FERRITE CHIP INDUCTORS L2 SERIES 1. PART NO. EXPRESSION : L2-47NK-10 (a) Series code (a) (b) Inductance code : 47N = 0.047uH (b) (c) (d) (d) : 10 : RoHS Compliant 11 ~ 99 : Internal controlled number (c) Tolerance code : K = ±10%, M = ±20% 2. CONFIGURATION & DIMENSIONS : A D L H G B C PCB Pattern Unit:m/m A B C D 1.60±0.15 0.80±0.15 0.80±0.15 0.30±0.20 G H L 0.60 Ref. 0.80 Ref. 2.60 Ref. 3. SCHEMATIC : 4. MATERIALS : b a Ag(100%) Ni(100%)-1.5um(min.) Sn(100%)-3.0um(min.) (a) Body : Ferrite (b) Termination : Ag/Ni/Sn 5. GENERAL SPECIFICATION : a) Temp. rise : 30°C Max. b) Rated current : Base on temp. rise c) Storage temp. : -40°C to +85°C d) Operating temp. : -40°C to +85°C e) Resistance to solder heat : 260°C.10secs NOTE : Specifications subject to change without notice. Please check our website for latest information. 03.08.2010 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 1 FERRITE CHIP INDUCTORS L2 SERIES 6. ELECTRICAL CHARACTERISTICS : Part Number EIA Size Inductance ( µH ) Q Min. Test Frequency ( MHz ) SRF ( MHz ) Min. DC Resistance (ȍ) Max. L2-47N - 0603 0.047 10 50 260 0.30 50 L2-68N - 0603 0.068 10 50 250 0.30 50 L2-82N - 0603 0.082 10 50 245 0.30 50 L2-R10 - 0603 0.100 15 25 240 0.50 50 L2-R12 - 0603 0.120 15 25 205 0.50 50 L2-R15 - 0603 0.150 15 25 180 0.60 50 L2-R18 - 0603 0.180 15 25 165 0.60 50 L2-R22 - 0603 0.220 15 25 150 0.80 50 L2-R27 - 0603 0.270 15 25 136 0.80 50 L2-R33 - 0603 0.330 15 25 125 0.85 35 L2-R39 - 0603 0.390 15 25 110 1.00 35 L2-R47 - 0603 0.470 15 25 105 1.35 35 L2-R56 - 0603 0.560 15 25 95 1.55 35 L2-R68 - 0603 0.680 15 25 80 1.70 35 L2-R82 - 0603 0.820 15 25 75 2.10 35 L2-1R0 - 0603 1.000 30 10 70 0.60 25 L2-1R2 - 0603 1.200 30 10 60 0.80 25 L2-1R5 - 0603 1.500 30 10 55 0.80 25 L2-1R8 - 0603 1.800 30 10 50 0.95 25 L2-2R2 - 0603 2.200 30 10 45 1.15 15 L2-2R7 - 0603 2.700 30 10 40 1.35 15 L2-3R3 - 0603 3.300 30 10 38 1.55 15 L2-3R9 - 0603 3.900 30 10 36 1.70 15 Rated Current ( mA ) L2-4R7 - 0603 4.700 30 10 33 2.10 15 L2-5R6 - 0603 5.600 30 4 22 1.55 15 L2-6R8 - 0603 6.800 30 4 20 1.70 15 L2-8R2 - 0603 8.200 30 4 18 2.10 15 L2-100 - 0603 10.000 30 2 17 2.55 15 Packaging : Paper Carrier Tape ( 47N ~ 3R9 ) Embossed Carrier Tape ( 4R7 ~ 100 ) Inductance tolerance : : K : ±10% M : ±20% NOTE : Specifications subject to change without notice. Please check our website for latest information. 03.08.2010 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 2 FERRITE CHIP INDUCTORS L2 SERIES 7. IMPEDANCE VS. FREQUENCY CURVES : Q vs Freq. FCI1608-Series Q vs Freq. 120 Inductance(uH) 100 80 60 R10 1R5 1R0 40 4R7 100 20 0 1 10 100 DC Current(mA) L vs IDC FCI1608-Series L vs IDC. Inductance(uH) 100 100 10 4R7 1R2 1 R12 0.1 1 10 100 1000 DC Current(mA) NOTE : Specifications subject to change without notice. Please check our website for latest information. 03.08.2010 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 3 FERRITE CHIP INDUCTORS L2 SERIES 8. RELIABILITY & TEST CONDITION : ITEM PERFORMANCE TEST CONDITION Electrical Characteristics Test Impedance Refer to standard electrical characteristics list DC Resistance HP4291A, HP4287A+16092A HP4338B Rated Current Temperature Rise Test 30°C max. (ǻt) 1. Applied the allowed DC current. 2. Temperature measured by digital surface thermometer. Solder Heat Resistance No mechanical damage Remaining terminal electrode : 70% min. Preheat : 150°C, 60sec. Solder : Sn-Ag3.0-Cu0.5 Solder Temperature : 260±5°C Flux for lead free : rosin Dip Time : 10±0.5sec. Preheating Dipping 260°C 150°C Solderability 60 seconds Natural cooling 10±0.5 seconds Preheat : 150°C, 60sec. Solder : Sn-Ag3.0-Cu0.5 Solder Temperature : 245±5°C Flux for lead free : rosin Dip Time : 4±1sec. More than 90% of the terminal electrode should be covered with solder. Preheating Dipping 245°C 150°C Terminal Strength 60 seconds Natural cooling 4±1.0 seconds The terminal electrode & the dielectric must not be damaged by the forces applied on the right conditions. W W Flexture Strength The terminal electrode & the dielectric must not be damaged by the forces applied on the right conditions. For Z / L Series : Size Force (Kfg) 1 0.2 2 0.5 3 0.6 4 1.0 5 1.0 6 1.0 7 1.5 8 2.0 Time (sec) > 25 Solder a chip on a test substrate, bend the substrate by 2mm (0.079in) and return. 20(.787) Bending 45(1.772) 45(1.772) 40(1.575) 100(3.937) NOTE : Specifications subject to change without notice. Please check our website for latest information. 03.08.2010 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 4 FERRITE CHIP INDUCTORS L2 SERIES 8. RELIABILITY & TEST CONDITION : ITEM Bending Strength PERFORMANCE TEST CONDITION The ferrite should not be damaged by forces applied on the right condition. For Z / L Series : Series name mm (inches) P-Kgf 2 0.80 (0.033) 0.3 3 1.40 (0.055) 1.0 2.00 (0.079) 2.5 2.70 (0.106) 2.5 1.0(0.039) R0.5(0.02) 4 Chip 5 6 A 7 8 Random Vibration Test Appearance : Cracking, shipping & any other defects harmful to the characteristics should not be allowed. Frequency : 10-55-10Hz for 1 min. Amplitude : 1.52mm Directions & times : X, Y, Z directions for 2 hours. A period of 2 hours in each of 3 mutually perpendicular directions (Total 6 hours). Drop Drop 10 times on a concrete floor from a height of 75cm. No mechanical damage Loading at High Temperature Appearance : No damage. Inductance : Within ±10% of initial value. Q : Within ±30% of initial value. Temperature : 85±5°C Applied Current : rated current Duration : 1008±12hrs Measured at room temperature after placing for 2 to 3hrs. Humidity Humidity : 90~95% RH. Temperature : 40±2°C Duration : 1008±12hrs Measured at room temperature after placing for 2 to 3hrs. Appearance : No damage. Inductance : Within ±10% of initial value. Q : Within ±30% of initial value. Thermal Shock Low temperature storage test Drop Phase Temperature (°C) Times (min.) 1 -40±2°C 30±3 2 +85±5°C 30±3 Measured : 100 times Drop 10 times on a concrete floor from a height of 75cm. For L Series : Condition for 1 cycle Step1 : -40±2°C 30±3 min. Step2 : +85±5°C 30±3 min. Number of cycles : 100 Measured at room temperature after placing for 2 to 3hrs. Temperature : -55±2°C Duration : 1008±12hrs Measured at room temperature after placing for 2 to 3hrs. No mechanical damage Derating Derating Curve 6 Derated Current(A) For the ferrite chip bead which withstanding current over 1.5A, as the operating temperature over 85°C, the derating current information is necessary to consider with. For the detail derating of current, please refer to the Derated Current vs. Operating Temperature curve. 5 4 3 2 1 0 6A 5A 4A 3A 2A 1.5A 1A 85 125 OperatingTemperature(¢X Tem perature(°C) Operating C) NOTE : Specifications subject to change without notice. Please check our website for latest information. 03.08.2010 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 5 FERRITE CHIP INDUCTORS L2 SERIES 9. SOLDERING AND MOUNTING : 9-1. Recommended PC Board Pattern 2.60 0.80 0.60 PC board should be designed so that products are not sufficient under mechanical stress as warping the board. Products shall be positioned in the sideway direction against the mechanical stress to prevent failure. 9-2. Soldering Mildly activated rosin fluxes are preferred. The minimum amount of solder can lead to damage from the stresses caused by the difference in coefficients of expansion between solder, chip and substrate. The terminations are suitable for all wave and re-flow soldering systems. If hand soldering cannot be avoided, the preferred technique is the utilization of hot air soldering tools. 9-2.1 Lead Free Solder Re-flow : Recommended temperature profiles for re-flow soldering in Figure 1. 9-2.2 Solder Wave : Wave soldering is perhaps the most rigorous of surface mount soldering processes due to the steep rise in temperature seen by the circuit when immersed in the molten solder wave, typical at 230°C. Due to the risk of thermal damage to products, wave soldering of large size products is discouraged. Recommended temperature profile for wave soldering is shown in Fig. 2 9-2.3 Soldering Iron (Figure 3) : Products attachment with soldering iron is discouraged due to the inherent process control limitations. In the event that a soldering iron must be employed the following precautions are recommended. Note : d) 1.0mm tip diameter (max) a) Preheat circuit and products to 150°C. e) Use a 20 watt soldering iron with tip diameter of 1.0mm b) 350°C tip temperature (max) f) Limit soldering time to 3 secs. c) Never contact the ceramic with the iron tip Soldering Natural cooling Preheating TEMPERATURE °C TEMPERATURE °C Preheating 10s max. 250 ~ 260 230 180 150 60~120s 30~60s Time(sec.) Soldering Natural cooling 260 245 150 Gradual Cooling Over 2min. Figure 1. Re-flow Soldering Within 3s TEMPERATURE °C Preheating Soldering 3s (max.) 350 Natural cooling Figure 2. Wave Soldering 10s (max.) 330 150 Over 1min. Gradual Cooling Figure 3. Hand Soldering NOTE : Specifications subject to change without notice. Please check our website for latest information. 03.08.2010 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 6 FERRITE CHIP INDUCTORS L2 SERIES 9-3. Solder Volume Accordingly increasing the solder volume, the mechanical stress to product is also increased. Exceeding solder volume may cause the failure of mechanical or electrical performance. Solder shall be used not to be exceed as shown in Fig. 4. Upper limit t Recommendable Figure 4 NOTE : Specifications subject to change without notice. Please check our website for latest information. 03.08.2010 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 7 FERRITE CHIP INDUCTORS L2 SERIES 10. PACKAGING INFORMATION : 10-1. Reel Dimension Type A(mm) B(mm) C(mm) D(mm) 7" x 8mm 9.0±0.5 60.0±2.0 13.5±0.5 178.0±2.0 7" x 12mm 13.5±0.5 60.0±2.0 13.5±0.5 178.0±2.0 C D B A 2±0.5 13.5±0.5 7" x 8mm 7" x 12mm R10.5 R1.9 R0.5 120° 10-2 Tape Dimension / 8mm Material : Paper D:1.56 +0.1 -0.05 t Bo Series Z/L Bo(mm) Ao(mm) Ko(mm) P(mm) t(mm) D1(mm) 1 1.12±0.03 0.62±0.03 0.60±0.03 2.0±0.1 0.60±0.03 none 2 1.85±0.05 1.05±0.05 0.95±0.05 4.0±0.1 0.95±0.05 none 3(09) 2.30±0.05 1.50±0.05 0.95±0.05 4.0±0.1 0.95±0.05 none Size Bo(mm) Ao(mm) Ko(mm) P(mm) t(mm) D1(mm) 2 1.95±0.10 1.05±0.10 1.05±0.10 4.0±0.1 0.23±0.05 none 3(09) 2.25±0.10 1.42±0.10 1.04±0.10 4.0±0.1 0.22±0.05 1.0±0.1 3(12) 2.35±0.10 1.50±0.10 1.45±0.10 4.0±0.1 0.22±0.05 1.0±0.1 Size Ko Ao P W:8.0±0.1 E:1.75±0.1 Po:4±0.1 F:3.5±0.1 P2:2±0.1 Material : Plastic D:1.5+0.1 Po:4±0.1 t Series P Ao A D1:1±0.1 Bo W:8.0±0.1 A F:3.5±0.05 E:1.75±0.1 P2:2±0.05 Z/L Ko 4 3.50±0.10 1.88±0.10 1.27±0.10 4.0±0.1 0.22±0.05 1.0±0.1 Section A-A 5 3.42±0.10 2.77±0.10 1.55±0.10 4.0±0.1 0.22±0.05 1.0±0.1 Size Bo(mm) Ao(mm) Ko(mm) P(mm) t(mm) D1(mm) 6 4.95±0.1 1.93±0.1 1.93±0.1 4.0±0.1 0.24±0.05 1.5±0.1 7 4.95±0.1 3.66±0.1 1.85±0.1 8.0±0.1 0.24±0.05 1.5±0.1 8 6.10±0.1 5.40±0.1 2.00±0.1 8.0±0.1 0.30±0.05 1.5±0.1 10-2.1 Tape Dimension / 12mm Po:4±0.1 P2:2±0.05 t A A D1:1.5±0.1 P Ao Bo W:12.0±0.1 Series F:5.5±0.05 E:1.75±0.1 D:1.5+0.1 Z/L Ko Section A-A NOTE : Specifications subject to change without notice. Please check our website for latest information. 03.08.2010 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 8 FERRITE CHIP INDUCTORS L2 SERIES 10-3. Packaging Quantity Chip Size 8 7 6 5 4 3 (12) 3 (09) 2 1 Chip / Reel 1000 1000 2000 2500 3000 2000 4000 4000 10000 Inner Box 4000 4000 8000 12500 15000 10000 20000 20000 50000 Middle Box 20000 20000 40000 62500 75000 50000 100000 100000 250000 Carton 40000 40000 80000 125000 150000 100000 200000 200000 500000 Bulk (Bags) 7000 12000 20000 30000 50000 100000 150000 200000 300000 10-4. Tearing Off Force The force for tearing off cover tape is 15 to 60 grams in the arrow direction under the following conditions. F 165° to 180° Top cover tape Room Temp. (°C) Room Humidity (%) Room atm (hPa) Tearing Speed (mm/min) 5~35 45~85 860~1060 300 Base tape Application Notice 1. Storage Conditions : To maintain the solderabililty of terminal electrodes : a) Temperature and humidity conditions : -10 ~ 40°C and 30 ~ 70% RH. b) Recommended products should be used within 6 months from the time of delivery. c) The packaging material should be kept where no chlorine or sulfur exists in the air. 2. Transportation : a) Products should be handled with care to avoid damage or contamination from perspiration and skin oils. b) The use of tweezers or vacuum pick up is strongly recommended for individual components. c) Bulk handling should ensure that abrasion and mechanical shock are minimized. NOTE : Specifications subject to change without notice. Please check our website for latest information. 03.08.2010 SUPERWORLD ELECTRONICS (S) PTE LTD PG. 9