ZTT5.00MT Ceramic Resonator 1 SCOPE This specification shall cover the characteristics of the ceramic resonator with the type ZTT5.00MT. 2 PART NO PART NUMBER CUSTOMER PART NO SPECIFICATION NO ZTT5.00MT 3 OUTLINE DRAWING AND DIMENSIONS 3.1 Appearance: No visible damage and dirt. 3.2 Construction: Leads are soldered on electrode and body is molded by resin. 3.3 Except the chip(ceramic element, ceramic base, capacitance slice), the materials don’t contain lead. 3.4 Dimensions Input Ground Output http://www.luguang.cn mail:[email protected] ZTT5.00MT Ceramic Resonator 4 RATING AND ELECTRICAL SPECIFICATIONS 4.1 RATING Items Withstanding Voltage (V) Insulation Resistance Ri, M min. Operating Temperature Range ( Storage Temperature Range ( ) ) 4.2 ELECTRICAL SPECIFICATIONS Items Oscillation Frequency Fosc MHz Frequency Accuracy % Resonant Impedance Ro Ω max. Temperature Coefficient of Oscillation Frequency % max. Rating Voltage UR Aging Rate % V max. max. Content 50 (DC 1min) 100 100V 1min -20 +80 -40 +85 Content 5.000 0.5 25 0.3 Oscillation Frequency drift -20 +80 6V DC 15V p-p 0.3 For Ten Years 5 MEASUREMENT 5.1 Measurement Conditions: Parts shall be measured under a condition ( Temp. 20±15 ,Humidity 65±20% R.H.) unless the standard condition(Temp. 25±3 ,Humidity 65±5% R.H.) is regulated to measure. 5.2 Test Circuit IC 1/6TC4069UBP×2 X CERAMIC RESONATOR http://www.luguang.cn mail:[email protected] ZTT5.00MT Ceramic Resonator 6 PHYSICAL AND ENVIRONMENTAL CHARACTERISTICS No. 6.1 6.2 6.3 6.4 6.5 6.6 6.7 6.8 Item Humidity High Temperature Exposure Low Temperature Exposure Condition of Test Subject the resonator at +40 2 and 90%-95% R.H. for 500h, resonator shall be measured after being placed in natural conditions for 1h. Subject the resonator to +85 5 for 500h, resonator shall be measured after being placed in natural conditions for 1hr. Performance Requirements It shall fulfill the specifications in Table 1. It shall fulfill the specifications in Table 1. Subject the resonator to –25 5 for It shall fulfill the 500h, resonator shall be measured after being specifications in placed in natural conditions for 1h. Table 1. Subject the resonator to 25 for 30 min. It shall fulfill the followed by a high temperature of 85 Temperature for 30 min. Cycling shall be repeated 5 times. specifications in Cycling Resonator shall be measured after being Table 1. placed in natural conditions for 1h. Subject the resonator to vibration for 2h each in x y and z axis with the amplitude of It shall fulfill the 1.5mm, the frequency shall be varied specifications in Vibration uniformly between the limits of 10Hz-55Hz Table 1. and then resonator shall be measured. No visible Resonator shall be measured after 3 times' damage and it Mechanical random dropping from the height of 100cm shall fulfill the Shock on concrete floor. specifications in Table 1. Lead terminals are immersed up to 2 mm Resistance to from resonator’s body in soldering bath of It shall fulfill the 260 5 for 5s 1s and then resonator specifications in Soldering shall be measured after being placed in Table 1. Heat natural conditions for 1h More than 95% of the terminal Lead terminals are immersed up to 2mm from surface of the Solderability resonator’s body in soldering bath of 250 resonator shall be 5 for 2s 0.5s. covered with fresh solder. (To be continued) http://www.luguang.cn mail:[email protected] ZTT5.00MT Ceramic Resonator 6. PHYSICAL AND ENVIRONMENTAL CHARACTERISTICS No. Item Terminal Strength 6.9.1 Terminal Pulling 6.9.2 Terminal Bending Performance Requirements Condition of Test 6.9 Force of 5N is applied to each lead in axial direction for 10s 1s. When force of 5N is applied to each lead in axial direction,the lead shall folded up 90 from the axial direction and folded back to the axial direction. The speed of folding shall be each 3s. No visible damage and it shall fulfill the specifications in Table 1. Table 1 Item Specification after test Oscillation Frequency Change fosc/fosc Resonant Impedance (%) max Ro max 0.3 25 Note:The limits in the above table are referenced to the initial measurements. http://www.luguang.cn mail:[email protected] ZTT5.00MT Ceramic Resonator 7 PACKAGE To protect the products in storage and transportation it is necessary to pack them outer and inner package .On paper pack, the following requirements are requested. 7.1 Dimensions and Mark At the end of package, the warning (moisture proof, upward put) should be stick to it. Dimensions and Mark (see below) NO. Name 1 Inner Quantity Box Notes 40 2 Box 2 3 Package 1 4 Adhesive tape 1.2m 5 Label 1 6 Belt 2.9m 7 Certificate of approval 1 7.2 Section of package Package is made of corrugated paper with thickness of 0.8cm.Package has 2 inner boxes, each has 20 inner box (each box http://www.luguang.cn for plastic bag). mail:[email protected] ZTT5.00MT Ceramic Resonator 7.3 Quantity of package Per plastic bag 500 pieces Per inner box 2 plastic bag Per package 40 inner boxes 40000 pieces of piezoelectric ceramic part 7.4 Inner box Dimensions 1.UNIT: mm 1 Label 2 QC Label 3 Inner Box Pars shall be packaged in box with hold down tape upside. Part No., quantity and lot No. http://www.luguang.cn mail:[email protected] ZTT5.00MT Ceramic Resonator 8 OTHER 8.1 Caution of use 8.1.1 Do not use this product with bend. Please don’t apply excess mechanical stress to the component and terminals at soldering. 8.1.2 The component may be damaged when an excess stress will be applied. 8.1.3 This specification mentions the quality of the component as a single unit. Please insure the component is thoroughly evaluated in your application circuit. 8.2 Notice 8.2.1 Please return one of this specification after your signature of acceptance. 8.2.2 When something gets doubtful with this specifications, we shall jointly work to get an agreement. http://www.luguang.cn mail:[email protected]