SS-223 R9 12/6/06 11:26 AM Page 1 SS-223 R9 AHA 12/06/06 Multi Layer Ferrite Inductors Type MCL CERTIFIED CERTIFIED 1. General ■ Nickel barrier with solder overcoat for excellent solderability ■ Magnetically shielded ■ Monolithic structure for closed magnetic path eliminates crosstalk and provides high reliability in a wide range of temperature and humidity ranges ■ Standard EIA packages: 1J, 2A, 2B 2. 2.1 Dimensions W L Solder Plating Ni Plating Silver Metallization t d Terminations (Metallization Bands) d Size Code L W t d 1J (0603) .063±.006 (1.6±0.15) .031±.006 (0.8±0.15) .031±.006 (0.8±0.15) .014±.006 (0.36±0.15) 2A (0805) .079±.008 (2.0±0.2) .049±.008 (1.25±0.2) .035±.008 (0.9±0.2) .02±.01 (0.51±0.25) 2B (1206) .126±.008 (3.2±0.2) .063±.008 (1.6±0.2) .043±.008 (1.1±0.2) .02±.01 (0.51±0.25) Electrodes 3. Ordering and Specifying Information* MCL 1J H T TE R10 J Type Size Material Termination Material Packaging Nominal Inductance Tolerance 1J 2A 2B Permeability Code: H J T: Sn (Other termination styles available, contact factory for options) TD: 7" Paper Tape (1J - 4,000 pcs/reel; 2A - 0.047µH - 2.2µH = 4,000 pcs/reel) TE: 7" Embossed Plastic (2A - 2.7µH - 10µH = 3,000 pcs/reel; 2B - 3,000 pcs/reel) 047 = .047µH R10 = .100µH K: ±10% M: ±20% Allowable DC Current Maximum (mA) Operating Temperature Range * Please note: KSE’s part numbers do not contain any spaces or hyphens. 4. Standard Applications Part Designation Inductance L (µH) MCL1JHTTD047M MCL1JHTTD068M MCL1JHTTD082M MCL1JHTTDR10* MCL1JHTTDR12* MCL1JHTTDR15* MCL1JHTTDR18* MCL1JHTTDR22* MCL1JHTTDR27* 0.047 0.068 0.082 0.10 0.12 0.15 0.18 0.22 0.27 Minimum Q L.Q. Test Frequency (MHz) 10 50 15 Self Resonant Frequency Typical (MHz) 260 250 245 240 205 180 165 150 136 25 DC Resistance Maximum (Ω) 0.30 0.50 50 0.60 0.80 * Add tolerance character (K, M) - Other tolerances available upon request Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ -55°C to +125°C PAGE 1 OF 6 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Spec ific ation s g iven herein m ay be cha nged a t any tim e w itho ut pr ior not ice. Pleas e c onf ir m te chnic al s pec if ica tions before you order an d/or u se. SS-223 R9 12/6/06 11:26 AM Page 2 SS-223 R9 4. Standard Applications (continued) Part Designation Inductance L (µH) MCL1JHTTDR33* MCL1JHTTDR39* MCL1JHTTDR47* MCL1JHTTDR56* MCL1JHTTDR68* MCL1JHTTDR82* MCL1JJTTD1R0* MCL1JJTTD1R2* MCL1JJTTD1R5* MCL1JJTTD1R8* MCL1JJTTD2R2* MCL1JJTTD2R7* MCL1JJTTD3R3* MCL1JJTTD3R9* MCL1JJTTD4R7* MCL1JJTTD5R6* MCL1JJTTD6R8* MCL1JJTTD8R2* MCL1JJTTD100* MCL1JJTTD120* MCL2AHTTD047M MCL2AHTTD068M MCL2AHTTD082M MCL2AHTTDR10* MCL2AHTTDR12* MCL2AHTTDR15* MCL2AHTTDR18* MCL2AHTTDR22* MCL2AHTTDR27* MCL2AHTTDR33* MCL2AHTTDR39* MCL2AHTTDR47* MCL2AHTTDR56* MCL2AHTTDR68* MCL2AHTTDR82* MCL2AJTTD1R0* MCL2AJTTD1R2* MCL2AJTTD1R5* MCL2AJTTD1R8* MCL2AJTTD2R2* MCL2AJTTE2R7* MCL2AJTTE3R3* MCL2AJTTE3R9* MCL2AJTTE4R7* 0.33 0.39 0.47 0.56 0.68 0.82 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 0.047 0.068 0.082 0.10 0.12 0.15 0.18 0.22 0.27 0.33 0.39 0.47 0.56 0.68 0.82 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 Minimum Q L.Q. Test Frequency (MHz) 15 25 Self Resonant Frequency Typical (MHz) 125 110 105 95 90 85 75 65 60 55 50 45 40 35 33 22 20 18 17 15 320 280 255 235 220 200 185 170 150 145 135 125 115 105 100 75 65 60 55 50 45 41 38 35 10 35 4 30 2 15 50 20 25 25 45 10 DC Resistance Maximum (Ω) 0.85 1.00 1.35 1.55 1.70 2.10 0.60 Allowable DC Current Maximum (mA) 0.80 25 0.95 1.15 1.35 1.55 1.70 2.10 1.55 1.70 2.10 1.85 2.10 0.20 Operating Temperature Range 35 -55°C to +125°C 15 5 3 300 0.30 0.40 250 0.50 0.55 0.65 0.75 0.80 1.00 0.40 0.50 0.60 0.65 0.75 0.80 0.90 1.00 200 150 -55°C to +125°C 50 30 * Add tolerance character (K, M) - Other tolerances available upon request PAGE 2 OF 6 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Spec ific ation s g iven herein m ay be cha nged a t any tim e w itho ut pr ior not ice. Pleas e c onf ir m te chnic al s pec if ica tions before you order an d/or u se. SS-223 R9 12/6/06 11:26 AM Page 3 SS-223 R9 4. Standard Applications (continued) Part Designation Inductance L (µH) MCL2AJTTE5R6* MCL2AJTTE6R8* MCL2AJTTE8R2* MCL2AJTTE100* MCL2BHTTE047M MCL2BHTTE068M MCL2BHTTER10* MCL2BHTTER12* MCL2BHTTER15* MCL2BHTTER18* MCL2BHTTER22* MCL2BHTTER27* MCL2BHTTER33* MCL2BHTTER39* MCL2BHTTER47* MCL2BHTTER56* MCL2BHTTER68* MCL2BHTTER82* MCL2BJTTE1R0* MCL2BJTTE1R2* MCL2BJTTE1R5* MCL2BJTTE1R8* MCL2BJTTE2R2* MCL2BJTTE2R7* MCL2BJTTE3R3* MCL2BJTTE3R9* MCL2BJTTE4R7* MCL2BJTTE5R6* MCL2BJTTE6R8* MCL2BJTTE8R2* MCL2BJTTE100* MCL2BJTTE120* MCL2BJTTE150* MCL2BJTTE180* 5.6 6.8 8.2 10 0.047 0.068 0.10 0.12 0.15 0.18 0.22 0.27 0.33 0.39 0.47 0.56 0.68 0.82 1.0 1.2 1.5 1.8 2.2 2.7 3.3 3.9 4.7 5.6 6.8 8.2 10 12 15 18 MCL2BJTTE220* MCL2BJTTE270* MCL2BJTTE330* Minimum Q Self Resonant Frequency Typical (MHz) 32 29 26 24 320 280 235 220 200 185 170 150 145 135 125 115 105 100 75 65 60 55 50 45 41 38 35 32 29 26 24 22 19 18 L.Q. Test Frequency (MHz) 4 50 2 50 20 25 25 45 10 4 50 2 22 27 33 1 30 DC Resistance Maximum (Ω) 0.90 1.00 1.10 1.15 0.15 15 Operating Temperature Range -55°C to +125°C 300 0.25 0.30 0.40 0.50 0.60 0.50 0.60 0.70 0.80 0.90 0.40 250 200 150 100 0.50 -55°C to +125°C 0.60 50 0.70 0.80 0.85 0.90 1.00 1.05 25 15 0.70 16 14 13 0.4 Allowable DC Current Maximum (mA) 0.90 5 1.05 * Add tolerance character (K, M) - Other tolerances available upon request PAGE 3 OF 6 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Spe cific at io ns g ive n herein m ay be ch anged a t any tim e w ith out p rior not ice. Pleas e c onf ir m t echn ic al s pec ifica tions before you order an d/or u se. SS-223 R9 12/6/06 11:26 AM Page 4 SS-223 R9 5. Characteristics Item Requirement Conditions Operating Temperature -25°C ~ +85°C Storage Temperature 40°C @ 70% Humidity Sealed plastic bags with desiccant shall be used to reduce the potential of oxidation on the terminations during storage. Resistance to Solder Heat Change in Inductance: Relative to value before test ±20%. Appearance: There shall be no cracking Solder Coverage: More than 75% of the terminal electrode shall be covered with solder. Flux: 5-10 sec dip After Flux: Air dry for 15 sec Preheat: 150°C ±10°C Preheat Time: 60 sec Solder Temp: 260°C ±5°C Dip Time: 10 ±1 sec Solderability Solder Coverage: More than 95% of the termination shall be covered with solder. Flux: 5-10 sec dip After Flux: Air dry for 15 sec Solder Temp: 245°C ±5°C Dip Time: 5 ±0.5 sec Leach Resistance Appearance: There shall be no visible signs of physical or mechanical damage (i.e. no cracks) Terminations: Termination must not be leached away for more than 5%. The bead shall be subjected to the following 5 steps for the period of time shown below. The 5 steps constitute one (1) rotation. 4 rotations shall be carried out. 1) Flux: 5-10 sec 2) After Flux: Air dry for 15 sec 3) Solder Temp: 230°C ±5°C 4) Dip Time: 5 ±0.5 sec 5) Cool: Air cool for 60 seconds Insulation Resistance Insulation Resistance: Min 1G ohms Solvent Resistance Change in Inductance: Relative to value before test ±10%. Terminal Strength (hanging test) Appearance: The terminal electrode shall not break off, nor shall there be damage to the body. Type 1J (0603) 2A (0805) 2B (1206) W(kgf) 0.5 1.0 1.5 Time 30 sec ±2 sec 30 sec ±2 sec 30 sec ±2 sec Terminal Strength (push test) Appearance: There shall be no evidence of mechanical degradations to terminals or body. Type 1J (0603) 2A (0805) 2B (1206) W(kgf) 1.4 1.8 2.3 Time 60 sec 60 sec 60 sec Bending Strength Appearance: There shall be no physical or mechanical damage Inductance: Relative to initial value before test ±10% Cleaning by: Washer: Ultrasonic washer (100W) Solvent: Isopropyl alcohol Time: 3 minutes Board: 90x40x1.6mm Bend: 1mm Time: 5 sec PAGE 4 OF 6 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Spec ific ation s g iven herein m ay be cha nged a t any tim e w itho ut pr ior not ice. Pleas e c onf ir m te chnic al s pec if ica tions before you order an d/or u se. SS-223 R9 12/6/06 11:26 AM Page 5 SS-223 R9 5. Characteristics (continued) Item Requirement Conditions Mechanical Shock Appearance: There shall be no physical or mechanical damage Inductance: Relative to initial value before test ±10% Force: 50G Time: 11 msec There shall be 3 shocks in each of 6 directions (18 shocks total). Vibration Inductance: Relative to initial value ±10% Only endurance conditioning by sweeping shall be made. The entire frequency range from 10-2,000 Hz and return to 10 Hz in 20 minutes (this shall constitute one cycle). Amplitude: 1.5mm The test shall have a 15G peak and shall be applied for a period of 4 hours (12 cycles) in each of 3 mutually perpendicular directions (a total of 36 cycles within a total of 12 hours). Thermal Shock Appearance: There shall be no physical or mechanical damage. Inductance: Relative to initial value ±20%. DCR: The DCR shall not exceed initial specified value. Testing of the parts will be made at 0 hours, 250 hours and 500 hours. Before testing the parts shall be allowed to cool to room temperature for 24 hours. Load Humidity Appearance: There shall be no physical or mechanical damage Inductance: Relative to initial value ±15% Step 1-start 2-hold 3-transfer 4-hold 5-transfer Temperature -40°C ±2°C -40°C ±2°C — +105°C ±2°C — Time — 30 min ±5 min 0.5 min max. 30 min ±5 min 0.5 min max. Steps 1 thru 5 constitute one complete cycle and the test shall consist of a total of 500 cycles. Temperature: 85°C ±2°C Relative Humidity: 85% Time: 1,000 hours total Apply: 100% rated current Measurements shall be taken at 0 hours, 250 hours, 500 hours and 1,000 hours and shall meet the conditions stated above. Life Test Appearance: There shall be no physical or mechanical damage Inductance: Relative to initial value ±15% Temperature: 85°C ±2°C Time: 1,000 hours total Apply: 100% rated current Measurements shall be taken at 0 hours, 250 hours, 500 hours and 1,000 hours and shall meet the conditions stated above. 6. Packaging Specifications KOA’s multi layer components are provided on tape-and-reel for use in pick-and-place machines. The reel size is 7 inch. PAGE 5 OF 6 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Spec ific ation s g iven herein m ay be cha nged a t any tim e w itho ut pr ior not ice. Pleas e c onf ir m te chnic al s pec if ica tions before you order an d/or u se. SS-223 R9 12/6/06 11:26 AM Page 6 SS-223 R9 7. Dimensions - inches (mm) Tape Ao Bo Do Ko 2A 0.063±0.002 0.093±0.002 0.046±0.002 (1.6±0.1) (2.4±0.1) (1.2±0.1) 2B 0.071±0.002 0.138±0.002 0.048±0.002 (1.8±0.1) (3.5±0.1) (1.2±0.1) F W Bo D1 Tape 1J 2A 2B E F t E 0.043±0.002 0.075±0.002 0.043±0.002 (1.1±0.1) (1.9±0.1) (1.1±0.1) 1J P2 Po W P1 Ao P1 Po P2 Do Ko D1 0.069±0.004 0.138±0.002 0.318±0.002 0.157±0.004 0.157±0.004 0.079±0.002 0.059±0.004 0.039 min. (1.75±0.10) (3.50±.005) (8.1±0.1) (4.0±0.1) (4.0±0.1) (2.00±0.05) (1.5+0.1/-0.0) (1.0 min.) Parts on 7 inch (178mm) Reel 1J 4,000 2A * 2,000/4,000 2B 3,000 0.009±0.001 (0.23±0.02) 9. Recommended PC Board Land Patterns - inches (mm) 8. Chip Quantities Per Reel Chip Size t Chip Size L G H 1J 0.102 (2.6) 0.022 (0.55) 0.037 (0.94) 2A 0.118 (3.0) 0.026 (0.66) 0.057 (1.45) 2B 0.173 (4.4) 0.059 (1.5) 0.071 (1.8) * MCL0805: 2.7µH ~ 12µH = 2K 0.047µH ~ 2.2µH = 4K H G L 10. Recommended Temperature Profiles for Soldering Recommended Temperature Profile Recommended Temperature Profile forfor Wave Soldering Wave Soldering Preheat 100100 Preheat Seconds Max. Seconds Max. Soldering Soldering 10 Seconds Max. 10 Seconds Max. Recommended Temperature Profile Recommended Temperature Profile forfor Reflow Soldering Reflow Soldering Natural Natural Cooling Cooling Preheat 100100 Preheat Seconds Max. Seconds Max. 250°C 250°C Soldering Soldering 10 Seconds Max. 10 Seconds Max. Natural Natural Cooling Cooling 230°C 230°C 200°C 200°C 150°C 150°C 150°C 150°C 60 Seconds Max. 60 Seconds Max. 20 Seconds Max. 20 Seconds Max. 60 Seconds Max. 60 Seconds Max. PAGE 6 OF 6 Bolivar Drive ■ P.O. Box 547 ■ Bradford, PA 16701 ■ USA ■ 814-362-5536 ■ Fax 814-362-8883 ■ www.koaspeer.com Spec ific ation s g iven herein m ay be cha nged a t any tim e w itho ut pr ior not ice. Pleas e c onf ir m te chnic al s pec if ica tions before you order an d/or u se.