB and reduce the cost for assembly. 3. Dimension and Structure a L p b W t Protective Coating Solder Plating Type (Inch Size Code) L W 1J (0603) .126±.008 (3.2±0.2) .063±.008 (1.6±0.2) Dimensions inches (mm) t a .031±.008 (0.8±0.2) .014±.008 (0.35±0.2) b p .012±.008 (0.3±0.2) .031±.008 (0.8±0.2) 3.1 Circuit PAGE 1 OF 8 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use. KOA SPEER ELECTRONICS, INC. SS-224 R5 4. Ordering and Specifying Information* FBA 1J 4 A T TE 300 P Type Size Circuits Characteristics Termination Material Packaging Impedance Tolerance 1J (0603) Number of Circuits A: Standard B: High Speed T: Sn L: SnPb TE: 7" Embossed Plastic 3000 pcs/reel 2 significant figure + 1 multipler Ex: 300 = 30Ω P: ±25% * Please note: KSE’s part numbers do not contain any spaces or hyphens. 5. Standard Applications Impedance @ 100MHz Ω Maximum DC Resistance Ω Allowable DC Current (mA) FBA1J4ATE300P FBA1J4ATE600P FBA1J4ATE121P FBA1J4ATE221P FBA1J4ATE301P FBA1J4ATE601P 30 60 120 220 300 600 0.1 0.25 0.3 0.3 0.4 0.5 200 400 350 250 250 100 FBA1J4ATE102P 1,000 0.7 200 FBA1J4BTE100P FBA1J4BTE220P 10 22 0.15 0.25 200 200 FBA1J4BTE470P FBA1J4BTE600P FBA1J4BTE121P FBA1J4BTE221P FBA1J4BTE471P 47 60 120 220 470 0.3 0.3 0.5 0.55 0.55 150 350 100 100 100 FBA1J4BTE601P 600 0.65 100 Ordering Code Operating Temperature -55°C to 125°C PAGE 2 OF 8 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use. KOA SPEER ELECTRONICS, INC. SS-224 R5 6. Graphs* * Bolivar Drive |Z| XL R ■ P.O. Box 547 PAGE 3 OF 8 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use. KOA SPEER ELECTRONICS, INC. SS-224 R5 6. Graphs* (continued) * Bolivar Drive |Z| XL R ■ P.O. Box 547 PAGE 4 OF 8 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use. KOA SPEER ELECTRONICS, INC. SS-224 R5 6. Graphs* (continued) * Bolivar Drive |Z| XL R ■ P.O. Box 547 PAGE 5 OF 8 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use. KOA SPEER ELECTRONICS, INC. SS-224 R5 6. Packaging Specifications KOA’s multilayer components are provided on tape-and-reel for use in pick-and-place machines. The reel size is 7 inch. 7. Dimensions - inches (mm) Do Tape 1J4 Ao Bo Ko P2 Po t E 0.071±0.002 0.138±0.002 0.048±0.002 (1.8±0.1) (3.5±0.1) (1.2±0.1) W F Bo Tape 1J4 E W 0.069±0.004 0.138±0.002 0.318±0.002 (1.75±0.10) (3.50±.005) (8.1±0.1) Tape 1J4 F P1 Po P2 D1 Do D1 0.157±0.004 0.157±0.004 0.079±0.002 0.059±0.004 0.039 min. (4.0±0.1) (4.0±0.1) (2.00±0.05) (1.5+0.1/-0.0) (1.0 min.) Ao P1 Ko t 0.009±0.001 (0.23±0.02) 8. Chip Quantities Per Reel Chip Size Parts on 7 inch (178mm) Reel 1J4 3,000 9. Characteristics Item Requirement Conditions Operating Temperature -55°C ~ +125°C Storage Temperature 40°C @ 70% Humidity Sealed plastic bags with desiccant shall be used to reduce the potential of oxidation on the terminations during storage. Resistance to Solder Heat Change in Impedance: Relative to value before test ±20%. Appearance: There shall be no cracking Solder Coverage: More than 75% of the terminal electrode shall be covered with solder. Flux: 5-10 sec dip After Flux: Air dry for 15 sec Preheat: 150°C ±10°C Preheat Time: 60 sec Solder Temp: 260°C ±5°C Dip Time: 10 ±1 sec PAGE 6 OF 8 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use. KOA SPEER ELECTRONICS, INC. SS-224 R5 9. Characteristics (continued) Item Requirement Conditions Solderability Solder Coverage: More than 95% of the termination shall be covered with solder. Flux: 5-10 sec dip After Flux: Air dry for 15 sec Solder Temp: 245°C ±5°C Dip Time: 5 ±0.5 sec Leach Resistance Appearance: There shall be no visible signs of physical or mechanical damage (i.e. no cracks) Terminations: Termination must not be leached away for more than 5%. The bead shall be subjected to the following 5 steps for the period of time shown below. The 5 steps constitute one (1) rotation. 4 rotations shall be carried out. 1) Flux: 5-10 sec 2) After Flux: Air dry for 15 sec 3) Solder Temp: 230°C ±5°C 4) Dip Time: 5 ±0.5 sec 5) Cool: Air cool for 60 seconds Insulation Resistance Insulation Resistance: Min 1G ohms Solvent Resistance Change in Impedance: Relative to value before test ±10%. Terminal Strength (hanging test) Appearance: The terminal electrode shall not break off, nor shall there be damage to the body. Type 1206 W(kgf) 1.5 Time 30 sec ±2 sec Terminal Strength (push test) Appearance: There shall be no evidence of mechanical degradations to terminals or body. Type 1206 W(kgf) 2.3 Time 60 sec Bending Strength Appearance: There shall be no physical or mechanical damage Impedance: Relative to initial value before test ±10% Board: 90x40x1.6mm Bend: 1mm Time: 5 sec Mechanical Shock Appearance: There shall be no physical or mechanical damage Impedance: Relative to initial value before test ±10% Force: 50G Time: 11 msec There shall be 3 shocks in each of 6 directions (18 shocks total). Vibration Impedance: Relative to initial value ±10% Only endurance conditioning by sweeping shall be made. The entire frequency range from 10-2,000Hz and return to 10Hz in 20 minutes (this shall constitute one cycle). Amplitude: 1.5mm The test shall have a 15G peak and shall be applied for a period of 4 hours (12 cycles) in each of 3 mutually perpendicular directions (a total of 36 cycles within a total of 12 hours). Cleaning by: Washer: Ultrasonic washer (100W) Solvent: Isopropyl alcohol Time: 3 minutes PAGE 7 OF 8 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use. KOA SPEER ELECTRONICS, INC. SS-224 R5 9. Characteristics (continued) Item Requirement Conditions Thermal Shock Appearance: There shall be no physical or mechanical damage. Impedance: Relative to initial value ±20%. DCR: The DCR shall not exceed initial specified value. Testing of the parts will be made at 0 hours, 250 hours and 500 hours. Before testing the parts shall be allowed to cool to room temperature for 24 hours. Load Humidity Appearance: There shall be no physical or mechanical damage Impedance: Relative to initial value ±15% Step 1-start 2-hold 3-transfer 4-hold 5-transfer Temperature -40°C ±2°C -40°C ±2°C — +105°C ±2°C — Time — 30 min ±5 min 0.5 min max. 30 min ±5 min 0.5 min max. Steps 1 thru 5 constitute one complete cycle and the test shall consist of a total of 500 cycles. Temperature: 85°C ±2°C Relative Humidity: 85% Time: 1,000 hours total Apply: 100% rated current Measurements shall be taken at 0 hours, 250 hours, 500 hours and 1,000 hours and shall meet the conditions stated above. Life Test Appearance: There shall be no physical or mechanical damage Impedance: Relative to initial value ±15% Temperature: 85°C ±2°C Time: 1,000 hours total Apply: 100% rated current Measurements shall be taken at 0 hours, 250 hours, 500 hours and 1,000 hours and shall meet the conditions stated above. 10. Recommended PC Board Land Patterns - inches (mm) Chip Component Size Size L W Soldering Pad B W A Chip Component 1206 (3216) .126 (3.2) .063 (1.6) A B C E .030 .120 .016 .031 (0.762) (3.048) (0.406) (0.787) E C L PAGE 8 OF 8 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Specifications given herein may be changed at any time without prior notice. Please confirm technical specifications before you order and/or use.