MATERIALS 1. HOUSING : GLASS FILLED POLYESTER UL 94V-0 (BLACK) PHYSICAL ASTM VALUES UNIT TEST RESULTS PROPERTIES TEST METHOD D638 D638 D790 110min 1.5min 7,800 Mpa % Mpa 131 OK 1.6 OK 11,380 OK D256 68min J/M 92 OK MECHANICAL Tensile Strength Elongation Flexural Modulus IMPACT Izod,Notched Thermal Deflection Temperature @1.8Mpa(264psi) D648 degree C 230min 240 OK OTHER Specific Gravity Flammability Rating D792 UL94 ----- 1.69 OK v-0 OK D149 kV/mm(V/mil) 580(22.8) OK @0.8mm(0.032in) ELECTRICAL Dielectric Strength @3.1mm(0.125in) Dielectric Constant D150 3.3/3.3 --3.3 1kHZ / 1MHZ Dissipation Factor D150 1kHZ / 1MHZ 0.003/0.008 OK --0.003/0.080 OK Working Temperature -25°C to +85°C Storage Temperature -40°C to +85°C Note: Measured at 23 degree C. ,D. A KINSUN INDUSTRIES INC. 2. CONTACT : PHOSPHOR BRONZE PROPERTIES STANDARD UNIT TEST RESULTS VALUE Thickness 0.35*0.46 mm 0.35*0.46 40-60 6 80-100 U“ u“ u“ Min 40 6 80 60.5-70.5 11mim Initial max 6.0 Kgf/mm2 % Lbs CONTACT FINISH Underplate Plated Gold In Contact Area Plated Pure Tin On Solder Tail OK max OVER OVER OVER MECHANICAL Tensile Strength Elongation Durability(Total Mating Force) min 5.5 68.3 OK 22.8 GOOD After Durability Test Max 6.7 GOOD min 5.5 GOOD PHYSICAL Hardness High Temperature Life Contact Resistance Insulation Resistance Resistance to Soldering Heat 210-230 250hours/50℃ HV ---- Initial max min 15 1.6 3 5x10 3x103 240℃/ 3-5 seconds milliohm milliohm ---- ELECTRICAL Current Rating Voltage Rating Dielectric Withstanding Voltage Insulation Resistance Contact Resistance max 1.5 max 150 1000 min max Note: Measured at 23 degree C. ,D. A. M. KINSUN INDUSTRIES INC. 500 40 amp volt volts RMS, 60HZ/minute Megohm/500Vdc Milliohm/20mVd c max 221 GOOD Passed Max min 11 1.5 5 5x10 1x105 Meet product spec. Detail dateSee testing record OK OK OK OK OK OK 3. SHIELDED : COPPER ALLOY WITH TIN PLATED SHELL PROPERTIES STANDARD UNIT TEST RESULTS VALUE THICKNESS TIN PLATED SHELL (-)0.10-(+)0.00 mm 0.250 OK 50-80 u“ OVER 50 OK 80-100 u” OVER 80 OK 42.0-52.0 14.0-17.0 kgf/mm % 51.20 16.78 105-175 HV --- % 24.6 OK 64.00-68.00 max. 0.050 max 0.070 REM. % % % % 65.296 0.023 0.013 REM. OK OK OK OK TIN PLATING ON SOLDER TAIL MECHANICAL Tensile Strength Elongation OK OK PHYSICAL Hardness 154.0-157 OK ELECTRICAL Electric Conductirity CHEMICAL Cu Fe Pb Zn Note: Measured at 23 degree C. ,D. A. M. KINSUN INDUSTRIES INC.