FERRITE CERAMICS DATA SHEET E22/6/16/R Planar E cores Product specification Supersedes data of November 1997 File under Ferrite Ceramics, MA01 1999 Dec 23 Philips Components Product specification Planar E cores E22/6/16/R CORES Effective core parameters of an E/PLT combination SYMBOL PARAMETER VALUE UNIT Σ(I/A) core factor (C1) 0.324 mm−1 Ve effective volume 2100 mm3 Ie effective length 26.1 mm Ae effective area 80.4 mm2 Amin minimum area 72.6 mm2 m mass of E core half ≈6.5 g m mass of plate ≈4 g 21.8 ±0.4 16.8 ±0.4 5 ±0.1 andbook, halfpage 3.2 ±0.1 Ordering information for plates GRADE 2.8 +0.2 0 15.8 ±0.3 TYPE NUMBER 3C90 PLT22/16/2.5/S-3C90 3C94 PLT22/16/2.5/S-3C94 3C96 PLT22/16/2.5/S-3C96 3F3 PLT22/16/2.5/S-3F3 3F35 PLT22/16/2.5/S-3F35 3F4 PLT22/16/2.5/S-3F4 3E6 PLT22/16/2.5/S-3E6 4.7 ±0.15 5.7 ±0.1 CBW177 Dimensions in mm. Fig.1 E22/6/16/R. 21.8 ±0.4 2.5 ±0.1 ndbook, halfpage 2.9 ±0.05 15.8 ±0.3 2.9 +0.2 0 CBW178 Dimensions in mm. Fig.2 PLT22/16/2.5/S. 1999 Dec 23 2 Philips Components Product specification Planar E cores E22/6/16/R Core halves for use in combination with a slotted plate (PLT/S) AL measured in combination with a slotted plate (PLT/S) clamping force for AL measurements, 20 ±10 N; measurement coil as for E22/6/16. GRADE 3C90 3C94 3C96 3F3 AL (nH) 160 ±3% AIR GAP (µm) µe ≈42 ≈950 TYPE NUMBER E22/6/R-3C90-A160-P 250 ±3% ≈66 ≈550 E22/6/R-3C90-A250-P 315 ±3% ≈83 ≈400 E22/6/R-3C90-A315-P 400 ±5% ≈106 ≈280 E22/6/R-3C90-A400-P 630 ±8% ≈166 ≈160 E22/6/R-3C90-A630-P 6150 ±25% ≈1620 ≈0 E22/6/16/R-3C90 160 ±3% ≈42 ≈950 E22/6/R-3C94-A160-P 250 ±3% ≈66 ≈550 E22/6/R-3C94-A250-P 315 ±3% ≈83 ≈400 E22/6/R-3C94-A315-P 400 ±5% ≈106 ≈280 E22/6/R-3C94-A400-P 630 ±8% ≈166 ≈160 6150 ±25% ≈1620 ≈0 E22/6/16/R-3C94 5450 ±25% ≈1440 ≈0 E22/6/16/R-3C96 E22/6/R-3C94-A630-P 160 ±3% ≈42 ≈950 E22/6/R-3F3-A160-P 250 ±3% ≈66 ≈550 E22/6/R-3F3-A250-P 315 ±3% ≈83 ≈400 E22/6/R-3F3-A315-P 400 ±5% ≈106 ≈280 E22/6/R-3F3-A400-P 630 ±8% ≈166 ≈160 5000 ±25% ≈1320 ≈0 E22/6/16/R-3F3 3F35 4100 ±25% ≈1080 ≈0 E22/6/16/R-3F35 3F4 160 ±3% ≈42 ≈950 E22/6/R-3F4-A160-P 250 ±3% ≈66 ≈550 E22/6/R-3F4-A250-P 3E6 1999 Dec 23 E22/6/R-3F3-A630-P 315 ±3% ≈83 ≈400 E22/6/R-3F4-A315-P 400 ±5% ≈106 ≈280 E22/6/R-3F4-A400-P 630 ±8% ≈166 ≈160 2900 ±25% ≈770 ≈0 E22/6/16/R-3F4 ≈6900 ≈0 E22/6/16/R-3E6 26000 +40/−30% 3 E22/6/R-3F4-A630-P Philips Components Product specification Planar E cores E22/6/16/R Properties of core sets under power conditions B (mT) at GRADE H = 250 A/m; f = 10 kHz; T = 100 °C CORE LOSS (W) at f = 100 kHz; ˆ = 100 mT; B T = 100 °C f = 100 kHz; ˆ = 200 mT; B T = 100 °C f = 400 kHz; ˆ = 50 mT; B T = 100 °C E18/R+PLT18/S-3C90 ≥320 ≤0.235 − − E18/R+PLT18/S-3C94 ≥320 ≤0.180 ≈0.88 ≈0.39 E18/R+PLT18/S-3C96 ≥320 ≈0.13 ≈0.62 ≈0.28 E18/R+PLT18/S-3F3 ≥300 ≤0.230 − ≤0.40 E18/R+PLT18/S-3F35 ≥300 ≤0.230 − ≈0.20 E18/R+PLT18/S-3F4 ≥250 − − − Properties of core sets under power conditions (continued) B (mT) at GRADE CORE LOSS (W) at H = 250 A/m; f = 10 kHz; T = 100 °C f = 500 kHz; ˆ = 50 mT; B T = 100 °C f = 500 kHz; ˆ = 100 mT; B T = 100 °C f = 1 MHz; ˆ = 30 mT; B T = 100 °C f = 3 MHz; ˆ = 10 mT; B T = 100 °C E18/R+PLT18/S-3C90 ≥320 − − − − E18/R+PLT18/S-3C94 ≥320 − − − − E18/R+PLT18/S-3C96 ≥320 − − − − E18/R+PLT18/S-3F3 ≥300 − − − − E18/R+PLT18/S-3F35 ≥300 ≈0.34 ≈2.50 − − E18/R+PLT18/S-3F4 ≥250 − − ≤0.41 ≤0.66 1999 Dec 23 4 Philips Components Product specification Planar E cores E22/6/16/R MOUNTING PARTS General data and ordering information ITEM Clamp MATERIAL FIGURE stainless steel (CrNi) TYPE NUMBER 3 CLM-E22/PLT22 R 0.8 max. 5.25 min. olumns 21.4 9 2.5 16.3 min. handbook, halfpage 8.7 ±0.1 0.4 22.2 ±0.3 CBW179 2.8 min. CBW554 16.2 max. 22.4 min. 25.8 min. Dimensions in mm. Dimensions in mm. Fig.4 Fig.3 Clamp for E22/R+PLT22/S. 1999 Dec 23 5 Recommended PCB cut-out for clamped cores.