Reliability Test Report Report No: W124017 TLL Pages:1 Purpose: ▓QUALIFICATION □ON-GOING RELIABILITY □OTHERS: 尼爾材料評估驗證 Test Item High Temp Reverse Bias Test Product tested 10T08A-BW Epoxy Molding Compound □1100S □1200S ▓Other Test Condition 125 ℃ /640V / 168hrs Lot No: N/A Test Standard Molding Package MIL-STD-750D METHOD 1038.3 Q’TY Tested 5 pcs Ambient Conditions Temp.:25 ℃;RH:58% Test TO-220AB Test Criteria See Table below Test Equipment PTI6000 Diode Tester Date tested 2012.4,5 Initial Reading conditionsIGT1(mA) No Of & Spec 20 IGT2(mA) IGT3(mA) VGT1(V) VGT2(V) VGT3(V) 30 30 1.35 1 1 IH1(mA) IH2(mA) 40 40 IH3(mA) 40 Test SampleVD=12V VD=12V VD=12V VD=12V VD=12V VD=12V 1 14.30 14.40 15.20 1.27 0.72 0.79 32.00 32.00 28.60 2 15.20 15.30 15.30 1.26 0.72 0.79 30.70 30.80 27.70 3 15.20 15.90 15.90 1.24 0.72 0.79 32.00 32.10 28.40 4 14.50 14.60 15.40 1.29 0.72 0.79 24.80 30.40 26.70 5 15.90 15.10 16.60 1.26 0.72 0.80 31.00 32.50 28.40 Fail/Sample Size 0/5 0/5 0/5 0/5 0/5 0/5 0/5 0/5 0/5 MAX. 15.90 15.90 16.60 1.29 0.72 0.80 32.00 32.50 28.60 MIN. 14.30 14.40 15.20 1.24 0.72 0.79 24.80 30.40 26.70 AVG. 15.02 15.06 15.68 1.26 0.72 0.79 30.10 31.56 27.96 ST. DEV. 0.638 0.594 0.581 0.018 0.002 0.002 3.020 0.907 0.783 Cpk 0.187 0.166 0.178 0.000 0.000 0.000 1.913 0.284 0.167 HTIR(High Temp IR) : Test result is attached. Judgement Standard :1.Per Y3P005 GPP Finished Good product spec. 2.Data shifting criteria degradation: (1)Refer to Y21002 IT=100mA IT=100mA : ▓ACC Final Result IT=100mA IL1(mA) IL2(mA) IL3(mA) 70 120 50 IG=1.2IGT IG=1.2IGT IG=1.2IGT 38.00 38.20 39.00 37.00 37.90 0/5 39.00 37.00 38.02 0.716 0.234 72.80 70.20 71.60 70.30 70.80 0/5 72.80 70.20 71.14 1.081 0.598 29.90 28.90 29.70 27.90 30.00 0/5 30.00 27.90 29.28 0.884 0.212 IDRM(uA) IRRM(uA) VTM1(V) VTM3(V) 5 5 1.35 1.35 VAK=800VVAK=800V ITM=16A ITM=16A 0.21 0.19 0.19 0.17 0.15 0/5 0.212 0.154 0.182 0.022 0.000 0.31 0.40 0.38 0.35 0.26 0/5 0.395 0.255 0.337 0.056 0.001 1.25 1.25 1.25 1.25 1.25 0/5 1.251 1.247 1.249 0.002 0.000 REJ. Approved by: Smart Kao Tested by:REX 1.24 1.24 1.24 1.34 1.24 0/5 1.338 1.235 1.257 0.046 0.001